Abstract
A Ruys, School of Aerospace, Mechanical and Mechatronic Engineering, University of Sydney, Sydney
The effects of bone anabolics can be maximised by systemic co-treatment with an anti-catabolic. Local treatment may reduce the total drug required and produce superior outcomes, although high dose local bisphosphonate has been reported to impair bone formation. We have explored local co-delivery of anabolic/anti- catabolic bone drugs at different doses.
We manufactured biodegradable poly-D,L-lactic acid (PDLLA) polymer pellets containing 25g BMP-7 as an anabolic with or without 0.002mg-2mg Pamidronate (PAM) as an anti-catabolic. Polymer pellets were surgically implanted into the hind limb muscle of female C57BL6 mice. Animals were sacrificed at three weeks post- implantation and bone formation was assessed by radiography, microcomputed tomography (microCT) and histology. Histological staining on five Âm paraffin sections included haematoxylin/eosin, alcian blue/picrosirius red, and tartrate- resistant acid phosphatase (TRAP).
Radiographic and microCT data confirmed that 0.02mg and 0.2mg local PAM doses significantly augmented BMP-7 induced bone formation. In contrast, 2mg local PAM dramatically reduced the amount of bone present. This dose was comparable to that used by Choi et al who also reported impaired bone formation in a skull defect model.2 three-dimensional microCT and histological analyses of the ectopic bone and surrounding muscle showed a cortical shell covering the polymer pellet, which had not completely resorbed.
Histological analysis at the pellet/bone interface showed tissue granulation and no inflammation, suggesting a high biocompatibility of the PDLLA polymer. The presence of bisphosphonate also decreased the amount of fatty marrow tissue seen within between the cortical shell and the unresorbed polymer.
For the first time we can demonstrate synergy with local BMP/bisphosphonate. This study confirms that high local PAM doses can have negative effects, indicating a need to avoid overdosing. The lack of implant degradation suggests a need to optimise polymer degradation for bone tissue engineering application.