Abstract
Bone is a dynamic tissue that undergoes continuous mechanical forces. Mechanical stimuli applied on scaffolds resembling a part of the human bone tissue affects the osteogenesis [1]. Poly(3,4-ethylenedioxythiophene) (PEDOT) is a piezoelectric material that responds to mechanical stimulation producing an electrical signal, which in turn promotes the osteogenic differentiation of bone-forming cells by opening voltage-gated calcium channels [2]. In this study we examined the biological behavior of pre-osteoblastic cells seeded onto lyophilized piezoelectric PEDOT-containing scaffolds applying uniaxial compression.
Two different concentrations of PEDOT (0.10 and 0.15% w/v) were combined with a 5% w/v poly(vinyl alcohol) (PVA) and 5% w/v gelatin, casted into wells, freeze dried and crosslinked with 2% v/v (3-glycidyloxypropyl)trimethoxysilane and 0.025% w/v glutaraldehyde. The scaffolds were physicochemically characterized by FTIR, measurement of the elastic modulus, swelling ratio and degradation rate. The cell-loaded scaffolds were subjected to uniaxial compression with a frequency of 1 Hz and a strain of 10% for 1 h every second day for 21 days. The loading parameters were selected to resemble the in vivo loading situation [3]. Cell viability and morphology on the PEDOT/PVA/gelatin scaffolds was determined. The alkaline phosphatase (ALP) activity, the collagen and calcium production were determined.
The elastic modulus of PEDOT/PVA/gelatin scaffolds ranged between 1 and 5 MPa. The degradation rate indicates a mass loss of 15% after 21 days. The cell viability assessment displays excellent biocompatibility, while SEM images display well-spread cells. The ALP activity at days 3, 7 and 18 as well as the calcium production are higher in the dynamic culture compared to the static one. Moreover, energy dispersive spectroscopy analysis revealed the presence of calcium phosphate in the extracellular matrix after 14 days. The results demonstrate that PEDOT/PVA/gelatin scaffolds promote the adhesion, proliferation, and osteogenic differentiation of pre-osteoblastic cells under mechanical stimulation, thus favoring bone regeneration.