We report the five-year outcome of a randomised controlled trial which used radiostereometric analysis (RSA) to assess the influence of surface oxidised zirconium (OxZr, Oxinium) on polyethylene wear in vivo.

A total of 120 patients, 85 women and 35 men with a mean age of 70 years (59 to 80) who were scheduled for primary cemented total hip arthroplasty were randomly allocated to four study groups. Patients were blinded to their group assignment and received either a conventional polyethylene (CPE) or a highly cross-linked (HXL) acetabular component of identical design. On the femoral side patients received a 28 mm head made of either cobalt-chromium (CoCr) or OxZr.

The proximal head penetration (wear) was measured with repeated RSA examinations over five years. Clinical outcome was measured using the Harris hip score.

There was no difference in polyethylene wear between the two head materials when used with either of the two types of acetabular component (p = 0.3 to 0.6). When comparing the two types of polyethylene there was a significant difference in favour of HXLPE, regardless of the head material used (p < 0.001).

In conclusion, we found no advantage of OxZr over CoCr in terms of polyethylene wear after five years of follow-up. Our findings do not support laboratory results which have shown a reduced rate of wear with OxZr. They do however add to the evidence on the better resistance to wear of HXLPE over CPE.

Cite this article: Bone Joint J 2015;97-B:1463–9.

The Articular Surface Replacement (ASR) hip resurfacing arthroplasty has a failure rate of 12.0% at five years, compared with 4.3% for the Birmingham Hip Resurfacing (BHR). We analysed 66 ASR and 64 BHR explanted metal-on-metal hip replacements with the aim of understanding their mechanisms of failure. We measured the linear wear rates of the acetabular and femoral components and analysed the clinical cause of failure, pre-revision blood metal ion levels and orientation of the acetabular component.

There was no significant difference in metal ion levels (chromium, p = 0.82; cobalt, p = 0.40) or head wear rate (p = 0.14) between the two groups. The ASR had a significantly increased rate of wear of the acetabular component (p = 0.03) and a significantly increased occurrence of edge loading (p < 0.005), which can be attributed to differences in design between the ASR and BHR. The effects of differences in design on the in vivo wear rates are discussed: these may provide an explanation as to why the ASR is more sensitive to suboptimal positioning than the BHR.

The peri-prosthetic tissue response to wear debris is complex and influenced by various factors including the size, area and number of particles. We hypothesised that the ‘biologically active area’ of all metal wear particles may predict the type of peri-prosthetic tissue response.

Peri-prosthetic tissue was sampled from 21 patients undergoing revision of a small diameter metal-on-metal (MoM) total hip arthroplasty (THA) for aseptic loosening. An enzymatic protocol was used for tissue digestion and scanning electron microscope was used to characterise particles. Equivalent circle diameters and particle areas were calculated. Histomorphometric analyses were performed on all tissue specimens. Aspirates of synovial fluid were collected for analysis of the cytokine profile analysis, and compared with a control group of patients undergoing primary THA (n = 11) and revision of a failed ceramic-on-polyethylene arthroplasty (n = 6).

The overall distribution of the size and area of the particles in both lymphocyte and non-lymphocyte-dominated responses were similar; however, the subgroup with lymphocyte-dominated peri-prosthetic tissue responses had a significantly larger total number of particles.

14 cytokines (interleukin (IL)-1ß, IL-2, IL-4, IL-5, IL-6, IL-10, IL-13, IL-17, interferon (IFN)-γ, and IFN-gamma-inducible protein 10), chemokines (macrophage inflammatory protein (MIP)-1α and MIP-1ß), and growth factors (granulocyte macrophage colony stimulating factor (GM-CSF) and platelet derived growth factor) were detected at significantly higher levels in patients with metal wear debris compared with the control group.

Significantly higher levels for IL-1ß, IL-5, IL-10 and GM-CSF were found in the subgroup of tissues from failed MoM THAs with a lymphocyte-dominated peri-prosthetic response compared with those without this response.

