Abstract
The static properties of bone cements have been widely reported in the literature (Lewis, 1997, Khun, 2000, Armstrong 2002). Commercial bone cements are expected to perform above the minimum values in static tests specified by ISO 5833: 2002. It has been suggested that the viscoelastic properties of bone cement, such as creep and stress relaxation, might bear more relevance to the in-vivo behaviour of the cement-implant construct (Lee 2002). This study aimed to compare numerous properties of Simplex P, Simplex Antibiotic and Simplex Tobramycin and identify those properties most sensitive to subtle changes in cement composition. The three cements were chosen on the basis that they are characterised by the same liquid and powder compositions, the only difference being represented by the type and amount of added antibiotics. In Simplex Antibiotic the additives are 0.5g Erythromycin and 3 million I.U. Colistin, while in Antibiotic Simplex with Tobramycin the only additive is 0.5g of Tobramycin. The static properties of the cements were assessed following protocols described in ISO 5833: 2002, while the viscoelastic properties of the cement were measured with in-house developed apparatus in quasi-static conditions. Creep and stress relaxation tests were performed in four point bending configuration. Porosity was measured on the mid cross section of the creep samples using a digital image technique. All cements exhibited properties compatible with the ISO standard, but in plain Simplex the ISO minimum for bending and compressive strength was within the variation of the batches tested. Bending strength measurements were the least sensitive to differences in the cements. Plain Simplex displayed lower bending and compressive strength but higher bending modulus than the antibiotic laden options. The bending modulus could only discriminate between Simplex P and Simplex Antibiotic (p=0.02). Differences in the compressive strength of the three cements were significant, with the plain option being the weakest. Stress relaxation only discriminated between plain and Tobramycin loaded cement (p=0.028), while creep was more sensitive to differences and allowed distinction between plain and antibiotic loaded bone cements. The creep behaviour correlated with the cross sectional porosity measurements. This study demonstrated that the static tests specified by the current international standard are not as sensitive to subtle changes in the composition of the material as the time temperature dependent parameters characteristic of creep and stress relaxation. The authors advocate the evaluation of time and temperature dependent characteristics as a complement to the current standard.
Theses abstracts were prepared by Professor Roger Lemaire. Correspondence should be addressed to EFORT Central Office, Freihofstrasse 22, CH-8700 Küsnacht, Switzerland.