LINEAR AND VOLUMETRIC WEAR IN TOTAL KNEE REPLACEMENTS

Abstract

Polyethylene wear can be an important cause of knee replacement failure.

Six TKRs in young, active patients with excellent Oxford Knee Scores and Knee Society Scores, mean 76 months post knee replacement and 5 control patients, 2 weeks post TKR, were selected. Each patient had weight bearing stereo radiographs of at 0, 15, 30, 45 and 60 degrees of flexion while standing in a calibration grid. These x-rays were analysed using our Radio Stereometric Analysis (RSA) system. The three-dimensional shape of the TKR (manufacturer’s computer aided design model) was matched to the TKR silhouette on the calibrated stereo radiographs for each angle of flexion. The relative positions of the femoral and tibial components in space were then determined and the linear and volumetric penetration was calculated using Matlab software.

The accuracy of the system was found to be 0.3mm (CAD model tolerance 0.25mm). The mean linear wear in the control patients was 0.02mm (range −0.19 to +0.23mm). Average linear penetration in the study group was found to be 0.6 mm at 6 years, giving an overall linear wear rate of 0.1mm/year. Average penetration volume at 76 months was 399mm3. The average volumetric wear rate was 63mm3/year.

It is possible to measure volumetric wear in vivo using RSA. Volumetric wear rate was found to be 63mm3 per year. Studies on retrieved normally functioning hip replacements have shown volumetric wear rates of 35mm3 per year. However, clinical outcomes of knee replacements are comparable to those of hip replacements, suggesting that the knee has a more effective mechanism for dealing with polyethylene wear particles.