Abstract
Using thermal spraying technique, we developed a novel titanium material coated with hydroxyapatite (HA) containing silver (Ag). In this study, antibacterial activities of the material were examined both in vitro and in vivo.
Two different titanium test pieces were prepared. One is the test piece that was coated by HA containing Ag (HA-Ag) and the other is that was coated by HA only, used as a negative control. Antibacterial activity and efficacy of HA-Ag against Staphylococcus aureus, Escherichia coli, and biofilm-forming methicillin-resistant S. aureus (BF-MRSA) was examined by using the Japanese Industrial Standards test (JIS Z2801). Furthermore, surface area where BF-MRSA was attached and proliferated on the test pieces after 24 hours of incubation was calculated by means of scanning electron microscope (SEM). To investigate the antibacterial activity in vivo, the test pieces were inserted subcutisly into the back of SD rats, and BF-MRSA was inoculated into the inserted pieces. On the 7th day after the inoculation, the numbers of adherent bacteria to the pieces were countered by a sterile cotton-tipped swabs method.
By the JIS Z2801 test, HA-Ag showed 104 to 105 times stronger antibacterial activity than HA against all bacteria tested in this study. SEM studies revealed the HA-Ag coated material had 30 to 50 times smaller area of attached bacteria than control. In vivo study showed that viable bacterial numbers on surfaces of HA-Ag were 1000 times less than control. These results indicated that the HA-Ag coated materials have antibacterial activities both in vitro and in vivo.
Titanium coated with HA containing Ag has a possibility to be a novel antibacterial biomaterial.
Correspondence should be addressed to Vasiliki Boukouvala at Department of Orthopaedic Surgery & Traumatology, University Hospital of Larissa, 110 Mezourlo, Larissa, GREECE. Tel: +30 2410 682722, Fax: +30 2410 670107, Email: malizos@med.uth.gr