We examined the behaviour of alumina ceramic heads in 156 cemented total hip arthroplasties, at a minimum follow-up of eight years. They were divided into three groups according to the size of the femoral head; 22, 26, and 28 mm. We measured polyethylene wear radiologically using a computer-aided technique. The linear wear rate of polyethylene sockets for the 28 mm heads was high (0.156 mm/year), whereas those for the 22 and 26 mm heads were relatively low (0.090 and 0.098 mm/year, respectively). Moreover, the surface roughness data of retrieved femoral heads clearly showed maintenance of an excellent surface finish of the current alumina. We conclude that the alumina ceramic femoral heads currently used are associated with a reduced rate of polyethylene wear

Our aim was to analyse the influence of the size, shape and number of particles on the pathogenesis of osteolysis. We obtained peri-implant tissues from 18 patients having revision surgery for aseptically loosened Freeman total knee replacements (10), Charnley total hip replacements (3) and Imperial College/London Hospital double-cup surface hip replacements (5). The size and shape of the polyethylene particles were characterised using SEM and their concentration was calculated. The results were analysed with reference to the presence of radiological osteolysis. The concentration of polyethylene particles in 6 areas with osteolysis was significantly higher than that in 12 areas without osteolysis. There were no significant differences between the size and shape of the particles in these two groups. We conclude that the most critical factor in the pathogenesis of osteolysis is the concentration of polyethylene particles accumulated in the tissue

Wear of high-density polyethylene on bone and cartilage has resulted in a large volume of plastic particles being shed into the two knees and two hips studied. The giant-cell foreign-body reaction of the synovium may not be sufficient to cope with the amount of debris presented and the destruction of the endosteal bone in one hip, caused by the wear particles and movement of the prosthesis, has made revision impossible. Articulation of high-density polyethylene against bone or cartilage either by design or by the failure of alignment of the component must be avoided

The aims of this study were to examine the repeatability of measurements of bone mineral density (BMD) around a cemented polyethylene Charnley acetabular component using dual-energy x-ray absorptiometry and to determine the longitudinal pattern of change in BMD during the first 24 months after surgery. The precision of measurements of BMD in 19 subjects ranged from 7.7% to 10.8% between regions, using a four-region-of-interest model. A longitudinal study of 27 patients demonstrated a transient decrease in net pelvic BMD during the first 12 months, which recovered to baseline at 24 months. The BMD in the region medial to the dome of the component reduced by between 7% and 10% during the first three months, but recovered to approximately baseline values by two years. Changes in BMD in the pelvis around cemented acetabular components may be measured using dual-energy x-ray absorptiometry. Bone loss after insertion of a cemented Charnley acetabular component is small, transient and occurs mainly at the medial wall of the acetabulum. After two years, bone mass returns to baseline values, with a pattern suggesting a uniform transmission of load to the acetabulum

We have followed up for a period of seven to nine years 100 consecutive arthroplasties of the hip in which an entirely HA-coated implant had been used. The clinical results were excellent and bony incorporation was extensive in all components. No stem became loose or subsided but five cups were revised because of loosening after 3.8 to 5.5 years, having functioned painlessly and shown radiological ingrowth. Revision procedures because of excessive polyethylene wear have been performed on 18 hips and are planned for six more. Two eroded metal backings with worn-through polyethylene were exchanged; six hips showed metallosis without polyethylene wear-through. There were two cases of granulomatous cysts in the groin and 66 hips had osteolysis located periarticularly, in the greater trochanter or in the acetabulum

The ideal acetabular component is characterised by reliable, long-term fixation with physiological loading of bone and a low rate of wear. Trabecular metal is a porous construct of tantalum which promotes bony ingrowth, has a modulus of elasticity similar to that of cancellous bone, and should be an excellent material for fixation. Between 2004 and 2006, 55 patients were randomised to receive either a cemented polyethylene or a monobloc trabecular metal acetabular component with a polyethylene articular surface. We measured the peri-prosthetic bone density around the acetabular components for up to two years using dual-energy x-ray absorptiometry. We found evidence that the cemented acetabular component loaded the acetabular bone centromedially whereas the trabecular metal monobloc loaded the lateral rim and behaved like a hemispherical rigid metal component with regard to loading of the acetabular bone. We suspect that this was due to the peripheral titanium rim used for the mechanism of insertion

