Aims. We investigated whether blood metal ion levels could effectively identify patients with bilateral Birmingham Hip Resurfacing (BHR) implants who have adverse reactions to metal debris (ARMD). Patients and Methods. Metal ion levels in whole blood were measured in 185 patients with bilateral BHRs. Patients were divided into those with ARMD who either had undergone a revision for ARMD or had ARMD on imaging (n = 30), and those without ARMD (n = 155). Receiver operating characteristic analysis was used to determine the optimal thresholds of blood metal ion levels for identifying patients with ARMD. Results. The maximum level of cobalt or chromium ions in the blood was the parameter which produced the highest area under the curve (91.0%). The optimal threshold for distinguishing between patients with and without ARMD was 5.5 µg/l (83.3% sensitivity, 88.4% specificity, 58.1% positive and 96.5% negative predictive values). Similar results were obtained in a subgroup of 111 patients who all underwent cross-sectional imaging. Between 3.2% and 4.3% of patients with ARMD were missed if United Kingdom (7 µg/l) and United States (10 µg/l) authority thresholds were used respectively, compared with 2.7% if our implant specific threshold was used, though these differences did not reach statistical significance (p ≥ 0.248). Conclusion. Patients with bilateral BHRs who have blood metal ion levels below our implant specific threshold were at low-risk of having ARMD. Cite this article: Bone Joint J 2016;98-B:1455–62

Objectives. Alarm over the reported high failure rates for metal-on-metal (MoM) hip implants as well as their potential for locally aggressive Adverse Reactions to Metal Debris (ARMDs) has prompted government agencies, internationally, to recommend the monitoring of patients with MoM hip implants. Some have advised that a blood ion level >7 µg/L indicates potential for ARMDs. We report a systematic review and meta-analysis of the performance of metal ion testing for ARMDs. Methods. We searched MEDLINE and EMBASE to identify articles from which it was possible to reconstruct a 2 × 2 table. Two readers independently reviewed all articles and extracted data using explicit criteria. We computed a summary receiver operating curve using a Bayesian random-effects hierarchical model. Results. Our literature search returned 575 unique articles; only six met inclusion criteria defined a priori. The discriminative capacity of ion tests was homogeneous across studies but that there was substantial cut-point heterogeneity. Our best estimate of the “true” area under curve (AUC) for metal ion testing is 0.615, with a 95% credible interval of 0.480 to 0.735, thus we can state that the probability that metal ion testing is actually clinically useful with an AUC ≥ 0.75 is 1.7%. Conclusion. Metal ion levels are not useful as a screening test for identifying high risk patients because ion testing will either lead to a large burden of false positive patients, or otherwise marginally modify the pre-test probability. With the availability of more accurate non-invasive tests, we did not find any evidence for using blood ion levels to diagnose symptomatic patients. Cite this article: M. Pahuta, J. M. Smolders, J. L. van Susante, J. Peck, P. R. Kim, P. E. Beaule. Blood metal ion levels are not a useful test for adverse reactions to metal debris: a systematic review and meta-analysis. Bone Joint Res 2016;5:379–386. DOI: 10.1302/2046-3758.59.BJR-2016-0027.R1

Objectives. The aims of this piece of work were to: 1) record the background concentrations of blood chromium (Cr) and cobalt (Co) concentrations in a large group of subjects; 2) to compare blood/serum Cr and Co concentrations with retrieved metal-on-metal (MoM) hip resurfacings; 3) to examine the distribution of Co and Cr in the serum and whole blood of patients with MoM hip arthroplasties; and 4) to further understand the partitioning of metal ions between the serum and whole blood fractions. Methods. A total of 3042 blood samples donated to the local transfusion centre were analysed to record Co and Cr concentrations. Also, 91 hip resurfacing devices from patients who had given pre-revision blood/serum samples for metal ion analysis underwent volumetric wear assessment using a coordinate measuring machine. Linear regression analysis was carried out and receiver operating characteristic curves were constructed to assess the reliability of metal ions to identify abnormally wearing implants. The relationship between serum and whole blood concentrations of Cr and Co in 1048 patients was analysed using Bland-Altman charts. This relationship was further investigated in an in vitro study during which human blood was spiked with trivalent and hexavalent Cr, the serum then separated and the fractions analysed. Results. Only one patient in the transfusion group was found to have a blood Co > 2 µg/l. Blood/Serum Cr and Co concentrations were reliable indicators of abnormal wear. Blood Co appeared to be the most useful clinical test, with a concentration of 4.5 µg/l showing sensitivity and specificity for the detection of abnormal wear of 94% and 95%, respectively. Generated metal ions tended to fill the serum compartment preferentially in vivo and this was replicated in the in vitro study when blood was spiked with trivalent Cr and bivalent Co. Conclusions. Blood/serum metal ion concentrations are reliable indicators of abnormal wear processes. Important differences exist however between elements and the blood fraction under study. Future guidelines must take these differences into account

