Objectives

The use of two implants to manage concomitant ipsilateral femoral shaft and proximal femoral fractures has been indicated, but no studies address the relationship of dynamic hip screw (DHS) side plate screws and the intramedullary nail where failure might occur after union. This study compares different implant configurations in order to investigate bridging the gap between the distal DHS and tip of the intramedullary nail.

We investigated a new intramedullary locking nail that allows the distal interlocking screws to be locked to the nail. We compared fixation using this new implant with fixation using either a conventional nail or a locking plate in a laboratory simulation of an osteoporotic fracture of the distal femur. A total of 15 human cadaver femora were used to simulate an AO 33-A3 fracture pattern. Paired specimens compared fixation using either a locking or non-locking retrograde nail, and using either a locking retrograde nail or a locking plate. The constructs underwent cyclical loading to simulate single-leg stance up to 125 000 cycles. Axial and torsional stiffness and displacement, cycles to failure and modes of failure were recorded for each specimen. When compared with locking plate constructs, locking nail constructs had significantly longer mean fatigue life (75 800 cycles (sd 33 900) vs 12 800 cycles (sd 6100); p = 0.007) and mean axial stiffness (220 N/mm (sd 80) vs 70 N/mm (sd 18); p = 0.005), but lower mean torsional stiffness (2.5 Nm/° (sd 0.9) vs 5.1 Nm/° (sd 1.5); p = 0.008). In addition, in the nail group the mode of failure was either cut-out of the distal screws or breakage of nails, and in the locking plate group breakage of the plate was always the mode of failure. Locking nail constructs had significantly longer mean fatigue life than non-locking nail constructs (78 900 cycles (sd 25 600) vs 52 400 cycles (sd 22 500); p = 0.04).

The new locking retrograde femoral nail showed better stiffness and fatigue life than locking plates, and superior fatigue life to non-locking nails, which may be advantageous in elderly patients.

Cite this article: Bone Joint J 2014;96-B:114–21.

The purpose of this study was to assess the stability of a developmental pelvic reconstruction system which extends the concept of triangular osteosynthesis with fixation anterior to the lumbosacral pivot point. An unstable Tile type-C fracture, associated with a sacral transforaminal fracture, was created in synthetic pelves. The new concept was compared with three other constructs, including bilateral iliosacral screws, a tension band plate and a combined plate with screws. The pubic symphysis was plated in all cases. The pelvic ring was loaded to simulate single-stance posture in a cyclical manner until failure, defined as a displacement of 2 mm or 2°. The screws were the weakest construct, failing with a load of 50 N after 400 cycles, with maximal translation in the craniocaudal axis of 12 mm. A tension band plate resisted greater load but failure occurred at 100 N, with maximal rotational displacement around the mediolateral axis of 2.3°.

The combination of a plate and screws led to an improvement in stability at the 100 N load level, but rotational failure still occurred around the mediolateral axis. The pelvic reconstruction system was the most stable construct, with a maximal displacement of 2.1° of rotation around the mediolateral axis at a load of 500 N.

Aims

The aims of this study were to identify means to quantify coronal plane displacement associated with distal radius fractures (DRFs), and to understand their relationship to radial inclination (RI).

There have been recent reports linking alendronate and a specific pattern of subtrochanteric insufficiency fracture. We performed a retrospective review of all subtrochanteric fractures admitted to our institution between 2001 and 2007. There were 20 patients who met the inclusion criteria, 12 of whom were on long-term alendronate. Alendronate-associated fractures tend to be bilateral (Fisher’s exact test, p = 0.018), have unique radiological features (p < 0.0005), be associated radiologically with a pre-existing ellipsoid thickening of the lateral femoral cortex and are likely to be preceded by prodromal pain. Biomechanical investigations did not suggest overt metabolic bone disease. Only one patient on alendronate had osteoporosis prior to the start of therapy. We used these findings to develop a management protocol to optimise fracture healing. We also advocate careful surveillance in individuals at-risk, and present our experience with screening and prophylactic fixation in selected patients

Aims

Minimally invasive fixation of pelvic fragility fractures is recommended to reduce pain and allow early mobilization. The purpose of this study was to evaluate the outcome of two different stabilization techniques in bilateral fragility fractures of the sacrum (BFFS).

