We compared and quantified the modes of failure and patterns of wear of 11 Mittelmeier and 11 Ceraver-Ostal retrieved alumina-alumina hip prostheses with reference to the corresponding clinical and radiological histories. Macroscopic wear was assessed using a three-dimensional co-ordinate measuring machine. Talysurf contacting profilometry was used to measure surface roughness on a microscopic scale and SEM to determine mechanisms of wear at the submicron level. The components were classified into one of three categories of wear: low (no visible/measurable wear), stripe (elliptical wear stripe on the heads and larger worn areas on the cups) and severe (macroscopic wear, large volumes of material lost). Overall, the volumetric wear of the alumina-alumina prostheses was substantially less than the widely used metal and ceramic-on-polyethylene combinations. By identifying and eliminating the factors which accelerate wear, it is expected that the lifetime of these devices can be further increased

Aims

Joint registries typically use revision of an implant as an endpoint and report survival rates after a defined number of years. However, reporting lifetime risk of revision may be more meaningful, especially in younger patients. We aimed to assess lifetime risk of revision for patients in defined age groups at the time of primary surgery.

Aims

This study used an artificial neural network (ANN) model to determine the most important pre- and perioperative variables to predict same-day discharge in patients undergoing total knee arthroplasty (TKA).

We reviewed the results at nine to 13 years of 125 total hip replacements in 113 patients using the monoblock uncemented Morscher press-fit acetabular component. The mean age at the time of operation was 56.9 years (36 to 74). The mean clinical follow-up was 11 years (9.7 to 13.5) and the mean radiological follow-up was 9.4 years (7.7 to 13.1). Three hips were revised, one immediately for instability, one for excessive wear and one for deep infection. No revisions were required for aseptic loosening. A total of eight hips (7.0%) had osteolytic lesions greater than 1 cm, in four around the acetabular component (3.5%). One required bone grafting behind a well-fixed implant. The mean wear rate was 0.11 mm/year (0.06 to 0.78) and was significantly higher in components with a steeper abduction angle. Kaplan-Meier survival curves at 13 years showed survival of 96.8% (95% confidence interval 90.2 to 99.0) for revision for any cause and of 95.7% (95% confidence interval 88.6 to 98.4) for any acetabular re-operation

Aims

The purpose of this study was to determine the access to and ability to use telemedicine technology in adult patients undergoing total hip arthroplasty (THA) and total knee arthroplasty (TKA), and to determine associations with the socioeconomic characteristics of the patients, including age, sex, race, and education. We also sought to understand the patients’ perceived benefits, risks, and preferences when dealing with telemedicine.

Objectives. Metal-on-metal (MoM) hip resurfacing was introduced into clinical practice because it was perceived to be a better alternative to conventional total hip replacement for young and active patients. However, an increasing number of reports of complications have arisen focusing on design and orientation of the components, the generation of metallic wear particles and serum levels of metallic ions. The procedure introduced a combination of two elements: large-dimension components and hard abrasive particles of metal wear. The objective of our study was to investigate the theory that microseparation of the articular surfaces draws in a high volume of bursal fluid and its contents into the articulation, and at relocation under load would generate high pressures of fluid ejection, resulting in an abrasive water jet. Methods. This theoretical concept using MoM resurfacing components (head diameter 55 mm) was modelled mathematically and confirmed experimentally using a material-testing machine that pushed the head into the cup at a rate of 1000 mm/min until fully engaged. Results. The mathematical model showed the pattern but not the force of fluid ejection, the highest pressures were expected when the separation of the components was only a fraction of one millimetre. The experimental work confirmed the results; with the mean peak ejection pressure of 43 763 N/m. 2. equivalent to 306 mmHg or 5 psi. Conclusions. The mechanical effect of the high-pressure abrasive water jet is the likely cause of the spectrum of complications reported with metal-on-metal resurfacing. Investigating serum levels of metallic elements may not be the best method for assessing the local mechanical effects of the abrasive water jet

We retrospectively reviewed 35 cemented unicompartmental knee replacements performed for medial unicompartmental osteoarthritis of the knee in 31 patients ≤50 years old (mean 46, 31 to 49). Patients were assessed clinically and radiologically using the Knee Society scores at a mean follow-up of 9.7 years (5 to 16) and survival at 12 years was calculated. The mean Knee Society Function Score improved from 54 points (25 to 64) pre-operatively to 89 (80 to 100) post-operatively (p < 0.0001). Six knees required revision, four for polyethylene wear treated with an isolated exchange of the tibial insert, one for aseptic loosening and one for progression of osteoarthritis. The 12-year survival according to Kaplan-Meier was 80.6% with revision for any reason as the endpoint. Despite encouraging clinical results, polyethylene wear remains a major concern affecting the survival of unicompartmental knee replacement in patients younger than 50