There have been no large comparative studies of the blood levels of metal ions after implantation of commercially available hip resurfacing devices which have taken into account the effects of femoral size and inclination and anteversion of the acetabular component. We present the results in 90 patients with unilateral articular surface replacement (ASR) hip resurfacings (mean time to blood sampling 26 months) and 70 patients with unilateral Birmingham Hip Resurfacing (BHR) implants (mean time 47 months).

The whole blood and serum chromium (Cr) and cobalt (Co) concentrations were inversely related to the size of the femoral component in both groups (p < 0.05). Cr and Co were more strongly influenced by the position of the acetabular component in the case of the ASR, with an increase in metal ions observed at inclinations > 45° and anteversion angles of < 10° and > 20°. These levels were only increased in the BHR group when the acetabular component was implanted with an inclination > 55°.

A significant relationship was identified between the anteversion of the BHR acetabular component and the levels of Cr and Co (p < 0.05 for Co), with an increase observed at anteversion angles < 10° and > 20°. The median whole blood and serum Cr concentrations of the male ASR patients were significantly lower than those of the BHR men (p < 0.001). This indicates that reduced diametral clearance may equate to a reduction in metal ion concentrations in larger joints with satisfactory orientation of the acetabular component.

Aims

In metal-on-polyethylene (MoP) total hip arthroplasty (THA), large metal femoral heads have been used to increase stability and reduce the risk of dislocation. The increased size of the femoral head can, however, lead to increased taper corrosion, with the release of metal ions and adverse reactions. The aim of this study was to investigate the relationship between the size of the femoral head and the levels of metal ions in the blood in these patients.

Blood metal ions have been widely used to investigate metal-on-metal hip replacements, but their ability to discriminate between well-functioning and failed hips is not known. The Medicines and Healthcare products Regulatory Agency (MHRA) has suggested a cut-off level of 7 parts per billion (ppb). We performed a pair-matched, case-control study to investigate the sensitivity and specificity of blood metal ion levels for diagnosing failure in 176 patients with a unilateral metal-on-metal hip replacement. We recruited 88 cases with a pre-revision, unexplained failed hip and an equal number of matching controls with a well-functioning hip. We investigated the 7 ppb cut-off level for the maximum of cobalt or chromium and determined optimal mathematical cut-off levels from receiver-operating characteristic curves. The 7 ppb cut-off level for the maximum of cobalt or chromium had a specificity of 89% and sensitivity 52% for detecting a pre-operative unexplained failed metal on metal hip replacement. The optimal cut-off level for the maximum of cobalt or chromium was 4.97 ppb and had sensitivity 63% and specificity 86%. Blood metal ions had good discriminant ability to separate failed from well-functioning hip replacements. The MHRA cut-off level of 7 ppb provides a specific test but has poor sensitivity.

Aims. To determine whether there is any association between glomerular filtration rate (GFR) and blood cobalt (Co) and chromium (Cr) levels in patients with metal-on-metal (MoM) hip arthroplasty. Patients and Methods. We identified 179 patients with a unilateral 36 mm diameter head as part of a stemmed Summit-Pinnacle MoM hip arthroplasty. GFR was calculated using the Modification of Diet in Renal Disease formula. Results. Normal renal function (GFR ≥ 90 ml/min/1.73 m. 2. ) was seen in 74 patients. Mild renal insufficiency (GFR 60 to 89 ml/min/1.73 m. 2. ) was seen in 90 patients and moderate renal insufficiency (GFR 30 to 59 ml/min/1.73 m. 2. ) in 15. There was no statistical difference in Co and Cr levels between patients with normal renal function and those with mild or moderate renal insufficiency. No correlation was seen between creatinine and blood metal ion levels or between GFR and blood metal ion levels. Linear regression analysis did not show any association between Co and Cr levels and GFR. Conclusion. We did not find any association between GFR and blood metal ion levels. Consequently, the accumulation of Co and Cr in blood due to renal insufficiency does not seem to be a major risk in patients with mild or moderate renal insufficiency. Cite this article Bone Joint J 2017;99-B:1147–52

