EDGE LOADING JOINT FORCE GENERATES DISLOCATING FORCE INFLUENCED BY ACETABULAR LINER RIM CAPTURE WALL HEIGHT

Abstract

Previous studies suggested the lack of capture wall of acetabular Ultra High Molecular Weight Polyethylene (UHMWPE) liner can significantly increase the risk of hip joint dislocation. To date, the dislocation studies have been focused on the femoral neck impingement models. The purpose of this study was to identify a new Dislocating Force (DF) generated by rim directed joint force alone and investigate the factors to affect the magnitudes of the DF. The 3 D Finite Element Analysis (FEA) models were constructed by (30) 10 mm thick UHMWPE liners with six inner bearing diameters ranging from 22 mm to 44 mm and five capture wall heights in each bearing size from 0 mm to 2 mm. A load of 2 446 N was applied through the corresponding CoCr femoral head to the rim of the liner. The DF was recorded as a function of capture wall height and head diameter. The results were verified by the physical tests of two 28 mm head bearing liners with 0 and 1.5 mm capture wall heights respectively.

The results showed that the highest DF was 1 269N in 0 mm capture wall and 22 mm head. The lowest DF was 171 N in 2 mm capture wall and 44 mm head. The DF decreased as the capture wall and head size increased. When capture wall increased from 0 mm to 1 mm, the DF was reduced more than 50%. Two experimental data points were consistent with the trend of DF curve found in the FEA.

We concluded that the new intrinsic dislocating force DF can be induced by the rim directed joint loading force alone and can reach as high as 51% of the femoral loading force. A capture wall height above 1mm can effectively reduce DF to less than 25% of the joint force. In addition, the larger head diameter also resulted in less DF generation.