The objective of this study was to investigate how a new customizable light-curable osteosynthesis method (AdFix) compared to traditional metal hardware when loaded in torsion in an ovine phalanx model.
Twenty-one ovine proximal phalanges were given a 3mm transverse osteotomy and four 1.5mm cortex screws were inserted bicortically on either side of the gap. The light-curable polymer composite was then applied using the method developed by Hutchinson [1] to create osteosyntheses in two groups, having either a narrow (6mm, N=9) or a wide (10mm, N=9) fixation patch. A final group (N=3) was fixated with conventional metal plates. The constructs were loaded in torsion at a rate of 6°/second until failure or 45° of rotation was reached. Torque and angular displacement were measured, torsional stiffness was calculated as the slope of the Torque-Displacement curve, and maximum torque was queried for each specimen.
The torsional stiffnesses of the narrow, wide, and metal plate constructs were 39.1 ± 6.2, 54.4 ± 6.3, and 16.2 ± 3.0 Nmm/° respectively. All groups were statistically different from each other (p<0.001). The maximum torques of the narrow, wide, and metal plate constructs were 424 ± 72, 600 ± 120, and 579 ± 20 Nmm respectively. The narrow constructs were statistically different from the other two (p<0.05), while the wide and metal constructs were not statistically different from each other (p=0.76).
This work demonstrated that the torsional performance of the novel solution is comparable to metal fixators. As a measure of the functional range, the torsional stiffness in the AdhFix exceeded that of the metal plate. Furthermore, the wide patches were able to sustain a similar maximum toque as the metal plates. These results suggest AdhFix to be a viable, customizable alternative to metal implants for fracture fixation in the hand.