Aims. Tantalum (Ta) trabecular metal components are increasingly used to reconstruct major bone defects in revision arthroplasty surgery. It is known that some metals such as silver have antibacterial properties. Recent reports have raised the question regarding whether Ta components are protective against infection in revision surgery. This laboratory study aimed to establish whether Ta has intrinsic antibacterial properties against planktonic bacteria, or the ability to inhibit biofilm formation. Materials and Methods. Equal-sized pieces of Ta and titanium (Ti) acetabular components were sterilised and incubated with a low dose inoculum of either Staphylococcus (S.) aureus or S. epidermidis for 24 hours. After serial dilution, colony forming units (cfu) were quantified on Mueller-Hinton agar plates. In order to establish whether biofilms formed to a greater extent on one material than the other, these Ta and Ti pieces were then washed twice, sonicated and washed again to remove loosely adhered planktonic bacteria. They were then re-incubated for 24 hours prior to quantifying the number of cfu. All experiments were performed in triplicate. Results. More than 1x10. 8. cfu/ml were observed in both the Ta and Ti experiments. After washing and sonication, more than 2x10. 7. cfu/ml were observed for both Ta and Ti groups. The results were the same for both S. aureus and S. epidermidis. Conclusion. Compared with Ti controls, Ta did not demonstrate any intrinsic antibacterial activity or ability to inhibit biofilm formation. Hence, intrinsic antimicrobial properties of Ta do not account for the previously observed reduction in the frequency of subsequent infections when Ta was used in revision procedures. . Cite this article: Bone Joint J 2017;99-B:1153–6

The introduction of a trabecular tantalum rod has been proposed for the management of early-stage osteonecrosis of the femoral head but serves as a single-point of support of the necrotic lesion. We describe a technique using two or three 4.2 mm (or later 4.7 mm) tantalum pegs for the prevention of collapse of the necrotic lesion. We prospectively studied 21 patients (26 hips) with non-traumatic osteonecrosis of the femoral head treated in this manner. Of these, 21 patients (24 hips) were available for radiological and clinical evaluation at a mean follow-up of 46 months (18 to 67). Radiological assessment showed that only eight hips deteriorated according to the Association Research Circulation Osseous classification, and four hips according to the Classification of the Japanese Investigation Committee of Health and Welfare. Functional improvement was obtained with an improvement in the mean Harris hip score from 65.2 (33.67 to 95) to 88.1 (51.72 to 100), the mean Merle D’Aubigné-Postel score from 13 (6 to 18) to 16 (11 to 18), a mean visual analogue score for pain from 5.2 (0 to 9.5) to 2.6 (0 to 7), and the mean Short-Form 36 score from 80.4 (56.8 to 107.1) to 92.4 (67.5 to 115.7). Of these 24 hips followed for a minimum of 18 months, three were considered as failures at the final follow-up, having required total hip replacement. One of the hips without full follow-up was also considered to be a failure. In more than two-thirds of the surviving hips a satisfactory clinical outcome was achieved with promising radiological findings. The estimated mean implant survival was 60 months (95% confidence interval 53.7 to 66.3)

Aims. One method of femoral head preservation following avascular necrosis (AVN) is core decompression and insertion of a tantalum rod. However, there may be a high failure rate associated with this procedure. The purpose of this study was to document the clinical and radiological outcomes following total hip arthroplasty (THA) subsequent to failed tantalum rod insertion. Patients and Methods. A total of 37 failed tantalum rods requiring total hip arthroplasty were identified from a prospective database. There were 21 hips in 21 patients (12 men and nine women, mean age 37 years, 18 to 53) meeting minimum two year clinical and radiographic follow-up whose THAs were carried out between November 2002 and April 2013 (mean time between tantalum rod implantation and conversion to a THA was 26 months, 6 to 72). These were matched by age and gender to individuals (12 men, nine women, mean age 40 years, 18 to 58) receiving THA for AVN without prior tantalum rod insertion. Results. There were no functional outcome differences between the two groups. Tantalum residue was identified on all post-operative radiographs in the tantalum group. Linear wear rates were comparable between groups with no evidence of catastrophic wear in either group. Conclusion. In the short term, tantalum rod implantation does not demonstrate an adverse effect on subsequent total joint replacement surgery. There is however, a high rate of retained tantalum debris on post-operative radiographs and thus there is an unknown risk of accelerated articular wear necessitating longer term study. Cite this article: Bone Joint J 2016;98-B:1175–9

