Aims. Periprosthetic joint infection (PJI) is a serious complication of total hip arthroplasty (THA). Different bearing surface materials have different surface properties and it has been suggested that the choice of bearing surface may influence the risk of PJI after THA. The objective of this meta-analysis was to compare the rate of PJI between metal-on-polyethylene (MoP), ceramic-on-polyethylene (CoP), and ceramic-on-ceramic (CoC) bearings. Patients and Methods. Electronic databases (Medline, Embase, Cochrane library, Web of Science, and Cumulative Index of Nursing and Allied Health Literature) were searched for comparative randomized and observational studies that reported the incidence of PJI for different bearing surfaces. Two investigators independently reviewed studies for eligibility, evaluated risk of bias, and performed data extraction. Meta-analysis was performed using the Mantel–Haenzel method and random-effects model in accordance with methods of the Cochrane group. Results. Our search strategy revealed 2272 studies, of which 17 met the inclusion criteria and were analyzed. These comprised 11 randomized controlled trials and six observational studies. The overall quality of included studies was high but the observational studies were at high risk of bias due to inadequate adjustment for confounding factors. The overall cumulative incidence of PJI across all studies was 0.78% (1514/193 378). For each bearing combination, the overall incidence was as follows: MoP 0.85% (1353/158 430); CoP 0.38% (67/17 489); and CoC 0.53% (94/17 459). The meta-analysis showed no significant difference between the three bearing combinations in terms of risk of PJI. Conclusion. On the basis of the clinical studies available, there is no evidence that bearing choice influences the risk of PJI. Future research, including basic science studies and large, adequately controlled registry studies, may be helpful in determining whether implant materials play a role in determining the risk of PJI following arthroplasty surgery. Cite this article: Bone Joint J 2018;100-B:134–42

Aims. The purpose of this study is to examine six types of bearing surfaces implanted at a single institution over three decades to determine whether the reasons for revision vary among the groups and how long it takes to identify differences in survival. Methods. We considered six cohorts that included a total of 1,707 primary hips done between 1982 and 2010. These included 223 conventional polyethylene sterilized with γ irradiation in air (CPE-GA), 114 conventional polyethylene sterilized with gas plasma (CPE-GP), 116 crosslinked polyethylene (XLPE), 1,083 metal-on-metal (MOM), 90 ceramic-on-ceramic (COC), and 81 surface arthroplasties (SAs). With the exception of the COC, all other groups used cobalt-chromium (CoCr) femoral heads. The mean follow-up was 10 (0.008 to 35) years. Descriptive statistics with revisions per 100 component years (re/100 yr) and survival analysis with revision for any reason as the endpoint were used to compare bearing surfaces. Results. XLPE liners demonstrated a lower cumulative incidence of revision at 15 years compared to the CPE-GA and CPE-GP groups owing to the absence of wear-related revisions (4% for XLPE vs 18%, p = 0.02, and 15%, p = 0.003, respectively). Revisions for adverse local tissue reactions occurred exclusively among the MOM (0.8 re/100 year) and SA groups (0.1 re/100 year). The revision rate for instability was lower among hips with 36 mm and larger head sizes compared to smaller head sizes (0.2% vs 2%, p < 0.001). Conclusion. The introduction of XLPE has eliminated wear-related revisions through 15-year follow-up compared to CPE-GP and CPE-GA. Dislocation incidence has been reduced with the introduction of larger diameter heads but remains a persistent concern. The potential for adverse local tissue reactions with MOM requires continued follow-up. Cite this article: Bone Joint J 2020;102-B(7 Supple B):105–111

Aims. We wished to investigate the influence of metal debris exposure on the subsequent immune response and resulting soft-tissue injury following metal-on-metal (MoM) hip arthroplasty. Some reports have suggested that debris generated from the head-neck taper junction is more destructive than equivalent doses from metal bearing surfaces. . Patients and Methods. We investigated the influence of the source and volume of metal debris on chromium (Cr) and cobalt (Co) concentrations in corresponding blood and hip synovial fluid samples and the observed agglomerated particle sizes in excised tissues using multiple regression analysis of prospectively collected data. A total of 199 explanted MoM hips (177 patients; 132 hips female) were analysed to determine rates of volumetric wear at the bearing surfaces and taper junctions. . Results. The statistical modelling suggested that a greater source contribution of metal debris from the taper junction was associated with smaller aggregated particle sizes in the local tissues and a relative reduction of Cr ion concentrations in the corresponding synovial fluid and blood samples. Metal debris generated from taper junctions appears to be of a different morphology, composition and therefore, potentially, immunogenicity to that generated from bearing surfaces. Conclusion. The differences in debris arising from the taper and the articulating surfaces may provide some understanding of the increased incidence of soft-tissue reactions reported in patients implanted with MoM total hip arthroplasties compared with patients with hip resurfacings. Cite this article: Bone Joint J 2016;98-B:925–33

Dislocation is a common reason for revision following total hip replacement. This study investigated the relationship between the bearing surface and the risk of revision due to dislocation. It was based on 110 239 primary total hip replacements with a diagnosis of osteoarthritis collected by the Australian Orthopaedic Association National Joint Replacement Registry between September 1999 and December 2007. A total of 862 (0.78%) were revised because of dislocation. Ceramic-on-ceramic bearing surfaces had a lower risk of requiring revision due to dislocation than did metal-on-polyethylene and ceramic-on-polyethylene surfaces, with a follow-up of up to seven years. However, ceramic-on-ceramic implants were more likely to have larger prosthetic heads and to have been implanted in younger patients. The size of the head of the femoral component and age are known to be independent predictors of dislocation. Therefore, the outcomes were stratified by the size of the head and age. There is a significantly higher rate of revision for dislocation in ceramic-on-ceramic bearing surfaces than in metal-on-polyethylene implants when smaller sizes (≤ 28 mm) of the head were used in younger patients (< 65 years) (hazard ratio = 1.53, p = 0.041) and also with larger (> 28 mm) and in older patients (≥ 65 years) (hazard ratio = 1.73, p = 0.016)

In a double-blinded randomised controlled trial, 83 patients with primary osteoarthritis of the hip received either a ceramic-on-metal (CoM) or metal-on-metal (MoM) total hip replacement (THR). The implants differed only in the bearing surfaces used. The serum levels of cobalt and chromium and functional outcome scores were compared pre-operatively and at six and 12 months post-operatively. Data were available for 41 CoM and 36 MoM THRs (four patients were lost to follow-up, two received incorrect implants). The baseline characteristics of both cohorts were similar. Femoral head size measured 36 mm in all but two patients who had 28 mm heads. The mean serum cobalt and chromium levels increased in both groups, with no difference noted between groups at six months (cobalt p = 0.67, chromium p = 0.87) and 12 months (cobalt p = 0.76, chromium p = 0.76) post-operatively. Similarly, the mean Oxford hip scores, Western Ontario and McMaster Universities Osteoarthritis index and University of California, Los Angeles activity scores showed comparable improvement at 12 months. Our findings indicate that CoM and MoM couplings are associated with an equivalent increase in serum cobalt and chromium levels, and comparable functional outcome scores at six and 12-months follow-up.

