We reviewed 142 consecutive primary total hip replacements implanted into 123 patients between 1988 and 1993 using the Exeter Universal femoral stem. A total of 74 patients (88 hips) had survived for ten years or more and were reviewed at a mean of 12.7 years (10 to 17). There was no loss to follow-up.

The rate of revision of the femoral component for aseptic loosening and osteolysis was 1.1% (1 stem), that for revision for any cause was 2.2% (2 stems), and for re-operation for any cause was 21.6% (19 hips). Re-operation was because of failure of the acetabular component in all but two hips.

All but one femoral component subsided within the cement mantle to a mean of 1.52 mm (0 to 8.3) at the final follow-up. One further stem had subsided excessively (8 mm) and had lucent lines at the cement-stem and cement-bone interfaces. This was classified as a radiological failure and is awaiting revision. One stem was revised for deep infection and one for excessive peri-articular osteolysis. Defects of the cement mantle (Barrack grade C and D) were found in 28% of stems (25 hips), associated with increased subsidence (p = 0.01), but were not associated with endosteal lysis or failure.

Peri-articular osteolysis was significantly related to the degree of polyethylene wear (p < 0.001), which was in turn associated with a younger age (p = 0.01) and male gender (p < 0.001).

The use of the Exeter metal-backed acetabular component was a notable failure with 12 of 32 hips (37.5%) revised for loosening. The Harris-Galante components failed with excessive wear, osteolysis and dislocation with 15% revised (5 of 33 hips). Only one of 23 hips with a cemented Elite component (4%) was revised for loosening and osteolysis.

Our findings show that the Exeter Universal stem implanted outside the originating centre has excellent medium-term results.

Our aim was to determine if the height of the cup, lateralisation or the abduction angle correlated with functional outcome or survivorship in revision total hip replacement in patients with a previous diagnosis of developmental dysplasia of the hip. A retrospective investigation of 51 patients (63 hips) who had undergone revision total hip replacement was performed. The mean duration of follow-up was 119 months. Forty-one patients (52 hips) were available for both determination of functional outcome and survivorship analysis. Ten patients (11 hips) were only available for survivorship analysis.

The height of the cup was found to have a statistically significant correlation with functional outcome and a high hip centre correlated with a worse outcome score. Patients with a hip centre of less than 3.5 cm above the anatomical level had a statistically better survivorship of the cup than those with centres higher than this. Restoration of the height of the centre of the hip to as near the anatomical position as possible improved functional outcome and survivorship of the cup.

The aim of this study was to investigate the possible benefit of large-head metal-on-metal bearing on a stem for primary hip replacement compared with a 28 mm diameter conventional metal-on-polyethylene bearing in a prospective randomised controlled trial. We investigated cemented stem behaviour between these two different bearings using Einzel-Bild-Röntgen-Analyse, clinical and patient reported measures (Harris hip score, Western Ontario and McMaster Universities osteoarthritis index, Short Form-36 and satisfaction) and whole blood metal ion levels at two years. A power study indicated that 50 hips were needed in each group to detect subsidence of > 5 mm at two years with a p-value of < 0.05.

Significant improvement (p < 0.001) was found in the mean clinical and patient reported outcomes at two years for both groups. Comparison of outcomes between the groups at two years showed no statistically significant difference for mean stem migration, clinical and patient reported outcomes; except overall patient satisfaction which was higher for metal-on-metal group (p = 0.05). Metal ion levels were raised above the Medicines and Healthcare products Regulatory Agency advised safety level (7 µg per litre) in 20% of the metal-on-metal group and in one patient in metal-on-polyethylene group (who had a metal-on-metal implant on the contralateral side). Two patients in the metal-on-metal group were revised, one for pseudotumour and one for peri-prosthetic fracture.

Use of large modular heads is associated with a risk of raised whole blood metal ion levels despite using a proven bearing from resurfacing. The head-neck junction or excess stem micromotion are possibly the weak links warranting further research.