The aim of this prospective randomised study was to compare the clinical and radiological results of a cemented all-polyethylene Ultima acetabular component with those of a cementless porous-coated acetabular component (PFC) following total hip replacement (THR). A total of 287 patients received either a polyethylene acetabular component (group A) or a cobalt–chromium porous-coated component (group B) with an identical cemented femoral component and 28 mm cobalt-chromium head, thus making it the largest study of its type. Patients were evaluated radiologically and clinically using the Harris hip score (HHS). Group A comprised 183 patients (73 male, 110 female) with a mean age of 71.3 years (55 to 89). Group B comprised 104 patients (48 male, 56 female) with a mean age of 69.8 years (56 to 89). A total of 16 patients (13 in Group A, three in Group B) did not have post-operative data for analysis. The mean follow-up in group A was 7.52 years (0.4 to 15.0) and in Group B 7.87 years (0.5 to 14.0). At final follow-up the mean HHS was similar between groups A and B (74.5 (25 to 100) and 78.0 (37 to 100), respectively; p = 0.068). The total number of revisions for any cause was 28, 17 of which were in group A and 11 in group B. The ten-year survivorship was 86.8% (95% confidence interval (CI) 78.4 to 92.1) and 89.2% (95% CI 78.3 to 94.8) for groups A and B, respectively (log-rank p-value = 0.938). A total of 20 cemented and two cementless acetabular components had evidence of acetabular radiolucencies or acetabular component migration at last follow-up (p = 0.001). These results indicate that patients with a cemented all-polyethylene and cementless porous-coated polyethylene lined acetabular component have similar long-term clinical outcomes

We have reviewed 70 patients with bilateral simultaneous total hip arthroplasties to determine the rate of failure and to compare polyethylene wear and osteolysis between an implant with a cobalt-chrome head and Hylamer liner with that of a zirconia head and Hylamer liner. The mean thickness of the polyethylene liner was 11.0 mm (8.8 to 12.2) in the hip with a zirconia head and 10.7 mm (8.8 to 12.2) in that with a cobalt-chrome head. At follow-up at 6.4 years no acetabular or femoral component had been revised for aseptic loosening and no acetabular or femoral component was loose according to radiological criteria in both the cemented and cementless groups. The mean rate of linear wear and annual wear rate were highest in the 22 mm zirconia femoral head (1.25 mm (SD 1.05) and 0.21 mm (SD 0.18), respectively) and lowest in the 22 mm cobalt-chrome femoral head (0.70 mm (SD 0.39) and 0.12 mm (SD 0.07), respectively). The mean volumetric wear was highest in the 28 mm zirconia femoral head (730.79 mm. 3. ) and lowest in the 22 mm cobalt-chrome femoral head (264.67 mm. 3. ), but if the results were compared by size of the femoral head and type of material there was no statistical difference (p > 0.05). Sequential measurements of annual wear showed that the zirconia femoral head had a relatively higher rate of penetration than the cobalt-chrome head over the first three years; thereafter the rate of wear was reduced and compared favourably with that of cobalt-chrome heads. There was a statistically significant relationship between the wear of the polyethylene liner and the age of the patient, male gender and the degree of abduction angle of the cup, but not diagnosis, weight, hip score, range of movement, or amount of anteversion. Osteolysis was identified on both sides of the acetabulum in six patients (9%). Of 12 hips with acetabular osteolysis, six had a 28 mm cobalt-chrome femoral head and the remaining six a 28 mm zirconia head. Osteolysis was observed in zones 1A and 7A of the femur in two hips (3%) with a 28 mm zirconia head (cemented hip) and in four (6%) with a 28 mm cobalt-chrome femoral head (cementless hip). Our findings suggest that although the performance of a zirconia femoral head with a Hylamer liner was not statistically different from that of a cobalt-chrome femoral head and Hylamer liner, there was a trend for the zirconia head to be worse than the cobalt-chrome femoral head