Aims. The purpose of this study was to compare two different types of metal-on-metal (MoM) bearing for total hip arthroplasty (THA): one with a large femoral head (38 mm to 52 mm) and the other with a conventional femoral head (28 mm or 32 mm). We compared clinical outcome, blood metal ion levels, and the incidence of pseudotumour in the two groups. Patients and Methods. Between December 2009 and December 2011, 62 patients underwent MoM THA with a large femoral head (Magnum group) and 57 patients an MoM THA with a conventional femoral head (conventional group). Clinical outcome was assessed using the Harris Hip score, University of California, Los Angeles (UCLA) activity score and EuroQol-5D (EQ-5D). Blood metal ion levels were measured and MRI scans were analyzed at a minimum of five years postoperatively. Results. No acetabular component was implanted with more than 50° of inclination in either group. The Harris Hip Score, UCLA activity score, and EQ-5D improved postoperatively in both groups; no significant clinical differences were noted between the groups. The blood cobalt ion levels in the conventional group continued to rise postoperatively to five years while reaching a plateau at two years postoperatively in the Magnum group. At five years, the mean cobalt ion level of 1.16 μg/l (. sd. 1.32) in the Magnum group was significantly lower than the 3.77 μg/l (. sd. 9.80) seen in the conventional group (p = 0.0015). The incidence of moderate to severe pseudotumour was 4.7% in the Magnum group and 20.6% in the conventional group. There were no dislocations in the Magnum group and two in the conventional group. One patient in the Magnum group underwent revision for pseudotumour at 4.7 years postoperatively. Conclusion. At five years, a well-positioned large head MoM THA has a significantly lower level of metal ion release and a lower incidence of moderate to severe pseudotumour than a MoM bearing of conventional size. Cite this article: Bone Joint J 2018;100-B:1018–24

This study compared component wear rates and pre-revision blood metal ions levels in two groups of failed metal-on-metal hip arthroplasties: hip resurfacing and modular total hip replacement (THR). There was no significant difference in the median rate of linear wear between the groups for both acetabular (p = 0.4633) and femoral (p = 0.0872) components. There was also no significant difference in the median linear wear rates when failed hip resurfacing and modular THR hips of the same type (ASR and Birmingham hip resurfacing (BHR)) were compared. Unlike other studies of well-functioning hips, there was no significant difference in pre-revision blood metal ion levels between hip resurfacing and modular THR. Edge loading was common in both groups, but more common in the resurfacing group (67%) than in the modular group (57%). However, this was not significant (p = 0.3479). We attribute this difference to retention of the neck in resurfacing of the hip, leading to impingement-type edge loading. This was supported by visual evidence of impingement on the femur. These findings show that failed metal-on-metal hip resurfacing and modular THRs have similar component wear rates and are both associated with raised pre-revision blood levels of metal ions

Aims. To find out if there is an inverse association between estimated glomerular filtration rate (eGFR) and whole blood cobalt (Co) and chromium (Cr) levels in patients with metal-on-metal (MoM) hip arthroplasties and renal insufficiency, suggesting that renal insufficiency could cause accumulation of Co and Cr in blood. Methods. Out of 2,520 patients with 3,013 MoM hip arthroplasties, we identified 1,244 patients with whole blood Co, Cr, and creatinine measured within no more than a one-year interval. We analyzed the correlation of blood metal ion levels and eGFR to identify a potential trend of accumulating Co or Cr with decreasing eGFR. Results. Of the 1,244 patients, 112 had normal renal function (eGFR > 90 ml/min/1.73 m. 2. ), 715 had mild renal insufficiency (eGFR 60 to 89), 384 had moderate renal insufficiency (eGFR 30 to 59), 27 had severe renal insufficiency (eGFR 15 to 29), and six had end-stage renal insufficiency (eGFR < 15). Median eGFR was 68 ml/min/1.73 m. 2. (interquartile range (IQR) 56 to 82), median whole blood Co was 3.3 µg/l (IQR 1.1 to 9.9), and median Cr was 2.0 µg/l (IQR 1.2 to 3.6). We did not observe an association between decreased eGFR and increased whole blood Co and Cr concentrations, but instead both increased Co and Cr were associated with higher eGFR, indicating better kidney function. Conclusion. As patients with MoM hip arthroplasties get older, the prevalence of renal insufficiency among them will increase, and orthopaedic surgeons will increasingly have to evaluate whether or not this affects patient follow-up. The USA Food and Drug Administration suggests that closer follow-up may be needed for MoM patients with renal insufficiency. We did not observe accumulation of blood Co or Cr in MoM hip arthroplasty patients with mild to severe renal insufficiency. Cite this article: Bone Joint J 2021;103-B(7):1231–1237