The ideal bearing surface for young patients undergoing total hip replacement (THR) remains controversial. We report the five-year results of a randomised controlled trial comparing the clinical and radiological outcomes of 102 THRs in 91 patients who were <  65 years of age. These patients were randomised to receive a cobalt–chrome on ultra-high-molecular-weight polyethylene, cobalt–chrome on highly cross-linked polyethylene, or a ceramic-on-ceramic bearing. In all, 97 hip replacements in 87 patients were available for review at five years. Two hips had been revised, one for infection and one for peri-prosthetic fracture. At the final follow-up there were no significant differences between the groups for the mean Western Ontario and McMaster Universities osteoarthritis index (pain, p = 0.543; function, p = 0.10; stiffness, p = 0.99), Short Form-12 (physical component, p = 0.878; mental component, p = 0.818) or Harris hip scores (p = 0.22). Radiological outcomes revealed no significant wear in the ceramic group. Comparison of standard and highly cross-linked polyethylene, however, revealed an almost threefold difference in the mean annual linear wear rates (0.151 mm/year versus 0.059 mm/year, respectively) (p < 0.001)

Aims. Metal and ceramic humeral head bearing surfaces are available choices in anatomical shoulder arthroplasties. Wear studies have shown superior performance of ceramic heads, however comparison of clinical outcomes according to bearing surface in total shoulder arthroplasty (TSA) and hemiarthroplasty (HA) is limited. This study aimed to compare the rates of revision and reoperation following metal and ceramic humeral head TSA and HA using data from the National Joint Registry (NJR), which collects data from England, Wales, Northern Ireland, Isle of Man and the States of Guernsey. Methods. NJR shoulder arthroplasty records were linked to Hospital Episode Statistics and the National Mortality Register. TSA and HA performed for osteoarthritis (OA) in patients with an intact rotator cuff were included. Metal and ceramic humeral head prostheses were matched within separate TSA and HA groups using propensity scores based on 12 and 11 characteristics, respectively. The primary outcome was time to first revision and the secondary outcome was non-revision reoperation. Results. A total of 4,799 TSAs (3,578 metal, 1,221 ceramic) and 1,363 HAs (1,020 metal, 343 ceramic) were included. The rate of revision was higher for metal compared with ceramic TSA, hazard ratio (HR) 3.31 (95% confidence interval (CI) 1.67 to 6.58). At eight years, prosthesis survival for ceramic TSA was 98.7% (95% CI 97.3 to 99.4) compared with 96.4% (95% CI 95.2 to 97.3) for metal TSA. The majority of revision TSAs were for cuff insufficiency or instability/dislocation. There was no significant difference in the revision rate for ceramic compared with metal head HA (HR 1.33 (95% CI 0.76 to 2.34)). For ceramic HA, eight-year prosthetic survival was 92.8% (95% CI 86.9 to 96.1), compared with 91.6% (95% CI 89.3 to 93.5) for metal HA. The majority of revision HAs were for cuff failure. Conclusion. The rate of all-cause revision was higher following metal compared with ceramic humeral head TSA in patients with OA and an intact rotator cuff. There was no difference in the revision rate for HA according to bearing surface. Cite this article: Bone Joint J 2024;106-B(5):482–491

Aims

We sought to establish whether an oxidised zirconium (OxZr) femoral component causes less loss of polyethylene volume than a cobalt alloy (CoCr) femoral component in total knee arthroplasty.

Metal-on-metal (MOM) is a commonly used bearing notable for its ‘suction fit’ when lubricated. In this study, we examined the capacity for MOM bearings to protect against dislocation after total hip replacement (THR).

We undertook a clinical investigation to compare the rate of dislocation of MOM bearings with those of ceramic-on-polyethylene (COP) bearings and found that one MOM bearing dislocated in a series of 109 hips (0.9%) compared with nine of 145 hips (6.2%) in the COP group (p = 0.02).

We also performed an in vitro investigation comparing the peak forces generated during forced separation of the two bearings of the same dimensions at velocities from 1 to 50 cm/s. This revealed that the MOM bearing generated significant resistance to separation at all velocities (maximum mean 24 N), whereas the COP did not (maximum mean 1.9 N, p < 0.001). We conclude that MOM bearings are more stable to dislocation than COP bearings as a result of the interfacial forces provided by a thin, lubricating fluid.

Aims

This study reports the ten-year wear rates, incidence of osteolysis, clinical outcomes, and complications of a multicentre randomized controlled trial comparing oxidized zirconium (OxZr) versus cobalt-chrome (CoCr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) and highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA).

Aims

Radiostereometric analysis (RSA) is the most accurate radiological method to measure in vivo wear of highly cross-linked polyethylene (XLPE) acetabular components. We have previously reported very low wear rates for a sequentially irradiated and annealed X3 XLPE liner (Stryker Orthopaedics, USA) when used in conjunction with a 32 mm femoral heads at ten-year follow-up. Only two studies have reported the long-term wear rate of X3 liners used in conjunction with larger heads using plain radiographs which have poor sensitivity. The aim of this study was to measure the ten-year wear of thin X3 XLPE liners against larger 36 or 40 mm articulations with RSA.

Aims

To find out if there is an inverse association between estimated glomerular filtration rate (eGFR) and whole blood cobalt (Co) and chromium (Cr) levels in patients with metal-on-metal (MoM) hip arthroplasties and renal insufficiency, suggesting that renal insufficiency could cause accumulation of Co and Cr in blood.