Objectives. The accuracy and precision of two new methods of model-based radiostereometric analysis (RSA) were hypothesised to be superior to a plain radiograph method in the assessment of polyethylene (PE) wear. Methods. A phantom device was constructed to simulate three-dimensional (3D) PE wear. Images were obtained consecutively for each simulated wear position for each modality. Three commercially available packages were evaluated: model-based RSA using laser-scanned cup models (MB-RSA), model-based RSA using computer-generated elementary geometrical shape models (EGS-RSA), and PolyWare. Precision (95% repeatability limits) and accuracy (Root Mean Square Errors) for two-dimensional (2D) and 3D wear measurements were assessed. Results. The precision for 2D wear measures was 0.078 mm, 0.102 mm, and 0.076 mm for EGS-RSA, MB-RSA, and PolyWare, respectively. For the 3D wear measures the precision was 0.185 mm, 0.189 mm, and 0.244 mm for EGS-RSA, MB-RSA, and PolyWare respectively. Repeatability was similar for all methods within the same dimension, when compared between 2D and 3D (all p > 0.28). For the 2D RSA methods, accuracy was below 0.055 mm and at least 0.335 mm for PolyWare. For 3D measurements, accuracy was 0.1 mm, 0.2 mm, and 0.3 mm for EGS-RSA, MB-RSA and PolyWare respectively. PolyWare was less accurate compared with RSA methods (p = 0.036). No difference was observed between the RSA methods (p = 0.10). Conclusions. For all methods, precision and accuracy were better in 2D, with RSA methods being superior in accuracy. Although less accurate and precise, 3D RSA defines the clinically relevant wear pattern (multidirectional). PolyWare is a good and low-cost alternative to RSA, despite being less accurate and requiring a larger sample size

In ten male rats we inserted ceramic ‘drawing-pin’ implants in weight-bearing positions within the right proximal tibia. Two animals were killed 6 weeks after surgery and two more 14 weeks after surgery. The remaining six received intra-articular injections of either high-density polyethylene (4 rats) or saline (2 rats) at 8, 10 and 12 weeks after surgery. These animals were killed two weeks after the last injection. Histological examination of the bone-implant interface in the control animals showed appositional bone growth around the implant at both 6 and 14 weeks. Polyethylene, but not saline, caused a chronic inflammatory response with numerous foreign-body giant cells in periprosthetic tissues. Our model of a stable, weight-bearing bone-implant interface provides a simple and reliable system in which to study in vivo the effects of particulate materials used in orthopaedic surgery

Polyethylene wear of acetabular components is a key factor in the development of periprosthetic osteolysis and wear at the articular surface has been well documented and quantified, but fewer data are available about changes which occur at the backside of the liner. At revision surgery for loosening of the femoral component we retrieved 35 conventional modular acetabular liners of the same design. Linear and volumetric articular wear, backside volumetric change and the volume of the screw-head indentations were quantified. These volumes, clinical data and the results from radiological Ein Bild Röntgen Analyse migration analysis were used to identify potential factors influencing the volumetric articular wear and backside volumetric change. The rate of backside volumetric change was found to be 2.8% of the rate of volumetric articular wear and decreased with increasing liner size. Migrated acetabular components showed significantly higher rates of backside volumetric change plus screw-head indentations than those without migration. The backside volumetric change was at least ten times larger than finite-element simulation had suggested. In a stable acetabular component with well-anchored screws, the amount of backside wear should not cause clinical problems. Impingement of the screw-heads could produce more wear particles than those generated at the liner-shell interface. Because the rate of backside volumetric change is only 2.8% of the rate of volumetric articular wear and since creep is likely to contribute a significant portion to this, the debris generated by wear at the backside of the liner may not be sufficient to create a strong osteolytic response

