Aims

A contact patch to rim (CPR) distance of < 10 mm has been associated with edge-loading and excessive wear. However, not all arthroplasties with a low CPR distance show problems with wear. Therefore, CPR distance may not be the only variable affecting the post-operative metal ion concentrations.

Objectives

The high revision rates of the DePuy Articular Surface Replacement (ASR) and the DePuy ASR XL (the total hip arthroplasty (THA) version) have led to questions over the viability of metal-on-metal (MoM) hip joints. Some designs of MoM hip joint do, however, have reasonable mid-term performance when implanted in appropriate patients. Investigations into the reasons for implant failure are important to offer help with the choice of implants and direction for future implant designs. One way to assess the performance of explanted hip prostheses is to measure the wear (in terms of material loss) on the joint surfaces.

Objectives

Hips with metal-on-metal total hip arthroplasty (MoM THA) have a high rate of adverse local tissue reactions (ALTR), often associated with hypersensitivity reactions. Dynamic contrast-enhanced magnetic resonance imaging (DCE-MRI) measures tissue perfusion with the parameter Ktrans (volume transfer constant of contrast agent). Our purpose was 1) to evaluate the feasibility of DCE-MRI in patients with THA and 2) to compare DCE-MRI in patients with MoM bearings with metal-on-polyethylene (MoP) bearings, hypothesising that the perfusion index Ktrans in hips with MoM THA is higher than in hips with MoP THA.

In this study of 41 patients, we used proteomic, Western blot and immunohistochemical analyses to show that several reactive oxygen species scavenging enzymes are expressed differentially in patients with primary osteoarthritis and those with non-loosening and aseptic loosening after total hip replacement (THR). The patients were grouped as A (n = 16, primary THR), B (n = 10, fixed THR but requiring revision for polyethylene wear) and C (n = 15, requiring revision due to aseptic loosening) to verify the involvement of the identified targets in aseptic loosening. When compared with Groups A and B, Group C patients exhibited significant up-regulation of transthyretin and superoxide dismutase 3, but down-regulation of glutathione peroxidase 2 in their hip synovial fluids. Also, higher levels of superoxide dismutase 2 and peroxiredoxin 2, but not superoxide dismutase 1, catalase and glutathione perioxidase 1, were consistently detected in the hip capsules of Group C patients.

We propose that dysregulated reactive oxygen species-related enzymes may play an important role in the pathogenesis and progression of aseptic loosening after THR.

As adverse events related to metal on metal hip arthroplasty have been better understood, there has been increased interest in toxicity related to the high circulating levels of cobalt ions. However, distinguishing true toxicity from benign elevations in cobalt levels can be challenging. The purpose of this review is to examine the use of cobalt alloys in total hip arthroplasty, to review the methods of measuring circulating cobalt levels, to define a level of cobalt which is considered pathological and to review the pathophysiology, risk factors and treatment of cobalt toxicity. To the best of our knowledge, there are 18 published cases where cobalt metal ion toxicity has been attributed to the use of cobalt-chromium alloys in hip arthroplasty. Of these cases, the great majority reported systemic toxic reactions at serum cobalt levels more than 100 μg/L. This review highlights some of the clinical features of cobalt toxicity, with the goal that early awareness may decrease the risk factors for the development of cobalt toxicity and/or reduce its severity.

Take home message: Severe adverse events can arise from the release of cobalt from metal-on-metal arthroplasties, and as such, orthopaedic surgeons should not only be aware of the presenting problems, but also have the knowledge to treat appropriately.

Cite this article: Bone Joint J 2016;98-B:14–20.

The recent resurgence in the use of metal-on-metal bearings has led to fresh concerns over metal wear and elevated systemic levels of metal ions.

In order to establish if bearing diameter influences the release of metal ions, we compared the whole blood levels of cobalt and chromium (at one year) and the urinary cobalt and chromium output (at one to three and four to six years) following either a 50 mm or 54 mm Birmingham hip resurfacing or a 28 mm Metasul total hip replacement. The whole blood concentrations and daily output of cobalt and chromium in these time periods for both bearings were in the same range and without significant difference.

