The design of the Charnley total hip replacement follows the principle of low frictional torque. It is based on the largest possible difference between the radius of the femoral head and that of the outer aspect of the acetabular component. The aim is to protect the bone-cement interface by movement taking place at the smaller radius, the articulation. This is achieved in clinical practice by a 22.225 mm diameter head articulating with a 40 mm or 43 mm diameter acetabular component of ultra-high molecular weight polyethylene. We compared the incidence of aseptic loosening of acetabular components with an outer diameter of 40 mm and 43 mm at comparable depths of penetration with a mean follow-up of 17 years (1 to 40). In cases with no measurable wear none of the acetabular components were loose. With increasing acetabular penetration there was an increased incidence of aseptic loosening which reflected the difference in the external radii, with 1.5% at 1 mm, 8.8% at 2 mm, 9.7% at 3 mm and 9.6% at 4 mm of penetration in favour of the larger 43 mm acetabular component. Our findings support the Charnley principle of low frictional torque. The level of the benefit is in keeping with the predicted values

The aim of this study was to assess the effect of frictional torque and bending moment on fretting corrosion at the taper interface of a modular femoral component and to investigate whether different combinations of material also had an effect. The combinations we examined were 1) cobalt–chromium (CoCr) heads on CoCr stems 2) CoCr heads on titanium alloy (Ti) stems and 3) ceramic heads on CoCr stems. In test 1 increasing torque was imposed by offsetting the stem in the anteroposterior plane in increments of 0 mm, 4 mm, 6 mm and 8 mm when the torque generated was equivalent to 0 Nm, 9 Nm, 14 Nm and 18 Nm. In test 2 we investigated the effect of increasing the bending moment by offsetting the application of axial load from the midline in the mediolateral plane. Increments of offset equivalent to head + 0 mm, head + 7 mm and head + 14 mm were used. Significantly higher currents and amplitudes were seen with increasing torque for all combinations of material. However, Ti stems showed the highest corrosion currents. Increased bending moments associated with using larger offset heads produced more corrosion: Ti stems generally performed worse than CoCr stems. Using ceramic heads did not prevent corrosion, but reduced it significantly in all loading configurations. Cite this article: Bone Joint J 2015;97-B:463–72

This systematic review of the literature summarises the clinical experience with ceramic-on-ceramic hip bearings over the past 40 years and discusses the concerns that exist in relation to the bearing combination. Loosening, fracture, liner chipping on insertion, liner canting and dissociation, edge-loading and squeaking have all been reported, and the relationship between these issues and implant design and surgical technique is investigated. New design concepts are introduced and analysed with respect to previous clinical experience.

Aims. This study investigates head-neck taper corrosion with varying head size in a novel hip simulator instrumented to measure corrosion related electrical activity under torsional loads. Methods. In all, six 28 mm and six 36 mm titanium stem-cobalt chrome head pairs with polyethylene sockets were tested in a novel instrumented hip simulator. Samples were tested using simulated gait data with incremental increasing loads to determine corrosion onset load and electrochemical activity. Half of each head size group were then cycled with simulated gait and the other half with gait compression only. Damage was measured by area and maximum linear wear depth. Results. Overall, 36 mm heads had lower corrosion onset load (p = 0.009) and change in open circuit potential (OCP) during simulated gait with (p = 0.006) and without joint movement (p = 0.004). Discontinuing gait’s joint movement decreased corrosion currents (p = 0.042); however, wear testing showed no significant effect of joint movement on taper damage. In addition, 36 mm heads had greater corrosion area (p = 0.050), but no significant difference was found for maximum linear wear depth (p = 0.155). Conclusion. Larger heads are more susceptible to taper corrosion; however, not due to frictional torque as hypothesized. An alternative hypothesis of taper flexural rigidity differential is proposed. Further studies are necessary to investigate the clinical significance and underlying mechanism of this finding. Cite this article: Bone Jt Open 2021;2(11):1004–1016

Aims

Periprosthetic fracture and implant loosening are two of the major reasons for revision surgery of cementless implants. Optimal implant fixation with minimal bone damage is challenging in this procedure. This pilot study investigates whether vibratory implant insertion is gentler compared to consecutive single blows for acetabular component implantation in a surrogate polyurethane (PU) model.

Aims

Periprosthetic hip fractures (PPFs) after total hip arthroplasty are difficult to treat. Therefore, it is important to identify modifiable risk factors such as stem selection to reduce the occurrence of PPFs. This study aimed to clarify differences in fracture torque, surface strain, and fracture type analysis between three different types of cemented stems.

Aims

In 2015, we published the results of our ceramic-on-metal (CoM) total hip arthroplasties (THAs) performed between October 2007 and July 2009 with a mean follow-up of 34 months (23 to 45) and a revision rate of 3.1%. The aim of this paper is to present the longer-term outcomes.

Aims

Post-traumatic periprosthetic acetabular fractures are rare but serious. Few studies carried out on small cohorts have reported them in the literature. The aim of this work is to describe the specific characteristics of post-traumatic periprosthetic acetabular fractures, and the outcome of their surgical treatment in terms of function and complications.

Aims

It is important to analyze objectively the hammering sound in cup press-fit technique in total hip arthroplasty (THA) in order to better understand the change of the sound during impaction. We hypothesized that a specific characteristic would present in a hammering sound with successful fixation. We designed the study to quantitatively investigate the acoustic characteristics during cementless cup impaction in THA.

Aims

It is important to analyze objectively the hammering sound in cup press-fit technique in total hip arthroplasty (THA) in order to better understand the change of the sound during impaction. We hypothesized that a specific characteristic would present in a hammering sound with successful fixation. We designed the study to quantitatively investigate the acoustic characteristics during cementless cup impaction in THA.

Aims

A significant reduction in wear at five and ten years was previously reported when comparing Durasul highly cross-linked polyethylene with nitrogen-sterilized Sulene polyethylene in total hip arthroplasty (THA). We investigated whether the improvement observed at the earlier follow-up continued, resulting in decreased osteolysis and revision surgery rates over the second decade.

We report the use of porous metal acetabular revision shells in the treatment of contained bone loss. The outcomes of 53 patients with ≤ 50% acetabular bleeding host bone contact were compared with a control group of 49 patients with > 50% to 85% bleeding host bone contact. All patients were treated with the same type of trabecular metal acetabular revision shell. The mean age at revision was 62.4 years (42 to 80) and the mean follow-up of both groups was 72.4 months (60 to 102). Clinical, radiological and functional outcomes were assessed. There were four (7.5%) mechanical failures in the ≤ 50% host bone contact group and no failures in the > 50% host bone contact group (p = 0.068). Out of both groups combined there were four infections (3.9%) and five recurrent dislocations (4.9%) with a stable acetabular component construct that were revised to a constrained liner. Given the complexity of the reconstructive challenge, porous metal revision acetabular shells show acceptable failure rates at five to ten years’ follow-up in the setting of significant contained bone defects. This favourable outcome might be due to the improved initial stability achieved by a high coefficient of friction between the acetabular implant and the host bone, and the high porosity, which affords good bone ingrowth

Increasing follow-up identifies the outcome in younger patients who have undergone total hip replacement (THR) and reveals the true potential for survival of the prosthesis. We identified 28 patients (39 THRs) who had undergone cemented Charnley low friction arthroplasty between 1969 and 2001. Their mean age at operation was 17.9 years (12 to 19) and the maximum follow-up was 34 years. Two patients (4 THRs) were lost to follow-up, 13 (16 THRs) were revised at a mean period of 19.1 years (8 to 34) and 13 (19 THRs) continue to attend regular follow-up at a mean of 12.6 years (2.3 to 29). In this surviving group one acetabular component was radiologically loose and all femoral components were secure. In all the patients the diameter of the femoral head was 22.225 mm with Charnley femoral components used in 29 hips and C-stem femoral components in ten. In young patients who require THR the acetabular bone stock is generally a limiting factor for the size of the component. Excellent long-term results can be obtained with a cemented polyethylene acetabular component and a femoral head of small diameter

Aims

This study reports the ten-year wear rates, incidence of osteolysis, clinical outcomes, and complications of a multicentre randomized controlled trial comparing oxidized zirconium (OxZr) versus cobalt-chrome (CoCr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) and highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA).