Ten cases are described of catastrophic failure of the polyethylene liner of three different designs of uncemented acetabular component. Failure occurred as a result of either 'wearthrough' to the metal backing, liner fracture or a combination of both, at a mean of 4.6 years after implantation (2 to 7.6). At revision there was metallosis in all hips and osteolysis of the femur or the pelvis in six. Catastrophic failure was seen only in cups with a minimum polyethylene thickness of less than 5 mm

We performed thermal analysis of polyethylene samples obtained from 73 new cups of the Weller hip prosthesis. There were marked individual differences in the degree of their crystallinity, ranging from 37.8% to 67.2% with a mean of 53%. Analysis of polyethylene from removed cups also showed differences in crystallinity in individual cups, with the mean value being higher in the removed implants than in the new ones. This difference in crystallinity between the groups was statistically significant. Marked individual differences in the degree of cup wear may result from these changes

We report the results of our continued review of 11 total hip arthroplasties using 22.225 mm alumina ceramic femoral heads on a Charnley flanged stem, articulating with chemically cross-linked polyethylene. There was an initial bedding-in of up to 0.41 mm at the articular surface in the first two years. This had not progressed further, at a minimum follow-up of 15 years. Radiographically no femoral or acetabular component showed loosening or osteolysis

Aims. The increased in vivo resistance to wear of highly crosslinked polyethylene (HXLPE) in total hip arthroplasty (THA) has led to an increased use of larger articulations which have been shown to reduce the incidence of early dislocation. To date, there are few reports of the wear of larger articulations using second generation HXLPE liners. Our prospective cohort study measured the bedding-in and early wear of large (36 mm and 40 mm diameter) articulations involving a second generation X3 HXLPE liner and compared our findings with previous clinical and in vitro studies of the same material. Patients and Methods. The proximal penetration of the femoral head five years post-operatively was measured for 15 patients using radiostereometric analysis (RSA). Results. The median proximal bedding-in within the first post-operative year was 0.022 mm (interquartile range (IQR) -0.050 to 0.091). The median proximal rate of wear between one and five years was -0.004 mm/year (IQR -0.021 to 0.022). The rates of proximal, medial, 2D or 3D wear between one and five years post-operatively of the X3 HXLPE liner did not increase with larger articulations compared with our previous study of 32 mm articulations. Conclusion. Although reassuring, the use of larger articulations requires continued monitoring to determine whether the low wear observed in the short-term continues to the mid- to long-term. Cite this article: Bone Joint J 2016;98-B:1604–10

We used a rat model in vivo to study the effects of the concentration of polyethylene particles on the bone-implant interface around stable implants in the proximal tibia. Intra-articular injections of 10. 4. , 10. 6. or 10. 8. high-density polyethylene (HDPE) particles per joint were given 8, 10 and 12 weeks after surgery. The animals were killed after 14 and 26 weeks and the response at the interface determined. Fibrous tissue was seen at the bone-implant interface when the head of the implant was flush with the top of the tibia but not when it was sunk below the tibial plateau. In the latter case the implant was completely surrounded by a shell of bone. The area of fibrous tissue and that of the gap between the implant and bone was related to the concentration of particles in the 14-week group (p < 0.05). Foreign-body granulomas containing HDPE particles were seen at the bone-implant interface in animals given 10. 8. particles. The pathology resembles that seen around prostheses with aseptic loosening and we suggest that this is a useful model by which to study this process