These results suggest that the ‘biologically active area’ predicts the type of peri-prosthetic tissue response. The cytokines IL-1ß, IL-5, IL-10, and GM-CSF are associated with lymphocyte-dominated tissue responses from failed small-diameter MoM THA.

Cite this article: Bone Joint J 2015;97-B:917–23.

Objective

In ex vivo hip fracture studies femoral pairs are split to create two comparable test groups. When more than two groups are required, or if paired femurs cannot be obtained, group allocation according to bone mineral density (BMD) is sometimes performed. In this statistical experiment we explore how this affects experimental results and sample size considerations.

Large femoral heads have become popular in total hip replacement (THR) as a method of reducing the risk of dislocation. However, if large heads are used in ceramic-on-ceramic THR, the liner must be thinner, which may increase the risk of fracture. To compare the rates of ceramic fracture and dislocation between 28 mm and 32 mm ceramic heads, 120 hips in 109 patients (51 men and 58 women, mean age 49.2 years) were randomised to THR with either a 28 mm or a 32 mm ceramic articulation. A total of 57/60 hips assigned to the 28 mm group and 55/60 hips assigned to the 32 mm group were followed for at least five years. No ceramic component fractures occured in any patient in either group. There was one dislocation in the 32 mm group and none in the 28 mm group (p = 0.464). No hip had detectable wear, focal osteolysis or prosthetic loosening. In our small study the 32 mm ceramic articulation appeared to be safe in terms of ceramic liner fracture.

Cite this article: Bone Joint J 2014;96-B:1459–63.

We studied 33 third generation, alumina ceramic-on-ceramic bearings retrieved from cementless total hip replacements after more than six months in situ. Wear volume was measured with a Roundtest machine, and acetabular orientation from the anteroposterior pelvic radiograph. The overall median early wear rate was 0.1 mm³/yr for the femoral heads, and 0.04 mm³/yr for the acetabular liners. We then excluded hips where the components had migrated. In this stable subgroup of 22 bearings, those with an acetabular anteversion of < 15° (seven femoral heads) had a median femoral head wear rate of 1.2 mm³/yr, compared with 0 mm³/yr for those with an anteversion of ≥15° (15 femoral heads, p < 0.001). Even under edge loading, wear volumes with ceramic-on-ceramic bearings are small in comparison to other bearing materials. Low acetabular anteversion is associated with greater wear.

We measured the orientation of the acetabular and femoral components in 45 patients (33 men, 12 women) with a mean age of 53.4 years (30 to 74) who had undergone revision of metal-on-metal hip resurfacings. Three-dimensional CT was used to measure the inclination and version of the acetabular component, femoral version and the horizontal femoral offset, and the linear wear of the removed acetabular components was measured using a roundness machine.

We found that acetabular version and combined version of the acetabular and femoral components were weakly positively correlated with the rate of wear. The acetabular inclination angle was strongly positively correlated with the rate of wear. Femoral version was weakly negatively correlated with the rate of wear. Application of a threshold of > 5 μm/year for the rate of wear in order to separate the revisions into low or high wearing groups showed that more high wearing components were implanted outside Lewinnek’s safe zone, but that this was mainly due to the inclination of the acetabular component, which was the only parameter that significantly differed between the groups.

We were unable to show that excess version of the acetabular component alone or combined with femoral version was associated with an increase in the rate of wear based on our assessment of version using CT.

A prospective study of serum and urinary ion levels was undertaken in a triathlete who had undergone a metal-on-metal resurfacing arthroplasty of the hip four years previously. The one month study period included the final two weeks of training, the day of the triathlon, and the two weeks immediately post-race. Serum cobalt and chromium levels did not vary significantly throughout this period, including levels recorded on the day after the 11-hour triathlon. Urinary excretion of chromium increased immediately after the race and had returned to pre-race levels six days later. The clinical implications are discussed.

