Previous studies have suggested that metal-on-metal (MoM) Pinnacle (DePuy Synthes, Warsaw, Indiana) hip arthroplasties implanted after 2006 exhibit higher failure rates. This was attributed to the production of implants with reduced diametrical clearances between their bearing surfaces, which, it was speculated, were outside manufacturing tolerances. This study aimed to better understand the performance of Pinnacle Systems manufactured before and after this event. A total of 92 retrieved MoM Pinnacle hips were analyzed, of which 45 were implanted before 2007, and 47 from 2007 onwards. The ‘pre-2007’ group contained 45 implants retrieved from 21 male and 24 female patients, with a median age of 61.3 years (interquartile range (IQR) 57.1 to 65.5); the ‘2007 onwards’ group contained 47 implants retrieved from 19 male and 28 female patients, with a median age of 61.8 years (IQR 58.5 to 67.8). The volume of material lost from their bearing and taper surfaces was measured using coordinate and roundness measuring machines. These outcomes were then compared statistically using linear regression models, adjusting for potentially confounding factors.Objectives
Methods
We investigated the reliability of the cobalt-chromium (CoCr) synovial joint fluid ratio (JFR) in identifying the presence of a severe aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL) response and/or suboptimal taper performance (SOTP) following metal-on-metal (MoM) hip arthroplasty. We then examined the possibility that the CoCr JFR may influence the serum partitioning of Co and Cr. For part A, we included all revision surgeries carried out at our unit with the relevant data, including volumetric wear analysis, joint fluid (JF) Co and Cr concentrations, and ALVAL grade (n = 315). Receiver operating characteristic curves were constructed to assess the reliability of the CoCr JFR in identifying severe ALVAL and/or SOTP. For part B, we included only patients with unilateral prostheses who had given matched serum and whole blood samples for Co and Cr analysis (n = 155). Multiple regression was used to examine the influence of JF concentrations on the serum partitioning of Co and Cr in the blood.Objectives
Methods
We have encountered patients who developed large joint fluid collections with massive elevations in chromium (Cr) and cobalt (Co) concentrations following metal-on-metal (MoM) hip arthroplasties. In some cases, retrieval analysis determined that these ion concentrations could not be explained simply by the wear rates of the components. We hypothesized that these effects may be associated with aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL). We examined the influence of the ALVAL grade on synovial fluid Co and Cr concentrations following adjustment for patient and device variables, including volumetric wear rates. Initially restricting the analysis to include only patients with one MoM hip resurfacing device, we performed multiple regression analyses of prospectively collected data. We then repeated the same statistical approach using results from a larger cohort with different MoM designs, including total hip arthroplasties.Objectives
Patients and Methods
Unicompartmental knee arthroplasty (UKA) is an alternative to total knee arthroplasty for patients who require treatment of single-compartment osteoarthritis, especially for young patients. To satisfy this requirement, new patient-specific prosthetic designs have been introduced. The patient-specific UKA is designed on the basis of data from preoperative medical images. In general, knee implant design with increased conformity has been developed to provide lower contact stress and reduced wear on the tibial insert compared with flat knee designs. The different tibiofemoral conformity may provide designers the opportunity to address both wear and kinematic design goals simultaneously. The aim of this study was to evaluate wear prediction with respect to tibiofemoral conformity design in patient-specific UKA under gait loading conditions by using a previously validated computational wear method. Three designs with different conformities were developed with the same femoral component: a flat design normally used in fixed-bearing UKA, a tibia plateau anatomy mimetic (AM) design, and an increased conforming design. We investigated the kinematics, contact stress, contact area, wear rate, and volumetric wear of the three different tibial insert designs.Objectives
Methods
To present a surgically relevant update of trunnionosis. Systematic review performed April 2017.Aims
Materials and Methods
Fretting and corrosion at the modular head/neck junction, known
as trunnionosis, in total hip arthroplasty (THA) is a cause of adverse
reaction to metal debris (ARMD). We describe the outcome of revision
of metal-on-polyethylene (MoP) THA for ARMD due to trunnionosis
with emphasis on the risk of major complications. A total of 36 patients with a MoP THA who underwent revision
for ARMD due to trunnionosis were identified. Three were excluded
as their revision had been to another metal head. The remaining
33 were revised to a ceramic head with a titanium sleeve. We describe
the presentation, revision findings, and risk of complications in
these patients.Aims
Patients and Methods
The aim of this study was to compare the design of the generic
OptiStem XTR femoral stem with the established Exeter femoral stem. We obtained five boxed, as manufactured, implants of both designs
at random (ten in total). Two examiners were blinded to the implant
design and independently measured the mass, volume, trunnion surface
topography, trunnion roughness, trunnion cone angle, Caput-Collum-Diaphyseal
(CCD) angle, femoral offset, stem length, neck length, and the width
and roughness of the polished stem shaft using peer-reviewed methods.