The peri-prosthetic tissue response to wear debris is complex and influenced by various factors including the size, area and number of particles. We hypothesised that the ‘biologically active area’ of all metal wear particles may predict the type of peri-prosthetic tissue response.

Peri-prosthetic tissue was sampled from 21 patients undergoing revision of a small diameter metal-on-metal (MoM) total hip arthroplasty (THA) for aseptic loosening. An enzymatic protocol was used for tissue digestion and scanning electron microscope was used to characterise particles. Equivalent circle diameters and particle areas were calculated. Histomorphometric analyses were performed on all tissue specimens. Aspirates of synovial fluid were collected for analysis of the cytokine profile analysis, and compared with a control group of patients undergoing primary THA (n = 11) and revision of a failed ceramic-on-polyethylene arthroplasty (n = 6).

The overall distribution of the size and area of the particles in both lymphocyte and non-lymphocyte-dominated responses were similar; however, the subgroup with lymphocyte-dominated peri-prosthetic tissue responses had a significantly larger total number of particles.

14 cytokines (interleukin (IL)-1ß, IL-2, IL-4, IL-5, IL-6, IL-10, IL-13, IL-17, interferon (IFN)-γ, and IFN-gamma-inducible protein 10), chemokines (macrophage inflammatory protein (MIP)-1α and MIP-1ß), and growth factors (granulocyte macrophage colony stimulating factor (GM-CSF) and platelet derived growth factor) were detected at significantly higher levels in patients with metal wear debris compared with the control group.

Significantly higher levels for IL-1ß, IL-5, IL-10 and GM-CSF were found in the subgroup of tissues from failed MoM THAs with a lymphocyte-dominated peri-prosthetic response compared with those without this response.

These results suggest that the ‘biologically active area’ predicts the type of peri-prosthetic tissue response. The cytokines IL-1ß, IL-5, IL-10, and GM-CSF are associated with lymphocyte-dominated tissue responses from failed small-diameter MoM THA.

Cite this article: Bone Joint J 2015;97-B:917–23.

Adverse reaction to wear and corrosion debris is a cause for concern in total hip arthroplasty (THA). Modular junctions are a potential source of such wear products and are associated with secondary pseudotumour formation.

We present a consecutive series of 17 patients treated at our unit for this complication following metal-on-highly cross-linked polyethylene (MoP) THA. We emphasise the risk of misdiagnosis as infection, and present the aggregate laboratory results and pathological findings in this series.

The clinical presentation was pain, swelling or instability. Solid, cystic and mixed soft-tissue lesions were noted on imaging and confirmed intra-operatively. Corrosion at the head–neck junction was noted in all cases. No bacteria were isolated on multiple pre- and intra-operative samples yet the mean erythrocyte sedimentation rate was 49 (9 to 100) and C-reactive protein 32 (0.6 to 106) and stromal polymorphonuclear cell counts were noted in nine cases.

Adverse soft–tissue reactions can occur in MoP THA owing to corrosion products released from the head–neck junction. The diagnosis should be carefully considered when investigating pain after THA. This may avoid the misdiagnosis of periprosthetic infection with an unidentified organism and mitigate the unnecessary management of these cases with complete single- or two-stage exchange.

Cite this article: Bone Joint J 2015;97-B:1024–1030.

Ceramic-on-metal (CoM) is a relatively new bearing combination for total hip arthroplasty (THA) with few reported outcomes. A total of 287 CoM THAs were carried out in 271 patients (mean age 55.6 years (20 to 77), 150 THAs in female patients, 137 in male) under the care of a single surgeon between October 2007 and October 2009. With the issues surrounding metal-on-metal bearings the decision was taken to review these patients between March and November 2011, at a mean follow-up of 34 months (23 to 45) and to record pain, outcome scores, radiological analysis and blood ion levels. The mean Oxford Hip Score was 19.2 (12 to 53), 254 patients with 268 hips (95%) had mild/very mild/no pain, the mean angle of inclination of the acetabular component was 44.8^o (28^o to 63^o), 82 stems (29%) had evidence of radiolucent lines of > 1 mm in at least one Gruen zone and the median levels of cobalt and chromium ions in the blood were 0.83 μg/L (0.24 μg/L to 27.56 μg/L) and 0.78 μg/L (0.21 μg/L to 8.84 μg/L), respectively. The five-year survival rate is 96.9% (95% confidence interval 94.7% to 99%).