Aims. We conducted a prospective study of a delta ceramic total hip arthroplasty (THA) to determine the rate of ceramic fracture, to characterise post-operative noise, and to evaluate the mid-term results and survivorship. Patients and Methods. Between March 2009 and March 2011, 274 patients (310 hips) underwent cementless THA using a delta ceramic femoral head and liner. At each follow-up, clinical and radiological outcomes were recorded. A Kaplan-Meier analysis was undertaken to estimate survival. Results. Four patients (four hips) died and 18 patients (20 hips) were lost to follow-up within five years. The remaining 252 patients (286 hips) were followed for a mean of 66.5 months (60 to 84). There were 144 men (166 hips) and 108 women (120 hips) with a mean age of 49.7 years (16 to 83) at surgery. The mean pre-operative Harris Hip Score of 47.1 points improved to 93.8 points at final follow-up. Six patients reported squeaking in seven hips; however, none were audible. Radiolucent lines involving Gruen zones one and/or seven were seen in 52 hips (18.2%). No hip had detectable wear, focal osteolysis or signs of loosening. One hip was revised because of fracture of the ceramic liner, which occurred due to an undetected malseating of the ceramic liner at the time of surgery. One hip was revised for a periprosthetic fracture of the femur, and one hip was treated for periprosthetic joint infection. The six-year survivorship with re-operation for any reason as the endpoint was 99.0% (95% confidence interval 97.8% to 100%). Discussion. The rate of delta ceramic fracture was 0.3% (one of 286). While ceramic head fracture was dominant in previous ceramic-on-ceramic THA, fracture of the delta ceramic liner due to malseating is a concern. Cite this article: Bone Joint J 2017;99-B:741–8

Aims

The reduction in mobility due to hip diseases in children is likely to affect their physical activity (PA) levels. Physical inactivity negatively influences quality of life and health. Our aim was to objectively measure PA in children with hip disease, and correlate it with the Patient-Reported Outcomes Measurement Information System (PROMIS) Mobility Score.

Aims

This is a multicentre, non-inventor, prospective observational study of 503 INFINITY fixed bearing total ankle arthroplasties (TAAs). We report our early experience, complications, and radiological and functional outcomes.

In laboratory tests, the ultra-high molecular weight polyethylene used for the acetabular cups of Charnley hip prostheses has a very low wear rate against steel. In the body radiographic measurements indicate that the polyethylene wears more rapidly. In order to investigate this higher wear rate, the sockets of acetabular cups removed at post-mortem have been examined using optical and electron microscopy. It has been shown that a socket wears predominantly on its superior part and that this is a direct consequence of the orientation of the cup in the body and the direction of loading of the hip. In the worn region the femoral head in effect bores out a new socket for itself, a process which is visible with the naked eye after approximately eight years. Electron microscopy shows that the predominant wear mechanism is adhesion, but after about eight years the appearance of surface cracks suggests that surface fatigue is taking place in addition to this. Laboratory wear tests have shown that pure surface fatigue is not sufficient to account for the high clinical wear rate. Other deformation processes are suggested and discussed with regard to the higher clinical wear rate

Early failure associated with adverse reactions to metal debris is an emerging problem after hip resurfacing but the exact mechanism is unclear. We analysed our entire series of 660 metal-on-metal resurfacings (Articular Surface Replacement (ASR) and Birmingham Hip Resurfacing (BHR)) and large-bearing ASR total hip replacements, to establish associations with metal debris-related failures. Clinical and radiological outcomes, metal ion levels, explant studies and lymphocyte transformation tests were performed. A total of 17 patients (3.4%) were identified (all ASR bearings) with adverse reactions to metal debris, for which revision was required. This group had significantly smaller components, significantly higher acetabular component anteversion, and significantly higher whole concentrations of blood and joint chromium and cobalt ions than asymptomatic patients did (all p < 0.001). Post-revision lymphocyte transformation tests on this group showed no reactivity to chromium or cobalt ions. Explants from these revisions had greater surface wear than retrievals for uncomplicated fractures. The absence of adverse reactions to metal debris in patients with well-positioned implants usually implies high component wear. Surgeons must consider implant design, expected component size and acetabular component positioning in order to reduce early failures when performing large-bearing metal-on-metal hip resurfacing and replacement