Aims

This study uses prospective registry data to compare early patient outcomes following arthroscopic repair or debridement of the acetabular labrum.

Aims

The main aims were to identify risk factors predictive of a radiolucent line (RLL) around the acetabular component with an interface bioactive bone cement (IBBC) technique in the first year after THA, and evaluate whether these risk factors influence the development of RLLs at five and ten years after THA.

Aims

We aimed to investigate if the use of the largest possible cobalt-chromium head articulating with polyethylene acetabular inserts would increase the in vivo wear rate in total hip arthroplasty.

Aims

Acetabular edge-loading was a cause of increased wear rates in metal-on-metal hip arthroplasties, ultimately contributing to their failure. Although such wear patterns have been regularly reported in retrieval analyses, this study aimed to determine their in vivo location and investigate their relationship with acetabular component positioning.

Aims

The main advantage of 3D-printed, off-the-shelf acetabular implants is the potential to promote enhanced bony fixation due to their controllable porous structure. In this study we investigated the extent of osseointegration in retrieved 3D-printed acetabular implants.

Aims

The optimum clearance between the bearing surfaces of hip arthroplasties is unknown. Theoretically, to minimize wear, it is understood that clearances must be low enough to maintain optimal contact pressure and fluid film lubrication, while being large enough to allow lubricant recovery and reduce contact patch size. This study aimed to identify the relationship between diametrical clearance and volumetric wear, through the analysis of retrieved components.

Aims

To compare the in vivo long-term fixation achieved by two acetabular components with different porous ingrowth surfaces using radiostereometric analysis (RSA).

Aims

We have previously demonstrated raised cobalt and chromium levels in patients with larger diameter femoral heads, following metal-on-polyethylene uncemented total hip arthroplasty. Further data have been collected, to see whether these associations have altered with time and to determine the long-term implications for these patients and our practice.

Aims

Cementless acetabular components rely on press-fit fixation for initial stability. In certain cases, initial stability is more difficult to obtain (such as during revision). No current study evaluates how a surgeon’s impaction technique (mallet mass, mallet velocity, and number of strikes) may affect component fixation. This study seeks to answer the following research questions: 1) how does impaction technique affect a) bone strain generation and deterioration (and hence implant stability) and b) seating in different density bones?; and 2) can an impaction technique be recommended to minimize risk of implant loosening while ensuring seating of the acetabular component?

Aims

The aim of this study was to develop a novel computational model for estimating head/stem taper mechanics during different simulated assembly conditions.

Aims

We evaluated a large database with mechanical failure of a single uncemented modular femoral component, used in revision hip arthroplasty, as the end point and compared them to a control group treated with the same implant. Patient- and implant-specific risk factors for implant failure were analyzed.

Aims

This study reports the mid-term results of total hip arthroplasty (THA) performed using a monoblock acetabular component with a large-diameter head (LDH) ceramic-on-ceramic (CoC) bearing.

Objectives

The paradoxical migration of the femoral neck element (FNE) superomedially against gravity, with respect to the intramedullary component of the cephalomedullary device, is a poorly understood phenomenon increasingly seen in the management of pertrochanteric hip fractures with the intramedullary nail. The aim of this study was to investigate the role of bidirectional loading on the medial migration phenomenon, based on unique wear patterns seen on scanning electron microscopy of retrieved implants suggestive of FNE toggling.

Objectives

Our primary aim was to describe migration of the Exeter stem with a 32 mm head on highly crosslinked polyethylene and whether this is influenced by age. Our secondary aims were to assess functional outcome, satisfaction, activity, and bone mineral density (BMD) according to age.

Aims

The aim of this study was to evaluate fretting and corrosion in retrieved oxidized zirconium (OxZr; OXINIUM, Smith & Nephew, Memphis, Tennessee) femoral heads and compare the results with those from a matched cohort of cobalt-chromium (CoCr) femoral heads.

Aims

There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs.

Aims

The use of trabecular metal (TM) shells supported by augments has provided good mid-term results after revision total hip arthroplasty (THA) in patients with a bony defect of the acetabulum. The aim of this study was to assess the long-term implant survivorship and radiological and clinical outcomes after acetabular revision using this technique.

Aims

Our aim in this study was to describe a continuing review of 11 total hip arthroplasties using 22.225 mm Alumina ceramic femoral heads on a Charnley flanged femoral component, articulating against a silane crosslinked polyethylene.

Aims

The present study investigated the five-year interval changes in pseudotumours and measured serum metal ions at long-term follow-up of a previous report of 28 mm diameter metal-on-metal (MoM) total hip arthroplasty (THA).

Aims

Instability continues to be a troublesome complication after total hip arthroplasty (THA). Patient-related risk factors associated with a higher dislocation risk include the preoperative diagnosis, an age of 75 years or older, high body mass index (BMI), a history of alcohol abuse, and neurodegenerative diseases. The goal of this study was to assess the dislocation rate, radiographic outcomes, and complications of patients stratified as high-risk for dislocation who received a dual mobility (DM) bearing in a primary THA at a minimum follow-up of two years.

Objectives

Previous studies have suggested that metal-on-metal (MoM) Pinnacle (DePuy Synthes, Warsaw, Indiana) hip arthroplasties implanted after 2006 exhibit higher failure rates. This was attributed to the production of implants with reduced diametrical clearances between their bearing surfaces, which, it was speculated, were outside manufacturing tolerances. This study aimed to better understand the performance of Pinnacle Systems manufactured before and after this event.

Objectives

Modular junctions are ubiquitous in contemporary hip arthroplasty. The head-trunnion junction is implicated in the failure of large diameter metal-on-metal (MoM) hips which are the currently the topic of one the largest legal actions in the history of orthopaedics (estimated costs are stated to exceed $4 billion). Several factors are known to influence the strength of these press-fit modular connections. However, the influence of different head sizes has not previously been investigated. The aim of the study was to establish whether the choice of head size influences the initial strength of the trunnion-head connection.

Objectives

Studies reporting specifically on squeaking in total hip arthroplasty have focused on cementless, and not on hybrid, fixation. We hypothesised that the cement mantle of the femur might have a damping effect on the sound transmitted through the metal stem. The objective of this study was to test the effect of cement on sound propagation along different stem designs and under different fixation conditions.

Aims

Osteolysis, secondary to local and systemic physiological effects, is a major challenge in total hip arthroplasty (THA). While osteolytic defects are commonly observed in long-term follow-up, how such lesions alter the distribution of stress is unclear. The aim of this study was to quantitatively describe the biomechanical implication of such lesions by performing subject-specific finite-element (FE) analysis on patients with osteolysis after THA.

Aims

This study presents the long-term survivorship, risk factors for prosthesis survival, and an assessment of the long-term effects of changes in surgical technique in a large series of patients treated by metal-on-metal (MoM) hip resurfacing arthroplasty (HRA).

Aims

Early evidence has emerged suggesting that ceramic-on-ceramic articulations induce a different tissue reaction to ceramic-on-polyethylene and metal-on-metal bearings. Therefore, the aim of this study was to investigate the tissue reaction and cellular response to ceramic total hip arthroplasty (THA) materials in vitro, as well as the tissue reaction in capsular tissue after revision surgery of ceramic-on-ceramic THAs.

Aims

The aim of this systematic review was to report the rate of dislocation following the use of dual mobility (DM) acetabular components in primary and revision total hip arthroplasty (THA).