Due to the presence of radiolucent lines and the higher than expected levels of metal ions in the blood, we would not recommend the use of CoM THA without further long-term follow-up. We plan to monitor all these patients regularly.

Cite this article: Bone Joint J 2015;97-B:300–5.

Metal ions generated from joint replacements are a cause for concern. There is no consensus on the best surrogate measure of metal ion exposure. This study investigates whether serum and whole blood concentrations can be used interchangeably to report results of cobalt and chromium ion concentrations.

Concentrations of serum and whole blood were analysed in 262 concurrent specimens using high resolution inductively-coupled plasma mass-spectrometry. The agreement was assessed with normalised scatterplots, mean difference and the Bland and Altman limits of agreement.

The wide variability seen in the normalised scatterplots, in the Bland and Altman plots and the statistically significant mean differences between serum and whole blood concentrations suggest that they cannot be used interchangeably. A bias was demonstrated for both ions in the Bland-Altman plots. Regression analysis provided a possible conversion factor of 0.71 for cobalt and 0.48 for chromium. However, even when the correction factors were applied, the limits of agreement were greater than ±67% for cobalt and greater than ±85% for chromium, suggesting that serum and whole blood cannot be used interconvertibly. This suggests that serum metal concentrations are not useful as a surrogate measure of systemic metal ion exposure.

Increased concentrations of metal ions after metal-on-metal resurfacing arthroplasty of the hip remain a concern. Although there has been no proven link to long-term health problems or early prosthetic failure, variables associated with high metal ion concentrations should be identified and, if possible, corrected. Our study provides data on metal ion levels from a series of 76 consecutive patients (76 hips) after resurfacing arthroplasty with the Articular Surface Replacement. Chromium and cobalt ion concentrations in the whole blood of patients with smaller (≤ 51 mm) femoral components were significantly higher than in those with the larger (≥ 53 mm) components (p < 0.01). Ion concentrations in the former group were significantly related to the inclination (p = 0.01) and anteversion (p = 0.01) of the acetabular component. The same relationships were not significant in the patients with larger femoral components (p = 0.61 and p = 0.49, respectively). Accurate positioning of the acetabular component intra-operatively is essential in order to reduce the concentration of metal ions in the blood after hip resurfacing arthroplasty with the Articular Surface Replacement implant.

We report serum metal ion level data in patients with unilateral and bilateral hip resurfacing over a ten-year period. In these patients there is an increase in both cobalt and chromium levels above the accepted reference ranges during the first 18 months after operation. Metal ion levels remain elevated, but decline slowly for up to five years. However, the levels then appear to start rising again in some patients up to the ten-year mark. There was no significant difference in cobalt or chromium levels between men and women. These findings appear to differ from much of the current literature.

The clinical significance of a raised metal ion level remains under investigation.

We investigated the role of ion release in the assessment of fixation of the implant after total knee replacement and hypothesised that ion monitoring could be a useful parameter in the diagnosis of prosthetic loosening. We enrolled 59 patients with unilateral procedures and measured their serum aluminium, titanium, chromium and cobalt ion levels, blinded to the clinical and radiological outcome which was considered to be the reference standard. The cut-off levels for detection of the ions were obtained by measuring the levels in 41 healthy blood donors who had no implants. Based on the clinical and radiological evaluation the patients were divided into two groups with either stable (n = 24) or loosened (n = 35) implants.

A significant increase in the mean level of Cr ions was seen in the group with failed implants (p = 0.001). The diagnostic accuracy was 71% providing strong evidence of failure when the level of Cr ions exceeded the cut-off value. The possibility of distinguishing loosening from other causes of failure was demonstrated by the higher diagnostic accuracy of 83%, when considering only patients with failure attributable to loosening.

Measurement of the serum level of Cr ions may be of value for detecting failure due to loosening when the diagnosis is in doubt. The other metal ions studies did not have any diagnostic value.