Aims

This study aimed to analyze the correlation between transverse process (TP) fractures of the fourth (L4) and fifth (L5) lumbar vertebrae and biomechanical and haemodynamic stability in patients with a pelvic ring injury, since previous data are inconsistent.

Aims

The aim of this study was to evaluate the clinical and radiological outcomes of locking plate fixation, with and without an associated fibular strut allograft, for the treatment of displaced proximal humeral fractures in elderly osteoporotic patients.

This article presents a unified clinical theory that links established facts about the physiology of bone and homeostasis, with those involved in the healing of fractures and the development of nonunion. The key to this theory is the concept that the tissue that forms in and around a fracture should be considered a specific functional entity. This ‘bone-healing unit’ produces a physiological response to its biological and mechanical environment, which leads to the normal healing of bone. This tissue responds to mechanical forces and functions according to Wolff’s law, Perren’s strain theory and Frost’s concept of the “mechanostat”. In response to the local mechanical environment, the bone-healing unit normally changes with time, producing different tissues that can tolerate various levels of strain. The normal result is the formation of bone that bridges the fracture – healing by callus. Nonunion occurs when the bone-healing unit fails either due to mechanical or biological problems or a combination of both. In clinical practice, the majority of nonunions are due to mechanical problems with instability, resulting in too much strain at the fracture site. In most nonunions, there is an intact bone-healing unit. We suggest that this maintains its biological potential to heal, but fails to function due to the mechanical conditions. The theory predicts the healing pattern of multifragmentary fractures and the observed morphological characteristics of different nonunions. It suggests that the majority of nonunions will heal if the correct mechanical environment is produced by surgery, without the need for biological adjuncts such as autologous bone graft.

Cite this article: Bone Joint J 2016;98-B:884–91.

It is becoming increasingly common for a patient to have ipsilateral hip and knee replacements. The inter-prosthetic (IP) distance, the distance between the tips of hip and knee prostheses, has been thought to be associated with an increased risk of IP fracture. Small gap distances are generally assumed to act as stress risers, although there is no real biomechanical evidence to support this.

The purpose of this study was to evaluate the influence of IP distance, cortical thickness and bone mineral density on the likelihood of an IP femoral fracture.

A total of 18 human femur specimens were randomised into three groups by bone density and cortical thickness. For each group, a defined IP distance of 35 mm, 80 mm or 160 mm was created by choosing the appropriate lengths of component. The maximum fracture strength was determined using a four-point bending test.

The fracture force of all three groups was similar (p = 0.498). There was a highly significant correlation between the cortical area and the fracture strength (r = 0.804, p <  0.001), whereas bone density showed no influence.

This study suggests that the IP distance has little influence on fracture strength in IP femoral fractures: the thickness of the cortex seems to be the decisive factor.

Cite this article: Bone Joint J 2014;96-B:1378–84.

We investigated the static and cyclical strength of parallel and angulated locking plate screws using rigid polyurethane foam (0.32 g/cm³) and bovine cancellous bone blocks. Custom-made stainless steel plates with two conically threaded screw holes with different angulations (parallel, 10° and 20° divergent) and 5 mm self-tapping locking screws underwent pull-out and cyclical pull and bending tests. The bovine cancellous blocks were only subjected to static pull-out testing. We also performed finite element analysis for the static pull-out test of the parallel and 20° configurations. In both the foam model and the bovine cancellous bone we found the significantly highest pull-out force for the parallel constructs. In the finite element analysis there was a 47% more damage in the 20° divergent constructs than in the parallel configuration. Under cyclical loading, the mean number of cycles to failure was significantly higher for the parallel group, followed by the 10° and 20° divergent configurations.

In our laboratory setting we clearly showed the biomechanical disadvantage of a diverging locking screw angle under static and cyclical loading.

