Despite the increasing interest and subsequent published literature on hip resurfacing arthroplasty, little is known about the prevalence of its complications and in particular the less common modes of failure. The aim of this study was to identify the prevalence of failure of hip resurfacing arthroplasty and to analyse the reasons for it.

From a multi-surgeon series (141 surgeons) of 5000 Birmingham hip resurfacings we have analysed the modes, prevalence, gender differences and times to failure of any hip requiring revision. To date 182 hips have been revised (3.6%). The most common cause for revision was a fracture of the neck of the femur (54 hips, prevalence 1.1%), followed by loosening of the acetabular component (32 hips, 0.6%), collapse of the femoral head/avascular necrosis (30 hips, 0.6%), loosening of the femoral component (19 hips, 0.4%), infection (17 hips, 0.3%), pain with aseptic lymphocytic vascular and associated lesions (ALVAL)/metallosis (15 hips, 0.3%), loosening of both components (five hips, 0.1%), dislocation (five hips, 0.1%) and malposition of the acetabular component (three hips, 0.1%). In two cases the cause of failure was unknown.

Comparing men with women, we found the prevalence of revision to be significantly higher in women (women = 5.7%; men = 2.6%, p < 0.001). When analysing the individual modes of failure women had significantly more revisions for loosening of the acetabular component, dislocation, infection and pain/ALVAL/metallosis (p < 0.001, p = 0.004, p = 0.008, p = 0.01 respectively).

The mean time to failure was 2.9 years (0.003 to 11.0) for all causes, with revision for fracture of the neck of the femur occurring earlier than other causes (mean 1.5 years, 0.02 to 11.0). There was a significantly shorter time to failure in men (mean 2.1 years, 0.4 to 8.7) compared with women (mean 3.6 years, 0.003 to 11.0) (p < 0.001).

We report the clinical and radiological outcomes of a series of contemporary cementless ceramic-on-ceramic total hip replacements (THRs) at ten years in patients aged ≤ 55 years of age. Pre- and post-operative activity levels are described. A total of 120 consecutive ceramic cementless THRs were performed at a single centre in 110 patients from 1997 to 1999. The mean age of the patients at operation was 45 years (20 to 55). At ten years, four patients had died and six were lost to follow-up, comprising ten hips. The mean post-operative Harris hip score was 94.7 (55 to 100). Radiological analysis was undertaken in 90 available THRs of the surviving 106 hips at final review: all had evidence of stable bony ingrowth, with no cases of osteolysis. Wear was undetectable. There were four revisions. The survival for both components with revision for any cause as an endpoint was 96.5% (95% confidence interval 94.5 to 98.7). The mean modified University of California, Los Angeles activity level rose from a mean of 6.4 (4 to 10) pre-operatively to 9.0 (6 to 10) at the ten-year post-operative period.

Alumina ceramic-on-ceramic bearings in cementless primary THR in this series have resulted in good clinical and radiological outcomes with undetectable rates of wear and excellent function in the demanding younger patient group at ten years.

Cite this article: Bone Joint J 2013;95-B:1603–9.

Focal femoral inlay resurfacing has been developed for the treatment of full-thickness chondral defects of the knee. This technique involves implanting a defect-sized metallic or ceramic cap that is anchored to the subchondral bone through a screw or pin. The use of these experimental caps has been advocated in middle-aged patients who have failed non-operative methods or biological repair techniques and are deemed unsuitable for conventional arthroplasty because of their age. This paper outlines the implant design, surgical technique and biomechanical principles underlying their use. Outcomes following implantation in both animal and human studies are also reviewed.

Cite this article: Bone Joint J 2013;95-B:301–4.

We report ten-year clinical and radiological follow-up data for the Sigma Press Fit Condylar total knee replacement system (Sigma PFC TKR). Between October 1998 and October 1999 a total of 235 consecutive PFC Sigma TKRs were carried out in 203 patients. Patients were seen at a specialist nurse-led clinic seven to ten days before admission and at six and 18 months, three, five and eight to ten years after surgery. Data were recorded prospectively at each clinic visit. Radiographs were obtained at the five- and eight- to ten-year follow-up appointments. Of the 203 patients, 147 (171 knees) were alive at ten years and 12 were lost to follow-up. A total of eight knees (3.4%) were revised, five for infection and three to change the polyethylene insert. The survival at ten years with an endpoint of revision for any reason was 95.9%, and with an endpoint of revision for aseptic failure was 98.7%. The mean American Knee Society Score (AKSS) was 79 (10 to 99) at eight to ten years, compared with 31 (2 to 62) pre-operatively. Of 109 knee with radiographs reviewed, 47 knees had radiolucent lines but none showed evidence of loosening.