Aims. The optimal bearing surface design for medial unicompartmental knee arthroplasty (UKA) remains controversial. The aim of this study was to compare outcomes of fixed-bearing (FB) and mobile-bearing (MB) UKAs from a single high-volume institution. Methods. Prospectively collected data were reviewed for all primary cemented medial UKAs performed by seven surgeons from January 2006 to December 2022. A total of 2,999 UKAs were identified, including 2,315 FB and 684 MB cases. The primary outcome measure was implant survival. Secondary outcomes included 90-day and cumulative complications, reoperations, component revisions, conversion arthroplasties, range of motion, and patient-reported outcome measures. Overall mean age at surgery was 65.7 years (32.9 to 94.3), 53.1% (1,593/2,999) of UKAs were implanted in female patients, and demographics between groups were similar (p > 0.05). The mean follow-up for all UKAs was 3.7 years (0.0 to 15.6). Results. Using revision for any reason as an endpoint, five-year survival for FB UKAs was 97.2% (95% CI 96.4 to 98.1) compared to 96.0% for MB (95% CI 94.1 to 97.9; p = 0.008). The FB group experienced fewer component revisions (14/2,315, 0.6% vs 12/684, 1.8%; p < 0.001) and conversion arthroplasties (38/2315, 1.6% vs 24/684, 3.5%; p < 0.001). A greater number of MB UKAs underwent revision due to osteoarthritis progression (FB = 21/2,315, 0.9% vs MB = 16/684, 2.3%; p = 0.003). In the MB group, 12 (1.8%) subjects experienced bearing dislocations which required revision surgery. There were 15 early periprosthetic tibia fractures (0.6%) in the FB group compared to 0 for MB (p = 0.035). Conclusion. In similar patient populations, FB UKAs demonstrated slightly higher survival than a commonly used MB design. Adverse event profiles differed by bearing type, with an increased risk of bearing dislocation and OA progression with MB designs, and early periprosthetic tibia fractures for FB designs. Cite this article: Bone Joint J 2024;106-B(9):916–923

Aims. Acetabular edge-loading was a cause of increased wear rates in metal-on-metal hip arthroplasties, ultimately contributing to their failure. Although such wear patterns have been regularly reported in retrieval analyses, this study aimed to determine their in vivo location and investigate their relationship with acetabular component positioning. Methods. 3D CT imaging was combined with a recently validated method of mapping bearing surface wear in retrieved hip implants. The asymmetrical stabilizing fins of Birmingham hip replacements (BHRs) allowed the co-registration of their acetabular wear maps and their computational models, segmented from CT scans. The in vivo location of edge-wear was measured within a standardized coordinate system, defined using the anterior pelvic plane. Results. Edge-wear was found predominantly along the superior acetabular edge in all cases, while its median location was 8° (interquartile range (IQR) -59° to 25°) within the anterosuperior quadrant. The deepest point of these scars had a median location of 16° (IQR -58° to 26°), which was statistically comparable to their centres (p = 0.496). Edge-wear was in closer proximity to the superior apex of the cups with greater angles of acetabular inclination, while a greater degree of anteversion influenced a more anteriorly centred scar. Conclusion. The anterosuperior location of edge-wear was comparable to the degradation patterns observed in acetabular cartilage, supporting previous findings that hip joint forces are directed anteriorly during a greater portion of walking gait. The further application of this novel method could improve the current definition of optimal and safe acetabular component positioning. Cite this article: Bone Joint Res 2021;10(10):639–649

Aims. Hip resurfacing remains a potentially valuable surgical procedure for appropriately-selected patients with optimised implant choices. However, concern regarding high early failure rates continues to undermine confidence in use. A large contributor to failure is adverse local tissue reactions around metal-on-metal (MoM) bearing surfaces. Such phenomena have been well-explored around MoM total hip arthroplasties, but comparable data in equivalent hip resurfacing procedures is lacking. In order to define genetic predisposition, we performed a case-control study investigating the role of human leucocyte antigen (HLA) genotype in the development of pseudotumours around MoM hip resurfacings. Methods. A matched case-control study was performed using the prospectively-collected database at the host institution. In all, 16 MoM hip resurfacing 'cases' were identified as having symptomatic periprosthetic pseudotumours on preoperative metal artefact reduction sequence (MARS) MRI, and were subsequently histologically confirmed as high-grade aseptic lymphocyte-dominated vasculitis-associated lesions (ALVALs) at revision surgery. ‘Controls’ were matched by implant type in the absence of evidence of pseudotumour. Blood samples from all cases and controls were collected prospectively for high resolution genetic a nalysis targeting 11 separate HLA loci. Statistical significance was set at 0.10 a priori to determine the association between HLA genotype and pseudotumour formation, given the small sample size. Results. Using a previously-reported ALVAL classification, the majority of pseudotumour-positive caseswere found to have intermediate-grade group 2 (n = 10; 63%) or group 3 (n = 4; 25%) histological findings. Two further patients (13%) had high-grade group 4 lesions. HLA-DQB1*05:03:01 (p = 0.0676) and HLA-DRB1*14:54:01 (p = 0.0676) alleles were significantly associated with a higher risk of pseudotumour formation, while HLA-DQA1*03:01:01 (p = 0.0240), HLA-DRB1*04:04:01 (p = 0.0453), HLA-C*01:02:01 (p = 0.0453), and HLA-B*27:05:02 (p = 0.0855) were noted to confer risk reduction. Conclusion. These findings confirm the association between specific HLA genotypes and the risk of pseudotumour development around MoM hip resurfacings. Specifically, the two ‘at risk’ alleles (DQB1*05:03:01 and DRB1*14:54:01) may hold clinical value in preoperative screening and prospective surgical decision-making. Cite this article: Bone Jt Open 2023;4(3):182–187

