EARLY ASEPTIC FAILURE OF LARGE METAL-ON-METAL HIP ARTHROPLASTY – IS METAL SENSITIVITY A CONSEQUENCE OF EXCESS WEAR?

Abstract

This report documents the clinical and histological findings, the operative management and the explant analyses of patients with early aseptic failure of large metal-on-metal (MonM) bearing joints.

Three hundred and fifty patients have been implanted with the ASR bearing surface (resurfacing or a modular THR) by a single surgeon at an independent centre since 2004. Six patients (all female) have been revised secondary to aseptic failure. All complained of severe groin pain exacerbated by straight leg raise and routine investigations were unable to establish a cause. Large amounts of sterile, highly viscous green fluid were aspirated from the hip joints in each case. Gross swelling of the pseudocapsule and a similar green fluid surrounding the implants were found at revision surgery. Histological examination of periprosthetic tissue samples showed changes consistent with ALVAL/metallosis, and analysis of the fluid revealed dense numbers of inflammatory cells. Symptoms in patients revised to ceramic-on-ceramic bearings improved post operatively. This was not the case with those reimplanted with MoM joints. Data from a subset of 76 patients (all unilateral resurfacings) showed that malaligned cups (anteverted > 20° +/− inclination angle > 45°) were associated with significantly higher whole blood metal ion levels than cups positioned within this range. All the patients with early aseptic failure had malaligned cups. Independent explant analysis revealed significant increases in the surface roughness values of the articular surfaces.

Our results suggest that some patients develop a significant inflammatory reaction to metal implants. This may be due to high levels of metal debris around the implant as a result of accelerated wear. Poor component alignment was found in all our patients with early aseptic failure.