We reviewed the results of 545 consecutive total hip replacements using a cementless non-coated high-density polyethylene acetabular component combined with a cemented Muller stem at five to 10 years. In all, 421 patients (445 hips) were available for review, 118 by questionnaire and 303 by examination and radiography. Of these, 86% had a good or excellent result. We found a high rate of radiological loosening of the cup after the sixth year, and a high rate of clinical loosening after the eighth year. Loosening was commoner in women, in younger patients and where a smaller size of acetabulum had been used. Calcar resorption was significantly related to loosening of the acetabulum. Loosening appeared to be mainly due to polyethylene debris produced by micro-movement of the acetabulum against the bone, which had resulted in a giant cell foreign body reaction and subsequent bone erosion. We have abandoned the use of this prosthesis and suggest that direct contact between bone and polyethylene should be prevented by a coating of metal or some other material

We report the results of our continued review of 14 hip arthroplasties using alumina ceramic femoral heads with cross-linked polyethylene cups. There have been no complications and a very low rate of penetration. This was 0.02 mm per year after an initial ‘bedding-in’ period of two years. There has been no change in the mean rate between our earlier study at six years and the current results at 10 to 11 years. The use of these bearing surfaces appears to reduce the potential amount of polyethylene debris and may provide the next logical stage in the development of the Charnley low-friction arthroplasty

In this prospective, randomised study, we have compared the wear rate of cemented, acetabular polyethylene cups articulating with either a 22 mm or a 32 mm cobalt-chromium head. We evaluated 89 patients who had a total of 484 radiographs. The mean follow-up period was 71.4 months (SD 29.1). All the radiographs were digitised and electronically measured. The linear wear rate was significantly higher during the first two years and decreased after this period to a constant value. We suggest that this is partly due to a ‘run-in’ process caused by irregularities between surfaces of the cup and head and an initial plastic deformation of the polyethylene. The mean volumetric wear was 120.3 mm. 3. /year for the 32 mm head, which was significantly higher than the 41.5 mm. 3. /year for the 22 mm heads. The mean linear wear rate was not significantly different. We were, however, unable to find radiological signs of osteolysis in the patients who had higher wear rates

Aims. The purpose of this study was to compare the long-term results of primary total hip arthroplasty (THA) in young patients using either a conventional (CPE) or a highly cross-linked (HXLPE) polyethylene liner in terms of functional outcome, incidence of osteolysis, radiological wear and rate of revision. Methods. We included all patients between the ages of 45 and 65 years who, between January 2000 and December 2001, had undergone a primary THA for osteoarthritis at our hospital using a CPE or HXLPE acetabular liner and a 28 mm cobalt-chrome femoral head. . From a total of 160 patients, 158 (177 hips) were available for review (CPE 89; XLPE 88). The mean age, body mass index (BMI) and follow-up in each group were: CPE: 56.8 years (46 to 65); 30.7 kg/m. 2. (19 to 58); 13.2 years (2.1 to 14.7) and HXLPE: 55.6 years (45 to 65); BMI: 30 kg/m. 2. (18 to 51); 13.1 years (5.7 to 14.4). Results. The mean Harris hip score (HHS) at final follow-up was 89.3 for the CPE group and 90.9 for the HXLPE group (p = 0.078). Osteolysis was present around 15 acetabular (17%) and 16 femoral (18%) components in the CPE hips compared with none (0%) in the HXLPE hips. The mean radiological linear wear of the CPE liners was 0.11 mm/year compared with 0.035 mm/year for the HXLPE liners (p = 0.006). The cumulative implant survival, with revision for polyethylene wear as the endpoint, was 86% (95% confidence interval 78 to 94) in the CPE group and 100% in the HXLPE group at 13 years (numbers at risk at 13 years - CPE: 65, XLPE: 61). Discussion. This study shows that HXLPE liners are associated with significantly less osteolysis and a lower rate of revision THA than CPE liners at long-term follow-up. Take home message: The findings of this study highlight the clinical benefits of using HXLPE liners in THA and support the routine use of the material in order to improve implant longevity and to decrease the number of patients needing revision for aseptic osteolysis. . Cite this article: Bone Joint J 2016;98-B:28–32