The acetabular labrum is a soft-tissue structure which lines the acetabular rim of the hip joint. Its role in hip joint biomechanics and joint health has been of particular interest over the past decade. In normal hip joint biomechanics, the labrum is crucial in retaining a layer of pressurised intra-articular fluid for joint lubrication and load support/distribution. Its seal around the femoral head is further regarded as a contributing to hip stability through its suction effect. The labrum itself is also important in increasing contact area thereby reducing contact stress. Given the labrum’s role in normal hip joint biomechanics, surgical techniques for managing labral damage are continuously evolving as our understanding of its anatomy and function continue to progress. The current paper aims to review the anatomy and biomechanical function of the labrum and how they are affected by differing surgical techniques.

Take home message: The acetabular labrum plays a critical role in hip function and maintaining and restoring its function during surgical intervention remain an essential goal.

Cite this article: Bone Joint J 2016;98-B:730–5.

We reviewed the literature on the currently available choices of bearing surface in total hip replacement (THR). We present a detailed description of the properties of articulating surfaces review the understanding of the advantages and disadvantages of existing bearing couples. Recent technological developments in the field of polyethylene and ceramics have altered the risk of fracture and the rate of wear, although the use of metal-on-metal bearings has largely fallen out of favour, owing to concerns about reactions to metal debris. As expected, all bearing surface combinations have advantages and disadvantages. A patient-based approach is recommended, balancing the risks of different options against an individual’s functional demands.

Cite this article: Bone Joint J 2014;96-B:147–56.

Aims

The purpose of this study was to determine the lifetime risk of revision surgery for patients undergoing Charnley cemented total hip arthroplasty (THA), with 40-year follow up, using death as a competing risk.

Aims

We report the incidence of radiolucent lines (RLLs) using two flanged acetabular components at total hip arthroplasty (THA) and the effect of the Rim Cutter.

Objectives

In total hip arthroplasty (THA), the cementless, tapered-wedge stem design contributes to achieving initial stability and providing optimal load transfer in the proximal femur. However, loading conditions on the femur following THA are also influenced by femoral structure. Therefore, we determined the effects of tapered-wedge stems on the load distribution of the femur using subject-specific finite element models of femurs with various canal shapes.

Aims

The aim of this study was to compare the incidence of aseptic loosening after the use of a cemented acetabular component and a Trabecular Metal (TM) acetabular component (Zimmer Inc., Warsaw, Indiana) at acetabular revision with bone impaction grafting.

Dual mobility cups have two points of articulation, one between the shell and the polyethylene (external bearing) and one between the polyethylene and the femoral head (internal bearing). Movement occurs at the inner bearing; the outer bearing only moves at extremes of movement.

Dislocation after total hip arthroplasty (THA) is a cause of much morbidity and its treatment has significant cost implications. Dual mobility cups provide an increased range of movement and a may reduce the risk of dislocation.

This paper reviews the use of these cups in THA, particularly where stability is an issue. Dual mobility cups may be of benefit in primary THA in patients at a high risk of dislocation, such as those who are older with increased comorbidities and a higher American Association of Anesthesiology grade and those with a neuromuscular disease. They may be used at revision surgery where the risk of dislocation is high, such as in patients with many prior dislocations, or those with abductor deficiency. They may also be used in THA for displaced fractures of the femoral neck, which has a notoriously high rate of dislocation.

Cite this article: Bone Joint J 2016;98-B(1 Suppl A):60–3.

Objectives

The use of ceramic femoral heads in total hip arthroplasty (THA) has increased due to their proven low bearing wear characteristics. Ceramic femoral heads are also thought to reduce wear and corrosion at the head-stem junction with titanium (Ti) stems when compared with metal heads. We sought to evaluate taper damage of ceramic compared with metal heads when paired with cobalt chromium (CoCr) alloy stems in a single stem design.

Aims

The aim of this study was to compare early functional and health related quality of life outcomes (HRQoL) in patients who have undergone total hip arthroplasty (THA) using a bone conserving short stem femoral component and those in whom a conventional length uncemented component was used. Outcome was assessed using a validated performance based outcome instrument as well as patient reported outcome measures (PROMs).

Aims

To determine ten-year failure rates following 36 mm metal-on-metal (MoM) Pinnacle total hip arthroplasty (THA), and identify predictors of failure.

Aims

Periprosthetic fracture (PF) after primary total hip arthroplasty (THA) is an uncommon but potentially devastating complication. This study aims to investigate the influence of cemented stem designs on the risk of needing a revision for a PF.

Aims

Reconstruction of the acetabulum after failed total hip arthroplasty (THA) can be a surgical challenge in the presence of severe bone loss. We report the long-term survival of a porous tantalum revision acetabular component, its radiological appearance and quality of life outcomes.

Bioengineering reasons for increased wear and failure of metal-on-metal (MoM) bearings in hip prostheses have been described. Low wear occurs in MoM hips when the centre of the femoral head is concentric with the centre of the acetabular component and the implants are correctly positioned. Translational or rotational malpositioning of the components can lead to the contact-patch of the femoral component being displaced to the rim of the acetabular component, resulting in a ten- to 100-fold increase in wear and metal ion levels. This may cause adverse tissue reactions, loosening of components and failure of the prosthesis.

The leading indication for revision total hip arthroplasty (THA) remains aseptic loosening owing to wear. The younger, more active patients currently undergoing THA present unprecedented demands on the bearings. Ceramic-on-ceramic (CoC) bearings have consistently shown the lowest rates of wear. The recent advances, especially involving alumina/zirconia composite ceramic, have led to substantial improvements and good results in vitro.

Alumina/zirconia composite ceramics are extremely hard, scratch resistant and biocompatible. They offer a low co-efficient of friction and superior lubrication and lower rates of wear compared with other bearings. The major disadvantage is the risk of fracture of the ceramic. The new composite ceramic has reduced the risk of fracture of the femoral head to 0.002%. The risk of fracture of the liner is slightly higher (0.02%).

Assuming that the components are introduced without impingement, CoC bearings have major advantages over other bearings. Owing to the superior hardness, they produce less third body wear and are less vulnerable to intra-operative damage.

The improved tribology means that CoC bearings are an excellent choice for young, active patients requiring THA.

Cite this article: Bone Joint J 2016;98-B(1 Suppl A):14–17.

An uncemented hemispherical acetabular component is the mainstay of acetabular revision and gives excellent long-term results.

Occasionally, the degree of acetabular bone loss means that a hemispherical component will be unstable when sited in the correct anatomical location or there is minimal bleeding host bone left for biological fixation. On these occasions an alternative method of reconstruction has to be used.

A major column structural allograft has been shown to restore the deficient bone stock to some degree, but it needs to be off-loaded with a reconstruction cage to prevent collapse of the graft. The use of porous metal augments is a promising method of overcoming some of the problems associated with structural allograft. If the defect is large, the augment needs to be protected by a cage to allow ingrowth to occur. Cup-cage reconstruction is an effective method of treating chronic pelvic discontinuity and large contained or uncontained bone defects.

This paper presents the indications, surgical techniques and outcomes of various methods which use acetabular reconstruction cages for revision total hip arthroplasty.

Cite this article: Bone Joint J 2016;98-B(1 Suppl A):73–7.

Objectives

High failure rates of metal-on-metal hip arthroplasty implants have highlighted the need for more careful introduction and monitoring of new implants and for the evaluation of the safety of medical devices. The National Joint Registry and other regulatory services are unable to detect failing implants at an early enough stage. We aimed to identify validated surrogate markers of long-term outcome in patients undergoing primary total hip arthroplasty (THA).

Aims

The purpose of this study was to compare the long-term results of primary total hip arthroplasty (THA) in young patients using either a conventional (CPE) or a highly cross-linked (HXLPE) polyethylene liner in terms of functional outcome, incidence of osteolysis, radiological wear and rate of revision.

Most published randomised controlled trials which compare the rates of wear of conventional and cross-linked (XL) polyethylene (PE) in total hip arthroplasty (THA) have described their use with a cementless acetabular component.

We conducted a prospective randomised study to assess the rates of penetration of two distinct types of PE in otherwise identical cemented all-PE acetabular components.