We conducted a retrospective study to assess the prevalence of adverse reactions to metal debris (ARMD) in patients operated on at our institution with metal-on-metal (MoM) total hip replacements with 36 mm heads using a Pinnacle acetabular shell. A total of 326 patients (150 males, 175 hips; 176 females, 203 hips) with a mean age of 62.7 years (28 to 85) and mean follow-up of 7.5 years (0.1 to 10.8) participating in our in-depth modern MoM follow-up programme were included in the study, which involved recording whole blood cobalt and chromium ion measurements, Oxford hip scores (OHS) and plain radiographs of the hip and targeted cross-sectional imaging. Elevated blood metal ion levels (> 5 parts per billion) were seen in 32 (16.1%) of the 199 patients who underwent unilateral replacement. At 23 months after the start of our modern MoM follow-up programme, 29 new cases of ARMD had been revealed. Hence, the nine-year survival of this cohort declined from 96% (95% CI 95 to 98) with the old surveillance routine to 86% (95% CI 82 to 90) following the new protocol. Although ARMD may not be as common in 36 mm MoM THRs as in those with larger heads, these results support the Medicines and Healthcare Products Regulatory Agency guidelines on regular reviews and further investigations, and emphasise the need for specific a follow-up programme for patients with MoM THRs.

Cite this article: Bone Joint J 2014; 96-B:1610–17.

The issues surrounding raised levels of metal ions in the blood following large head metal-on-metal total hip replacement (THR), such as cobalt and chromium, have been well documented. Despite the national popularity of uncemented metal-on-polyethylene (MoP) THR using a large-diameter femoral head, few papers have reported the levels of metal ions in the blood following this combination. Following an isolated failure of a 44 mm Trident–Accolade uncemented THR associated with severe wear between the femoral head and the trunnion in the presence of markedly elevated levels of cobalt ions in the blood, we investigated the relationship between modular femoral head diameter and the levels of cobalt and chromium ions in the blood following this THR.

A total of 69 patients received an uncemented Trident–Accolade MoP THR in 2009. Of these, 43 patients (23 men and 20 women, mean age 67.0 years) were recruited and had levels of cobalt and chromium ions in the blood measured between May and June 2012. The patients were then divided into three groups according to the diameter of the femoral head used: 12 patients in the 28 mm group (controls), 18 patients in the 36 mm group and 13 patients in the 40 mm group. A total of four patients had identical bilateral prostheses in situ at phlebotomy: one each in the 28 mm and 36 mm groups and two in the 40 mm group.

There was a significant increase in the mean levels of cobalt ions in the blood in those with a 36 mm diameter femoral head compared with those with a 28 mm diameter head (p = 0.013). The levels of cobalt ions in the blood were raised in those with a 40 mm diameter head but there was no statistically significant difference between this group and the control group (p = 0.152). The levels of chromium ions in the blood were normal in all patients.

The clinical significance of this finding is unclear, but we have stopped using femoral heads with a diameter of ≤ 36 mm, and await further larger studies to clarify whether, for instance, this issue particularly affects this combination of components.

Cite this article: Bone Joint J 2014;96-B:43–7.

We describe three cases of fracture of the titanium JRI-Furlong hydroxyapatite-ceramic (HAC)-coated femoral component. We have examined previous case reports of failure of this stem and conclude that fracture may occur in two places, namely at the neck-shoulder junction and at the conical-distal cylindrical junction. These breakages are the result of fatigue in a metallurgically-proven normal femoral component. All the cases of failure of the femoral component have occurred in patients with a body mass index of more than 25 in whom a small component, either size 9 or 10, had been used.

In patients with a body mass index above normal size 9 components should be avoided and the femoral canal should be reamed sufficiently to accept a large femoral component to ensure that there is adequate metaphyseal fixation.

The aims of this study were to evaluate the incidence of local argyria in patients with silver-coated megaprostheses and to identify a possible association between argyria and elevated levels of silver both locally and in the blood. Between 2004 and 2011, 32 megaprostheses with silver coatings were implanted in 20 female and 12 male patients following revision arthroplasty for infection or resection of a malignant tumour, and the levels of silver locally in drains and seromas and in the blood were determined. The mean age of the patients was 46 years (10 to 81); one patient died in the immediate post-operative period and was excluded.

