Abstract
Introduction
Distal triceps tendon rupture is related to high complication rates with up to 25% failures. Elbow stiffness is another severe complication, as the traditional approach considers prolonged immobilization to ensure tendon healing. Recently a dynamic high-strength suture tape was designed, implementing a silicone-infused core for braid shortening and preventing repair elongation during mobilization, thus maintaining constant tissue approximation. The aim of this study was to biomechanically compare the novel dynamic tape versus a conventional high-strength suture tape in a human cadaveric distal triceps tendon rupture repair model.
Method
Sixteen paired arms from eight donors were used. Distal triceps tendon rupture tenotomies and repairs were performed via the crossed transosseous locking Krackow stitch technique for anatomic footprint repair using either conventional suture tape (ST) or novel dynamic tape (DT). A postoperative protocol mimicking intense early rehabilitation was simulated, by a 9-day, 300-cycle daily mobilization under 120N pulling force followed by a final destructive test.
Result
Significant differences were identified between the groups regarding the temporal progression of the displacement in the distal, intermediate, and proximal tendon aspects, p<0.001. DT demonstrated significantly less displacement compared to ST (4.6±1.2mm versus 7.8±2.1mm) and higher load to failure (637±113N versus 341±230N), p≤0.037. DT retracted 0.95±1.95mm after each 24-hour rest period and withstood the whole cyclic loading sequence without failure. In contrast, ST failed early in three specimens.
Conclusion
From a biomechanical perspective, DT revealed lower tendon displacement and greater resistance in load to failure over ST during simulated daily mobilization, suggesting its potential for earlier elbow mobilization and prevention of postoperative elbow stiffness.