The August 2013 Hip & Pelvis Roundup³⁶⁰ looks at: are we getting it right first time?; tantalum augments in revision hip surgery; lower wear in dual mobility?; changing faces changes outcomes; synovial fluid aspiration in MOM hips; taper disease: the new epidemic of hip surgery; the super-obese and THR; and whether well fixed stems can remain in infected hips

Objectives

Wear debris released from bearing surfaces has been shown to provoke negative immune responses in the recipient. Excessive wear has been linked to early failure of prostheses. Analysis using coordinate measuring machines (CMMs) can provide estimates of total volumetric material loss of explanted prostheses and can help to understand device failure. The accuracy of volumetric testing has been debated, with some investigators stating that only protocols involving hundreds of thousands of measurement points are sufficient. We looked to examine this assumption and to apply the findings to the clinical arena.

The April 2012 Hip & Pelvis Roundup³⁶⁰ looks at osteoporotic hip fractures, retrotrochanteric pain, fibrin adhesive and reattachment of articular cartilage, autologous bone marrow mononuclear cells and avascular necrosis, bearing surfaces, stability after THR, digital templating, pelvic tilt after THR, custom-made sockets for DDH, and dogs and THR

An international faculty of orthopaedic surgeons presented their work on the current challenges in hip surgery at the London Hip Meeting which was attended by over 400 delegates. The topics covered included femoroacetabular impingement, thromboembolic phenomena associated with hip surgery, bearing surfaces (including metal-on-metal articulations), outcomes of hip replacement surgery and revision hip replacement. We present a concise report of the current opinions on hip surgery from this meeting with appropriate references to the current literature.

We present a case of early retrieval of an Oxinium femoral head and corresponding polyethylene liner where there was significant surface damage to the head and polyethylene. The implants were retrieved at the time of revision surgery to correct leg-length discrepancy just 48 hours after the primary hip replacement. Appropriate analysis of the retrieved femoral head demonstrated loss of the Oxinium layer with exposure of the underlying substrate and transfer of titanium from the acetabular shell at the time of a reduction of the index total hip replacement. In addition, the level of damage to the polyethylene was extensive despite only 48 hours in situ.

The purpose of this report is to highlight the care that is required at the time of reduction, especially with these hard femoral counter-faces such as Oxinium. To our knowledge, the damage occurring at the time of reduction has not been previously reported following the retrieval of an otherwise well-functioning hip replacement.

We report the survival, radiological and functional outcomes of a single surgeon series of his first 144 consecutive Birmingham hip resurfacing procedures (130 patients) at a minimum of ten years. There were ten revisions during this time. Although no patients were lost to follow-up some did not complete the scoring assessment or undergo radiological assessment at ten years.

The ten-year survival for male patients was 98.0% (95% confidence interval 95.2 to 100). The ten-year survival for the total cohort with aseptic revision as the endpoint was 95.5% (95% confidence interval 91.8 to 99.0) and including revisions for sepsis was 93.5% (95% confidence interval 89.2 to 97.6). The median modified Oxford hip score at ten years was 4.2% (interquartile range 0 to 19) and the median University of California, Los Angeles score was 7.0 (interquartile range 5.0 to 8.0).

This study confirms the midterm reports that metal-on-metal hip resurfacing using the Birmingham Hip provides a durable alternative to total hip replacement, particularly in younger male patients wishing to maintain a high level of function, with low risk of revision for at least ten years.

Lately, concerns have arisen following the use of large metal-on-metal bearings in hip replacements owing to reports of catastrophic soft-tissue reactions resulting in implant failure and associated complications. This review examines the literature and contemporary presentations on current clinical dilemmas in metal-on-metal hip replacement.

The presence of pseudotumours, which are soft-tissue masses relating to the hip, after metal-on-metal hip resurfacing arthroplasty has been associated with elevated levels of metal ions in serum, suggesting that pseudotumours occur when there is increased wear. We aimed to quantify the wear in vivo of implants revised for pseudotumours (eight) and of a control group of implants (22) revised for other reasons of failure.

