Abstract
This study aims to assess the changes in mechanical behaviour over time in ‘haemarthritic’ articular cartilage compared to ‘healthy’ articular cartilage.
Pin-on-plate and indentation tests were used to determine the coefficient of friction (COF) and deformation of ‘healthy’ and ‘haemarthritic articular cartilage. Osteochondral pins (8 mm) were extracted from porcine tali and immersed in exposure fluid for two hours prior to test. Pins were articulated against a larger bovine femoral plate for 3600 seconds under a load of 50 N. Osteochondral pins (8 mm) were loaded during indentation testing for 3600 seconds under a load of 0.25 N. To mimic the effect of a joint bleed in vitro; serum, whole blood and 50% v/v were used as exposure and lubricant fluids. COF and deformation were expressed as mean (n=3) and statistically analysed using a one-way ANOVA and post-hoc Tukey test (p>0.05).
The serum condition yielded a COF of 0.0428 ± 0.02 with 0.08mm ± 0.04 deformation. The 50% v/v condition produced a higher COF of 0.0485 ± 0.02 and 0.21mm ± 0.04 deformation. The lowest COF and deformation were produced by the whole blood condition (0.0292 ± 0.02 and 0.06mm ± 0.006 respectively). Statistical analysis indicated no significant difference across the friction test conditions but a significant difference across all indentation test conditions (ANOVA, p>0.05). Combination of creep deformation and wear was observed on the articular surface up to 24 hours post-test in 50% v/v and whole blood conditions.
The average haemophilia patient can experience multiple joint bleeds per year of which this study demonstrates the effect of just one joint bleed. This study has provided evidence of potential reversible and irreversible mechanical changes to articular cartilage surface during a joint bleed.