We then compared the stems using these parameters.Aims
Materials and Methods
We wished to investigate the influence of metal debris exposure
on the subsequent immune response and resulting soft-tissue injury
following metal-on-metal (MoM) hip arthroplasty. Some reports have
suggested that debris generated from the head-neck taper junction
is more destructive than equivalent doses from metal bearing surfaces. We investigated the influence of the source and volume of metal
debris on chromium (Cr) and cobalt (Co) concentrations in corresponding
blood and hip synovial fluid samples and the observed agglomerated
particle sizes in excised tissues using multiple regression analysis
of prospectively collected data. A total of 199 explanted MoM hips
(177 patients; 132 hips female) were analysed to determine rates
of volumetric wear at the bearing surfaces and taper junctions. Aims
Patients and Methods
The high revision rates of the DePuy Articular Surface Replacement (ASR) and the DePuy ASR XL (the total hip arthroplasty (THA) version) have led to questions over the viability of metal-on-metal (MoM) hip joints. Some designs of MoM hip joint do, however, have reasonable mid-term performance when implanted in appropriate patients. Investigations into the reasons for implant failure are important to offer help with the choice of implants and direction for future implant designs. One way to assess the performance of explanted hip prostheses is to measure the wear (in terms of material loss) on the joint surfaces. In this study, a coordinate measuring machine (CMM) was used to measure the wear on five failed cementless Biomet Magnum/ReCap/ Taperloc large head MoM THAs, along with one Biomet ReCap resurfacing joint. Surface roughness measurements were also taken. The reason for revision of these implants was pain and/or adverse reaction to metal debris (ARMD) and/or elevated blood metal ion levels.Objectives
Methods
The aim of this study was to assess the effect
of frictional torque and bending moment on fretting corrosion at
the taper interface of a modular femoral component and to investigate
whether different combinations of material also had an effect. The
combinations we examined were 1) cobalt–chromium (CoCr) heads on
CoCr stems 2) CoCr heads on titanium alloy (Ti) stems and 3) ceramic
heads on CoCr stems. In test 1 increasing torque was imposed by offsetting the stem
in the anteroposterior plane in increments of 0 mm, 4 mm, 6 mm and
8 mm when the torque generated was equivalent to 0 Nm, 9 Nm, 14
Nm and 18 Nm. In test 2 we investigated the effect of increasing the bending
moment by offsetting the application of axial load from the midline
in the mediolateral plane. Increments of offset equivalent to head
+ 0 mm, head + 7 mm and head + 14 mm were used. Significantly higher currents and amplitudes were seen with increasing
torque for all combinations of material. However, Ti stems showed
the highest corrosion currents. Increased bending moments associated
with using larger offset heads produced more corrosion: Ti stems
generally performed worse than CoCr stems. Using ceramic heads did
not prevent corrosion, but reduced it significantly in all loading
configurations. Cite this article:
An ongoing prospective study to investigate failing metal-on-metal
hip prostheses was commenced at our centre in 2008. We report on
the results of the analysis of the first consecutive 126 failed
mated total hip prostheses from a single manufacturer. Analysis was carried out using highly accurate coordinate measuring
to calculate volumetric and linear rates of the articular bearing
surfaces and also the surfaces of the taper junctions. The relationship
between taper wear rates and a number of variables, including bearing
diameter and orientation of the acetabular component, was investigated.Objectives
Methods
A modular femoral head–neck junction has practical
advantages in total hip replacement. Taper fretting and corrosion
have so far been an infrequent cause of revision. The role of design
and manufacturing variables continues to be debated. Over the past
decade several changes in technology and clinical practice might
result in an increase in clinically significant taper fretting and
corrosion. Those factors include an increased usage of large diameter
(36 mm) heads, reduced femoral neck and taper dimensions, greater
variability in taper assembly with smaller incision surgery, and
higher taper stresses due to increased patient weight and/or physical
activity. Additional studies are needed to determine the role of
taper assembly compared with design, manufacturing and other implant
variables. Cite this article:
The June 2012 Hip &
Pelvis Roundup360 looks at: whether metal-on-metal is really such a disaster; resurfacings with unexplained pain; large heads and high ion levels; hip arthroscopy for FAI; the inaccuracy of clinical tests for impingement; arthroscopic lengthening of iliopsoas; the OA hip; the injured hamstring – football’s most common injury; an algorithm for hip fracture surgery; and sparing piriformis at THR.