Aims. The optimum clearance between the bearing surfaces of hip arthroplasties is unknown. Theoretically, to minimize wear, it is understood that clearances must be low enough to maintain optimal contact pressure and fluid film lubrication, while being large enough to allow lubricant recovery and reduce contact patch size. This study aimed to identify the relationship between diametrical clearance and volumetric wear, through the analysis of retrieved components. Methods. A total of 81 metal-on-metal Pinnacle hips paired with 12/14 stems were included in this study. Geometrical analysis was performed on each component, using coordinate and roundness measuring machines. The relationship between their as-manufactured diametrical clearance and volumetric wear was investigated. The Mann-Whitney U test and unpaired t-test were used, in addition to calculating the non-parametric Spearman's correlation coefficient, to statistically evaluate the acquired data. Results. The hips in this study were found to have had a median unworn diametrical clearance of 90.31 μm (interquartile range (IQR) 77.59 to 97.40); 32% (n = 26) were found to have been below the manufacturing tolerance. There was no correlation found between clearance and bearing (r. s. = -0.0004, p = 0.997) or taper (r. s. = 0.0048, p = 0.966) wear rates. The wear performance of hips manufactured within and below these specifications was not significantly different (bearing: p = 0.395; taper: p = 0.653). Pinnacles manufactured from 2007 onwards had a greater prevalence of bearing clearance below tolerance (p = 0.004). Conclusion. The diametrical clearance of Pinnacle hips did not influence their wear performance, even when below the manufacturing tolerance. The optimum clearance for minimizing hip implant wear remains unclear. Cite this article: Bone Joint Res 2020;9(8):515–523

We reviewed the literature on the currently available choices of bearing surface in total hip replacement (THR). We present a detailed description of the properties of articulating surfaces review the understanding of the advantages and disadvantages of existing bearing couples. Recent technological developments in the field of polyethylene and ceramics have altered the risk of fracture and the rate of wear, although the use of metal-on-metal bearings has largely fallen out of favour, owing to concerns about reactions to metal debris. As expected, all bearing surface combinations have advantages and disadvantages. A patient-based approach is recommended, balancing the risks of different options against an individual’s functional demands. Cite this article: Bone Joint J 2014;96-B:147–56

Aims. Dual mobility (DM) bearings are an attractive treatment option to obtain hip stability during challenging primary and revision total hip arthroplasty (THA) cases. The purpose of this study was to analyze data submitted to the American Joint Replacement Registry (AJRR) to characterize utilization trends of DM bearings in the USA. Methods. All primary and revision THA procedures reported to AJRR from 2012 to 2018 were analyzed. Patients of all ages were included and subdivided into DM and traditional bearing surface cohorts. Patient demographics, geographical region, hospital size, and teaching affiliation were assessed. Associations were determined by chi-squared analysis and logistic regression was performed to assess outcome variables. Results. A total of 406,900 primary and 34,745 revision THAs were identified, of which 35,455 (8.7%) and 8,031 (23.1%) received DM implants respectively. For primary THA, DM usage increased from 6.7% in 2012 to 12.0% in 2018. Among revision THA, DM use increased from 19.5% in 2012 to 30.6% in 2018. Patients < 50 years of age had the highest rates of DM implantation in every year examined. For each year of increase in age, there was a 0.4% decrease in the rate of DM utilization (odds ratio (OR) 0.996 (95% confidence interval (CI) 0.995 to 0.997); p < 0.001). Females were more likely to receive a DM implant compared to males (OR 1.077 (95% CI 1.054 to 1.100); p < 0.001). Major teaching institutions and smaller hospitals were associated with higher rates of utilization. DM articulations were used more commonly for dysplasia compared with osteoarthritis (OR 2.448 (95% CI 2.032 to 2.949); p < 0.001) during primary THA and for instability (OR 3.130 (95% CI 2.751 to 3.562) vs poly-wear; p < 0.001) in the revision setting. Conclusion. DM articulations showed a marked increase in utilization during the period examined. Younger patient age, female sex, and hospital characteristics such as teaching status, smaller size, and geographical location were associated with increased utilization. DM articulations were used more frequently for primary THA in patients with dysplasia and for revision THA in patients being treated for instability. Cite this article: Bone Joint J 2020;102-B(7 Supple B):27–32

Oxidised zirconium (OxZi) has been developed as an alternative bearing surface for femoral heads in total hip arthroplasty (THA). This study has investigated polyethylene wear, functional outcomes and complications, comparing OxZi and cobalt–chrome (CoCr) as part of a three-arm, multicentre randomised controlled trial. Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and highly cross-linked polyethylene (XLPE) liner; Group B received an OxZi femoral head and XLPE liner; Group C received an OxZi femoral head and ultra-high molecular weight polyethylene (UHMWPE) liner. At five years, 368 patients had no statistically significant differences in short-form-36 (p = 0.176 mental, p = 0.756 physical), Western Ontario and McMaster Universities Osteoarthritis Index (p = 0.847), pain scores (p = 0.458) or complications. The mean rate of linear wear was 0.028 mm/year (standard deviation (. sd) 0.010). for Group A, 0.023 mm/year (. sd. 0.010) for Group B, and 0.09 mm/year (. sd. 0.045) for Group C. Penetration was significantly higher in the UHMWPE liner group compared with both XLPE liner groups (p < 0.001) but no significant difference was noted between CoCr and OxZi when articulating with XLPE (p = 0.153). In this, the largest randomised study of this bearing surface, it appears that using a XLPE acetabular liner is more important in reducing THA component wear than the choice of femoral head bearing, at mid-term follow-up. There is a non-significant trend towards lower wear, coupling OxZi rather than CoCr with XLPE but long-term analysis is required to see if this observation changes with time and becomes significant. Cite this article: Bone Joint J 2015;97-B:883–9

Aims. The aim of this study was to evaluate blood metal ion levels, leucocyte profiles, and serum cytokines in patients with a total hip arthroplasty (THA) involving modular dual-mobility components. Patients and Methods. A total of 39 patients were recruited, with clinical follow-up of up to two years. Outcome was assessed using the Harris Hip Score (HHS, the 12-Item Short-Form Health Survey (SF-12), the Western Ontario and McMaster Universities Osteoarthritis Index (WOMAC), and a visual analogue scale (VAS) for pain. Blood concentrations of cobalt (Co), chromium (Cr), and serum cytokines were measured. Subpopulations of leucocytes were analyzed by flow cytometry. Results. The clinical performance was good. Blood Co levels (ref 1.0 µg/l) were mildly elevated in seven patients at three months, and two patients at two years’ follow-up. The preoperative Cr levels were normal except for one patient with a detectable Cr (1.2 µg/l). Cr levels were detectable in three patients at three months, two patients at one year, and three patients at two years’ follow-up. No patients had symptoms suggestive of failure. Although flow cytometry showed constant circulating leucocyte profiles, there was a significant reduction of serum interleukin (IL)-4, IL-5, and interferon gamma (IFNγ) postoperatively compared with the preoperative levels (p < 0.05). Conclusion. These results suggest that THA using modular dual-mobility components is safe. This allows an opportunity to use a large femoral head and a thick polyethylene bearing surface, which is especially useful in revision procedures or high-risk situations when added stability is required. Cite this article: Bone Joint J 2019;101-B:1035–1041