Aims. Dual mobility (DM) implants have been shown to reduce the dislocation rate after total hip arthroplasty (THA), but there remain concerns about the use of cobalt chrome liners inserted into titanium shells. The aim of this study was to assess the clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) at mid-term follow-up in young, active patients receiving a modular DM THA. Methods. This was a prospective study involving patients aged < 65 years, with a BMI of < 35 kg/m. 2. , and University of California, Los Angeles activity score of > 6 who underwent primary THA with a modular cobalt chrome acetabular liner, highly cross-linked polyethylene mobile bearing, and a cementless titanium femoral stem. Patient-reported outcome measures, whole blood metal ion levels (μg/l), and periprosthetic femoral BMD were measured at baseline and at one, two, and five years postoperatively. The results two years postoperatively for this cohort have been previously reported. Results. A total of 43 patients were enrolled. At minimum follow-up of five years, 23 (53.4%) returned for clinical and radiological review, 25 (58.1%) had metal ion analysis performed, 19 (44.2%) underwent dual energy x-ray absorptiometry scans, and 25 (58%) completed a pain-drawing questionnaire. The mean modified Harris Hip Scores improved significantly from 54.8 (SD 19) preoperatively to 93.08 (SD 10.5) five years postoperatively (p < 0.001). One patient was revised for aseptic acetabular loosening. The mean cobalt levels increased from 0.065 μg/l (SD 0.03) to 0.08 (SD 0.05) and the mean titanium levels increased from 0.35 (SD 0.13) to 0.78 (SD 0.29). The femoral BMD ratio decreased in Gruen Zone 1 (91.9%) at five years postoperatively compared with the baseline scores at six weeks potoperatively. The femoral BMD ratio was maintained in Gruen zones 2 to 7. Conclusion. The use of a modular DM component and a cementless, tapered femoral stem shows excellent mid-term survivorship with minimal concerns for corrosion and metal ion release in a cohort of young, active patients undergoing primary THA. Cite this article: Bone Joint J 2021;103-B(7 Supple B):73–77

The aim of this study was to investigate the possible benefit of large-head metal-on-metal bearing on a stem for primary hip replacement compared with a 28 mm diameter conventional metal-on-polyethylene bearing in a prospective randomised controlled trial. We investigated cemented stem behaviour between these two different bearings using Einzel-Bild-Röntgen-Analyse, clinical and patient reported measures (Harris hip score, Western Ontario and McMaster Universities osteoarthritis index, Short Form-36 and satisfaction) and whole blood metal ion levels at two years. A power study indicated that 50 hips were needed in each group to detect subsidence of > 5 mm at two years with a p-value of < 0.05. . Significant improvement (p < 0.001) was found in the mean clinical and patient reported outcomes at two years for both groups. Comparison of outcomes between the groups at two years showed no statistically significant difference for mean stem migration, clinical and patient reported outcomes; except overall patient satisfaction which was higher for metal-on-metal group (p = 0.05). Metal ion levels were raised above the Medicines and Healthcare products Regulatory Agency advised safety level (7 µg per litre) in 20% of the metal-on-metal group and in one patient in metal-on-polyethylene group (who had a metal-on-metal implant on the contralateral side). Two patients in the metal-on-metal group were revised, one for pseudotumour and one for peri-prosthetic fracture. . Use of large modular heads is associated with a risk of raised whole blood metal ion levels despite using a proven bearing from resurfacing. The head-neck junction or excess stem micromotion are possibly the weak links warranting further research