Aims. Reconstruction of the acetabulum after failed total hip arthroplasty (THA) can be a surgical challenge in the presence of severe bone loss. We report the long-term survival of a porous tantalum revision acetabular component, its radiological appearance and quality of life outcomes. Patients and Methods. We reviewed the results of 46 patients who had undergone revision of a failed acetabular component with a Paprosky II or III bone defect and reconstruction with a hemispherical, tantalum acetabular component, supplementary screws and a cemented polyethylene liner. Results. After a minimum follow-up of ten years (ten to 12), the survivorship of the porous tantalum acetabular component was 96%, with further revision of the acetabular component as the end point. The ten-year survivorship, with hip revision for any reason as the end point, was 92%. We noted excellent pain relief (mean Western Ontario and McMaster Universities Arthritis Index (WOMAC) score pain 92.6, (40 to 100)) and good functional outcomes (mean WOMAC function 90.3 (30.9 to 100), mean University of California Los Angeles activity scale 5 (2 to 10)) and generic quality of life measures (mean Short Form-12 (SF-12) physical component 48.3 (18.1 to 56.8), mean SF-12 mental component 56.7 (32.9 to 70.3)). Patient satisfaction with pain relief, function and return to recreational activities were excellent. Take home message: Uncemented acetabular reconstruction using a tantalum acetabular component gives excellent clinical and quality of life outcomes at a minimum follow-up of ten years. Cite this article: Bone Joint J 2016;98-B:767–71

We hypothesised that the use of tantalum (Ta) acetabular components in revision total hip arthroplasty (THA) was protective against subsequent failure due to infection. We identified 966 patients (421 men, 545 women and 990 hips) who had undergone revision THA between 2000 and 2013. The mean follow up was 40.2 months (3 months to 13.1 years). The mean age of the men and women was 62.3 years (31 to 90) and 65.1 years (25 to 92), respectively. . Titanium (Ti) acetabular components were used in 536 hips while Ta components were used in 454 hips. In total, 73 (7.3%) hips experienced subsequent acetabular failure. The incidence of failure was lower in the Ta group at 4.4% (20/454) compared with 9.9% (53/536) in the Ti group (p < 0.001, odds ratio 2.38; 95% CI 1.37 to 4.27). Among the 144 hips (64 Ta, 80 Ti) for which revision had been performed because of infection, failure due to a subsequent infection was lower in the Ta group at 3.1% (2/64) compared with 17.5% (14/80) for the Ti group (p = 0.006). . Thus, the use of Ta acetabular components during revision THA was associated with a lower incidence of failure from all causes and Ta components were associated with a lower incidence of subsequent infection when used in patients with periprosthetic joint infection. . Cite this article: Bone Joint J 2015;97-B:45–9

There are several techniques for the accurate measurement of the migration of components after arthroplasty some of which require the operative placement of tantalum balls. We have reviewed the position and migration of these markers in 64 patients after total hip arthroplasty. In 40% of cases, one or more balls was seen to be outside the proximal femur on the postoperative radiograph, although all were considered to be within the bone at operation. In two hips, one ball appeared to have migrated towards the joint, although none was seen within the joint. Misplacement was not related to the experience of the surgeon or the operative approach. Migration analysis which necessitates the insertion of tantalum balls requires careful technique to avoid a potential source of third-body wear. It should probably be used only for research in small series of patients

Aims

The use of trabecular metal (TM) shells supported by augments has provided good mid-term results after revision total hip arthroplasty (THA) in patients with a bony defect of the acetabulum. The aim of this study was to assess the long-term implant survivorship and radiological and clinical outcomes after acetabular revision using this technique.

