Abstract
Introduction: Treatment of osteoarthritis by total joint replacement generally shows a high success rate; however challenges remain. Prostheses inserted without cement are popular worldwide. Insertion of uncemented implants is intended to be pressfit. Early bone growth on the implant is critical to long-term fixation.
Parathyroid hormone (PTH) is a regulator of bone metabolism. When PTH is administered intermittently it induces strong anabolic effect by increasing osteoblastic activity. Our understanding of PTH is mainly based on research on osteoporosis, in which bone formation is known to be coupled to the bone resorption. In the orthopaedic situation of a joint replacement other conditions apply.
We therefore find it of interest to examine PTH’s role as an adjuvant in implant surgery. We examine the effect of PTH on the osseointegration of an experimental orthopaedic implant in which the implant due to insertion initiates a bone repair in the implant bed. We hypothesize that parathyroid hormone will improve the bone ongrowth at the bone-implant interface.
Methods: An unpaired canine study was carried out following approval of our Institutional Animal Care and Use Committee. In 20 skeletally mature dogs cylindrical titanium alloy porous coated implants (6×10mm) were inserted pressfit (0.1 mm under-drill) in the extraarticular cancellous bone site of the proximal tibia. Test animal were postoperatively randomised to daily treatment of placebo or parathyroid hormon rhPTH (1–34)(t eriparatide)(Bachem) 5 μg/kg s.c. After 4 weeks observation time specimen blocks were harvested, sectioned and evaluated by unbiased stereological histomorphometry (CAST-grid system (Olympus Denmark)). The endpoints were bone-to-implant contact and tissue density in a 500 μm region of interest. Since data were not normally distributed a non-parametric analysis two-sample Wilcoxon rank-sum test was applied with p-value < 0.05 considered statistically significant. Data are accordingly presented as median and interquartile ranges.
Results: Two implants in the PTH group were excluded. At the implant interface tissue density for PTH was 0,193 (0,157–0,229) for bone, 0,796 (0,764–0,821) for marrow and 0 (0–0,009) for fibrous tissue, as for control 0,163 (0,141–0,193) for bone, 0,837 (0,805–0,859) for marrow and 0 (0-0) for fibrous tissue. Bone tissue showed no significant differences.
In the peri-centric region the tissue fraction for PTH was 0,238 (0,211–0,276) for bone, 0,752 (0,724–0,785) for marrow and 0 (0–0,007) for fibrous tissue, as for control 0,223 (0,201–0,235) for bone, 0,777 (0,765–0,799) for marrow and 0 (0–0) for fibrous tissue.
Conclusion: In conclusion parathyroid hormone does not show significantly induced bone formation at a titanium alloy implant that has a porous coating of titanium alloy and inserted pressfit.