Aims. The aim of this study was to evaluate blood metal ion levels, leucocyte profiles, and serum cytokines in patients with a total hip arthroplasty (THA) involving modular dual-mobility components. Patients and Methods. A total of 39 patients were recruited, with clinical follow-up of up to two years. Outcome was assessed using the Harris Hip Score (HHS, the 12-Item Short-Form Health Survey (SF-12), the Western Ontario and McMaster Universities Osteoarthritis Index (WOMAC), and a visual analogue scale (VAS) for pain. Blood concentrations of cobalt (Co), chromium (Cr), and serum cytokines were measured. Subpopulations of leucocytes were analyzed by flow cytometry. Results. The clinical performance was good. Blood Co levels (ref 1.0 µg/l) were mildly elevated in seven patients at three months, and two patients at two years’ follow-up. The preoperative Cr levels were normal except for one patient with a detectable Cr (1.2 µg/l). Cr levels were detectable in three patients at three months, two patients at one year, and three patients at two years’ follow-up. No patients had symptoms suggestive of failure. Although flow cytometry showed constant circulating leucocyte profiles, there was a significant reduction of serum interleukin (IL)-4, IL-5, and interferon gamma (IFNγ) postoperatively compared with the preoperative levels (p < 0.05). Conclusion. These results suggest that THA using modular dual-mobility components is safe. This allows an opportunity to use a large femoral head and a thick polyethylene bearing surface, which is especially useful in revision procedures or high-risk situations when added stability is required. Cite this article: Bone Joint J 2019;101-B:1035–1041

Aims. To analyze the short-term outcome of two types of total wrist arthroplasty (TWA) in terms of wrist function, migration, and periprosthetic bone behaviour. Methods. A total of 40 patients suffering from non-rheumatoid wrist arthritis were enrolled in a randomized controlled trial comparing the ReMotion and Motec TWAs. Patient-rated and functional outcomes, radiological changes, blood metal ion levels, migration measured by model-based radiostereometric analysis (RSA), bone mineral density (BMD) measured by dual-energy X-ray absorptiometry (DXA), complications, loosening, and revision rates at two years were compared. Results. Patient-Rated Wrist and Hand Evaluation (PRWHE) scores, abbreviated version of the Disabilities of the Arm, Shoulder and Hand questionnaire (QuickDASH) scores, and pain improved similarly and significantly in both groups. Wrist motion improved significantly in the Motec group only, and forearm rotation in the ReMotion group only. Cobalt (Co) and chromium (Cr) blood ion levels were significantly higher in the metal-on-metal (MoM) Motec group than in the metal-on-polyethylene (MoP) ReMotion group. Mean total translation was 0.65 mm (95% confidence interval (CI) 0.26 to 1.12) and 0.27 mm (95% CI 0.14 to 0.47) for the ReMotion carpal and radial components, and 0.32 mm (95% CI 0.22 to 0.45) and 0.26 mm (95% CI 0.20 to 0.34) for the Motec metacarpal and radial components, respectively. Apart from dorsal and volar tilts, which were significantly higher for the radial ReMotion than for the Motec component, no significant differences in absolute migration occurred. BMD around the radial components never returned to baseline. Almost one-third of patients required reoperation due to complications. Two ReMotion implants were revised to Motec TWAs due to carpal component loosening, and three Motec MoM articulations were revised to metal-on-polyether ether ketone due to painful synovitis. Conclusion. Both implants provided matched function and were stable at short-term follow-up, but with a high complication rate. This procedure should be restricted to specialist centres undertaking prospective analysis until its role is clarified. Cite this article: Bone Joint J 2022;104-B(10):1132–1141