Between January 1998 and December 1998, 82 consecutive patients (86 hips) underwent total hip arthroplasty using a trabecular metal monoblock acetabular component. All patients had a clinical and radiological follow-up evaluation at six, 12 and 24 weeks, 12 months, and then annually thereafter. On the initial post-operative radiograph 25 hips had a gap between the outer surface of the component and the acetabular host bed which ranged from 1 to 5 mm. All patients were followed up clinically and radiologically for a mean of 7.3 years (7 to 7.5). The 25 hips with the 1 to 5 mm gaps were studied for component migration at two years using the Einzel-Bild-Roentgen-Analyse (EBRA) digital measurement method. At 24 weeks all the post-operative gaps were filled with bone and no acetabular component had migrated. The radiographic outcome of all 86 components showed no radiolucent lines and no evidence of lysis. No acetabular implant was revised. There were no dislocations or other complications. The bridging of the interface gaps (up to 5 mm) by the trabecular metal monoblock acetabular component indicates the strong osteoconductive, and possibly osteoinductive, properties of trabecular metal.

Aims. Reconstruction of the acetabulum after resection of a periacetabular malignancy is technically challenging and many different techniques have been used with varying success. Our aim was to prepare a systematic review of the literature dealing with these techniques in order to clarify the management, the rate of complications and the outcomes. Patients and Methods. A search of PubMed and MEDLINE was conducted for English language articles published between January 1990 and February 2017 with combinations of key search terms to identify studies dealing with periacetabular resection with reconstruction in patients with a malignancy. Studies in English that reported radiographic or clinical outcomes were included. Data collected from each study included: the number and type of reconstructions, the pathological diagnosis of the lesions, the mean age and follow-up, gender distribution, implant survivorship, complications, functional outcome, and mortality. The results from individual studies were combined for the general analysis, and then grouped according to the type of reconstruction. . Results. A total of 57 studies met the inclusion criteria and included 1700 patients. Most lesions were metastatic (41%), followed by chondrosarcoma (29%), osteosarcoma (10%), Ewing’s sarcoma (7%), and multiple myeloma (2%). The techniques of reconstruction were divided into seven types for analysis: those involving a Harrington reconstruction, a saddle prosthesis, an allograft and allograft prosthesis composite, a pasteurised autograft, a porous tantalum implant, a custom-made prosthesis and a modular hemipelvic reconstruction. The rate of complications was 50%, with infection (14%) and instability (8%) being the most common. Mortality data were available for 1427 patients (84%); 50% had died of disease progression, 23% were alive with disease, and 27% had no evidence of disease at a mean follow-up of 3.4 years (0 to 34). . Conclusion. Both the rate of complications and mortality are high following resection of oncological periacetabular lesions and reconstruction. Many types of reconstruction have been used with unique challenges and complications for each technique. Newer prostheses, including custom-made prostheses and porous tantalum implants and augments, have shown promising early functional and radiographic outcomes. . Cite this article: Bone Joint J 2018;100-B(1 Supple A):22–30

A pelvic discontinuity occurs when the superior and inferior parts of the hemi-pelvis are no longer connected, which is difficult to manage when associated with a failed total hip replacement. Chronic pelvic discontinuity is found in 0.9% to 2.1% of hip revision cases with risk factors including severe pelvic bone loss, female gender, prior pelvic radiation and rheumatoid arthritis. Common treatment options include: pelvic plating with allograft, cage reconstruction, custom triflange implants, and porous tantalum implants with modular augments. The optimal technique is dependent upon the degree of the discontinuity, the amount of available bone stock and the likelihood of achieving stable healing between the two segments. A method of treating pelvic discontinuity using porous tantalum components with a distraction technique that achieves both initial stability and subsequent long-term biological fixation is described. Cite this article: Bone Joint J 2014;96-B(11 Suppl A):73–7

