Abstract
Introduction
The main postoperative complications in fixation of ulna shaft fractures are non-union and implant irritation using currently recommended 3.5-mm locking compression plates. An alternative approach using a combination of two smaller plates in orthogonal configuration has been proposed. The aim of this study was to compare the biomechanical properties of a single 3.5-mm locking compression plate versus double plating using one 2.5-mm and one 2.0-mm mandible plate in a human ulna shaft fracture model.
Method
Eight pairs human ulnar specimens with a standardized 10-mm fracture gap were pairwise assigned for instrumentation with either a single 3.5-mm plate placed posteriorly, or for double plating using a 2.5-mm and a 2.0-mm mandible plate placed posteriorly under the flexor muscles and laterally under the extensor muscles. All constructs were initially non-destructively biomechanically tested in axial compression, torsion, and bending, which was followed by cyclic torsional loading to failure. Interfragmentary movements were monitored by means of optical motion tracking.
Result
There were no significant differences between the two plating techniques for axial stiffness (p=0.335), torsional stiffness in supination (p=0.462), torsional stiffness in pronation (p=0.307), medio-lateral bending stiffness (p=0.522), and antero-posterior bending stiffness (p=0.143). During cyclic torsional loading over the first 3000 cycles, there were no significant differences between the two plating techniques for shear displacement across the fracture gap, p=0.324. The numbers of cycles until clinically relevant failure of 5° angular deformation were 1366±685 for double plating and 2024±958 for single plating, which was statistically non-significantly different, p>0.05. The constructs treated with both plating techniques failed due to bone breakage at the most distal screw.
Conclusion
From a biomechanical perspective double plating of ulna shaft fractures using a 2.5-mm and a 2.0-mm locking mandible plate demonstrated equivalent fixation strength as conventional plating using a single 3.5-mm locking compression plate.