Abstract
Reducing wear of endoprosthetic implants is still an important goal in order to increase the life time of the implant. Endoprosthesis failure can be caused by many different mechanisms, such as abrasive wear, corrosion, fretting or foreign body reactions due to wear accumulation. Especially, modular junctions exhibit high wear rates and corrosion due to micromotions at the connection of the individual components. The wear generation of cobalt-chromium-molybdenum alloys (CoCrMo) is strongly influenced by the microstructure. Therefore, the aim of this work is to investigate the subsurface phase transformation by deep rolling manufacturing processes in combination with a “sub-zero” cooling strategy.
We analyzed the influence on the phase structure and the mechanical properties of wrought CoCr28Mo6 alloy (ISO 5832-12) by a deep rolling manufacturing process at various temperatures (+25°C,-10°C,-35°C) and different normal forces (700N and 1400N). Surface (Sa,Sz) and subsurface characteristics (residual stress) as well as biological behavior were investigated for a potential implant application.
We showed that the microstructure of CoCr28Mo6 wrought alloy changes depending on applied force and temperature. The face centered cubic (fcc) phase could be transformed to a harder hexagonal-close-packed (hcp) phase structure in the subsurface. The surface could be smoothed (up to Sa = 0.387 µm±0.185 µm) and hardened (≥ 700 HV 0.1) at the same time. The residual stress was increased by more than 600% (n=3). As a readout for metabolic activity of MonoMac (MM6) and osteosarcoma (SaOS-2) cells a WST assay (n=3) was used. The cells showed no significant negative effect of the sub-zero manufacturing process.
We showed that deep rolling in combination with an innovative cooling strategy for the manufacturing process has a great potential to improve the mechanical properties of CoCr28Mo6 wrought alloy, by subsurface hardening and phase transformation for implant applications.