A retrospective review was performed of patients undergoing primary cementless total knee replacement (TKR) using porous tantalum performed by a group of surgical trainees. Clinical and radiological follow-up involved 79 females and 26 males encompassing 115 knees. The mean age was 66.9 years (36 to 85). Mean follow-up was 7 years (2 to 11). Tibial and patellar components were porous tantalum monoblock implants, and femoral components were posterior stabilised (PS) in design with cobalt–chromium fibre mesh. Radiological assessments were made for implant positioning, alignment, radiolucencies, lysis, and loosening. There was 95.7% survival of implants. There was no radiological evidence of loosening and no osteolysis found. No revisions were performed for aseptic loosening. Average tibial component alignment was 1.4° of varus (4°of valgus to 9° varus), and 6.2° (3° anterior to 15° posterior) of posterior slope. Mean femoral component alignment was 6.6° (1° to 11°) of valgus. Mean tibiofemoral alignment was 5.6° of valgus (7° varus to 16° valgus). Patellar tilt was a mean of 2.4° lateral (5° medial to 28° lateral). Patient satisfaction with improvement in pain was 91%. Cementless TKR incorporating porous tantalum yielded good clinical and radiological outcomes at a mean of follow-up of seven-years. Cite this article: Bone Joint J 2014;96-B(11 Suppl A):87–92

Between November 1997 and December 2000 we performed 27 total hip replacements in 22 patients with high congenital dislocation of the hip using porous tantalum monoblock acetabular components implanted in the true acetabular bed. Clinical and radiological evaluation was performed at regular intervals for a mean of 10.2 years (8.5 to 12). The mean Harris Hip Score improved from 48.3 (15 to 65) pre-operatively to 89.5 (56 to 100) at the final follow-up. The mean Oxford Hip Score was 49.5 (35 to 59) pre-operatively and decreased to 21.2 (12 to 48) at one year and 15.2 (10 to 28) at final follow-up. Migration of the acetabular component was assessed with the EBRA software system. There was a mean migration of 0.68 mm (0.49 to 0.8) in the first year and a mean 0.89 mm (0.6 to 0.98) in the second year, after excluding one initial excessive migration. No revision was necessary for any reason, no acetabular component became loose, and no radiolucent lines were observed at the final follow-up. The porous tantalum monoblock acetabular component is an implant offering adequate initial stability in conjunction with a modulus of elasticity and porosity close to that of cancellous bone. It favours bone ingrowth, leading to good mid-term results

Objectives. Favourable results for collarless polished tapered stems have been reported, and cement creep due to taper slip may be a contributing factor. However, the ideal cement thickness around polished stems remains unknown. We investigated the influence of cement thickness on stem subsidence and cement creep. Methods. We cemented six collarless polished tapered (CPT) stems (two stems each of small, medium and large sizes) into composite femurs that had been reamed with a large CPT rasp to achieve various thicknesses of the cement mantle. Two or three tantalum balls were implanted in the proximal cement in each femur. A cyclic loading test was then performed for each stem. The migration of the balls was measured three-dimensionally, using a micro-computed tomography (CT) scanner, before and after loading. A digital displacement gauge was positioned at the stem shoulder, and stem subsidence was measured continuously by the gauge. Final stem subsidence was measured at the balls at the end of each stem. Results. A strong positive correlation was observed between mean cement thickness and stem subsidence in the CT slices on the balls. In the small stems, the balls moved downward to almost the same extent as the stem. There was a significant negative correlation between cement thickness and the horizontal:downward ratio of ball movement. Conclusion. Collarless polished tapered stems with thicker cement mantles resulted in greater subsidence of both stem and cement. This suggests that excessive thickness of the cement mantle may interfere with effective radial cement creep. Cite this article: E. Takahashi, A. Kaneuji, R. Tsuda, Y. Numata, T. Ichiseki, K. Fukui, N. Kawahara. The influence of cement thickness on stem subsidence and cement creep in a collarless polished tapered stem: When are thick cement mantles detrimental? Bone Joint Res 2017;6:–357. DOI: 10.1302/2046-3758.65.BJR-2017-0028.R1

Aims

Refobacin Bone Cement R and Palacos R + G bone cement were introduced to replace the original cement Refobacin Palacos R in 2005. Both cements were assumed to behave in a biomechanically similar fashion to the original cement. The primary aim of this study was to compare the migration of a polished triple-tapered femoral stem fixed with either Refobacin Bone Cement R or Palacos R + G bone cement. Repeated radiostereometric analysis was used to measure migration of the femoral head centre. The secondary aims were evaluation of cement mantle, stem positioning, and patient-reported outcome measures.

