Abstract
Modular hip prostheses were introduced to optimize the intra-surgical adaptation of the implant design to the native anatomy und biomechanics of the hip. The downside of a modular implant design with an additional modular interface is the potential susceptibility to fretting, crevice corrosion and wear. For testing hip implants with proximal femoral modularity according to ISO & ASTM, sodium chloride solutions are frequently used to determine the fatigue strength and durability of the stem-neck connection. The present study illustrate that the expansion of standard requirements of biomechanical testing is necessary to simulate metal ion release as well as fretting and crevice corrosion by using alternative test fluids. To assess the primary stability of tibial plateaus in vitro, different approaches had been undergone: cement penetration depth analysis, static tension or compression loading until interface failure. However, these test conditions do not reflect the in vivo physiologic loading modes, where the tibial plateau is predominantly subjected to combined compression and shear forces. The objectives were to evaluate the impact of the tibial keel & stem length on the primary stability of a posterior-stabilised tibial plateau under dynamic compression-shear loading conditions in human tibiae.