The Bone & Joint Journal
Vol. 96-B, Issue 1 | Pages 114 - 121
1 Jan 2014
Pekmezci M McDonald E Buckley J Kandemir U

We investigated a new intramedullary locking nail that allows the distal interlocking screws to be locked to the nail. We compared fixation using this new implant with fixation using either a conventional nail or a locking plate in a laboratory simulation of an osteoporotic fracture of the distal femur. A total of 15 human cadaver femora were used to simulate an AO 33-A3 fracture pattern. Paired specimens compared fixation using either a locking or non-locking retrograde nail, and using either a locking retrograde nail or a locking plate. The constructs underwent cyclical loading to simulate single-leg stance up to 125 000 cycles. Axial and torsional stiffness and displacement, cycles to failure and modes of failure were recorded for each specimen. When compared with locking plate constructs, locking nail constructs had significantly longer mean fatigue life (75 800 cycles (sd 33 900) vs 12 800 cycles (sd 6100); p = 0.007) and mean axial stiffness (220 N/mm (sd 80) vs 70 N/mm (sd 18); p = 0.005), but lower mean torsional stiffness (2.5 Nm/° (sd 0.9) vs 5.1 Nm/° (sd 1.5); p = 0.008). In addition, in the nail group the mode of failure was either cut-out of the distal screws or breakage of nails, and in the locking plate group breakage of the plate was always the mode of failure. Locking nail constructs had significantly longer mean fatigue life than non-locking nail constructs (78 900 cycles (sd 25 600) vs 52 400 cycles (sd 22 500); p = 0.04).

The new locking retrograde femoral nail showed better stiffness and fatigue life than locking plates, and superior fatigue life to non-locking nails, which may be advantageous in elderly patients.

Cite this article: Bone Joint J 2014;96-B:114–21.


The Journal of Bone & Joint Surgery British Volume
Vol. 94-B, Issue 2 | Pages 241 - 248
1 Feb 2012
Firoozabadi R McDonald E Nguyen T Buckley JM Kandemir U

Filling the empty holes in peri-articular locking plates may improve the fatigue strength of the fixation. The purpose of this in vitro study was to investigate the effect of plugging the unused holes on the fatigue life of peri-articular distal femoral plates used to fix a comminuted supracondylar fracture model.

A locking/compression plate was applied to 33 synthetic femurs and then a 6 cm metaphyseal defect was created (AO Type 33-A3). The specimens were then divided into three groups: unplugged, plugged with locking screw only and fully plugged holes. They were then tested using a stepwise or run-out fatigue protocol, each applying cyclic physiological multiaxial loads.

All specimens in the stepwise group failed at the 770 N load level. The mean number of cycles to failure for the stepwise specimen was 25 500 cycles (sd 1500), 28 800 cycles (sd 6300), and 26 400 cycles (sd 2300) cycles for the unplugged, screw only and fully plugged configurations, respectively (p = 0.16). The mean number of cycles to failure for the run-out specimens was 42 800 cycles (sd 10 700), 36 000 cycles (sd 7200), and 36 600 cycles (sd 10 000) for the unplugged, screw only and fully plugged configurations, respectively (p = 0.50). There were also no differences in axial or torsional stiffness between the constructs. The failures were through the screw holes at the level of comminution.

In conclusion, filling the empty combination locking/compression holes in peri-articular distal femur locking plates at the level of supracondylar comminution does not increase the fatigue life of the fixation in a comminuted supracondylar femoral fracture model (AO 33-A3) with a 6 cm gap.