We have updated our previous randomised controlled trial comparing release of chromium (Cr) and cobalt (Co) ions and included levels of titanium (Ti) ions. We have compared the findings from 28 mm metal-on-metal total hip replacement, performed using titanium CLS/Spotorno femoral components and titanium AlloFit acetabular components with Metasul bearings, with Durom hip resurfacing using a Metasul articulation or bearing and a titanium plasma-sprayed coating for fixation of the acetabular component. Although significantly higher blood ion levels of Cr and Co were observed at three months in the resurfaced group than in total hip replacement, no significant difference was found at two years post-operatively for Cr, 1.58 μg/L and 1.62 μg/L respectively (p = 0.819) and for Co, 0.67 μg/L and 0.94 μg/L respectively (p = 0.207). A steady state was reached at one year in the resurfaced group and after three months in the total hip replacement group. Interestingly, Ti, which is not part of the bearing surfaces with its release resulting from metal corrosion, had significantly elevated ion levels after implantation in both groups. The hip resurfacing group had significantly higher Ti levels than the total hip replacement group for all periods of follow-up. At two years the mean blood levels of Ti ions were 1.87 μg/L in hip resurfacing and and 1.30 μg/L in total hip replacement (p = 0.001). The study confirms even with different bearing diameters and clearances, hip replacement and 28 mm metal-on-metal total hip replacement produced similar Cr and Co metal ion levels in this randomised controlled trial study design, but apart from wear on bearing surfaces, passive corrosion of exposed metallic surfaces is a factor which influences ion concentrations. Ti plasma spray coating the acetabular components for hip resurfacing produces significantly higher release of Ti than Ti grit-blasted surfaces in total hip replacement

Aims. The aim of this study was to describe temporal trends and survivorship of total hip arthroplasty (THA) in very young patients, aged ≤ 20 years. Patients and Methods. A descriptive observational study was undertaken using data from the National Joint Registry (NJR) for England, Wales, Northern Ireland and the Isle of Man between April 2003 and March 2017. All patients aged ≤ 20 years at the time of THA were included and the primary outcome was revision surgery. Descriptive statistics were used to summarize the data and Kaplan–Meier estimates calculated for the cumulative implant survival. Results. A total of 769 THAs were performed in 703 patients. The median follow-up was 5.1 years (interquartile range (IQR) 2.6 to 7.8). Eight patients died and 35 THAs were revised. The use of metal-on-metal (MoM) bearings and resurfacing procedures declined after 2008. The most frequently recorded indications for revision were loosening (20%) and infection (20%), although the absolute risk of these events occurring was low (0.9%). Factors associated with lower implant survival were MoM and metal-on-polyethylene (MoP) bearings and resurfacing arthroplasty (vs ceramic-on-polyethylene (CoP) and ceramic-on-ceramic (CoC) bearings, p = 0.002), and operations performed by surgeons who undertook few THAs in this age group as recorded in the NJR (vs those with five or more recorded operations, p = 0.030). Kaplan–Meier estimates showed 96% (95% confidence interval (CI) 94% to 98%) survivorship of implants at five years. Conclusion. Within the NJR, the overall survival for very young patients undergoing THA exceeded 96% during the first five postoperative years. In the absence of studies that can better account for differences in the characteristics of the patients, surgeons should consider the association between early revision and the type of implant, the number of THAs performed in these patients, and the bearing surface when performing THA in very young patients. Cite this article: Bone Joint J 2018;100-B:1320–9

Objectives. Previous studies have suggested that metal-on-metal (MoM) Pinnacle (DePuy Synthes, Warsaw, Indiana) hip arthroplasties implanted after 2006 exhibit higher failure rates. This was attributed to the production of implants with reduced diametrical clearances between their bearing surfaces, which, it was speculated, were outside manufacturing tolerances. This study aimed to better understand the performance of Pinnacle Systems manufactured before and after this event. Methods. A total of 92 retrieved MoM Pinnacle hips were analyzed, of which 45 were implanted before 2007, and 47 from 2007 onwards. The ‘pre-2007’ group contained 45 implants retrieved from 21 male and 24 female patients, with a median age of 61.3 years (interquartile range (IQR) 57.1 to 65.5); the ‘2007 onwards’ group contained 47 implants retrieved from 19 male and 28 female patients, with a median age of 61.8 years (IQR 58.5 to 67.8). The volume of material lost from their bearing and taper surfaces was measured using coordinate and roundness measuring machines. These outcomes were then compared statistically using linear regression models, adjusting for potentially confounding factors. Results. There was no significant difference between the taper and bearing wear rates of the ‘pre-2007’ and ‘2007 onwards’ groups (p = 0.67 and p = 0.39, respectively). Pinnacles implanted from 2007 onwards were revised after a mean time of 50 months, which was significantly earlier than the ‘pre-2007’ hips (96 months) (p < 0.001). A reduction in the time to revision was present year on year from 2003 to 2011. Conclusion. We found no difference in the wear rate of these implants based on the year of implantation. The ‘pre-2007’ hips had a two-fold greater time to revision than those implanted after 2007; this may be due to the increased surveillance of MoM hips following UK regulatory advice and several high-profile failures. Interestingly, we observed a decreasing trend in the mean time to revision every year from 2003 onwards. Cite this article: S. Bergiers, H. S. Hothi, J. Henckel, A. Eskelinen, J. Skinner, A. Hart. Wear performance of retrieved metal-on-metal Pinnacle hip arthroplasties implanted before and after 2007. Bone Joint Res 2018;7:595–600. DOI: 10.1302/2046-3758.711.BJR-2018-0143.R1