Bicondylar tibial plateau fractures result from high-energy injuries. Fractures of the tibial plateau can involve the tibial tubercle, which represents a disruption to the extensor mechanism and logically must be stabilised. The purpose of this study was to identify the incidence of an independent tibial tubercle fracture in bicondylar tibial plateau fractures, and to report management strategies and potential complications. We retrospectively reviewed a prospectively collected orthopaedic trauma database for the period January 2003 to December 2008, and identified 392 bicondylar fractures of the tibial plateau, in which 85 tibial tubercle fractures (21.6%) were identified in 84 patients. There were 60 men and 24 women in our study group, with a mean age of 45.4 years (18 to 71). In 84 fractures open reduction and internal fixation was undertaken, either with screws alone (23 patients) or with a plate and screws (61 patients). The remaining patient was treated non-operatively. In all, 52 fractures were available for clinical and radiological assessment at a mean follow-up of 58.5 weeks (24 to 94). All fractures of the tibial tubercle united, but 24 of 54 fractures (46%) required a secondary procedure for their tibial plateau fracture. Four patients reported pain arising from prominent tubercle plates and screws, which in one patient required removal. Tibial tubercle fractures occurred in over one-fifth of the bicondylar tibial plateau fractures in our series. Fixation is necessary and can be reliably performed with screws alone or with a screw and plate, which restores the extensor mechanism and facilitates early knee flexion.

Cite this article: Bone Joint J 2013;95-B:1697–1702.

Although the importance of lateral femoral wall integrity is increasingly being recognised in the treatment of intertrochanteric fracture, little attention has been put on the development of a secondary post-operative fracture of the lateral wall. Patients with post-operative fractures of the lateral wall were reported to have high rates of re-operation and complication. To date, no predictors of post-operative lateral wall fracture have been reported. In this study, we investigated the reliability of lateral wall thickness as a predictor of lateral wall fracture after dynamic hip screw (DHS) implantation.

A total of 208 patients with AO/OTA 31-A1 and -A2 classified intertrochanteric fractures who received internal fixation with a DHS between January 2003 and May 2012 were reviewed. There were 103 men and 150 women with a mean age at operation of 78 years (33 to 94). The mean follow-up was 23 months (6 to 83). The right side was affected in 97 patients and the left side in 111. Clinical information including age, gender, side, fracture classification, tip–apex distance, follow-up time, lateral wall thickness and outcome were recorded and used in the statistical analysis.

Fracture classification and lateral wall thickness significantly contributed to post-operative lateral wall fracture (both p < 0.001). The lateral wall thickness threshold value for risk of developing a secondary lateral wall fracture was found to be 20.5 mm.

To our knowledge, this is the first study to investigate the risk factors of post-operative lateral wall fracture in intertrochanteric fracture. We found that lateral wall thickness was a reliable predictor of post-operative lateral wall fracture and conclude that intertrochanteric fractures with a lateral wall thickness < 20.5 mm should not be treated with DHS alone.

Cite this article: Bone Joint J 2013;95-B:1134–8.

Most fractures of the radial head are stable undisplaced or minimally displaced partial fractures without an associated fracture of the elbow or forearm or ligament injury, where stiffness following non-operative management is the primary concern. Displaced unstable fractures of the radial head are usually associated with other fractures or ligament injuries, and restoration of radiocapitellar contact by reconstruction or prosthetic replacement of the fractured head is necessary to prevent subluxation or dislocation of the elbow and forearm. In fractures with three or fewer fragments (two articular fragments and the neck) and little or no metaphyseal comminution, open reduction and internal fixation may give good results. However, fragmented unstable fractures of the radial head are prone to early failure of fixation and nonunion when fixed. Excision of the radial head is associated with good long-term results, but in patients with instability of the elbow or forearm, prosthetic replacement is preferred.

This review considers the characteristics of stable and unstable fractures of the radial head, as well as discussing the debatable aspects of management, in light of the current best evidence.

Cite this article: Bone Joint J 2013;95-B:151–9.

Introduction

The objective of this study was to determine if a synthetic bone substitute would provide results similar to bone from osteoporotic femoral heads during in vitro testing with orthopaedic implants. If the synthetic material could produce results similar to those of the osteoporotic bone, it could reduce or eliminate the need for testing of implants on bone.

Objectives

We aimed to further evaluate the biomechanical characteristics of two locking screws versus three standard bicortical screws in synthetic models of normal and osteoporotic bone.

Filling the empty holes in peri-articular locking plates may improve the fatigue strength of the fixation. The purpose of this in vitro study was to investigate the effect of plugging the unused holes on the fatigue life of peri-articular distal femoral plates used to fix a comminuted supracondylar fracture model.

A locking/compression plate was applied to 33 synthetic femurs and then a 6 cm metaphyseal defect was created (AO Type 33-A3). The specimens were then divided into three groups: unplugged, plugged with locking screw only and fully plugged holes. They were then tested using a stepwise or run-out fatigue protocol, each applying cyclic physiological multiaxial loads.