Cite this article: Bone Joint J 2013;95-B:177–80.

Mechanical failure because of wear or fracture of the polyethylene tibial post in posteriorly-stabilised total knee replacements has been extensively described. In this study of 12 patients with a clinically and radiologically successful NexGen LPS posteriorly-stabilised prosthesis impingement of the anterior tibial post was evaluated in vivo in three dimensions during gait using radiologically-based image-matching techniques.

Impingement was observed in all images of the patients during the stance phase, although the NexGen LPS was designed to accommodate 14° of hyperextension of the component before impingement occurred. Impingement arises as a result of posterior translation of the femur during the stance phase. Further attention must therefore be given to the configuration of the anterior portion of the femoral component and the polyethylene post when designing posteriorly-stabilised total knee replacements.

We report 17 patients (20 hips) in whom metal-on-metal resurfacing had been performed and who presented with various symptoms and a soft-tissue mass which we termed a pseudotumour. Each patient underwent plain radiography and in some, CT, MRI and ultrasonography were also performed. In addition, histological examination of available samples was undertaken.

All the patients were women and their presentation was variable. The most common symptom was discomfort in the region of the hip. Other symptoms included spontaneous dislocation, nerve palsy, a noticeable mass or a rash. The common histological features were extensive necrosis and lymphocytic infiltration. To date, 13 of the 20 hips have required revision to a conventional hip replacement. Two are awaiting revision.

We estimate that approximately 1% of patients who have a metal-on-metal resurfacing develop a pseudotumour within five years. The cause is unknown and is probably multifactorial. There may be a toxic reaction to an excess of particulate metal wear debris or a hypersensitivity reaction to a normal amount of metal debris. We are concerned that with time the incidence of these pseudotumours may increase. Further investigation is required to define their cause.

We describe the medium-term results of a prospective study of 200 total ankle replacements at a single-centre using the Scandinavian Total Ankle Replacement. A total of 24 ankles (12%) have been revised, 20 by fusion and four by further replacement and 27 patients (33 ankles) have died. All the surviving patients were seen at a minimum of five years after operation. The five-year survival was 93.3% (95% confidence interval (CI) 89.8 to 96.8) and the ten-year survival 80.3% (95% CI 71.0 to 89.6).

Anterior subluxation of the talus, often seen on the lateral radiograph in osteoarthritic ankles, was corrected and, in most instances, the anatomical alignment was restored by total ankle replacement. The orientation of the tibial component, as seen on the lateral radiograph, also affects the position of the talus and if not correct can hold the talus in an abnormal anterior position. Subtalar arthritis may continue to progress after total ankle replacement. Our results are similar to those published previously.

The dysplasia cup, which was devised as an adjunct to the Birmingham Hip Resurfacing system, has a hydroxyapatite-coated porous surface and two supplementary neutralisation screws to provide stable primary fixation, permit early weight-bearing, and allow incorporation of morcellised autograft without the need for structural bone grafting.

A total of 110 consecutive dysplasia resurfacing arthroplasties in 103 patients (55 men and 48 women) performed between 1997 and 2000 was reviewed with a minimum follow-up of six years. The mean age at operation was 47.2 years (21 to 62) and 104 hips (94%) were Crowe grade II or III.

During the mean follow-up of 7.8 years (6 to 9.6), three hips (2.7%) were converted to a total hip replacement at a mean of 3.9 years (2 months to 8.1 years), giving a cumulative survival of 95.2% at nine years (95% confidence interval 89 to 100). The revisions were due to a fracture of the femoral neck, a collapse of the femoral head and a deep infection. There was no aseptic loosening or osteolysis of the acetabular component associated with either of the revisions performed for failure of the femoral component. No patient is awaiting a revision.

