Abstract
With the plasma–spray technique of applying a hydrox-ylapatite (HA) coating bone ingrowth can be enhanced and early migration of hip prostheses reduced. The significance of coating resorption is controversial. In this study the bone growth and the degradation of the HA coatings were evaluated and compared by SEM.
Premature loosening was identified in four cups with an Ha coating over a porous-coated surface 3 years post-operatively.The Ha coating has a thickness of up to 50 μm. The cup specimens were soaked in 6% sodium hypochlorite to render them anorganic, dehydrated, and sputter-coated with gold-palladium. Secondary electron images of all specimens were obtained by field emission SEM (Zeiss:DSM.962).
Ultrastructural analysis showed that all porous-coated Ha-coated cups had bridges of lamellar bone in direct contact with the implant surface (30% bone in-on growth). Different types of coating degradation were observed. Delamination between the coating and implant surface releases numerous particles or fragments; the resorption by osteoclasts of the amorphous phase was shown to expose the crystalline phase of the coating grains.
This study suggests that resorption disintegrates the Ha coating and reduces the bonding strength between implant and bone and the strength of the coating-implant interface, which might lead to implant loosening,coating delamination and acceleration of third-body wear processes.