Abstract
Ultra high molecular weight polyethylene (UHMWPE) was introduced into clinical practice by Charnley in November 1962 and has remained the standard material for the hip and other total joint arthroplasties.
Wear of the UHMWPE cup, although studied from the beginning, did not appear to be a clinical problem although Charnley suspected that this would be so in the long term.
A review of the outcome of the Charnley low-friction arthroplasty in patients under the age of 40 years at the time of the operation has shown that the incidence of cup migration was exponentially related to the depth of cup penetration. A prospective study using 22.225 mm alumina ceramic (Al 20 3 ) head articulating with cross linked polyethylene was set up with the initial penetration of 0.2 – 0.4 mm in about 2.5 years with no further penetration. The clinical results mirrored closely the experimental results obtained with the identical set of materials and design. The clinical results have now reached 14 year follow-up and the initial total penetration of 0.2 – 0.4mm has remained unchanged.
Review of long term results of the Charnley LFA has shown a mean penetration rate of 0.1 mm/year (0.02 – 0.6). With a mean penetration rate of 0.1 mm/year, the revision rate for cup wear and loosening in patients under the age of 50 at the time of the LFA, and with a follow-up to 32 years, is in the region of 10%. If the penetration rate remained at 0.02 mm/year or less then no cups have been revised for aseptic loosening. Ceramic / UHMWPE articulation is the next stage of evolution of the Charnley LFA. A prospective study using zirconia 22.225 mm head is approaching 7 year follow-up in over 1000 cases.
The abstracts were prepared by Mr Simon Donell. Correspondence should be addressed to him at the Department of Orthopaedics, Norfolk & Norwich Hospital, Level 4, Centre Block, Colney Lane, Norwich NR4 7UY, United Kingdom.