A total of 100 consecutive patients for THA were randomised to receive an acetabular component which had been either highly XL then remelted or moderately XL then annealed.

After a minimum of eight years follow-up, 38 hips in the XL group and 30 hips in the annealed group had complete data (mean follow-up of 9.1 years (7.6 to 10.7) and 8.7 years (7.2 to 10.2), respectively). In the XL group, the steady state rate of penetration from one year onwards was -0.0002 mm/year (sd 0.108): in the annealed group it was 0.1382 mm/year (sd 0.129) (Mann–Whitney U test, p < 0.001). No complication specific to either material was recorded.

These results show that the yearly linear rate of femoral head penetration can be significantly reduced by using a highly XLPE cemented acetabular component.

Cite this article: Bone Joint J 2015;97-B:1458–62.

Squeaking arising from a ceramic-on-ceramic (CoC) total hip replacement (THR) may cause patient concern and in some cases causes patients to seek revision surgery. We performed a meta-analysis to determine the incidence of squeaking and the incidence of revision surgery for squeaking. A total of 43 studies including 16 828 CoC THR that reported squeaking, or revision for squeaking, were entered into the analysis. The incidence of squeaking was 4.2% and the incidence of revision for squeaking was 0.2%. The incidence of squeaking in patients receiving the Accolade femoral stem was 8.3%, and the incidence of revision for squeaking in these patients was 1.3%.

Cite this article: Bone Joint J 2014;96-B:181–7.

Oxidised zirconium (OxZi) has been developed as an alternative bearing surface for femoral heads in total hip arthroplasty (THA). This study has investigated polyethylene wear, functional outcomes and complications, comparing OxZi and cobalt–chrome (CoCr) as part of a three-arm, multicentre randomised controlled trial. Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and highly cross-linked polyethylene (XLPE) liner; Group B received an OxZi femoral head and XLPE liner; Group C received an OxZi femoral head and ultra-high molecular weight polyethylene (UHMWPE) liner. At five years, 368 patients had no statistically significant differences in short-form-36 (p = 0.176 mental, p = 0.756 physical), Western Ontario and McMaster Universities Osteoarthritis Index (p = 0.847), pain scores (p = 0.458) or complications. The mean rate of linear wear was 0.028 mm/year (standard deviation (sd) 0.010) for Group A, 0.023 mm/year (sd 0.010) for Group B, and 0.09 mm/year (sd 0.045) for Group C. Penetration was significantly higher in the UHMWPE liner group compared with both XLPE liner groups (p < 0.001) but no significant difference was noted between CoCr and OxZi when articulating with XLPE (p = 0.153). In this, the largest randomised study of this bearing surface, it appears that using a XLPE acetabular liner is more important in reducing THA component wear than the choice of femoral head bearing, at mid-term follow-up. There is a non-significant trend towards lower wear, coupling OxZi rather than CoCr with XLPE but long-term analysis is required to see if this observation changes with time and becomes significant.

Cite this article: Bone Joint J 2015;97-B:883–9.

Objectives

An ongoing prospective study to investigate failing metal-on-metal hip prostheses was commenced at our centre in 2008. We report on the results of the analysis of the first consecutive 126 failed mated total hip prostheses from a single manufacturer.

Cemented femoral stems with force closed fixation designs have shown good clinical results despite high early subsidence. A new triple-tapered stem in this category (C-stem AMT) was introduced in 2005. This study compares this new stem with an established stem of similar design (Exeter) in terms of migration (as measured using radiostereometric analysis), peri-prosthetic bone remodelling (measured using dual energy x-ray densitometry, DXA), Oxford Hip Score, and plain radiographs.

A total of 70 patients (70 hips) with a mean age of 66 years (53 to 78) were followed for two years. Owing to missing data of miscellaneous reasons, the final analysis represents data from 51 (RSA) and 65 (DXA) patients. Both stems showed a typical pattern of migration: Subsidence and retroversion that primarily occurred during the first three months. C-stem AMT subsided less during the first three months (p = 0.01), before stabilising at a subsidence rate similar to the Exeter stem from years one to two. The rate of migration into retroversion was slightly higher for C-stem AMT during the second year (p = 0.03). Whilst there were slight differences in movement patterns between the stems, the C-stem AMT exhibits good early clinical outcomes and displays a pattern of migration and bone remodelling that predicts good clinical performance.

Cite this article: Bone Joint J 2015;97-B:755–61.

We developed a method of applying vibration to the impaction bone grafting process and assessed its effect on the mechanical properties of the impacted graft. Washed morsellised bovine femoral heads were impacted into shear test rings. A range of frequencies of vibration was tested, as measured using an accelerometer housed in a vibration chamber. Each shear test was repeated at four different normal loads to generate stress-strain curves. The Mohr-Coulomb failure envelope from which shear strength and interlocking values are derived was plotted for each test. The experiments were repeated with the addition of blood in order to replicate a saturated environment.

Graft impacted with the addition of vibration at all frequencies showed improved shear strength when compared with impaction without vibration, with 60 Hz giving the largest effect. Under saturated conditions the addition of vibration was detrimental to the shear strength of the aggregate. The civil-engineering principles of particulate settlement and interlocking also apply to impaction bone grafting. Although previous studies have shown that vibration may be beneficial in impaction bone grafting on the femoral side, our study suggests that the same is not true in acetabular revision.

We investigated factors that were thought to be associated with an increased incidence of squeaking of ceramic-on-ceramic total hip replacements. Between June 1997 and December 2008 the three senior authors implanted 2406 primary total hip replacements with a ceramic-on-ceramic bearing surface. The mean follow-up was 10.6 years. The diagnosis was primary osteoarthritis in each case, and no patient had undergone previous surgery to the hip. We identified 74 squeaking hips (73 patients) giving an incidence of 3.1% at a mean follow-up of 9.5 years (4.1 to 13.3).

Taller, heavier and younger patients were significantly more likely to have hips that squeaked. Squeaking hips had a significantly higher range of post-operative internal (p = 0.001) and external rotation (p = 0.003) compared with silent hips. Patients with squeaking hips had significantly higher activity levels (p = 0.009). A squeaking hip was not associated with a significant difference in patient satisfaction (p = 0.24) or Harris hip score (p = 0.34). Four implant position factors enabled good prediction of squeaking. These were high acetabular component inclination, high femoral offset, lateralisation of the hip centre and either high or low acetabular component anteversion.

This is the largest study to date to examine patient factors and implant position factors that predispose to squeaking of a ceramic-on-ceramic hip. The results suggest that factors which increase the mechanical forces across the hip joint and factors which increase the risk of neck-to-rim impingement, and therefore edge-loading, are those that predispose to squeaking.

Dislocation remains among the most common complications of, and reasons for, revision of both primary and revision total hip replacements (THR). Hence, there is great interest in maximising stability to prevent this complication. Head size has been recognised to have a strong influence on the risk of dislocation post-operatively. As femoral head size increases, stability is augmented, secondary to an increase in impingement-free range of movement. Larger head sizes also greatly increase the ‘jump distance’ required for the head to dislocate in an appropriately positioned cup. Level-one studies support the use of larger diameter heads as they decrease the risk of dislocation following primary and revision THR. Highly cross-linked polyethylene has allowed us to increase femoral head size, without a marked increase in wear. However, the thin polyethylene liners necessary to accommodate larger heads may increase the risk of liner fracture and larger heads have also been implicated in causing soft-tissue impingement resulting in groin pain. Larger diameter heads also impart larger forces on the femoral trunnion, which may contribute to corrosion, metal release, and adverse local tissue reactions. Alternative large bearings including large ceramic heads and dual mobility bearings may mitigate some of these risks, and several of these devices have been used with clinical success.

Cite this article: Bone Joint J 2014;96-B(11 Suppl A):23–6.