We have reviewed five adult patients treated with endoprosthetic reconstruction of the proximal radius following resection of non-traumatic lesions. The patients had a mean age of 33.4 years (20 to 60) at the time of surgery and the mean follow-up was 7.6 years (0.8 to 16).

Following surgery, all elbows were clinically stable and there was 100% survivorship of the prosthesis. Evaluation of function was assessed clinically and by the Mayo Elbow Performance Score, achieving a mean of 86% (70 to 100).

Results at medium-term follow-up are encouraging with regards to elbow stability, implant survivorship and functional outcome.

Four uncemented Symax hip stems were extracted at three weeks and nine, 13 and 32 months, respectively, for reasons other than loosening. The reasons for implant removal were infection in two cases, recurrent dislocation in one and acetabular fracture in one. They were analysed to assess the effect and behaviour of an electrochemically deposited, completely resorbable biomimetic BONIT-hydroxyapatite (HA) coating (proximal part) and a DOTIZE surface treatment (distal part) using qualitative histology, quantitative histomorphometry and scanning electron microscopy (SEM). Early and direct bone-implant bonding with signs of active remodelling of bone and the HA coating were demonstrated by histology and SEM. No loose BONIT-HA particles or delamination of the coating were observed, and there was no inflammation or fibrous interposition at the interface.

Histomorphometry showed bone-implant contact varying between 26.5% at three weeks and 83.5% at 13 months at the HA-coated implant surface. The bone density in the area of investigation was between 24.6% at three weeks and 41.1% at 32 months. The DOTIZE surface treatment of the distal part of the stem completely prevented tissue and bone apposition in all cases, thereby optimising proximal stress transfer.

The overall features of this implant, in terms of geometry and surface texture, suggest a mechanically stable design with a highly active biomimetic coating, resulting in rapid and extensive osseo-integration, exclusively in the metaphyseal part of the stem. Early remodelling of the HA coating does not seem to have a detrimental effect on short-term bone-implant coupling. There were no adverse effects identified from either the BONIT-HA coating or the DOTIZE surface treatment.

This study reports the mid-term results of a large-bearing hybrid metal-on-metal total hip replacement in 199 hips (185 patients) with a mean follow-up of 62 months (32 to 83).

Two patients died of unrelated causes and 13 were lost to follow-up. In all, 17 hips (8.5%) have undergone revision, and a further 14 are awaiting surgery. All revisions were symptomatic. Of the revision cases, 14 hips showed evidence of adverse reactions to metal debris. The patients revised or awaiting revision had significantly higher whole blood cobalt ion levels (p = 0.001), but no significant difference in acetabular component size or position compared with the unrevised patients. Wear analysis (n = 5) showed increased wear at the trunnion-head interface, normal levels of wear at the articulating surfaces and evidence of corrosion on the surface of the stem.

The cumulative survival rate, with revision for any reason, was 92.4% (95% confidence interval 87.4 to 95.4) at five years. Including those awaiting surgery, the revision rate would be 15.1% with a cumulative survival at five years of 89.6% (95% confidence interval 83.9 to 93.4).

This hybrid metal-on-metal total hip replacement series has shown an unacceptably high rate of failure, with evidence of high wear at the trunnion-head interface and passive corrosion of the stem surface. This raises concerns about the use of large heads on conventional 12/14 tapers.

There is little information available at present regarding the mechanisms of failure of modern metallic radial head implants. Between 1998 and 2008, 44 consecutive patients (47 elbows) underwent removal of a failed metallic radial head replacement. In 13 patients (13 elbows) the initial operation had been undertaken within one week of a fracture of the radial head, at one to six weeks in seven patients (seven elbows) and more than six weeks (mean of 2.5 years (2 to 65 months)) in 22 patients (25 elbows). In the remaining two elbows the replacement was inserted for non-traumatic reasons. The most common indication for further surgery was painful loosening (31 elbows). Revision was undertaken for stiffness in 18 elbows, instability in nine, and deep infection in two. There were signs of over-lengthening of the radius in 11 elbows. Degenerative changes were found in all but one. Only three loose implants had been fixed with cement. Instability was not identified in any of the bipolar implants.