Aims

Dual mobility implants in total hip arthroplasty are designed to increase the functional head size, thus decreasing the potential for dislocation. Modular dual mobility (MDM) implants incorporate a metal liner (e.g. cobalt-chromium alloy) in a metal shell (e.g. titanium alloy), raising concern for mechanically assisted crevice corrosion at the modular liner-shell connection. We sought to examine fretting and corrosion on MDM liners, to analyze the corrosion products, and to examine histologically the periprosthetic tissues.

The long-term effects of metal-on-metal arthroplasty are currently under scrutiny because of the potential biological effects of metal wear debris. This review summarises data describing the release, dissemination, uptake, biological activity, and potential toxicity of metal wear debris released from alloys currently used in modern orthopaedics. The introduction of risk assessment for the evaluation of metal alloys and their use in arthroplasty patients is discussed and this should include potential harmful effects on immunity, reproduction, the kidney, developmental toxicity, the nervous system and carcinogenesis

Aims

Aseptic loosening is a leading cause of uncemented arthroplasty failure, often accompanied by fibrotic tissue at the bone-implant interface. A biological target, neutrophil extracellular traps (NETs), was investigated as a crucial connection between the innate immune system’s response to injury, fibrotic tissue development, and proper bone healing. Prevalence of NETs in peri-implant fibrotic tissue from aseptic loosening patients was assessed. A murine model of osseointegration failure was used to test the hypothesis that inhibition (through Pad4^-/- mice that display defects in peptidyl arginine deiminase 4 (PAD4), an essential protein required for NETs) or resolution (via DNase 1 treatment, an enzyme that degrades the cytotoxic DNA matrix) of NETs can prevent osseointegration failure and formation of peri-implant fibrotic tissue.

Aims

Uncemented mobile bearing designs in medial unicompartmental knee arthroplasty (UKA) have seen an increase over the last decade. However, there are a lack of large-scale studies comparing survivorship of these specific designs to commonly used cemented mobile and fixed bearing designs. The aim of this study was to evaluate the survivorship of these designs.

Given the increasing number of total hip arthroplasty procedures being performed annually, it is imperative that orthopaedic surgeons understand factors responsible for instability. In order to treat this potentially complex problem, we recommend correctly classifying the type of instability present based on component position, abductor function, impingement, and polyethylene wear. Correct classification allows the treating surgeon to choose the appropriate revision option that ultimately will allow for the best potential outcome. Cite this article: Bone Joint J 2016;98-B(1 Suppl A):44–9

Most published randomised controlled trials which compare the rates of wear of conventional and cross-linked (XL) polyethylene (PE) in total hip arthroplasty (THA) have described their use with a cementless acetabular component. . We conducted a prospective randomised study to assess the rates of penetration of two distinct types of PE in otherwise identical cemented all-PE acetabular components. . A total of 100 consecutive patients for THA were randomised to receive an acetabular component which had been either highly XL then remelted or moderately XL then annealed. . After a minimum of eight years follow-up, 38 hips in the XL group and 30 hips in the annealed group had complete data (mean follow-up of 9.1 years (7.6 to 10.7) and 8.7 years (7.2 to 10.2), respectively). In the XL group, the steady state rate of penetration from one year onwards was -0.0002 mm/year (. sd. 0.108): in the annealed group it was 0.1382 mm/year (. sd. 0.129) (Mann–Whitney U test, p < 0.001). No complication specific to either material was recorded. These results show that the yearly linear rate of femoral head penetration can be significantly reduced by using a highly XLPE cemented acetabular component. Cite this article: Bone Joint J 2015;97-B:1458–62

Aims

Hydroxyapatite (HA)-coated collars have been shown to reduce aseptic loosening of massive endoprostheses following primary surgery. Limited information exists about their effectiveness in revision surgery. The aim of this study was to radiologically assess osteointegration to HA-coated collars of cemented massive endoprostheses following revision surgery.

Aims

Traditionally, acetabular component insertion during total hip arthroplasty (THA) is visually assisted in the posterior approach and fluoroscopically assisted in the anterior approach. The present study examined the accuracy of a new surgeon during anterior (NSA) and posterior (NSP) THA using robotic arm-assisted technology compared to two experienced surgeons using traditional methods.