The ideal acetabular component is characterised by reliable, long-term fixation with physiological loading of bone and a low rate of wear. Trabecular metal is a porous construct of tantalum which promotes bony ingrowth, has a modulus of elasticity similar to that of cancellous bone, and should be an excellent material for fixation. Between 2004 and 2006, 55 patients were randomised to receive either a cemented polyethylene or a monobloc trabecular metal acetabular component with a polyethylene articular surface. We measured the peri-prosthetic bone density around the acetabular components for up to two years using dual-energy x-ray absorptiometry. We found evidence that the cemented acetabular component loaded the acetabular bone centromedially whereas the trabecular metal monobloc loaded the lateral rim and behaved like a hemispherical rigid metal component with regard to loading of the acetabular bone. We suspect that this was due to the peripheral titanium rim used for the mechanism of insertion

Aims

Dislocation remains a leading cause of failure following revision total hip arthroplasty (THA). While dual-mobility (DM) bearings have been shown to mitigate this risk, options are limited when retaining or implanting an uncemented shell without modular DM options. In these circumstances, a monoblock DM cup, designed for cementing, can be cemented into an uncemented acetabular shell. The goal of this study was to describe the implant survival, complications, and radiological outcomes of this construct.

Aims

Instability is a common cause of failure after total hip arthroplasty. A novel reverse total hip has been developed, with a femoral cup and acetabular ball, creating enhanced mechanical stability. The purpose of this study was to assess the implant fixation using radiostereometric analysis (RSA), and the clinical safety and efficacy of this novel design.

Aims

The primary outcome was investigating differences in wear, as measured by femoral head penetration, between cross-linked vitamin E-diffused polyethylene (vE-PE) and cross-linked polyethylene (XLPE) acetabular component liners and between 32 and 36 mm head sizes at the ten-year follow-up. Secondary outcomes included acetabular component migration and patient-reported outcome measures (PROMs) such as the EuroQol five-dimension questionnaire, 36-Item Short-Form Health Survey, Harris Hip Score, and University of California, Los Angeles Activity Scale (UCLA).

Aims

The primary aim of this trial was to compare the subsidence of two similar hydroxyapatite-coated titanium femoral components from different manufacturers. Secondary aims were to compare rotational migration (anteversion/retroversion and varus/valgus tilt) and patient-reported outcome measures between both femoral components.

Aims

Radiostereometric analysis (RSA) is the most accurate radiological method to measure in vivo wear of highly cross-linked polyethylene (XLPE) acetabular components. We have previously reported very low wear rates for a sequentially irradiated and annealed X3 XLPE liner (Stryker Orthopaedics, USA) when used in conjunction with a 32 mm femoral heads at ten-year follow-up. Only two studies have reported the long-term wear rate of X3 liners used in conjunction with larger heads using plain radiographs which have poor sensitivity. The aim of this study was to measure the ten-year wear of thin X3 XLPE liners against larger 36 or 40 mm articulations with RSA.

Aims

The duration of systemic antibiotic treatment following first-stage revision surgery for periprosthetic joint infection (PJI) after total hip arthroplasty (THA) is contentious. Our philosophy is to perform an aggressive debridement, and to use a high local concentration of targeted antibiotics in cement beads and systemic prophylactic antibiotics alone. The aim of this study was to assess the success of this philosophy in the management of PJI of the hip using our two-stage protocol.

Aims

The objective of this study was to compare the two-year migration and clinical outcomes of a new cementless hydroxyapatite (HA)-coated titanium acetabular shell with its previous version, which shared the same geometrical design but a different manufacturing process for applying the titanium surface.

Aims

The Exeter short stem was designed for patients with Dorr type A femora and short-term results are promising. The aim of this study was to evaluate the minimum five-year stem migration pattern of Exeter short stems in comparison with Exeter standard stems.

Aims

Although the Fitmore Hip Stem has been on the market for almost 15 years, it is still not well documented in randomized controlled trials. This study compares the Fitmore stem with the CementLeSs (CLS) in several different clinical and radiological aspects. The hypothesis is that there will be no difference in outcome between stems.

