Abstract
Currently, fibrin glue obtained from fibrinogen and thrombin of human and animal blood are widely investigated to use as injectable hydrogel for tissue engineering which contributes to minimally invasive surgery, superior biodegradability, cell attachment, proliferation and regenerating new tissue. However, most of them fail to achieve to be used for tissue engineering application because of a risk of immune response and poor mechanical properties. To overcome the limitation of fibrin glue and to reduce the usage of products from human and animal blood, the artificial fibrin glue materials were developed. Recently, cellulose nanofiber (CNF) as reinforcing agent has been explored for many tissue engineering applications such as bone and cartilage due to its impressive biological compatibility, biodegradability and mechanical properties. CNF was extracted from cassava pulp. PEO-PPO-PEO diacrylate block copolymer is a biodegradable synthetic polymers which is water insoluble hydrogel after curing by UV light at low intensity. To enhance the cell adhesion abilities, gelatin methacrylate (GelMA), the denature form of collagen was used to incorporate into hydrogel. The aim of this study was to develop the artificial fibrin glue from CNF reinforced PEO-PPO-PEO diacrylate block copolymer/GelMA injectable hydrogel.
CNF/PEO-PPO-PEO diacrylate block copolymer/GelMA injectable hydrogels were prepared with 2-hydroxy-1-(4-(hydroxy ethoxy) phenyl)-2-methyl-1-propanone (Irgacure 2959) as a photoinitiator. The physicochemical properties were investigated by measuring various properties such as thickness, gel fraction, mechanical properties and water uptake.
At optimal preparation condition, CNF reinforced injectable hydrogel was successful prepared after curing with UV light within 7 minutes. This hydrogel showed gel fraction and water uptake of 81 and 85%, respectively. The cytotoxicity, cell adhesion and proliferation of CNF reinforced injectable hydrogel was presented.
Cellulose nanofiber from casava pulp was successfully used to prepare injectable hydrogel as artificial fibrin glue for tissue engineering. The hydrogel showed good physical properties which can be applied to use for tissue engineering application.