Aims. Modular dual mobility (DM) prostheses in which a cobalt-chromium liner is inserted into a titanium acetabular shell (vs a monoblock acetabular component) have the advantage of allowing supplementary screw fixation, but the potential for corrosion between the liner and acetabulum has raised concerns. While DM prostheses have shown improved stability in patients deemed ‘high-risk’ for dislocation undergoing total hip arthroplasty (THA), their performance in young, active patients has not been reported. This study’s purpose was to assess clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) in young, active patients receiving a modular DM acetabulum and recently introduced titanium, proximally coated, tapered femoral stem design. Patients and Methods. This was a prospective study of patients between 18 and 65 years of age, with a body mass index (BMI) < 35 kg/m. 2. and University of California at Los Angeles (UCLA) activity score > 6, who received a modular cobalt-chromium acetabular liner, highly crosslinked polyethylene mobile bearing, and cementless titanium femoral stem for their primary THA. Patients with a history of renal disease and metal hardware elsewhere in the body were excluded. A total of 43 patients (30 male, 13 female; mean age 52.6 years (. sd. 6.5)) were enrolled. All patients had a minimum of two years’ clinical follow-up. Patient-reported outcome measures, whole blood metal ion levels (ug/l), and periprosthetic femoral BMD were measured at baseline, as well as at one and two years postoperatively. Power analysis indicated 40 patients necessary to demonstrate a five-fold increase in cobalt levels from baseline (alpha = 0.05, beta = 0.80). A mixed model with repeated measures was used for statistical analysis. Results. Mean Harris Hip Scores improved from 54.1 (. sd. 20.5) to 91.2 (. sd. 10.8) at two years postoperatively (p < 0.001). All patients had radiologically well-fixed components, no patients experienced any instability, and no patients required any further intervention. Mean cobalt levels increased from 0.065 ug/l (. sd. 0.03) preoperatively to 0.30 ug/l (. sd. 0.51) at one year postoperatively (p = 0.01) but decreased at two years postoperatively to 0.16 ug/l (. sd. 0.23; p = 0.2). Four patients (9.3%) had a cobalt level outside the reference range (0.03 ug/l to 0.29 ug/l) at two years postoperatively, with values from 0.32 ug/l to 0.94 ug/l. The mean femoral BMD ratio was maintained in Gruen zones 2 to 7 at both one and two years postoperatively using this stem design. At two years postoperatively, mean BMD in the medial calcar was 101.5% of the baseline value. Conclusion. Use of a modular DM prosthesis and cementless, tapered femoral stem has shown encouraging results in young, active patients undergoing primary THA. Elevation in mean cobalt levels and the presence of four patients outside the reference range at two years postoperatively demonstrates the necessity of continued surveillance in this cohort. Cite this article: Bone Joint J 2019;101-B:365–371

The Articular Surface Replacement (ASR) hip resurfacing arthroplasty has a failure rate of 12.0% at five years, compared with 4.3% for the Birmingham Hip Resurfacing (BHR). We analysed 66 ASR and 64 BHR explanted metal-on-metal hip replacements with the aim of understanding their mechanisms of failure. We measured the linear wear rates of the acetabular and femoral components and analysed the clinical cause of failure, pre-revision blood metal ion levels and orientation of the acetabular component. There was no significant difference in metal ion levels (chromium, p = 0.82; cobalt, p = 0.40) or head wear rate (p = 0.14) between the two groups. The ASR had a significantly increased rate of wear of the acetabular component (p = 0.03) and a significantly increased occurrence of edge loading (p < 0.005), which can be attributed to differences in design between the ASR and BHR. The effects of differences in design on the in vivo wear rates are discussed: these may provide an explanation as to why the ASR is more sensitive to suboptimal positioning than the BHR

Objectives. The high revision rates of the DePuy Articular Surface Replacement (ASR) and the DePuy ASR XL (the total hip arthroplasty (THA) version) have led to questions over the viability of metal-on-metal (MoM) hip joints. Some designs of MoM hip joint do, however, have reasonable mid-term performance when implanted in appropriate patients. Investigations into the reasons for implant failure are important to offer help with the choice of implants and direction for future implant designs. One way to assess the performance of explanted hip prostheses is to measure the wear (in terms of material loss) on the joint surfaces. Methods. In this study, a coordinate measuring machine (CMM) was used to measure the wear on five failed cementless Biomet Magnum/ReCap/ Taperloc large head MoM THAs, along with one Biomet ReCap resurfacing joint. Surface roughness measurements were also taken. The reason for revision of these implants was pain and/or adverse reaction to metal debris (ARMD) and/or elevated blood metal ion levels. Results. The mean wear rate of the articulating surfaces of the heads and acetabular components of all six joints tested was found to be 6.1 mm. 3. /year (4.1 to 7.6). The mean wear rate of the femoral head tapers of the five THAs was 0.054 mm. 3. /year (0.021 to 0.128) with a mean maximum wear depth of 5.7 µm (4.3 to 8.5). Conclusion. Although the taper wear was relatively low, the wear from the articulating surfaces was sufficient to provide concern and was potentially large enough to have been the cause of failure of these joints. The authors believe that patients implanted with the ReCap system, whether the resurfacing prosthesis or the THA, should be closely monitored. Cite this article: S. C. Scholes, B. J. Hunt, V. M. Richardson, D. J. Langton, E. Smith, T. J. Joyce. Explant analysis of the Biomet Magnum/ReCap metal-on-metal hip joint. Bone Joint Res 2017;6:113–122. DOI: 10.1302/2046-3758.62.BJR-2016-0130.R2

