Our aim was to analyse the influence of the size, shape and number of particles on the pathogenesis of osteolysis. We obtained peri-implant tissues from 18 patients having revision surgery for aseptically loosened Freeman total knee replacements (10), Charnley total hip replacements (3) and Imperial College/London Hospital double-cup surface hip replacements (5). The size and shape of the polyethylene particles were characterised using SEM and their concentration was calculated. The results were analysed with reference to the presence of radiological osteolysis.

The concentration of polyethylene particles in 6 areas with osteolysis was significantly higher than that in 12 areas without osteolysis. There were no significant differences between the size and shape of the particles in these two groups.

We conclude that the most critical factor in the pathogenesis of osteolysis is the concentration of polyethylene particles accumulated in the tissue.

Foreign-body reaction to polyglycolide (PGA) implants has been described in man. Many animal experiments have verified the mechanical properties of fixation devices made from PGA, but a significant foreign-body reaction has not been described. We studied the effect of PGA rods in 12 sheep with standardized osteochondral fractures of the medial femoral condyle fixed with uncoloured, self-reinforced PGA rods (Biofix). Radiographs were taken at intervals ranging from two weeks to two years, and the sheep were killed at intervals ranging from six to 24 months. All knees were examined histologically.

Eleven of the 12 fractures healed radiologically and histologically. Moderate to severe osteolysis was seen at four to six weeks with maximum changes at 12 weeks in ten animals. Six knees showed fistula-like connections between the implant site and the joint space. Three developed synovitis, one with inflammatory changes involving the whole cartilage and one with destruction of the medial condyle.

Although in our study osteochondral fractures fixed with PGA rods healed reliably, there were frequent, significant foreign-body reactions. Caution is needed when considering the use of PGA fixation devices in vulnerable regions such as the knee.

We have reviewed 70 patients with bilateral simultaneous total hip arthroplasties to determine the rate of failure and to compare polyethylene wear and osteolysis between an implant with a cobalt-chrome head and Hylamer liner with that of a zirconia head and Hylamer liner. The mean thickness of the polyethylene liner was 11.0 mm (8.8 to 12.2) in the hip with a zirconia head and 10.7 mm (8.8 to 12.2) in that with a cobalt-chrome head. At follow-up at 6.4 years no acetabular or femoral component had been revised for aseptic loosening and no acetabular or femoral component was loose according to radiological criteria in both the cemented and cementless groups. The mean rate of linear wear and annual wear rate were highest in the 22 mm zirconia femoral head (1.25 mm (SD 1.05) and 0.21 mm (SD 0.18), respectively) and lowest in the 22 mm cobalt-chrome femoral head (0.70 mm (SD 0.39) and 0.12 mm (SD 0.07), respectively). The mean volumetric wear was highest in the 28 mm zirconia femoral head (730.79 mm. 3. ) and lowest in the 22 mm cobalt-chrome femoral head (264.67 mm. 3. ), but if the results were compared by size of the femoral head and type of material there was no statistical difference (p > 0.05). Sequential measurements of annual wear showed that the zirconia femoral head had a relatively higher rate of penetration than the cobalt-chrome head over the first three years; thereafter the rate of wear was reduced and compared favourably with that of cobalt-chrome heads. There was a statistically significant relationship between the wear of the polyethylene liner and the age of the patient, male gender and the degree of abduction angle of the cup, but not diagnosis, weight, hip score, range of movement, or amount of anteversion. Osteolysis was identified on both sides of the acetabulum in six patients (9%). Of 12 hips with acetabular osteolysis, six had a 28 mm cobalt-chrome femoral head and the remaining six a 28 mm zirconia head. Osteolysis was observed in zones 1A and 7A of the femur in two hips (3%) with a 28 mm zirconia head (cemented hip) and in four (6%) with a 28 mm cobalt-chrome femoral head (cementless hip). Our findings suggest that although the performance of a zirconia femoral head with a Hylamer liner was not statistically different from that of a cobalt-chrome femoral head and Hylamer liner, there was a trend for the zirconia head to be worse than the cobalt-chrome femoral head

Objectives

The Attune total knee arthroplasty (TKA) has been used in over 600 000 patients worldwide. Registry data show good clinical outcome; however, concerns over the cement-tibial interface have been reported. We used retrieval analysis to give further insight into this controversial topic.