Abstract
Introduction: The London Implant Retrieval Centre (LIRC) was founded to investigate the high incidence of unexplained failures of Metal-on-Metal (MoM) hips. A multidisciplinary team analyse the failed hips, investigations include CT and MRI scans, blood and synovial fluid tests, wear measurements, X-rays and clinical data from the explanting surgeons.
Wear measurements of 100 explanted hips have been carried out on a Taylor Hobson 365 Roundness Machine using the LIRC Wear Protocol. It was found that 50% of explanted cups were wearing less than 5 μm/year and 60% of components were wearing less than 10 μm/year. Wear tests on hip joint simulators predict wear rates between 2 and 8 μm/year. However, 6% of cups are wearing faster than 100 μm/year, with 16% of cups have wear patches deeper than 100 μm and that 4% have a wear patch deeper than 300 μm.
Discussion: This paper considers the common characteristics of components in this very high wearing category. Engineering parameters such as head/cup clearance, surface finish, form errors and head cup contact conditions are investigated. This is correlated with clinical data and other results from the LIRC.
Cup position is an important factor, all of the high wearing components are outside the Lewinick’s Box, however it is shown that mal position is does not always lead to extreme wear. Further analysis is taking place to calculate the size of the contact patch between head and cup (based on patient data and biomechanics) and the proximity of the contact patch to the edge of the cup.
Conclusion: The study of explanted components shows that 6% exhibit extreme wear, and although several “risk” factors can be identified, it is not clear why only a proportion of these components show extremely high wear rates. This is the subject of current investigation.
Correspondence should be addressed to: British Hip Society, 35–43 Lincoln’s Inn Fields, London, WC2A 3PE, England. Email: c.wilson@boa.ac.uk