Abstract
Critical-sized bone defects can result from trauma, inflammation, and tumor resection. Such bone defects, often have irregular shapes, resulting in the need for new technologies to produce suitable implants. Bioprinting is an additive manufacturing method to create complex and individualised bone constructs, which can already include vital cells.
In this study, we established an extrusion-based printing technology to produce osteoinductive scaffolds based on polycaprolactone (PCL) combined with calcium phosphate, which is known to induce osteogenic differentiation of stem cells.
The model was created in python based on the signed distance functions. The shape of the 3D model is a ring with a diameter of 20 mm and a height of 10 mm with a spongiosa-like structure. The interconnected irregular pores have a diameter of 2 mm +/− 0.2 mm standard deviation.
Extrusion-based printing was performed using the BIO X6. To produce the bioink, PCL (80 kDa) was combined with calcium phosphate nanopowder (> 150 nm particle size) under heating. After printing, 5 × 106 hMSC were seeded on the construct using a rotating incubator.
We were able to print a highly accurate ring construct with an interconnected pore structure. The PCL combined with calcium phosphate particles resulted in a precise printed construct, which corresponded to the 3D model. The bioink containing calcium phosphate nanoparticles had a higher printing accuracy compared to PCL alone. We found that hMSC cultured on the construct settled in close proximity to the calcium phosphate particles. The hMSC were vital for 22 days on the construct as demonstrated by life/dead staining.
The extrusion printing technology enables to print a mechanically stable construct with a spongiosa-like structure. The porous PCL ring could serve as an outer matrix for implants, providing the construct the stability of natural bone. To extend this technology and to improve the implant properties, a biologised inner structure will be integrated into the scaffold in the future.