Aims . The primary aim of this independent prospective randomised trial was to compare serum metal ion levels for ceramic-on-metal (CoM) and metal-on-metal (MoM) bearing surfaces in total hip arthroplasty (THA). Our one-year results demonstrated elevation in metal ion levels above baseline with no significant difference between the CoM and MoM groups. This paper reviews the five-year data. Patients and Methods. The implants used in each patient differed only in respect to the type of femoral head (ceramic or metal). At five-year follow-up of the 83 enrolled patients, data from 67 (36 CoM, 31 MoM) was available for comparison. Results. The mean serum cobalt (Co) and chromium (Cr) ion levels remained above baseline in both groups (CoM: Co 1.16 μg/l (0.41 to 14.67), Cr 1.05 μg/l (0.16 to 12.58); MoM: Co 2.93 μg/l (0.35 to 30.29), Cr 1.85 μg/l (0.36 to 17.00)) but the increase was significantly less in the CoM cohort (Co difference p = 0.001, Cr difference p = 0.002). These medium-term results, coupled with lower revision rates from national joint registries, suggest that the performance of CoM THA may be superior to that of MoM. . Conclusion. While both bearing combinations have since been withdrawn these results provide useful information for planning clinical surveillance of CoM THAs and warrants continued monitoring. Cite this article: Bone Joint J 2017;99-B:1298–1303

The use of large-diameter metal-on-metal (MoM) components in total hip arthroplasty (THA) is associated with an increased risk of early failure due to adverse local tissue reaction to metal debris (ARMD) in response to the release of metal ions from the bearing couple and/or head-neck taper corrosion. The aim of this paper was to present a review of the incidence and natural history of ARMD and the forms of treatment, with a focus on the need for and extent of resection or debulking of the pseudotumour. An illustrative case report is presented of a patient with an intra-pelvic pseudotumour associated with a large diameter MoM THA, which was treated successfully with revision of the bearing surface to a dual mobility couple and retention of the well-fixed acetabular and femoral components. The pseudotumour was left in situ. Resolution of the intra-pelvic mass and normalisation of metal ion levels was observed seven months post-operatively. Cite this article: Bone Joint J 2016;98-B:736–40

Aims. Femoral stems with exchangeable (modular) necks were introduced to offer surgeons an increased choice when determining the version, offset and length of the femoral neck during total hip arthroplasty (THA). It was hoped that this would improve outcomes and reduce complications, particularly dislocation. In 2010, the Australian Orthopaedic Association National Joint Replacement Registry (AOANJRR) first reported an increased rate of revision after primary THA using femoral stems with an exchangeable neck. The aim of this study was to provide a more comprehensive up-to-date analysis of primary THA using femoral stems with exchangeable and fixed necks. Materials and Methods. The data included all primary THA procedures performed for osteoarthritis (OA), reported to the AOANJRR between 01 September 1999 and 31 December 2014. There were 9289 femoral stems with an exchangeable neck and 253 165 femoral stems with a fixed neck. The characteristics of the patients and prostheses including the bearing surface and stem/neck metal combinations were examined using Cox proportional hazard ratios (HRs) and Kaplan-Meier estimates of survivorship. . Results. It was found that prostheses with an exchangeable neck had a higher rate of revision and this was evident regardless of the bearing surface or the size of the femoral head. Exchangeable neck prostheses with a titanium stem and a cobalt-chromium neck had a significantly higher rate of revision compared with titanium stem/titanium neck combinations (HR 1.83, 95% confidence interval 1.49 to 2.23, p < 0.001). Revisions were higher for these combinations compared with femoral stems with a fixed neck. Conclusion . There appears to be little evidence to support the continued use of prostheses with an exchangeable neck in primary THA undertaken for OA. Cite this article: Bone Joint J 2017;99-B:766–73

Aims. We present the ten-year data of a cohort of patients, aged between 18 and 65 years (mean age 52.7 years; 19 to 64), who underwent total hip arthroplasty. Patients were randomised to be treated with a cobalt-chrome (CoCr) femoral head with an ultra-high molecular weight polyethylene (UHMWPE), highly cross-linked polyethylene (XLPE) or ceramic-on-ceramic (CoC) bearing surface. Patients and Methods. A total of 102 hips (91 patients) were randomised into the three groups. At ten years, 97 hips were available for radiological and functional follow-up. Two hips (two patients) had been revised (one with deep infection and one for periprosthetic fracture) and three were lost to follow-up. Radiological analysis was performed using a validated digital assessment programme to give linear, directional and volumetric wear of the two polyethylene groups. Results. There was a significantly reduced rate of steady-state linear wear with XLPE (0.07 mm/yr) compared with UHMWPE (0.37 mm/yr) (p = 0.001). Volumetric wear was also significantly reduced in the XLPE group (29.29 mm. 3. /yr) compared with the UHMWPE group (100.75mm. 3. /yr) (p = 0.0001). There were six patients with UHMWPE who had non-progressive osteolysis and none in the XLPE group. All three bearing groups had significant improvements in 12-item short form health survey scores, Western Ontario and McMaster Universities Osteoarthritis Index score and Harris Hip Score. However, the improvement in HSS was significantly less in the UHMWPE group (p = 0.0188) than in the other two groups. At ten years, the rates of volumetric and linear wear in the XLPE group remain low and predominantly below the estimated threshold for osteolysis (1 mm/yr). The rate of linear wear in the XLPE group was three times less than in the UHMWPE group at five-year follow-up and five times less at ten years. The rate of volumetric wear was also three times less in the XLPE group at ten years. Conclusion. While CoC also performs well, XLPE at ten years remains a safe and excellent bearing option in young patients, with low rates of wear and no evidence of osteolysis. Cite this article: Bone Joint J 2017;99-B:1590–5

The inherent challenges of total hip replacement (THR) in children include the choice of implant for the often atypical anatomical morphology, its fixation to an immature growing skeleton and the bearing surface employed to achieve a successful long-term result. We report the medium-term results of 52 consecutive uncemented THRs undertaken in 35 paediatric patients with juvenile idiopathic arthritis. The mean age at the time of surgery was 14.4 years (10 to 16). The median follow-up was 10.5 years (6 to 15). During the study period 13 THRs underwent revision surgery. With revision as an endpoint, subgroup analysis revealed 100% survival of the 23 ceramic-on-ceramic THRs and 55% (16 of 29) of the metal- or ceramic-on-polyethylene. This resulted in 94% (95% CI 77.8 to 98.4) survivorship of the femoral component and 62% (95% CI 41.0 to 78.0) of the acetabular component. Revision of the acetabular component for wear and osteolysis were the most common reasons for failure accounting for 11 of the 13 revisions. The success seen in patients with a ceramic-on-ceramic articulation seems to indicate that this implant strategy has the potential to make a major difference to the long-term outcome in this difficult group of patients

The April 2012 Hip & Pelvis Roundup. 360. looks at osteoporotic hip fractures, retrotrochanteric pain, fibrin adhesive and reattachment of articular cartilage, autologous bone marrow mononuclear cells and avascular necrosis, bearing surfaces, stability after THR, digital templating, pelvic tilt after THR, custom-made sockets for DDH, and dogs and THR

We report the use of a 15° face-changing cementless acetabular component in patients undergoing total hip replacement for osteoarthritis secondary to developmental dysplasia of the hip. The rationale behind its design and the surgical technique used for its implantation are described. It is distinctly different from a standard cementless hemispherical component as it is designed to position the bearing surface at the optimal angle of inclination, that is, < 45°, while maximising the cover of the component by host bone.

