Modern metal-on-metal (MoM) hip resurfacing arthroplasty (HRA), while achieving good results with well-orientated, well-designed components in ideal patients, is contraindicated in women, men with head size under 50 mm, or metal hypersensitivity. These patients currently have no access to the benefits of HRA. Highly crosslinked polyethylene (XLPE) has demonstrated clinical success in total hip arthroplasty (THA) and, when used in HRA, potentially reduces metal ion-related sequelae. We report the early performance of HRA using a direct-to-bone cementless mono-bloc XLPE component coupled with a cobalt-chrome femoral head, in the patient group for whom HRA is currently contraindicated. This is a cross-sectional, observational assessment of 88 consecutive metal-on-XLPE HRAs performed in 84 patients between 2015 and 2018 in three centres (three surgeons, including the designer surgeon). Mean follow-up is 1.6 years (0.7 to 3.9). Mean age at operation was 56 years (Objectives
Methods
There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs. We examined an existing retrieval database to identify all Exeter V40 and Universal MoP THAs. Volumetric wear analysis of the taper surfaces was conducted using previously validated methodology. These values were compared with those obtained from a series of MoM THAs using non-parametric statistical methodology. A number of patient and device variables were accounted for using multiple regression modelling.Aims
Patients and Methods
We have encountered patients who developed large joint fluid collections with massive elevations in chromium (Cr) and cobalt (Co) concentrations following metal-on-metal (MoM) hip arthroplasties. In some cases, retrieval analysis determined that these ion concentrations could not be explained simply by the wear rates of the components. We hypothesized that these effects may be associated with aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL). We examined the influence of the ALVAL grade on synovial fluid Co and Cr concentrations following adjustment for patient and device variables, including volumetric wear rates. Initially restricting the analysis to include only patients with one MoM hip resurfacing device, we performed multiple regression analyses of prospectively collected data. We then repeated the same statistical approach using results from a larger cohort with different MoM designs, including total hip arthroplasties.Objectives
Patients and Methods
We sought to determine whether cobalt-chromium alloy (CoCr) femoral
stem tapers (trunnions) wear more than titanium (Ti) alloy stem
tapers (trunnions) when used in a large diameter (LD) metal-on-metal
(MoM) hip arthroplasty system. We performed explant analysis using validated methodology to
determine the volumetric material loss at the taper surfaces of
explanted LD CoCr MoM hip arthroplasties used with either a Ti alloy
(n = 28) or CoCr femoral stem (n = 21). Only 12/14 taper constructs
with a rough male taper surface and a nominal included angle close
to 5.666° were included. Multiple regression modelling was undertaken
using taper angle, taper roughness, bearing diameter (horizontal
lever arm) as independent variables. Material loss was mapped using
a coordinate measuring machine, profilometry and scanning electron
microscopy.Aims
Patients and Methods
We present the clinical results and survivorship
of consecutive 100 Birmingham Hip Resurfacings in 90 patients at
a minimum follow-up of ten years. All procedures were carried out
by an independent surgeon who commenced a prospective study in 1998.
Patients were assessed clinically using the Western Ontario and
McMaster Universities osteoarthritis index, Short-Form 36, Harris
hip score and University of California, Los Angeles activity score. Radiological
analysis was performed by an independent observer and blood metal
ion levels concentrations were measured at ten years post-operatively
in 62 patients. The median acetabular component inclination was
46.2° (34° to 59°) and anteversion 11.0° (0° to 30°). The median
chromium concentration in the unilateral group was 1.74 (0.41 to
15.23) and for the bilateral group was 2.98 (1.57 to 18.01). The
equivalent values for cobalt were 1.67 (0.54 to 20.4) and 1.88 (1.38
to 19.32). In total there were eight failures giving an overall survival
at ten years of 92% (95% confidence interval (CI) 86.7 to 97.3).
BHR in male patients had an improved survivorship of 94.6% (95%
CI 89.4 to 100) compared with females at 84.6% (95% CI 70.7 to 98.5),
but this did not reach statistical significance (p = 0.119). Four
of the nine BHRs with a bearing diameter of 42 mm failed. The overall results were consistent with data produced from other
centres in that the clinical outcome of large male patients was
extremely encouraging, whereas the survival of the smaller joints
was less satisfactory.