The median Oxford hip score in 98 patients with surviving hips at the final review was 13 and the 10th and the 90th percentiles were 12 and 23, respectively.

Radiostereometric analysis (RSA) can detect early micromovement in unstable implant designs which are likely subsequently to have a high failure rate. In 2010, the Articular Surface Replacement (ASR) was withdrawn because of a high failure rate. In 19 ASR femoral components, the mean micromovement over the first two years after implantation was 0.107 mm (sd 0.513) laterally, 0.055 mm (sd 0.204) distally and 0.150 mm (sd 0.413) anteriorly. The mean backward tilt around the x-axis was -0.08° (sd 1.088), mean internal rotation was 0.165° (sd 0.924) and mean varus tilt 0.238° (sd 0.420). The baseline to two-year varus tilt was statistically significant from zero movement, but there was no significant movement from one year onwards.

We conclude that the ASR femoral component achieves initial stability and that early migration is not the mode of failure for this resurfacing arthroplasty.

Stems improve the mechanical stability of tibial components in total knee replacement (TKR), but come at a cost of stress shielding along their length. Their advantages include resistance to shear, reduced tibial lift-off and increased stability by reducing micromotion. Longer stems may have disadvantages including stress shielding along the length of the stem with associated reduction in bone density and a theoretical risk of subsidence and loosening, peri-prosthetic fracture and end-of-stem pain. These features make long stems unattractive in the primary TKR setting, but often desirable in revision surgery with bone loss and instability. In the revision scenario, stems are beneficial in order to convey structural stability to the construct and protect the reconstruction of bony defects. Cemented and uncemented long stemmed implants have different roles depending on the nature of the bone loss involved.

This review discusses the biomechanics of the design of tibial components and stems to inform the selection of the component and the technique of implantation.

The purpose of this study was to assess the long-term results (more than ten years) of two types of cemented ulnar component with type-5 Kudo total elbow arthroplasty in a consecutive series of 56 patients (60 elbows) with rheumatoid arthritis, and to compare the results in elbows above and below a Larsen grade IV.

There was no radiolucency around the humeral component. Patients in whom a metal-backed ulnar component and a porous-coated stem were used had better clinical results and significantly less progression of radiolucent line formation around the ulnar component. They also had a significantly better long-term survival than patients with an all-polyethylene ulnar component. The clinical results of arthroplasty using all-polyethylene ulnar components were inferior, regardless of the degree of joint destruction.

We conclude that the type-5 Kudo total elbow arthroplasty with cementless fixation of the porous-coated humeral component and cemented fixation of a metal-backed ulnar component is acceptable and well-tolerated by rheumatoid patients.

In a double-blinded randomised controlled trial, 83 patients with primary osteoarthritis of the hip received either a ceramic-on-metal (CoM) or metal-on-metal (MoM) total hip replacement (THR). The implants differed only in the bearing surfaces used. The serum levels of cobalt and chromium and functional outcome scores were compared pre-operatively and at six and 12 months post-operatively.

Data were available for 41 CoM and 36 MoM THRs (four patients were lost to follow-up, two received incorrect implants). The baseline characteristics of both cohorts were similar. Femoral head size measured 36 mm in all but two patients who had 28 mm heads. The mean serum cobalt and chromium levels increased in both groups, with no difference noted between groups at six months (cobalt p = 0.67, chromium p = 0.87) and 12 months (cobalt p = 0.76, chromium p = 0.76) post-operatively. Similarly, the mean Oxford hip scores, Western Ontario and McMaster Universities Osteoarthritis index and University of California, Los Angeles activity scores showed comparable improvement at 12 months.

Our findings indicate that CoM and MoM couplings are associated with an equivalent increase in serum cobalt and chromium levels, and comparable functional outcome scores at six and 12-months follow-up.

Objectives

Metal-on-metal (MoM) hip resurfacing was introduced into clinical practice because it was perceived to be a better alternative to conventional total hip replacement for young and active patients. However, an increasing number of reports of complications have arisen focusing on design and orientation of the components, the generation of metallic wear particles and serum levels of metallic ions. The procedure introduced a combination of two elements: large-dimension components and hard abrasive particles of metal wear. The objective of our study was to investigate the theory that microseparation of the articular surfaces draws in a high volume of bursal fluid and its contents into the articulation, and at relocation under load would generate high pressures of fluid ejection, resulting in an abrasive water jet.

