PSEUDOTUMOURS FOLLOWING METAL-ON-METAL HIP RESURFACING ARTHROPLASTY: METAL ION AND LYMPHOCYTE PROLIFERATION STUDY



Abstract

Introduction: Symptomatic abnormal soft-tissue masses relating to the hip joint, such as those described as pseudotumours, are being increasingly reported following metal-on-metal hip resurfacing arthroplasty (MoMHRA). These were found to be locally destructive, requiring revision surgery in a high proportion (75%) of patients. Lymphocyte infiltrations seen in pseudotumours were similar to aseptic lymphocyte vascular associated lesion (ALVAL), which is thought to represent a T-lymphocyte-mediated delayed type hypersensitivity. Therefore, a delayed hypersensitivity reaction to nickel (Ni), chromium (Cr) or cobalt (Co) has been suggested to play a role in pseudotumour aetiology. In patients with bilateral MoMHRA who presented with symptoms on one side, subsequent scans have demonstrated pseudotumours both on the symptomatic and asymptomatic side. Thus, there are concerns that there may be an appreciable number of asymptomatic pseudotumours that surgeons are unaware of and these may eventually become symptomatic.

Aim: The aims of this study were:

  1. to determine the prevalence of asymptomatic pseudotumours after MoMHRA; and

  2. to measure Co and Cr ion levels as well as lymphocyte proliferation responses to Ni, Co and Cr (the principal elements in the CoCr alloy used in MoMHRA) in MoMHRA patients with and without asymptomatic pseudotumours.

Methods: A total of 201 MoMHRA implanted hips in 158 patients (97 male, 61 female) with a mean age of 56 years (range 33–73 years) were evaluated. The mean follow-up was 61 months (range 13–88 months). Resurfacing devices implanted included 128 Birmingham Hip Resurfacing, 66 Conserve Plus and seven ReCap. The control groups included additional 20 patients, 10 male and 10 female (a mean age 68 years, range 57–80 years) with metal-on-polyethylene total hip arthroplasty and a further 22 age-matched patients (a mean age 55 years) without any metal implants. Ultrasound was used as the initial imaging modality and MRI was used to assess the extent of the identified masses. Patients with a soft-tissue mass had ultrasound-guided aspiration or core biopsy performed. Venous blood samples were collected in all patients for serum cobalt and chromium ion levels analysis using Inductively-Coupled Plasma Mass Spectrometer and lymphocyte transformation tests (LTT). The Oxford Hip Score (OHS) was used to measure the functional outcomes of patients. Acetabular component abduction angle was measured from standardised anteroposterior pelvis radiographs.

Results: Prevalence – Pseudotumours were found in 7 patients (6 female and 1 male). The overall prevalence of asymptomatic pseudotumours was 4%, with a relatively very high (30%) prevalence in females with bilateral implants. Histological examinations showed extensive necrosis of connective tissue, in which there were scattered aggregates of metal particles and a diffuse lymphocyte infiltrate.

Metal Ion Levels – The presence of pseudotumour was associated with significantly higher median serum cobalt levels (9.2mg/L vs. 1.9mg/L, p< 0.001), chromium levels (12.0mg/L vs. 2.1mg/L, p< 0.001), hip aspirate cobalt levels (1182 mg/L vs. 86.2mg/L, p=0.003), and aspirate chromium levels (883mg/L vs. 114.8mg/ L, p=0.006), as well as with inferior functional scores (OHS 41 vs. 47 p< 0.001). There was no significant difference in acetabular cup inclination angle (p=0.51). Lymphocyte Reactivity: A higher incidence and level of enhanced lymphocyte reactivity to Ni (p=0.001), but not to Co or Cr (the principal elements in the CoCr alloy used in metal-on-metal hip resurfacing implants), was found in patients with MoMHRA compared to the patients without MoM implants. However, lymphocyte reactivity to Co, Cr and Ni did not significantly differ in patients with pseudotumours compared to those patients without pseudotumours.

Conclusion: The prevalence of asymptomatic pseudotumours in females was high, especially in females with bilateral MoMHRA implants (30%). The patients with ‘asymptomatic’ pseudotumours were in fact mildly symptomatic. Lymphocyte reactivity to Co, Cr and Ni did not differ in patients with pseudotumour compared to those patients without pseudotumours, suggesting that systemic hypersensitivity type IV reactions, mediated by lymphocyte reactivity to these metals, is not the dominant mechanism in pathogenesis of the soft tissue pseudotumours. Furthermore, pseudotumours were not detected in those patients who had normal levels of cobalt and chromium ions. This suggests that pseudotumours do not occur if MoM articulations are well functioning. Therefore, pseudotumours are likely to be a biological consequence of the large amount of metal debris generated in vivo due to excessive wear.