A pelvic discontinuity occurs when the superior and inferior parts of the hemi-pelvis are no longer connected, which is difficult to manage when associated with a failed total hip replacement. Chronic pelvic discontinuity is found in 0.9% to 2.1% of hip revision cases with risk factors including severe pelvic bone loss, female gender, prior pelvic radiation and rheumatoid arthritis. Common treatment options include: pelvic plating with allograft, cage reconstruction, custom triflange implants, and porous tantalum implants with modular augments. The optimal technique is dependent upon the degree of the discontinuity, the amount of available bone stock and the likelihood of achieving stable healing between the two segments. A method of treating pelvic discontinuity using porous tantalum components with a distraction technique that achieves both initial stability and subsequent long-term biological fixation is described.

Cite this article: Bone Joint J 2014;96-B(11 Suppl A):73–7.

Surgical interventions consisting of internal fixation (IF) or total hip replacement (THR) are required to restore patient mobility after hip fractures. Conventionally, this decision was based solely upon the degree of fracture displacement. However, in the last ten years, there has been a move to incorporate patient characteristics into the decision making process. Research demonstrating that joint replacement renders superior functional results when compared with IF, in the treatment of displaced femoral neck fractures, has swayed the pendulum in favour of THR. However, a high risk of dislocation has always been the concern. Fortunately, there are newer technologies and alternative surgical approaches that can help reduce the risk of dislocation. The authors propose an algorithm for the treatment of femoral neck fractures: if minimally displaced, in the absence of hip joint arthritis, IF should be performed; if arthritis is present, or the fracture is displaced, then THR is preferred.

Cite this article: Bone Joint J 2014;96-B(11 Suppl A):43–7.

A retrospective review was performed of patients undergoing primary cementless total knee replacement (TKR) using porous tantalum performed by a group of surgical trainees. Clinical and radiological follow-up involved 79 females and 26 males encompassing 115 knees. The mean age was 66.9 years (36 to 85). Mean follow-up was 7 years (2 to 11). Tibial and patellar components were porous tantalum monoblock implants, and femoral components were posterior stabilised (PS) in design with cobalt–chromium fibre mesh. Radiological assessments were made for implant positioning, alignment, radiolucencies, lysis, and loosening. There was 95.7% survival of implants. There was no radiological evidence of loosening and no osteolysis found. No revisions were performed for aseptic loosening. Average tibial component alignment was 1.4° of varus (4°of valgus to 9° varus), and 6.2° (3° anterior to 15° posterior) of posterior slope. Mean femoral component alignment was 6.6° (1° to 11°) of valgus. Mean tibiofemoral alignment was 5.6° of valgus (7° varus to 16° valgus). Patellar tilt was a mean of 2.4° lateral (5° medial to 28° lateral). Patient satisfaction with improvement in pain was 91%. Cementless TKR incorporating porous tantalum yielded good clinical and radiological outcomes at a mean of follow-up of seven-years.

Cite this article: Bone Joint J 2014;96-B(11 Suppl A):87–92.

Conventional cemented acetabular components are reported to have a high rate of failure when implanted into previously irradiated bone. We recommend the use of a cemented reconstruction with the addition of an acetabular reinforcement cross to improve fixation.

We reviewed a cohort of 45 patients (49 hips) who had undergone irradiation of the pelvis and a cemented total hip arthroplasty (THA) with an acetabular reinforcement cross. All hips had received a minimum dose of 30 Gray (Gy) to treat a primary nearby tumour or metastasis. The median dose of radiation was 50 Gy (Q1 to Q3: 45 to 60; mean: 49.57, 32 to 72).

The mean follow-up after THA was 51 months (17 to 137). The cumulative probability of revision of the acetabular component for a mechanical reason was 0% (0 to 0%) at 24 months, 2.9% (0.2 to 13.3%) at 60 months and 2.9% (0.2% to 13.3%) at 120 months, respectively. One hip was revised for mechanical failure and three for infection.

Cemented acetabular components with a reinforcement cross provide good medium-term fixation after pelvic irradiation. These patients are at a higher risk of developing infection of their THA.

Cite this article: Bone Joint J 2015;97-B:177–84.

We present our experience with a double-mobility acetabular component in 155 consecutive revision total hip replacements in 149 patients undertaken between 2005 and 2009, with particular emphasis on the incidence of further dislocation. The mean age of the patients was 77 years (42 to 89) with 59 males and 90 females. In all, five patients died and seven were lost to follow-up. Indications for revision were aseptic loosening in 113 hips, recurrent instability in 29, peri-prosthetic fracture in 11 and sepsis in two. The mean follow-up was 42 months (18 to 68). Three hips (2%) in three patients dislocated within six weeks of surgery; one of these dislocated again after one year. All three were managed successfully with closed reduction. Two of the three dislocations occurred in patients who had undergone revision for recurrent dislocation. All three were found at revision to have abductor deficiency. There were no dislocations in those revised for either aseptic loosening or sepsis.

These results demonstrate a good mid-term outcome for this component. In the 29 patients revised for instability, only two had a further dislocation, both of which were managed by closed reduction.

It is probable that both genetic and environmental factors play some part in the aetiology of most cases of degenerative hip disease. Geneticists have identified some single gene disorders of the hip, but have had difficulty in identifying the genetics of many of the common causes of degenerative hip disease. The heterogeneity of the phenotypes studied is part of the problem. A detailed classification of phenotypes is proposed. This study is based on careful documentation of 2003 consecutive total hip replacements performed by a single surgeon between 1972 and 2000. The concept that developmental problems may initiate degenerative hip disease is supported. The influences of gender, age and body mass index are outlined. Biomechanical explanations for some of the radiological appearances encountered are suggested. The body weight lever, which is larger than the abductor lever, causes the abductor power to be more important than body weight. The possibility that a deficiency in joint lubrication is a cause of degenerative hip disease is discussed. Identifying the phenotypes may help geneticists to identify genes responsible for degenerative hip disease, and eventually lead to a definitive classification.

The conventional method for reconstructing acetabular bone loss at revision surgery includes using structural bone allograft. The disadvantages of this technique promoted the advent of metallic but biocompatible porous implants to fill bone defects enhancing initial and long-term stability of the acetabular component. This paper presents the indications, surgical technique and the outcome of using porous metal acetabular augments for reconstructing acetabular defects.

Cite this article: Bone Joint J 2013;95-B, Supple A:103–8.

Between November 1997 and December 2000 we performed 27 total hip replacements in 22 patients with high congenital dislocation of the hip using porous tantalum monoblock acetabular components implanted in the true acetabular bed. Clinical and radiological evaluation was performed at regular intervals for a mean of 10.2 years (8.5 to 12). The mean Harris Hip Score improved from 48.3 (15 to 65) pre-operatively to 89.5 (56 to 100) at the final follow-up. The mean Oxford Hip Score was 49.5 (35 to 59) pre-operatively and decreased to 21.2 (12 to 48) at one year and 15.2 (10 to 28) at final follow-up. Migration of the acetabular component was assessed with the EBRA software system. There was a mean migration of 0.68 mm (0.49 to 0.8) in the first year and a mean 0.89 mm (0.6 to 0.98) in the second year, after excluding one initial excessive migration. No revision was necessary for any reason, no acetabular component became loose, and no radiolucent lines were observed at the final follow-up.

The porous tantalum monoblock acetabular component is an implant offering adequate initial stability in conjunction with a modulus of elasticity and porosity close to that of cancellous bone. It favours bone ingrowth, leading to good mid-term results.

We prospectively studied 217 patients who underwent 234 Elite Plus total hip arthroplasties. At a mean of 6.4 (SD 0.7) years post-operatively, 39 patients had died and 22 were either lost to follow-up or had no radiographs available. Clinical (Oxford hip score) and radiological assessments were performed on 156 patients (168 hip arthroplasties) who had a mean age of 67.7 (SD 9.7) years at operation.

In the assessed group, 26 of 159 (16.4%) of femoral stems which had not already been revised and 19 of 159 (11.9%) of acetabular cups were definitely loose. In total, 52 of 168 (31%) of hips had either been revised or had definite evidence of loosening of a component. We could not establish any relationship between clinical and radiological outcomes.

