Abstract
In the past, the clinical outcome of earlier types of resurfacing hip arthroplasty was often characterised by a high percentage of failures and early mobilisations. An implant retrieval of a Co-Cr head and UHMWPE cup cemented resurfacing hip prosthesis was analysed. The implant was in place 11 years, without any clinical problem for nearly 10 years. The cup was highly worn. There was a complete fracture of the interface between cement and bone at the base of the femural neck. A significant hyperplastic reaction was present at the level of the synovial membrane, with fibrin deposits, hyperplasia of lining cells and a cellular infiltrate formed mostly by macrophages, with occasional giant cells and localised groups of perivascular lymphocytes. Immunohistochemical analysis showed that all lymphocytes were of the T type and that the largest part of macrophages containing debris were not activated. Inside the prosthetic head there were only traces of ossified tissue. This picture indicated that for a long time no viable bone tissue had been in contact with the cement and bone rarefaction was massive.
The study shows an important cause of the failure of earlier types of hip resurfacing arthroplasty, namely the abnormal stress distribution that caused the complete bone rarefaction.