We have evaluated the difference in the migration patterns over two years of two cementless stems in a randomised, controlled trial using radiostereophotogrammetric analysis (RSA). The implants studied were the Furlong HAC stem, which has good long-term results and the Furlong Active stem, which is a modified version of the former designed to minimise stress concentrations between the implant and bone, and thus to improve fixation. A total of 23 Furlong HAC and 20 Furlong Active stems were implanted in 43 patients. RSA examinations were carried out immediately post-operatively and at six, 12 and 24 months post-operatively. The subsidence during the first year in the Furlong HAC stem, was approximately one-third that of the Furlong Active stem, the measured mean subsidence of the femoral head at six months being 0.27 mm (95% confidence interval (CI) 0.03 to 0.51) and 0.99 mm (95% CI 0.38 to 1.60), respectively (p = 0.03). One Active stem continued to subside during the second year. All hips, regardless of the type of stem were clinically successful as judged by the Oxford hip score and a derived pain score without any distinction between the two types of stem. The initial stability of the Furlong Active stem was not as good as the established stem which might compromise osseo-integration to the detriment of long-term success. The changes in the geometry of the stem, to minimise stress have affected the attainment of initial stability.
The presence of pseudotumours, which are soft-tissue masses relating to the hip, after metal-on-metal hip resurfacing arthroplasty has been associated with elevated levels of metal ions in serum, suggesting that pseudotumours occur when there is increased wear. We aimed to quantify the wear in vivo of implants revised for pseudotumours (eight) and of a control group of implants (22) revised for other reasons of failure. We found that the implant group with pseudotumours had a significantly higher rate of median linear wear of the femoral component at 8.1 μm/year (2.75 to 25.4) than the 1.79 μm/year (0.82 to 4.15; p = 0.002) of the non-pseudotumour group. For the acetabular component a significantly higher rate of median linear wear of 7.36 μm/year (1.61 to 24.9) was observed in the pseudotumour group compared with 1.28 μm/year (0.81 to 3.33, p = 0.001) in the other group. Wear of the acetabular component in the pseudotumour group always involved the edge of the implant, indicating that edge-loading had occurred. Our findings are the first direct evidence that pseudotumour is associated with increased wear at the metal-on-metal articulation. Furthermore, edge-loading with the loss of fluid-film lubrication may be an important mechanism of generation of wear in patients with a pseudotumour.