Despite the fact that the clinical outcome and rate of revision for the Elite Plus appeared to meet international standards, our findings give us cause for concern. We believe that joint registries should include radiological surveillance in order to provide reliable information about medium-term outcomes for hip prostheses.

Between January 1998 and December 1998, 82 consecutive patients (86 hips) underwent total hip arthroplasty using a trabecular metal monoblock acetabular component. All patients had a clinical and radiological follow-up evaluation at six, 12 and 24 weeks, 12 months, and then annually thereafter. On the initial post-operative radiograph 25 hips had a gap between the outer surface of the component and the acetabular host bed which ranged from 1 to 5 mm. All patients were followed up clinically and radiologically for a mean of 7.3 years (7 to 7.5). The 25 hips with the 1 to 5 mm gaps were studied for component migration at two years using the Einzel-Bild-Roentgen-Analyse (EBRA) digital measurement method. At 24 weeks all the post-operative gaps were filled with bone and no acetabular component had migrated. The radiographic outcome of all 86 components showed no radiolucent lines and no evidence of lysis. No acetabular implant was revised. There were no dislocations or other complications. The bridging of the interface gaps (up to 5 mm) by the trabecular metal monoblock acetabular component indicates the strong osteoconductive, and possibly osteoinductive, properties of trabecular metal.

The rate and mode of early failure in 463 Birmingham hip resurfacings in a two-centre, multisurgeon series were examined. Of the 463 patients two have died and three were lost to follow-up. The mean radiological and clinical follow-up was for 43 months (6 to 90).

We have revised 13 resurfacings (2.8%) including seven for pain, three for fracture, two for dislocation and another for sepsis. Of these, nine had macroscopic and histological evidence of metallosis. The survival at five years was 95.8% (95% confidence interval (CI) 94.1 to 96.8) for revision for all causes and 96.9% (95% CI 95.5 to 98.3) for metallosis.

The rate of metallosis related revision was 3.1% at five years. Risk factors for metallosis were female gender, a small femoral component, a high abduction angle and obesity. We do not advocate the use of the Birmingham Hip resurfacing procedure in patients with these risk factors.

Large femoral heads have been used with increasing frequency over the last decade. The prime reason is likely the effect of large heads on stability. The larger head neck ratio, combined with the increased jump distance of larger heads result in a greater arc of impingement free motion, and greater resistance to dislocation in a provocative position. Multiple studies have demonstrated clear clinical efficacy in diminishing dislocation rates with the use of large femoral heads. With crosslinked polyethylene, wear has been shown to be equivalent between larger and smaller heads. However, the stability advantages of increasing diameter beyond 38 mm have not been clearly demonstrated. More importantly, recent data implicates large heads in the increasing prevalence of groin pain and psoas impingement. There are clear benefits with larger femoral head diameters, but the advantages of diameters beyond 38 mm have not yet been demonstrated clinically.

The practice of removing a well-fixed cementless femoral component is associated with high morbidity. Ceramic bearing couples are low wearing and their use minimises the risk of subsequent further revision due to the production of wear debris. A total of 165 revision hip replacements were performed, in which a polyethylene-lined acetabular component was revised to a new acetabular component with a ceramic liner, while retaining the well-fixed femoral component. A titanium sleeve was placed over the used femoral trunnion, to which a ceramic head was added. There were 100 alumina and 65 Delta bearing couples inserted.

The mean Harris hip score improved significantly from 71.3 (9.0 to 100.0) pre-operatively to 91.0 (41.0 to 100.0) at a mean follow up of 4.8 years (2.1 to 12.5) (p < 0.001). No patients reported squeaking of the hip.

There were two fractures of the ceramic head, both in alumina bearings. No liners were seen to fracture. No fractures were observed in components made of Delta ceramic. At 8.3 years post-operatively the survival with any cause of failure as the endpoint was 96.6% (95% confidence interval (CI) 85.7 to 99.3) for the acetabular component and 94.0% (95% CI 82.1 to 98.4) for the femoral component.

The technique of revising the acetabular component in the presence of a well-fixed femoral component with a ceramic head placed on a titanium sleeve over the used trunnion is a useful adjunct in revision hip practice. The use of Delta ceramic is recommended.

Cite this article: Bone Joint J 2013;95-B:333–8.

In this paper, we will consider the current role of metal-on-metal bearings by looking at three subtypes of MoM hip arthroplasty separately: Hip resurfacing, large head (> 36 mm) MoM THA and MoM THA with traditional femoral head sizes.

Trabecular metal (TM) augments are a relatively new option for reconstructing segmental bone loss during acetabular revision. We studied 34 failed hip replacements in 34 patients that were revised between October 2003 and March 2010 using a TM acetabular shell and one or two augments. The mean age of the patients at the time of surgery was 69.3 years (46 to 86) and the mean follow-up was 64.5 months (27 to 107). In all, 18 patients had a minor column defect, 14 had a major column defect, and two were associated with pelvic discontinuity. The hip centre of rotation was restored in 27 patients (79.4%). The Oxford hip score increased from a mean of 15.4 points (6 to 25) before revision to a mean of 37.7 (29 to 47) at the final follow-up. There were three aseptic loosenings of the construct, two of them in the patients with pelvic discontinuity. One septic loosening also occurred in a patient who had previously had an infected hip replacement. The augments remained stable in two of the failed hips. Whenever there was a loose acetabular component in contact with a stable augment, progressive metal debris shedding was evident on the serial radiographs. Complications included another deep infection treated without revision surgery. Good clinical and radiological results can be expected for bone-deficient acetabula treated by a TM cup and augment, but for pelvic discontinuities this might not be a reliable option.

Cite this article: Bone Joint J 2013;95-B:166–72.

Following the recall of modular neck hip stems in July 2012, research into femoral modularity will intensify over the next few years. This review aims to provide surgeons with an up-to-date summary of the clinically relevant evidence. The development of femoral modularity, and a classification system, is described. The theoretical rationale for modularity is summarised and the clinical outcomes are explored. The review also examines the clinically relevant problems reported following the use of femoral stems with a modular neck.

Joint replacement registries in the United Kingdom and Australia have provided data on the failure rates of modular devices but cannot identify the mechanism of failure. This information is needed to determine whether modular neck femoral stems will be used in the future, and how we should monitor patients who already have them implanted.

Cite this article: Bone Joint J 2013;95-B:1011–21.

The popularity of cementless total hip replacement (THR) has surpassed cemented THR in England and Wales. This retrospective cohort study records survival time to revision following primary cementless THR with the most common combination (accounting for almost a third of all cementless THRs), and explores risk factors independently associated with failure, using data from the National Joint Registry for England and Wales. Patients with osteoarthritis who had a DePuy Corail/Pinnacle THR implanted between the establishment of the registry in 2003 and 31 December 2010 were included within analyses. There were 35 386 procedures. Cox proportional hazard models were used to analyse the extent to which the risk of revision was related to patient, surgeon and implant covariates. The overall rate of revision at five years was 2.4% (99% confidence interval 2.02 to 2.79). In the final adjusted model, we found that the risk of revision was significantly higher in patients receiving metal-on-metal (MoM: hazard ratio (HR) 1.93, p < 0.001) and ceramic-on-ceramic bearings (CoC: HR 1.55, p = 0.003) compared with the best performing bearing (metal-on-polyethylene). The risk of revision was also greater for smaller femoral stems (sizes 8 to 10: HR 1.82, p < 0.001) compared with mid-range sizes. In a secondary analysis of only patients where body mass index (BMI) data were available (n = 17 166), BMI ≥ 30 kg/m² significantly increased the risk of revision (HR 1.55, p = 0.002). The influence of the bearing on the risk of revision remained significant (MoM: HR 2.19, p < 0.001; CoC: HR 2.09, p = 0.001). The risk of revision was independent of age, gender, head size and offset, shell, liner and stem type, and surgeon characteristics.