We prospectively assessed the efficacy of a ceramic-on-metal (CoM) hip bearing with uncemented acetabular and femoral components in which cobalt­–chrome acetabular liners and alumina ceramic heads were used. The cohort comprised 94 total hip replacements (THRs) in 83 patients (38 women and 45 men) with a mean age of 58 years (42 to 70). Minimum follow-up was two years. All patients had pre- and post-operative assessment using the Western Ontario and McMaster Universities osteoarthritis index (WOMAC), Oxford hip score and Short-Form 12 scores. All showed a statistically significant improvement from three months post-operatively onwards (all p < 0.001). After two years whole blood metal ion levels were measured and chromosomal analysis was performed. The levels of all metal ions were elevated except vanadium. Levels of chromium, cobalt, molybdenum and titanium were significantly higher in patients who underwent bilateral THR compared with those undergoing unilateral THR (p < 0.001). Chromosomal analysis demonstrated both structural and aneuploidy mutations. There were significantly more breaks and losses than in the normal population (p < 0.001). There was no significant difference in chromosomal aberration between those undergoing unilateral and bilateral procedures (all analyses p ≥ 0.62). The use of a CoM THR is effective clinically in the short-term, with no concerns, but the significance of high metal ion levels and chromosomal aberrations in the long-term remains unclear. Cite this article: Bone Joint J 2013;95-B:1040–44

This study reports on ceramic-on-metal (CoM) bearings in total hip replacement. Whole blood metal ion levels were measured. The median increase in chromium and cobalt at 12 months was 0.08 μg/1 and 0.22 μg/1, respectively, in CoM bearings. Comparable values for metal-on-metal (MoM) were 0.48 μg/1 and 0.32 μg/1. The chromium levels were significantly lower in CoM than in MoM bearings (p = 0.02). The cobalt levels were lower, but the difference was not significant. Examination of two explanted ceramic heads revealed areas of thin metal transfer. CoM bearings (one explanted head and acetabular component, one explanted head and new acetabular component, and three new heads and acetabular components) were tested in a hip joint simulator. The explanted head and acetabular component had higher bedding-in. However, after one million cycles all the wear rates were the same and an order of magnitude less than that reported for MoM bearings. There were four outliers in each clinical group, primarily related to component malposition

Objectives. This study aimed to characterise and qualitatively grade the severity of the corrosion particles released into the hip joint following taper corrosion. Methods. The 26 cases examined were CoC/ABG Modular (n = 13) and ASR/SROM (n = 13). Blood serum metal ion levels were collected before and after revision surgery. The haematoxylin and eosin tissue sections were graded on the presence of fibrin exudates, necrosis, inflammatory cells and corrosion products. The corrosion products were identified based on visible observation and graded on abundance. Two independent observers blinded to the clinical patient findings scored all cases. Elemental analysis was performed on corrosion products within tissue sections. X-Ray diffraction was used to identify crystalline structures present in taper debris. Results. The CoC/ABG Modular patients had a mean age of 64.6 years (49.4 to 76.5) and ASR/SROM patients had a mean age of 58.2 years (33.3 to 85.6). The mean time in situ for CoC/ABG was 4.9 years (2 to 6.4) and ASR/SROM was 6.1 years (2.5 to 8.1). The blood serum metal ion concentrations reduced following revision surgery with the exception of Cr levels within CoC/ABG. The grading of tissue sections showed that the macrophage response and metal debris were significantly higher for the ASR/SROM patients (p < 0.001). The brown/red particles were significantly higher for ASR/SROM (p < 0.001). The taper debris contained traces of titanium oxide, chromium oxide and aluminium nitride. Conclusion. This study characterised and qualitatively graded the severity of the corrosion particles released into the hip joint from tapers that had corrosion damage. Cite this article: S. Munir, R. A. Oliver, B. Zicat, W. L. Walter, W. K. Walter, W. R. Walsh. The histological and elemental characterisation of corrosion particles from taper junctions. Bone Joint Res 2016;5:370–378. DOI: 10.1302/2046-3758.59.2000507