We found that the implant group with pseudotumours had a significantly higher rate of median linear wear of the femoral component at 8.1 μm/year (2.75 to 25.4) than the 1.79 μm/year (0.82 to 4.15; p = 0.002) of the non-pseudotumour group. For the acetabular component a significantly higher rate of median linear wear of 7.36 μm/year (1.61 to 24.9) was observed in the pseudotumour group compared with 1.28 μm/year (0.81 to 3.33, p = 0.001) in the other group. Wear of the acetabular component in the pseudotumour group always involved the edge of the implant, indicating that edge-loading had occurred.

Our findings are the first direct evidence that pseudotumour is associated with increased wear at the metal-on-metal articulation. Furthermore, edge-loading with the loss of fluid-film lubrication may be an important mechanism of generation of wear in patients with a pseudotumour.

During open reduction of an irreducible anterior dislocation of a total hip replacement with an Oxinium femoral head, it was observed that the head had been significantly damaged. Gross and scanning electron microscopic examination revealed cracking, gouging, and delamination of the surface. Because of the risk which this poses for damaging the polyethylene acetabular liner, it is strongly recommended that patients with this type of prosthetic head be carefully monitored after a dislocation.

In a randomised study, 28 patients with a mean age of 62.2 years (32 to 81) with osteoarthritis or avascular necrosis of the hip received either a ceramic-on-ceramic or a metal-on-metal total hip replacement. Apart from the liners the acetabular and femoral components were made of Ti-Al-Nb alloy. The serum aluminium and cobalt levels were measured before, and at one year after surgery.

The 15 patients in the ceramic-on-ceramic group had a median pre-operative aluminium level of 1.3 μg/l (0.25 to 8.4) and a cobalt level below the detection limit. At one year the aluminium level was 1.1 μg/l (0.25 to 2.3) and the cobalt level was 0.4 μg/l (0.15 to 0.7). The 13 patients in the metal-on-metal group had a median pre-operative aluminium level of 1.9 μg/l (0.25 to 4.4) and a cobalt level below the detection limit. At one year the median aluminium level was 0.9 μg/l (0.25 to 3.9) whereas the cobalt level was 1.4 μg/l (0.5 to 10.5). This increase in the cobalt level at one year was significant (p < 0.001).

Our findings indicate that ceramic-on-ceramic bearings do not cause elevated levels of serum aluminium in the first post-operative year.

The creep and wear behaviour of highly cross-linked polyethylene and standard polyethylene liners were examined in a prospective, double-blind randomised, controlled trial using radiostereometric analysis.

We randomised 54 patients to receive hip replacements with either highly cross-linked polyethylene or standard liners and determined the three-dimensional penetration of the liners over three years.

After three years the mean total penetration was 0.35 mm (SD 0.14) for the highly cross-linked polyethylene group and 0.45 mm (SD 0.19) for the standard group. The difference was statistically significant (p = 0.0184). From the pattern of penetration it was possible to discriminate creep from wear. Most (95%) of the creep occurred within six months of implantation and nearly all within the first year. There was no difference in the mean degree of creep between the two types of polyethylene (highly cross-linked polyethylene 0.26 mm, SD 0.17; standard 0.27 mm, SD 0.2; p = 0.83). There was, however, a significant difference (p = 0.012) in the mean wear rate (highly cross-linked polyethylene 0.03 mm/yr, SD 0.06; standard 0.07 mm/yr, SD 0.05). Creep and wear occurred in significantly different directions (p = 0.01); creep was predominantly proximal whereas wear was anterior, proximal and medial.

We conclude that penetration in the first six months is creep-dominated, but after one year virtually all penetration is due to wear. Highly cross-linked polyethylene has a 60% lower rate of wear than standard polyethylene and therefore will probably perform better in the long term.