Aims

BoneMaster is a thin electrochemically applied hydroxyapatite (HA) coating for orthopaedic implants that is quickly resorbed during osseointegration. Early stabilization is a surrogacy marker of good survival of femoral stems. The hypothesis of this study was that a BoneMaster coating yields a fast early and lasting fixation of stems.

Aims

One-stage exchange for periprosthetic joint infection (PJI) in total hip arthroplasty (THA) is gaining popularity. The outcome for a repeat one-stage revision THA after a failed one-stage exchange for infection remains unknown. The aim of this study was to report the infection-free and all-cause revision-free survival of repeat one-stage exchange, and to investigate the association between the Musculoskeletal Infection Society (MSIS) staging system and further infection-related failure.

Aims

The aim of this study was to compare the mid-term patient-reported outcome, bone remodelling, and migration of a short stem (Collum Femoris Preserving; CFP) with a conventional uncemented stem (Corail).

Aims

The main advantage of 3D-printed, off-the-shelf acetabular implants is the potential to promote enhanced bony fixation due to their controllable porous structure. In this study we investigated the extent of osseointegration in retrieved 3D-printed acetabular implants.

Aims

Femoral bone preparation using compaction technique has been shown to preserve bone and improve implant fixation in animal models. No long-term clinical outcomes are available. There are no significant long-term differences between compaction and broaching techniques for primary total hip arthroplasty (THA) in terms of migration, clinical, and radiological outcomes.

Aims

We aimed to investigate if the use of the largest possible cobalt-chromium head articulating with polyethylene acetabular inserts would increase the in vivo wear rate in total hip arthroplasty.

Aims

Highly polished stems with force-closed design have shown satisfactory clinical results despite being related to relatively high early migration. It has been suggested that the minimal thickness of cement mantles surrounding the femoral stem should be 2 mm to 4 mm to avoid aseptic loosening. The line-to-line cementing technique of the femoral stem, designed to achieve stem press-fit, challenges this opinion. We compared the migration of a highly polished stem with force-closed design by standard and line-to-line cementing to investigate whether differences in early migration of the stems occur in a clinical study.

Aims

The aim of this prospective cohort study was to evaluate the early migration of the TriFit cementless proximally coated tapered femoral stem using radiostereometric analysis (RSA).

Aims

Vitamin E-infused highly crosslinked polyethylene (VEPE) has been introduced into total hip arthroplasty (THA) with the aim of further improving the wear characteristics of moderately and highly crosslinked polyethylenes (ModXLPE and HXLPE). There are few studies analyzing the outcomes of vitamin E-infused components in cemented arthroplasty, though early acetabular component migration has been reported. The aim of this study was to measure five-year polyethylene wear and acetabular component stability of a cemented VEPE acetabular component compared with a ModXLPE cemented acetabular component.

Aims

To compare the in vivo long-term fixation achieved by two acetabular components with different porous ingrowth surfaces using radiostereometric analysis (RSA).

Aims

The most frequent indication for revision surgery in total hip arthroplasty (THA) is aseptic loosening. Aseptic loosening is associated with polyethylene liner wear, and wear may be reduced by using vitamin E-doped liners. The primary objective of this study was to compare proximal femoral head penetration into the liner between a) two cross-linked polyethylene (XLPE) liners (vitamin E-doped (vE-PE)) versus standard XLPE liners, and b) two modular femoral head diameters (32 mm and 36 mm).

Aims

Various surgical techniques have been described for total hip arthroplasty (THA) in patients with Crowe type III dislocated hips, who have a large acetabular bone defect. The aim of this study was to evaluate the long-term clinical results of patients in whom anatomical reconstruction of the acetabulum was performed using a cemented acetabular component and autologous bone graft from the femoral neck.

Aims

Bone stock restoration of acetabular bone defects using impaction bone grafting (IBG) in total hip arthroplasty may facilitate future re-revision in the event of failure of the reconstruction. We hypothesized that the acetabular bone defect during re-revision surgery after IBG was smaller than during the previous revision surgery. The clinical and radiological results of re-revisions with repeated use of IBG were also analyzed.

