Abstract
Osteosarcoma and other types of bone cancers often require bone resection, and backfill with cement. A novel silorane-based cement without PMMA's drawbacks, previously developed for dental applications, has been reformulated for orthopedic use. The aim of this study is to assess each cement's ability to elute doxorubicin, maintain its potency, and maintain suitable weight-bearing strength.
The silorane-based epoxy cement was synthesized using a platinum-based Lamoreaux's catalyst. Four groups of cement were prepared. Two PMMA groups, one without any additives, one with 200 mg of doxorubicin. Two silorane groups: one without any additive, one with doxorubicin, added so that the w% of drug into both cements were equal. Pellets 6 × 12 mm were used for testing (ASTM F451). n=10. Ten pellets from each group were kept dry. All others were placed into tubes containing 2.5 mL of PBS and stored at 37 °C. Elution from doxorubicin-containing groups were collected every day for 7 days, with daily PBS changeout. Antibiotic concentrations were determined via HPLC. Compressive strength and compressive modulus of all groups were determined for unsoaked specimens, and those soaked for 7 and 14 days. MTT assays were done using an MG63 osteosarcoma cell line.
Both cements were able to elute doxorubicin over 7 days in clinically-favorable quantities. For PMMA samples, the incorporation of doxorubicin was shown to significantly affect the compressive strength and modulus of the samples (p<0.01). Incorporation of doxorubicin into silorane had no significant effect on either (p>.05). MTT assays indicated that doxorubicin incorporated into the silorane cement maintained its effectiveness whereas that into PMMA did not. At the dosing used, both cements remained above the 70 MPa.
Both PMMA and silorane-based cements can deliver doxorubicin. Doxorubicin, however, interacts chemically with PMMA, inhibiting polymerization and lowering the chemotherapeutic's effectiveness.