The management of bone loss in revision replacement of the knee remains a challenge despite an array of options available to the surgeon. Bone loss may occur as a result of the original disease, the design of the prosthesis, the mechanism of failure or technical error at initial surgery. The aim of revision surgery is to relieve pain and improve function while addressing the mechanism of failure in order to reconstruct a stable platform with transfer of load to the host bone. Methods of reconstruction include the use of cement, modular metal augmentation of prostheses, custom-made, tumour-type or hinged implants and bone grafting.

The published results of the surgical techniques are summarised and a guide for the management of bone defects in revision surgery of the knee is presented.

We used a knee-sparing distal femoral endoprosthesis in young patients with malignant bone tumours of the distal femur in whom it was possible to resect the tumour and to preserve the distal femoral condyles. The proximal shaft of the endoprosthesis had a coated hydroxyapatite collar, while the distal end had hydroxyapatite-coated extracortical plates to secure it to the small residual femoral condylar fragment. We reviewed the preliminary results of this endoprosthesis in eight patients with primary bone tumours of the distal femur. Their mean age at surgery was 17.years (14 to 21). The mean follow-up was 24 months (20 to 31). At final follow-up the mean flexion at the knee was 102° (20° to 120°) and the mean Musculoskeletal Tumour Society score was 80% (57% to 96.7%).

There was excellent osteointegration at the prosthesis-proximal bone interface with formation of new bone around the hydroxyapatite collar. The prosthesis allowed preservation of the knee and achieved a good functional result. Formation of new bone and remodelling at the interface make the implant more secure. Further follow-up is required to determine the long-term structural integrity of the prosthesis.

Periprosthetic fracture of the femur is an uncommon complication after total hip replacement, but appears to be increasing. We undertook a nationwide observational study to determine the risk factors for failure after treatment of these fractures, examining patient- and implant-related factors, the classification of the fractures and the outcome.

Between 1979 and 2000, 1049 periprosthetic fractures of the femur were reported to the Swedish National Hip Arthroplasty Register. Of these, 245 had a further operation after failure of their initial management. Data were collected from the Register and hospital records. The material was analysed by the use of Poisson regression models.

It was found that the risk of failure of treatment was reduced for Vancouver type B2 injuries (p = 0.0053) if revision of the implant was undertaken (p = 0.0033) or revision and open reduction and internal fixation (p = 0.0039) were performed. Fractures classified as Vancouver type B1 had a significantly higher risk of failure (p = 0.0001). The strongest negative factor was the use of a single plate for fixation (p = 0.001). The most common reasons for failure in this group were loosening of the femoral prosthesis, nonunion and re-fracture.

It is probable that many fractures classified as Vancouver type B1 (n = 304), were in reality type B2 fractures with a loose stem which were not recognised. Plate fixation was inadequate in these cases. The difficulty in separating type B1 from type B2 fractures suggests that the prosthesis should be considered as loose until proven otherwise.

We carried out a clinical and radiological review of 103 cementless primary hip arthroplasties with a tapered rectangular grit-blasted titanium press-fit femoral component and a threaded conical titanium acetabular component at a mean follow-up of 14.4 years (10.2 to 17.1).

The mean Harris hip score at the last follow-up was 89.2 (32 to 100). No early loosening and no fracture of the implant were found. One patient needed revision surgery because of a late deep infection. In 11 hips (10.7%), the reason for revision was progressive wear of the polyethylene liner. Exchange of the acetabular component because of aseptic loosening without detectable liner wear was carried out in three hips (2.9%).

After 15 years the survivorship with aseptic loosening as the definition for failure was 95.6% for the acetabular component and 100% for the femoral component.