Aims

The direct anterior (DA) approach has been associated with rapid patient recovery after total hip arthroplasty (THA) but may be associated with more frequent femoral complications including implant loosening. The objective of this study was to determine whether the addition of a collar to the femoral stem affects implant migration, patient activity, and patient function following primary THA using the DA approach.

Aims

The purpose of this study was to evaluate the biological fixation of a 3D printed porous implant, with and without different hydroxyapatite (HA) coatings, in a canine model.

Aims

Short, bone-conserving femoral components are increasingly used in total hip arthroplasty (THA). They are expected to allow tissue-conserving implantation and to render future revision surgery more straightforward but the long-term data on such components is limited. One such component is the global tissue-sparing (GTS) stem. Following the model for stepwise introduction of new orthopaedic implants, we evaluated early implant fixation and clinical outcome of this novel short-stem THA and compared it to that of a component with established good long-term clinical outcome.

Aims

Radiostereometric analysis (RSA) studies of vitamin E-doped, highly crosslinked polyethylene (VEPE) liners show low head penetration rates in cementless acetabular components. There is, however, currently no data on cemented VEPE acetabular components in total hip arthroplasty (THA). The aim of this study was to evaluate the safety of a new cemented VEPE component, compared with a conventional polyethylene (PE) component regarding migration, head penetration, and clinical results.

Aims

Single-stage revision is not widely pursued due to restrictive inclusion criteria. In this study, we evaluated the results of single-stage revision of chronically infected total hip arthroplasty (THA) using broad inclusion criteria and cementless implants.

Aims

The purpose of this retrospective study was to evaluate the minimum five-year outcome of revision total hip arthroplasty (THA) using the Kerboull acetabular reinforcement device (KARD) in patients with Paprosky type III acetabular defects and destruction of the inferior margin of the acetabulum.

Aims

Vitamin E-diffused, highly crosslinked polyethylene (VEPE) and porous titanium-coated (PTC) shells were introduced in total hip arthroplasty (THA) to reduce the risk of aseptic loosening. The purpose of this study was: 1) to compare the wear properties of VEPE to moderately crosslinked polyethylene; 2) to assess the stability of PTC shells; and 3) to report their clinical outcomes at seven years.

Objectives

In order to address acetabular defects, porous metal revision acetabular components and augments have been developed, which require fixation to each other. The fixation technique that results in the smallest relative movement between the components, as well as its influence on the primary stability with the host bone, have not previously been determined.

Aims

The advent of trabecular metal (TM) augments has revolutionized the management of severe bone defects during acetabular reconstruction. The purpose of this study was to evaluate patients undergoing revision total hip arthroplasty (THA) with the use of TM augments for reconstruction of Paprosky IIIA and IIIB defects.

Aims

The aim of this study was to determine the stability of a new short femoral stem compared with a conventional femoral stem in patients undergoing cementless total hip arthroplasty (THA), in a prospective randomized controlled trial using radiostereometric analysis (RSA).

Aims

Post-operative migration of cemented acetabular components as measured by radiostereometric analysis (RSA) has a strong predictive power for late, aseptic loosening. Also, radiolucent lines predict late loosening. Migration has been reduced by systemic bisphosphonate treatment in randomised trials of hip and knee arthroplasty. Used as a local treatment, a higher local dose of bisphosphonate can be achieved without systemic exposure. We wished to see if this principle could be applied usefully in total hip arthroplasty (THA).

Aims

Few reconstructive techniques are available for patients requiring complex acetabular revisions such as those involving Paprosky type 2C, 3A and 3B deficiencies and pelvic discontinuity. Our aim was to describe the development of the patient specific Triflange acetabular component for use in these patients, the surgical technique and mid-term results. We include a description of the pre-operative CT scanning, the construction of a model, operative planning, and surgical technique. All implants were coated with porous plasma spray and hydroxyapatite if desired.

Aims

Severe acetabular bone loss and pelvic discontinuity (PD) present particular challenges in revision total hip arthroplasty. To deal with such complex situations, cup-cage reconstruction has emerged as an option for treating this situation. We aimed to examine our success in using this technique for these anatomical problems.