Abstract
The goal was to analyze the cellular response, specifically the osteogenic capacity, of titanium (Ti) implants harbouring a novel laserbased-surface-structure with the overall aim: augmented osteointegration. Surface micro-/nanoproperties greatly influence cell behaviour at the tissue-implant-interface and subsequent osteointegration. We investigated Ti-materials subjected to a specially developed shifted-Laser-Surface-Texturing (sLST) technology and compared them to a standard roughening-technique (sand-blasting-acid-etching, SLA). The biological response was evaluated with hMSCs, which are naturally available at the bone-implant-interface. We hypothesized: the novel surface is beneficial for our three different (young/healthy-YH; aged/healthy-AH;aged/osteoporotic-OP) cohorts.
The sLST was performed using a SPI-G3-series laser (beam-wavelength=1064nm, pulse-duration=200ns). For the SLA surface, Ti was sandblasted, afterwards acid-etched (HCl/H2SO4). Three different hMSC cohorts were studied: YH: n=6,29±6; AH: n=5,79±5; OP: n=5,76±5 years (osteoporosis confirmed via DEXA-scan). OP hMSCs show e.g. ColI-deficient-matrix and decreased mineralization. Cells were examined for survival, cell proliferation and cytoskeleton arrangement. Osteogenic differentiation was carried out over 21 days, matrix mineralization was validated with Alizarin-Red-S-staining and quantification.
Laser-texturing generated precisely the desired microgeometry. On nanostructural level, differently-sized Ti-droplets were formed stochastically by laser-induced-Ti-plasma. Live/dead-/Actin-stainings showed comparable results for all cohorts and surfaces in terms of survival and cell shape. On Ti-materials, cell growth showed no significant difference between the 3 cohorts. Alizarin quantification revealed the highest levels on laser-textured-surfaces; highest value for YH, followed by AH, lastly OP; no significance between AH/YH, but between OP/YH (p<0.0001). However, mineralization of all cohorts cultured on laser-textured-surfaces increased significantly (p<0.0001) compared to respective SLA-group, with >20fold higher value in the OP-cohort (AH:11fold, YH:6fold).
The data proves the biocompatibility of the laser-structured-Ti for young+aged cohorts. Osteogenic differentiation was significantly augmented on laser-treated-Ti. Most intriguingly, OP-donors could reach manifold increased mineralization, suggesting the novel laser texturing can counteract the osteoporotic phenotype. As osteogenesis-enhancing capacities may be related to mechanisms controlling cellular shape/fate, further investigations referring to this are currently ongoing. In conclusion, our laser-textured-Ti-materials are safe, can have a demand-oriented designer-surface-topography and represent a great potential for development into next-generation-implants suitable for different patient-cohorts, especially osteoporosis patients.