We found significant differences in failure between bearing surfaces and femoral stem size after adjustment for a range of covariates in a large cohort of single-brand cementless THRs. In this study of procedures performed since 2003, hard bearings had significantly higher rates of revision, but we found no evidence that head size had an effect. Patient characteristics, such as BMI and American Society of Anesthesiologists grade, also influence the survival of cementless components.

Cite this article: Bone Joint J 2013;95-B:747–57.

The aim of this review is to evaluate the current available literature evidencing on peri-articular hip endoscopy (the third compartment). A comprehensive approach has been set on reports dealing with endoscopic surgery for recalcitrant trochanteric bursitis, snapping hip (or coxa-saltans; external and internal), gluteus medius and minimus tears and endoscopy (or arthroscopy) after total hip arthroplasty. This information can be used to trigger further research, innovation and education in extra-articular hip endoscopy.

A modular layered acetabular component (metal-polyethylene-ceramic) was developed in Japan for use in alumina ceramic-on-ceramic total hip replacement. Between May 1999 and July 2000, we performed 35 alumina ceramic-on-ceramic total hip replacements in 30 consecutive patients, using this layered component and evaluated the clinical and radiological results over a mean follow-up of 5.8 years (5 to 6.5). A total of six hips underwent revision, one for infection, two for dislocation with loosening of the acetabular component, two for alumina liner fractures and one for component dissociation with pelvic osteolysis. There were no fractures of the ceramic heads, and no loosening of the femoral or acetabular component in the unrevised hips was seen at final follow-up. Osteolysis was not observed in any of the unrevised hips. The survivorship analysis at six years after surgery was 83%. The layered acetabular component in our experience, has poor durability because of unexpected mechanical failures including alumina liner fracture and component dissociation.

Alumina–alumina bearings are among the most resistant to wear in total hip replacement. Examination of their surfaces is one way of comparing damage caused by wear of hip joints simulated in vitro to that seen in explanted bearings. The aim of this study was to determine whether second-generation ceramic bearings exhibited a better pattern of wear than those reported in the literature for first-generation bearings. We considered both macro- and microscopic findings.

We found that long-term alumina wear in association with a loose acetabular component could be categorised into three groups. Of 20 specimens, four had ‘low wear’, eight ‘crescent wear’ and eight ‘severe wear’, which was characterised by a change in the physical shape of the bearing and a loss of volume. This suggests that the wear in alumina–alumina bearings in association with a loose acetabular component may be variable in pattern, and may explain, in part, why the wear of a ceramic head in vivo may be greater than that seen after in vitro testing.

We analysed 54 alumina ceramic-on-ceramic bearings from total hip replacements retrieved at one centre after a mean duration of 3.5 years (0.2 to 10.6) in situ. These implants were obtained from 54 patients (16 men and 38 women) with a mean age of 67 years (33 to 88) who underwent revision for a variety of reasons. Posterior edge loading was found in the majority of these retrievals (32 out of 54). Anterosuperior edge loading occurred less often but produced a higher rate of wear. Stripe wear on the femoral heads had a median volumetric wear rate of 0.2 mm³/year (0 to 7.2). The wear volume on the femoral heads corresponded to the width of edge wear on the matching liner. Anteversion of the acetabular component was found to be a more important determinant than inclination for wear in ceramic bearings. Posterior edge loading may be considered to be a normal occurrence in ceramic-on-ceramic bearings, with minimal clinical consequences. Edge loading should be defined as either anterosuperior or posterior, as each edge loading mechanism may result in different clinical implications.

The ideal acetabular component is characterised by reliable, long-term fixation with physiological loading of bone and a low rate of wear. Trabecular metal is a porous construct of tantalum which promotes bony ingrowth, has a modulus of elasticity similar to that of cancellous bone, and should be an excellent material for fixation.

Between 2004 and 2006, 55 patients were randomised to receive either a cemented polyethylene or a monobloc trabecular metal acetabular component with a polyethylene articular surface. We measured the peri-prosthetic bone density around the acetabular components for up to two years using dual-energy x-ray absorptiometry.

We found evidence that the cemented acetabular component loaded the acetabular bone centromedially whereas the trabecular metal monobloc loaded the lateral rim and behaved like a hemispherical rigid metal component with regard to loading of the acetabular bone. We suspect that this was due to the peripheral titanium rim used for the mechanism of insertion.

We investigated the early results of modular porous metal components used in 23 acetabular reconstructions associated with major bone loss. The series included seven men and 15 women with a mean age of 67 years (38 to 81), who had undergone a mean of two previous revisions (1 to 7).

Based on Paprosky’s classification, there were 17 type 3A and six type 3B defects. Pelvic discontinuity was noted in one case. Augments were used in 21 hips to support the shell and an acetabular component-cage construct was implanted in one case. At a mean follow-up of 41 months (24 to 62), 22 components remained well fixed. Two patients required rerevision of the liners for prosthetic joint instability. Clinically, the mean Harris Hip Score improved from 43.0 pre-operatively (14 to 86) to 75.7 post-operatively (53 to 100). The mean pre-operative Merle d’Aubigné score was 8.2 (3 to 15) and improved to a mean of 13.7 (11 to 18) post-operatively.

These short-term results suggest that modular porous metal components are a viable option in the reconstruction of Paprosky type 3 acetabular defects. More data are needed to determine whether the system yields greater long-term success than more traditional methods, such as reconstruction cages and structural allografts.

Of the 11 054 Charnley low-frictional torque arthroplasties carried out at our hospital between 1962 and 1977, 110 (94 patients) had a minimum follow-up of 30 years with a mean of 32.3 years (30.0 to 40.5). The mean age of the patients at operation was 43.3 years (17.0 to 65.0) and 75.7 years (51.0 to 97.0) at follow-up. Overall, 90% of hips (99) were free from pain and activity was reported as normal in 58% of the patients.

A total of 13 hips (11.8%) were revised at a mean follow-up of 32.3 years (30.0 to 39.5), with wear and loosening of the acetabular component as the main indications.

The clinical results did not reflect the mechanical state of the implant. Follow-up with sequential radiographs of good quality is essential. Revision for radiological changes alone must be accepted if gross loss of bone stock is to be avoided.

Improvements in the design, materials and operative technique, based on the long-term outcome, are highlighted.

Dislocation is a common reason for revision following total hip replacement. This study investigated the relationship between the bearing surface and the risk of revision due to dislocation. It was based on 110 239 primary total hip replacements with a diagnosis of osteoarthritis collected by the Australian Orthopaedic Association National Joint Replacement Registry between September 1999 and December 2007. A total of 862 (0.78%) were revised because of dislocation. Ceramic-on-ceramic bearing surfaces had a lower risk of requiring revision due to dislocation than did metal-on-polyethylene and ceramic-on-polyethylene surfaces, with a follow-up of up to seven years. However, ceramic-on-ceramic implants were more likely to have larger prosthetic heads and to have been implanted in younger patients. The size of the head of the femoral component and age are known to be independent predictors of dislocation. Therefore, the outcomes were stratified by the size of the head and age.

There is a significantly higher rate of revision for dislocation in ceramic-on-ceramic bearing surfaces than in metal-on-polyethylene implants when smaller sizes (≤ 28 mm) of the head were used in younger patients (< 65 years) (hazard ratio = 1.53, p = 0.041) and also with larger (> 28 mm) and in older patients (≥ 65 years) (hazard ratio = 1.73, p = 0.016).

This study reports on ceramic-on-metal (CoM) bearings in total hip replacement. Whole blood metal ion levels were measured. The median increase in chromium and cobalt at 12 months was 0.08 μg/1 and 0.22 μg/1, respectively, in CoM bearings. Comparable values for metal-on-metal (MoM) were 0.48 μg/1 and 0.32 μg/1. The chromium levels were significantly lower in CoM than in MoM bearings (p = 0.02). The cobalt levels were lower, but the difference was not significant. Examination of two explanted ceramic heads revealed areas of thin metal transfer. CoM bearings (one explanted head and acetabular component, one explanted head and new acetabular component, and three new heads and acetabular components) were tested in a hip joint simulator. The explanted head and acetabular component had higher bedding-in. However, after one million cycles all the wear rates were the same and an order of magnitude less than that reported for MoM bearings. There were four outliers in each clinical group, primarily related to component malposition.