All specimens in the stepwise group failed at the 770 N load level. The mean number of cycles to failure for the stepwise specimen was 25 500 cycles (sd 1500), 28 800 cycles (sd 6300), and 26 400 cycles (sd 2300) cycles for the unplugged, screw only and fully plugged configurations, respectively (p = 0.16). The mean number of cycles to failure for the run-out specimens was 42 800 cycles (sd 10 700), 36 000 cycles (sd 7200), and 36 600 cycles (sd 10 000) for the unplugged, screw only and fully plugged configurations, respectively (p = 0.50). There were also no differences in axial or torsional stiffness between the constructs. The failures were through the screw holes at the level of comminution.

In conclusion, filling the empty combination locking/compression holes in peri-articular distal femur locking plates at the level of supracondylar comminution does not increase the fatigue life of the fixation in a comminuted supracondylar femoral fracture model (AO 33-A3) with a 6 cm gap.

The aim of this study was to review the number of patients operated on for traumatic disruption of the pubic symphysis who developed radiological signs of movement of the anterior pelvic metalwork during the first post-operative year, and to determine whether this had clinical implications. A consecutive series of 49 patients undergoing internal fixation of a traumatic diastasis of the pubic symphysis were studied. All underwent anterior fixation of the diastasis, which was frequently combined with posterior pelvic fixation. The fractures were divided into groups using the Young and Burgess classification for pelvic ring fractures. The different combinations of anterior and posterior fixation adopted to stabilise the fractures and the type of movement of the metalwork which was observed were analysed and related to functional outcome during the first post-operative year.

In 15 patients the radiographs showed movement of the anterior metalwork, with broken or mobile screws or plates, and in six there were signs of a recurrent diastasis. In this group, four patients required revision surgery; three with anterior fixation and one with removal of anterior pelvic metalwork; the remaining 11 functioned as well as the rest of the study group.

We conclude that radiological signs of movement in the anterior pelvic metalwork, albeit common, are not in themselves an indication for revision surgery.

We carried out a retrospective review of 47 intra-articular fractures of the calcaneum treated by open reduction and internal fixation in 45 patients by a single surgeon between 1993 and 2001. The fractures were evaluated before operation by plain radiographs and a CT scan using Sanders’ classification. Osteosynthesis involved a lateral approach and the use of the AO calcaneal plate. The mean follow-up was for ten years (7 to 15). Clinical assessment included the American Orthopaedic Foot and Ankle Society Score (AOFAS), the Creighton-Nebraska Score, the Kerr, Prothero, Atkins Score and the SF-36 Health Questionnaire. The radiological evaluation consisted of lateral and axial views of the os calcis. Arthritic changes in the subtalar joint were assessed with an internal oblique view and were graded using the Morrey and Wiedeman scale.

There were 18 excellent (38.3%), 17 good (36.2%), three fair (6.3%) and nine poor (19.2%) results. Five patients had a superficial wound infection and five others eventually had a subtalar arthrodesis because of continuing pain. Restoration of Böhler’s angle was associated with a better outcome. The degree of arthritic change in the subtalar joint did not correlate with the outcome scores or Sanders’ classification. Prompt osteosynthesis should be considered for intra-articular fractures of the calcaneum in order to restore the shape of the hindfoot and Böhler’s angle.

A series of 103 acute fractures of the coronoid process of the ulna in 101 patients was reviewed to determine their frequency. The Regan-Morrey classification, treatment, associated injuries, course and outcomes were evaluated. Of the 103 fractures, 34 were type IA, 17 type IB, ten type IIA, 19 type IIB, ten type IIIA and 13 type IIIB. A total of 44 type-I fractures (86%) were treated conservatively, while 22 type-II (76%) and all type-III fractures were managed by operation.

At follow-up at a mean of 3.4 years (1 to 8.9) the range of movement differed significantly between the types of fracture (p = 0.002). Patients with associated injuries had a lower Mayo elbow performance score (p = 0.03), less extension (p = 0.03), more pain (p = 0.007) and less pronosupination (p = 0.004), than those without associated injuries. The presence of a fracture of the radial head had the greatest effect on outcome. An improvement in outcome relative to that of a previous series was noted, perhaps because of more aggressive management and early mobilisation. While not providing complete information about the true details of a fracture and its nature, the Regan-Morrey classification is useful as a broad index of severity and prognosis.