The aim of this study was to investigate the
possible benefit of large-head metal-on-metal bearing on a stem
for primary hip replacement compared with a 28 mm diameter conventional
metal-on-polyethylene bearing in a prospective randomised controlled
trial. We investigated cemented stem behaviour between these two
different bearings using Einzel-Bild-Röntgen-Analyse, clinical and
patient reported measures (Harris hip score, Western Ontario and
McMaster Universities osteoarthritis index, Short Form-36 and satisfaction)
and whole blood metal ion levels at two years. A power study indicated
that 50 hips were needed in each group to detect subsidence of >
5 mm at two years with a
p-value of <
0.05. Significant improvement (p <
0.001) was found in the mean
clinical and patient reported outcomes at two years for both groups.
Comparison of outcomes between the groups at two years showed no
statistically significant difference for mean stem migration, clinical
and patient reported outcomes; except overall patient satisfaction which
was higher for metal-on-metal group (p = 0.05). Metal ion levels
were raised above the Medicines and Healthcare products Regulatory
Agency advised safety level (7 µg per litre) in 20% of the metal-on-metal
group and in one patient in metal-on-polyethylene group (who had
a metal-on-metal implant on the contralateral side). Two patients
in the metal-on-metal group were revised, one for pseudotumour and
one for peri-prosthetic fracture. Use of large modular heads is associated with a risk of raised
whole blood metal ion levels despite using a proven bearing from
resurfacing. The head-neck junction or excess stem micromotion are
possibly the weak links warranting further research.
There is widespread concern regarding the incidence of adverse soft-tissue reactions after metal-on-metal (MoM) hip replacement. Recent National Joint Registry data have shown clear differences in the rates of failure of different designs of hip resurfacing. Our aim was to update the failure rates related to metal debris for the Articular Surface Replacement (ASR). A total of 505 of these were implanted. Kaplan-Meier analysis showed a failure rate of 25% at six years for the ASR resurfacing and of 48.8% for the ASR total hip replacement (THR). Of 257 patients with a minimum follow-up of two years, 67 (26.1%) had a serum cobalt concentration which was greater than 7 μg/l. Co-ordinate measuring machine analysis of revised components showed that all patients suffering adverse tissue reactions in the resurfacing group had abnormal wear of the bearing surfaces. Six THR patients had relatively low rates of articular wear, but were found to have considerable damage at the trunion-taper interface. Our results suggest that wear at the modular junction is an important factor in the development of adverse tissue reactions after implantation of a large-diameter MoM THR.
Two Durasul highly crosslinked polyethylene liners were exchanged during revision surgery four and five years after implantation, respectively. The retrieved liners were evaluated macroscopically and surface analysis was performed using optical and electron microscopy. A sample of each liner was used to determine the oxidation of the material by Fourier transform infrared spectroscopy. Samples of the capsule were examined histologically. The annual wear rate was found to be 0.010 and 0.015 mm/year, respectively. Surface analysis showed very little
We report positive and negative factors associated with the most commonly-used methods of reconstruction after pathological fracture of the proximal femur. The study was based on 142 patients treated surgically for 146 metastatic lesions between 1996 and 2003. The local rate of failure was 10.3% (15 of 146). Of 37 operations involving osteosynthetic devices, six failed (16.2%) compared with nine (8.3%) in 109 operations involving endoprostheses. Of nine cases of prosthetic failure, four were due to periprosthetic fractures and three to recurrent dislocation. In the osteosynthesis group, three (13.6%) of 22 reconstruction nails failed. The two-year risk of re-operation after any type of osteosynthesis was 0.35 compared with 0.18 after any type of endoprosthetic reconstruction (p = 0.07). Endoprosthetic reconstructions are preferable to the use of reconstruction nails and other osteosynthetic devices for the treatment of metastatic lesions in the proximal third of the femur.