There is widespread concern regarding the incidence of adverse soft-tissue reactions after metal-on-metal (MoM) hip replacement. Recent National Joint Registry data have shown clear differences in the rates of failure of different designs of hip resurfacing. Our aim was to update the failure rates related to metal debris for the Articular Surface Replacement (ASR). A total of 505 of these were implanted. Kaplan-Meier analysis showed a failure rate of 25% at six years for the ASR resurfacing and of 48.8% for the ASR total hip replacement (THR). Of 257 patients with a minimum follow-up of two years, 67 (26.1%) had a serum cobalt concentration which was greater than 7 μg/l. Co-ordinate measuring machine analysis of revised components showed that all patients suffering adverse tissue reactions in the resurfacing group had abnormal wear of the bearing surfaces. Six THR patients had relatively low rates of articular wear, but were found to have considerable damage at the trunion-taper interface. Our results suggest that wear at the modular junction is an important factor in the development of adverse tissue reactions after implantation of a large-diameter MoM THR

Objectives. Wear debris released from bearing surfaces has been shown to provoke negative immune responses in the recipient. Excessive wear has been linked to early failure of prostheses. Analysis using coordinate measuring machines (CMMs) can provide estimates of total volumetric material loss of explanted prostheses and can help to understand device failure. The accuracy of volumetric testing has been debated, with some investigators stating that only protocols involving hundreds of thousands of measurement points are sufficient. We looked to examine this assumption and to apply the findings to the clinical arena. . Methods. We examined the effects on the calculated material loss from a ceramic femoral head when different CMM scanning parameters were used. Calculated wear volumes were compared with gold standard gravimetric tests in a blinded study. . Results. Various scanning parameters including point pitch, maximum point to point distance, the number of scanning contours or the total number of points had no clinically relevant effect on volumetric wear calculations. Gravimetric testing showed that material loss can be calculated to provide clinically relevant degrees of accuracy. . Conclusions. Prosthetic surfaces can be analysed accurately and rapidly with currently available technologies. Given these results, we believe that routine analysis of explanted hip components would be a feasible and logical extension to National Joint Registries. Cite this article: Bone Joint Res 2014;3:60–8

Osteolysis remains a common reason for revision after total hip arthroplasty (THA). For osteolysis associated with loose cups, revision is indicated. For osteolysis around a well-fixed cup, the decision is more controversial. The data available data support retention of the cupwith lesional treatment, working through screw holes and access channels for debridement and grafting. The choice of graft material to fill defects, if any, remains controversial. Several studies demonstrate good survivorship with cup retention strategies. Complete revision allows more complete debridement of the lesion and better graft fill, and allows implantation of a modern cup, typically with a full line of liners and bearing surfaces available. Additionally, revision allows fine tuning of the orientation of the cup, which may be advantageous for optimising hip stability. The author prefers to retain a well-fixed cup if it meets the following criteria: it is well-fixed to intra-operative testing, it is well-positioned, it is of sufficient size to allow insertion of a new liner with a reasonable head size, new liners are available, and the hip is stable to intra-operative trialing after liner insertion

A number of studies have reported satisfactory results from the isolated revision of an acetabular component. However, many of these studies reported only the short- to intermediate-term results of heterogeneous bearing surfaces in a mixed age group. We present our experience of using a ceramic-on-ceramic (CoC) bearing for isolated revision of an uncemented acetabular component in 166 patients (187 hips) who were under the age of 50 years at the time of revision. There were 78 men and 88 women with a mean age of 47.4 years (28 to 49). The most common reason for revision was polyethylene wear and acetabular osteolysis in 123 hips (66%), followed by aseptic loosening in 49 hips (26%). . We report the clinical and radiological outcome, complication rate, and survivorship of this group. The mean duration of follow-up was 15.6 years (11 to 19). . The mean pre-operative Harris hip score was 33 points (1 to 58), and improved to a mean of 88 points (51 to 100) at follow-up. The mean pre-operative total Western Ontario and McMaster Universities Osteoarthritis Index score was 63.2 (43 to 91) and improved to 19.8 points (9 to 61) post-operatively. Overall, 153 of 166 patients (92%) were satisfied with their outcome. Kaplan–Meier survivorship analysis, with revision or radiological evidence of implant failure (13 patients, 8%) as end-points, was 92% at 15 years (95% confidence interval 0.89 to 0.97). . Isolated revision of a cementless acetabular component using a CoC bearing gives good results in patients under 50 years of age. Cite this article: Bone Joint J 2015;97-B:1197–1203

Aims

Modular dual-mobility (DM) articulations are increasingly used during total hip arthroplasty (THA). However, concerns remain regarding the metal liner modularity. This study aims to correlate metal artifact reduction sequence (MARS)-MRI abnormalities with serum metal ion levels in patients with DM articulations.

An international faculty of orthopaedic surgeons presented their work on the current challenges in hip surgery at the London Hip Meeting which was attended by over 400 delegates. The topics covered included femoroacetabular impingement, thromboembolic phenomena associated with hip surgery, bearing surfaces (including metal-on-metal articulations), outcomes of hip replacement surgery and revision hip replacement. We present a concise report of the current opinions on hip surgery from this meeting with appropriate references to the current literature

Aims

The aim of this study was to evaluate medium- to long-term outcomes and complications of the Stanmore Modular Individualised Lower Extremity System (SMILES) rotating hinge implant in revision total knee arthroplasty (rTKA) at a tertiary unit. It is hypothesized that this fully cemented construct leads to satisfactory clinical outcomes.