We report a case of a male patient presenting with bilateral painful but apparently well-positioned and -fixed large-diameter metal-on-metal hip replacements four years post-operatively. Multiple imaging modes revealed a thick-walled, cystic expansile mass in communication with the hip joint (a pseudotumour). Implant retrieval analysis and tissue culture eliminated high bearing wear or infection as causes for the soft-tissue reaction, but noted marked corrosion of the modular neck taper adaptor and corrosion products in the tissues. Therefore, we believe corrosion products from the taper caused by mismatch of the implant components led to pseudotumour formation requiring revision.

Objectives

Pseudotumours (abnormal peri-prosthetic soft-tissue reactions) following metal-on-metal hip resurfacing arthroplasty (MoMHRA) have been associated with elevated metal ion levels, suggesting that excessive wear may occur due to edge-loading of these MoM implants. This study aimed to quantify in vivo edge-loading in MoMHRA patients with and without pseudotumours during functional activities.

Ceramic-on-ceramic bearings in hip replacement have low rates of wear and are increasingly being used in young adults. Our aim was to determine the incidence of audible phenomena or other bearing-related complications.

We retrospectively analysed 250 ceramic-on-ceramic hip replacements in 224 patients which had been implanted between April 2000 and December 2007. The mean age of the patients at operation was 44 years (14 to 83) and all the operations were performed using the same surgical technique at a single centre.

At a mean follow-up of 59 months (24 to 94), the mean Oxford hip score was 40.89 (11 to 48). There were six revisions, three of which were for impingement-related complications. No patient reported squeaking, but six described grinding or clicking, which was usually associated with deep flexion. No radiological evidence of osteolysis or migration of the components was observed in any hip.

The early to mid-term results of contemporary ceramic-on-ceramic hip replacement show promising results with few concerns in terms of noise and squeaking. Positioning of the acetabular component remains critical in regard to the reduction of other impingement-related complications.

Objectives

An ongoing prospective study to investigate failing metal-on-metal hip prostheses was commenced at our centre in 2008. We report on the results of the analysis of the first consecutive 126 failed mated total hip prostheses from a single manufacturer.

This systematic review of the literature summarises the clinical experience with ceramic-on-ceramic hip bearings over the past 40 years and discusses the concerns that exist in relation to the bearing combination. Loosening, fracture, liner chipping on insertion, liner canting and dissociation, edge-loading and squeaking have all been reported, and the relationship between these issues and implant design and surgical technique is investigated. New design concepts are introduced and analysed with respect to previous clinical experience.

The aim of this study was to compare the outcome of bilateral sequential total ankle replacement (TAR) with that of unilateral TAR. We reviewed 23 patients who had undergone sequential bilateral TAR under a single anaesthetic and 46 matched patients with a unilateral TAR. There were no significant pre-operative differences between the two groups in terms of age, gender, body mass index, American Society of Anaesthesiologists classification and aetiology of the osteoarthritis of the ankle. Clinical and radiological follow-up was carried out at four months, one and two years.

After four months, patients with simultaneous bilateral TAR reported a significantly higher mean pain score than those with a unilateral TAR. The mean American Orthopaedic Foot and Ankle Society hindfoot score and short-form 36 physical component summary score were better in the unilateral group. However, this difference disappeared at the one-and two-year follow-ups.

Bilateral sequential TAR under one anaesthetic can be offered to patients with bilateral severe ankle osteoarthritis. However, they should be informed of the long recovery period.

We report serum metal ion level data in patients with unilateral and bilateral hip resurfacing over a ten-year period. In these patients there is an increase in both cobalt and chromium levels above the accepted reference ranges during the first 18 months after operation. Metal ion levels remain elevated, but decline slowly for up to five years. However, the levels then appear to start rising again in some patients up to the ten-year mark. There was no significant difference in cobalt or chromium levels between men and women. These findings appear to differ from much of the current literature.

The clinical significance of a raised metal ion level remains under investigation.