We sought to establish the incidence of joint failure secondary to adverse reaction to metal debris (ARMD) following metal-on-metal hip resurfacing in a large, three surgeon, multicentre study involving 4226 hips with a follow-up of 10 to 142 months. Three implants were studied: the Articular Surface Replacement; the Birmingham Hip Resurfacing; and the Conserve Plus. Retrieved implants underwent analysis using a co-ordinate measuring machine to determine volumetric wear. There were 58 failures associated with ARMD. The median chromium and cobalt concentrations in the failed group were significantly higher than in the control group (p <
0.001). Survival analysis showed a failure rate in the patients with Articular Surface Replacement of 9.8% at five years, compared with <
1% at five years for the Conserve Plus and 1.5% at ten years for the Birmingham Hip Resurfacing. Two ARMD patients had relatively low wear of the retrieved components. Increased wear from the metal-on-metal bearing surface was associated with an increased rate of failure secondary to ARMD. However, the extent of tissue destruction at revision surgery did not appear to be dose-related to the volumetric wear.
This study compared the demographic, clinical and patient-reported outcomes after total hip replacement (THR) and Birmingham Hip Resurfacing (BHR) carried out by a single surgeon. Patients completed a questionnaire that included the WOMAC, SF-36 scores and comorbid medical conditions. Data were collected before operation and one year after. The outcome scores were adjusted for age, gender, comorbid conditions and, at one year, for the pre-operative scores. There were 214 patients with a THR and 132 with a BHR. Patients with a BHR were significantly younger (49 vs 67 years, p <
0.0001), more likely to be male (68% vs 42% of THR, p <
0.0001) and had fewer comorbid conditions (1.3 vs 2.0, p <
0.0001). Before operation there was no difference in WOMAC and SF-36 scores, except for function, in which patients awaiting THR were worse than those awaiting a BHR. At one year patients with a BHR reported significantly better WOMAC pain scores (p = 0.04) and in all SF-36 domains (p <
0.05). Patients undergoing BHR report a significantly greater improvement in general health compared with those with a THR.
Resurfacing arthroplasty of the hip is being performed more frequently in the United Kingdom. The majority of these patients are younger than 55 years of age, and in this group the key benefits include conservation of femoral bone stock and the potential reduction in the rate of dislocation afforded by the larger resurfacing head. Early aseptic loosening is well recognised in patients younger than 55 years of age, and proponents of resurfacing believe that the improved wear characteristics of the metal-on-metal bearing may improve the long-term survival of this implant. There has been some concern, however, that resurfacing may not be conservative of acetabular bone. We compared a series of 33 consecutive patients who had a hybrid total hip arthroplasty with an uncemented acetabular component and a cemented femoral implant, with 35 patients undergoing a Birmingham hip resurfacing arthroplasty. We compared the diameter of the implanted acetabulum in both groups and, because they were not directly comparable, we corrected for patient size by measuring the diameter of the contralateral femoral head. The data were analysed using unpaired There was a significantly larger acetabulum in the Birmingham arthroplasty group (mean diameter 56.6 mm
Hip resurfacing is being performed more frequently in the United Kingdom. The possible benefits include more accurate restoration of leg length, femoral offset and femoral anteversion than occurs after total hip arthroplasty (THA). We compared anteroposterior radiographs from 26 patients who had undergone hybrid THA (uncemented cup/cemented stem), with 28 who had undergone Birmingham Hip Resurfacing arthroplasty (BHR). We measured the femoral offset, femoral length, acetabular offset and acetabular height with reference to the normal contralateral hip. The data were analysed by paired There was a significant reduction in femoral offset (p = 0.0004) and increase in length (p = 0.001) in the BHR group. In the THA group, there was a significant reduction in acetabular offset (p = 0.0003), but femoral offset and overall hip length were restored accurately. We conclude that hip resurfacing does not restore hip mechanics as accurately as THA.