Aims

Oxidized zirconium (OxZi) and highly cross-linked polyethylene (HXLPE) were developed to minimize wear and risk of osteolysis in total hip arthroplasty (THA). However, retrieval studies have shown that scratched femoral heads may lead to runaway wear, and few reports of long-term results have been published. The purpose of this investigation is to report minimum ten-year wear rates and clinical outcomes of THA with OxZi femoral heads on HXLPE, and to compare them with a retrospective control group of cobalt chrome (CoCr) or ceramic heads on HXLPE.

Hip implant retrieval analysis is the most important source of insight into the performance of new materials and designs of hip arthroplasties. Even the most rigorous in vitro testing will not accurately simulate the behavior of implant materials and new designs of prosthetic arthroplasties. Retrieval analysis has revealed such factors as the effects of gamma-in-air sterilisation of polyethylene, fatigue failure mechanisms of polymethylmethacrylate bone cement, fretting corrosion of Morse taper junctions, third body wear effects of both hard-on-hard and hard-on-soft bearing couples, and the effects of impingement of components on the full spectrum of bearing surfaces, none of which was predicted by pre-implantation in vitro testing of these materials and combinations. The temporal sequence of the retrieval process is approximately six years from first implantation through retrieval analysis, laboratory investigation, and publication of results, and thus, in addition to rigorous clinical evaluation, represents the true development and insight cycle for new designs and materials

Finite element analysis was used to examine the initial stability after hip resurfacing and the effect of the procedure on the contact mechanics at the articulating surfaces. Models were created with the components positioned anatomically and loaded physiologically through major muscle forces. Total micromovement of less than 10 μm was predicted for the press-fit acetabular components models, much below the 50 μm limit required to encourage osseointegration. Relatively high compressive acetabular and contact stresses were observed in these models. The press-fit procedure showed a moderate influence on the contact mechanics at the bearing surfaces, but produced marked deformation of the acetabular components. No edge contact was predicted for the acetabular components studied. It is concluded that the frictional compressive stresses generated by the 1 mm to 2 mm interference-fit acetabular components, together with the minimal micromovement, would provide adequate stability for the implant, at least in the immediate post-operative situation

Aims

Contemporary outcomes of primary total hip arthroplasties (THAs) with highly cross-linked polyethylene (HXLPE) liners in patients with inflammatory arthritis have not been well studied. This study examined the implant survivorship, complications, radiological results, and clinical outcomes of THA in patients with inflammatory arthritis.

Retrieval studies of total hip replacements with highly cross-linked ultra-high-molecular-weight polyethylene liners have shown much less surface damage than with conventional ultra-high-molecular-weight polyethylene liners. A recent revision hip replacement for recurrent dislocation undertaken after only five months revealed a highly cross-linked polyethylene liner with a large area of visible delamination. In order to determine the cause of this unusual surface damage, we analysed the bearing surfaces of the cobalt-chromium femoral head and the acetabular liner with scanning electron microscopy, energy dispersive x-ray spectroscopy and optical profilometry. We concluded that the cobalt-chromium modular femoral head had scraped against the titanium acetabular shell during the course of the dislocations and had not only roughened the surface of the femoral head but also transferred deposits of titanium onto it. The largest deposits were 1.6 μm to 4.3 μm proud of the surrounding surface and could lead to increased stresses in the acetabular liner and therefore cause accelerated wear and damage. This case illustrates that dislocations can leave titanium deposits on cobalt-chromium femoral heads and that highly cross-linked ultra-high-molecular-weight polyethylene remains susceptible to surface damage

Aims

In metal-on-polyethylene (MoP) total hip arthroplasty (THA), large metal femoral heads have been used to increase stability and reduce the risk of dislocation. The increased size of the femoral head can, however, lead to increased taper corrosion, with the release of metal ions and adverse reactions. The aim of this study was to investigate the relationship between the size of the femoral head and the levels of metal ions in the blood in these patients.

Aims

The primary outcome was investigating differences in wear, as measured by femoral head penetration, between cross-linked vitamin E-diffused polyethylene (vE-PE) and cross-linked polyethylene (XLPE) acetabular component liners and between 32 and 36 mm head sizes at the ten-year follow-up. Secondary outcomes included acetabular component migration and patient-reported outcome measures (PROMs) such as the EuroQol five-dimension questionnaire, 36-Item Short-Form Health Survey, Harris Hip Score, and University of California, Los Angeles Activity Scale (UCLA).

Aims

The primary aim of this study is to assess the survival of the uncemented hydroxyapatite (HA) coated Trident II acetabular component as part of a hybrid total hip arthroplasty (THA) using a cemented Exeter stem. The secondary aims are to assess the complications, joint-specific function, health-related quality of life, and radiological signs of loosening of the acetabular component.

We aim to explore the potential technologies for monitoring and assessment of patients undergoing arthroplasty by examining selected literature focusing on the technology currently available and reflecting on possible future development and application. The reviewed literature indicates a large variety of different hardware and software, widely available and used in a limited manner, to assess patients’ performance. There are extensive opportunities to enhance and integrate the systems which are already in existence to develop patient-specific pathways for rehabilitation.

Cite this article: Bone Joint J 2022;104-B(10):1104–1109.

We sought to establish the incidence of joint failure secondary to adverse reaction to metal debris (ARMD) following metal-on-metal hip resurfacing in a large, three surgeon, multicentre study involving 4226 hips with a follow-up of 10 to 142 months. Three implants were studied: the Articular Surface Replacement; the Birmingham Hip Resurfacing; and the Conserve Plus. Retrieved implants underwent analysis using a co-ordinate measuring machine to determine volumetric wear. There were 58 failures associated with ARMD. The median chromium and cobalt concentrations in the failed group were significantly higher than in the control group (p < 0.001). Survival analysis showed a failure rate in the patients with Articular Surface Replacement of 9.8% at five years, compared with < 1% at five years for the Conserve Plus and 1.5% at ten years for the Birmingham Hip Resurfacing. Two ARMD patients had relatively low wear of the retrieved components. Increased wear from the metal-on-metal bearing surface was associated with an increased rate of failure secondary to ARMD. However, the extent of tissue destruction at revision surgery did not appear to be dose-related to the volumetric wear