Abstract
Decellularised porcine superflexor tendon (pSFT) has been demonstrated to be a suitable scaffold for anterior cruciate ligament reconstruction[1]. While the role of collagen in tendons is well known, the mechanical role of glycosaminoglycans (GAGs) is less clear and may be altered by the decellularisation process.
To determine the effects of decellularisation on pSFT GAG content and mechanical function and to investigate the consequences of GAG loss in tensile and compressive loading.
pSFTs were decellularised following previous techniques [2]. For GAG removal, native pSFTs were treated with chondroitinase ABC (ChABC; 0.1U/mL, 72h). Cell and GAG removal was validated using histology and quantitative assays. Native, decellularised and ChABC treated groups (n=6) were biomechanically characterised. In tension, specimens underwent stress relaxation and strength testing using previous protocols [1]. Stress relaxation data was fitted to a modified Maxwell-Weichert model to determine time-dependent (E1 & E2) and time-independent moduli (E0). The toe and linear region moduli (Etoe, Elinear), in addition to tensile strength (UTS) and failure strain were determined from strength testing. In compression, specimens underwent confined loading conditions (ramp at 10 s-1 to 10% strain and hold). The aggregate modulus (HA) and zero-strain permeability (k0) were determined using previous techniques [3]. Data was analysed by one-way ANOVA with Tukey post-hoc test to determine significant differences between test groups (p<0.05).
Quantitative assays showed no GAG reduction post-decellularisation, but a significant reduction after ChABC treatment. HA was only significantly reduced in the ChABC group. k0 was significantly higher for the ChABC group compared to decellularised. E0 was significantly reduced in the decellularised group compared to native and ChABC groups, while E1 and E2 were not different between groups. Etoe, Elinear, UTS and failure strain were not different between groups.
Decellularisation does not affect GAG content or impair mechanical function in pSFT. GAG loss adversely affects pSFT compressive properties, revealing major mechanical contribution under compression, but no significant role under tension.