Polyethylene wear of acetabular components is a key factor in the development of periprosthetic osteolysis and wear at the articular surface has been well documented and quantified, but fewer data are available about changes which occur at the backside of the liner.

At revision surgery for loosening of the femoral component we retrieved 35 conventional modular acetabular liners of the same design. Linear and volumetric articular wear, backside volumetric change and the volume of the screw-head indentations were quantified. These volumes, clinical data and the results from radiological Ein Bild Röntgen Analyse migration analysis were used to identify potential factors influencing the volumetric articular wear and backside volumetric change.

The rate of backside volumetric change was found to be 2.8% of the rate of volumetric articular wear and decreased with increasing liner size. Migrated acetabular components showed significantly higher rates of backside volumetric change plus screw-head indentations than those without migration.

The backside volumetric change was at least ten times larger than finite-element simulation had suggested. In a stable acetabular component with well-anchored screws, the amount of backside wear should not cause clinical problems. Impingement of the screw-heads could produce more wear particles than those generated at the liner-shell interface. Because the rate of backside volumetric change is only 2.8% of the rate of volumetric articular wear and since creep is likely to contribute a significant portion to this, the debris generated by wear at the backside of the liner may not be sufficient to create a strong osteolytic response.

We reviewed 1039 revision total hip replacements where an angle-bore acetabular component was used. After a mean follow-up of nine years (0 to 20.6), the incidence of revision for dislocation was 2.1% (22 revisions), a success rate of 97.9%. In 974 revisions, where the indication was other than dislocation, the success rate was 98.5%. Of the 65 revisions for dislocation, 58 (89.2%) were successful after the first revision and a further five after the second revision, an overall success of 96.9%. Two patients elected to have their implants removed. Dislocation after revision of failed total hip replacement is a complex issue. There is often no single cause and no simple solution. The angle-bore acetabular component, in combination with a 22.225-mm diameter femoral head, offers a high level of success.

It has been suggested that the wear of ultra-high molecular weight polyethylene (UHMWPE) in total hip replacement is substantially reduced when the femoral head is ceramic rather than metal. However, studies of alumina and zirconia ceramic femoral heads on the penetration of an UHMWPE liner in vivo have given conflicting results.

The purpose of this study was to examine the surface characteristics of 30 alumina and 24 zirconia ceramic femoral heads and to identify any phase transformation in the zirconia heads. We also studied the penetration rate of alumina and zirconia heads into contemporary UHMWPE liners. The alumina heads had been implanted for a mean of 11.3 years (8.1 to 16.2) and zirconia heads for a mean of 9.8 years (7.5 to 15).

The mean surface roughness values of the explanted alumina heads (Ra 40.12 nm and Rpm 578.34 nm) were similar to those for the explanted zirconia heads (Ra 36.21 nm and Rpm 607.34 nm). The mean value of the monoclinic phase of two control zirconia heads was 1% (0.8% to 1.5%) and 1.2% (0.9% to 1.3%), respectively. The mean value of the monoclinic phase of 24 explanted zirconia heads was 7.3% (1% to 26%).

In the alumina group, the mean linear penetration rate of the UMWPE liner was 0.10 mm/yr (0.09 to 0.12) in hips with low Ra and Rpm values (13.22 nm and 85.91 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.13 mm/yr (0.07 to 0.23) in hips with high Ra and Rpm values (198.72 nm and 1329 nm, respectively). This difference was significant (p = 0.041).

In the zirconia head group, the mean linear penetration rate of the UHMWPE liner was 0.09 mm/yr (0.07 to 0.14) in hips with low Ra and Rpm values (12.78 nm and 92.99 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.12 mm/yr (0.08 to 0.22) in hips with high Ra and Rpm values (199.21 nm and 1381 nm, respectively). This difference was significant (p = 0.039).

The explanted zirconia heads which had a minimal phase transformation had similar surface roughness and a similar penetration rate of UHMWPE liner as the explanted alumina head.

In developmental dysplasia of the hip, a deficient acetabulum may be augmented by placing local autogenous iliac osseous graft, or the ilium itself, over the head of the femur with the expectation that the added bone will function as a bearing surface. We analysed this bone obtained en bloc during subsequent surgery which was performed for degenerative osteoarthritis in three patients at 6, 25 and 30 years after the initial augmentation procedure. In each patient, the augmentation comprised of red cancellous bone covered on its articulating surface by a distinct layer of white tissue. Microscopy of this tissue showed parallel rows of spindle-shaped cells lying between linearly arranged collagen bundles typical of joint capsule. Biochemical analysis showed type I collagen, the principal collagen of joint capsule and bone, with no significant quantity of type II collagen, the principal collagen of cartilage. While the added bone produced by acetabular augmentation was durable, histological and biochemical analyses suggested that it had not undergone cartilage metaplasia. The augmented acetabulum articulates with the head of the femur by means of an interposed hip joint capsule.

Increased concentrations of metal ions after metal-on-metal resurfacing arthroplasty of the hip remain a concern. Although there has been no proven link to long-term health problems or early prosthetic failure, variables associated with high metal ion concentrations should be identified and, if possible, corrected. Our study provides data on metal ion levels from a series of 76 consecutive patients (76 hips) after resurfacing arthroplasty with the Articular Surface Replacement. Chromium and cobalt ion concentrations in the whole blood of patients with smaller (≤ 51 mm) femoral components were significantly higher than in those with the larger (≥ 53 mm) components (p < 0.01). Ion concentrations in the former group were significantly related to the inclination (p = 0.01) and anteversion (p = 0.01) of the acetabular component. The same relationships were not significant in the patients with larger femoral components (p = 0.61 and p = 0.49, respectively). Accurate positioning of the acetabular component intra-operatively is essential in order to reduce the concentration of metal ions in the blood after hip resurfacing arthroplasty with the Articular Surface Replacement implant.

Metal-on-metal hip bearings are being implanted into younger patients. The consequence of elevated levels of potentially carcinogenic metal ions is therefore a cause for concern. We have determined the levels of cobalt (Co), chromium (Cr), titanium (Ti) and vanadium (Va) in the urine and whole blood of patients who had had metal-on-metal and metal-on-polyethylene articulations in situ for more than 30 years. We compared these with each other and with the levels for a control group of subjects.

We found significantly elevated levels of whole blood Ti, Va and urinary Cr in all arthroplasty groups. The whole blood and urine levels of Co were grossly elevated, by a factor of 50 and 300 times respectively in patients with loose metal-on-metal articulations when compared with the control group. Stable metal-on-metal articulations showed much lower levels. Elevated levels of whole blood or urinary Co may be useful in identifying metal-on-metal articulations which are loose.

The Cambridge Cup has been designed to replace the horseshoe-shaped articular cartilage of the acetabulum and the underlying subchondral bone. It is intended to provide physiological loading with minimal resection of healthy bone.

The cup has been used in 50 women with displaced, subcapital fractures of the neck of the femur. In 24 cases, the cup was coated with hydroxyapatite. In 26, the coating was removed before implantation in order to simulate the effect of long-term resorption.

The mean Barthel index and the Charnley-modified Merle d’Aubigné scores recovered to their levels before fracture. We reviewed 30 women at two years, 21 were asymptomatic and nine reported minimal pain. The mean scores deteriorated slightly after five years reflecting the comorbidity of advancing age. Patients with the hydroxyapatite-coated components remained asymptomatic, with no wear or loosening. The uncoated components migrated after four years and three required revision. This trial shows good early results using a novel, hydroxyapatite-coated, physiological acetabular component.