Abstract
This prospective randomised controlled trial aims to compare the clinical and radiological outcomes of ceramic on ceramic, cobalt chrome on ultra-high molecular weight polyethylene, and cobalt chrome on highly cross-linked polyethylene bearing surfaces at a minimum of five years.
One hundred and two primary total hip replacements were performed in ninety one patients between February 2003 and March 2005. All patients were younger than 65 (mean 52.7, 19–64). They were randomised to receive one of the three bearing surfaces. All patients had 28mm articulations with a Reflection uncemented acetabular component and a Synergy stem (Smith & Nephew, Memphis, Tennessee). Patients were followed up periodically up to at least sixty months following surgery. Outcome measures included WOMAC and SF12 scores. Radiological assessment included implant position, evidence of osteolysis and measurement of linear wear.
Ninety seven hip replacements in eighty seven patients were available for review at a minimum of five years. Two hips were revised (one for infection and one for periprosthetic fracture), leaving a total of ninety four hips available for final review. There were no differences in age, gender, body mass index, diagnosis, level of activity, and co-morbidities between the three groups. At a minimum of five years there were no statistical differences in the clinical outcomes using the WOMAC or SF12 scores. Three patients in the ceramic group reported squeaking. Radiological evaluation revealed mean annual wear rates in the ceramic group of 0.006mm/yr, standard polyethylene of 0.151mm/yr and highly cross linked polyethylene of 0.059mm/yr. ANOVA analysis revealed these differences in wear rates to be significant (p<0.0001).
In the mid term there are no differences in clinical outcome between ceramic on ceramic, cobalt chrome on ultra-high molecular weight polyethylene, and cobalt chrome on highly cross-linked polyethylene bearing surfaces in total hip arthroplasty. Ultra high molecular weight polyethylene has a significantly greater annual linear wear rate than highly cross-linked polyethylene.