Seven patients (23%) developed local argyria after a median of 25.7 months (interquartile range 2 to 44.5). Patients with and without local argyria had comparable levels of silver in the blood and aspiration fluids. The length of the implant did not influence the development of local argyria. Patients with clinical evidence of local argyria had no neurological symptoms and no evidence of renal or hepatic failure. Thus, we conclude that the short-term surveillance of blood silver levels in these patients is not required.

Cite this article: Bone Joint J 2013;95-B:988–92.

We carried out a cross-sectional study with analysis of the demographic, clinical and laboratory characteristics of patients with metal-on-metal hip resurfacing, ceramic-on-ceramic and metal-on-polyethylene hip replacements. Our aim was to evaluate the relationship between metal-on-metal replacements, the levels of cobalt and chromium ions in whole blood and the absolute numbers of circulating lymphocytes. We recruited 164 patients (101 men and 63 women) with hip replacements, 106 with metal-on-metal hips and 58 with non-metal-on-metal hips, aged < 65 years, with a pre-operative diagnosis of osteoarthritis and no pre-existing immunological disorders.

Laboratory-defined T-cell lymphopenia was present in13 patients (15%) (CD8⁺ lymphopenia) and 11 patients (13%) (CD3⁺ lymphopenia) with unilateral metal-on-metal hips. There were significant differences in the absolute CD8⁺ lymphocyte subset counts for the metal-on-metal groups compared with each control group (p-values ranging between 0.024 and 0.046). Statistical modelling with analysis of covariance using age, gender, type of hip replacement, smoking and circulating metal ion levels, showed that circulating levels of metal ions, especially cobalt, explained the variation in absolute lymphocyte counts for almost all lymphocyte subsets.

A retrospective study was conducted to investigate the changes in metal ion levels in a consecutive series of Birmingham Hip Resurfacings (BHRs) at a minimum ten-year follow-up. We reviewed 250 BHRs implanted in 232 patients between 1998 and 2001. Implant survival, clinical outcome (Harris hip score), radiographs and serum chromium (Cr) and cobalt (Co) ion levels were assessed.

Of 232 patients, 18 were dead (five bilateral BHRs), 15 lost to follow-up and ten had been revised. The remaining 202 BHRs in 190 patients (136 men and 54 women; mean age at surgery 50.5 years (17 to 76)) were evaluated at a minimum follow-up of ten years (mean 10.8 years (10 to 13.6)). The overall implant survival at 13.2 years was 92.4% (95% confidence interval 90.8 to 94.0). The mean Harris hip score was 97.7 (median 100; 65 to 100). Median and mean ion levels were low for unilateral resurfacings (Cr: median 1.3 µg/l, mean 1.95 µg/l (< 0.5 to 16.2); Co: median 1.0 µg/l, mean 1.62 µg/l (< 0.5 to 17.3)) and bilateral resurfacings (Cr: median 3.2 µg/l, mean 3.46 µg/l (< 0.5 to 10.0); Co: median 2.3 µg/l, mean 2.66 µg/l (< 0.5 to 9.5)). In 80 unilateral BHRs with sequential ion measurements, Cr and Co levels were found to decrease significantly (p < 0.001) from the initial assessment at a median of six years (4 to 8) to the last assessment at a median of 11 years (9 to 13), with a mean reduction of 1.24 µg/l for Cr and 0.88 µg/l for Co. Three female patients had a > 2.5 µg/l increase of Co ions, associated with head sizes ≤ 50 mm, clinical symptoms and osteolysis. Overall, there was no significant difference in change of ion levels between genders (Cr, p = 0.845; Co, p = 0.310) or component sizes (Cr, p = 0.505; Co, p = 0.370). Higher acetabular component inclination angles correlated with greater change in ion levels (Cr, p = 0.013; Co, p = 0.002). Patients with increased ion levels had lower Harris hip scores (p = 0.038).

In conclusion, in well-functioning BHRs the metal ion levels decreased significantly at ten years. An increase > 2.5 µg/l was associated with poor function.

Cite this article: Bone Joint J 2013;95-B:1332–8.