Abstract
We have developed a decellularised porcine superflexor tendon (pSFT), which has shown promising regenerative capacity in an ovine model of anterior cruciate ligament (ACL) repair. This study investigated the strain rate dependent and dynamic mechanical properties of native and decellularised pSFTs.
Decellularisation was carried out using a previously established procedure, including antibiotic washes, low concentration detergent (0.1% sodium dodecyl sulphate) washes and nuclease treatments.
Three different strain rates were employed: 1, 10 & 100%s-1 (n=6 for all groups). Toe-region modulus (E0), linear-region modulus (E1), transition coordinates (εT, σT), tensile strength (UTS) and failure strain were calculated. For DMA, specimens were loaded between 1 & 5MPa with increasing frequency up to 2Hz. Dynamic (E*), storage (E') and loss (E'') moduli, and tan delta were calculated for native and decellularised groups (n=6). Data was analysed by 2-way ANOVA and Tukey post-hoc test (p<0.05).
For decellularised tendons, altering the strain rate did not affect any of the static tensile properties. For native pSFTs, the UTS, failure strain and E1 were not affected by changing the strain rate. Increasing the strain rate significantly increased E0 (1% vs 10% and 1% vs 100%) and σT (1% vs 100%) and decreased εT (1% vs 10% and 1% vs 100%) for native pSFT. E*, E' and E'' were all significantly reduced in decellularised specimens compared to native controls across all frequencies investigated. No significant differences were found for tan delta.
Evidence of strain rate dependency was witnessed in the native pSFTs by increase of the toe region modulus and displacements of the transition point coordinates. This response was not seen in the tissue following decellularisation. DMA demonstrated a reduction in dynamic, storage and loss moduli. Tan delta (E''/E') remained unchanged, indicating reductions in solid and fluid components are interlinked.