Lately, concerns have arisen following the use of large metal-on-metal bearings in hip replacements owing to reports of catastrophic soft-tissue reactions resulting in implant failure and associated complications. This review examines the literature and contemporary presentations on current clinical dilemmas in metal-on-metal hip replacement.

Pseudotumours are a rare complication of hip resurfacing. They are thought to be a response to metal debris which may be caused by edge loading due to poor orientation of the acetabular component. Our aim was to determine the optimal acetabular orientation to minimise the risk of pseudotumour formation.

We matched 31 hip resurfacings revised for pseudotumour formation with 58 controls who had a satisfactory outcome from this procedure. The radiographic inclination and anteversion angles of the acetabular component were measured on anteroposterior radiographs of the pelvis using Einzel-Bild-Roentgen-Analyse software. The mean inclination angle (47°, 10° to 81°) and anteversion angle (14°, 4° to 34°) of the pseudotumour cases were the same (p = 0.8, p = 0.2) as the controls, 46° (29° to 60°) and 16° (4° to 30°) respectively, but the variation was greater. Assuming an accuracy of implantation of ± 10° about a target position, the optimal radiographic position was found to be approximately 45° of inclination and 20° of anteversion. The incidence of pseudotumours inside the zone was four times lower (p = 0.007) than outside the zone.

In order to minimise the risk of pseudotumour formation we recommend that surgeons implant the acetabular component at an inclination of 45° (± 10) and anteversion of 20° (± 10) on post-operative radiographs. Because of differences between the radiographic and the operative angles, this may be best achieved by aiming for an inclination of 40° and an anteversion of 25°.

We sought to establish the incidence of joint failure secondary to adverse reaction to metal debris (ARMD) following metal-on-metal hip resurfacing in a large, three surgeon, multicentre study involving 4226 hips with a follow-up of 10 to 142 months. Three implants were studied: the Articular Surface Replacement; the Birmingham Hip Resurfacing; and the Conserve Plus. Retrieved implants underwent analysis using a co-ordinate measuring machine to determine volumetric wear. There were 58 failures associated with ARMD. The median chromium and cobalt concentrations in the failed group were significantly higher than in the control group (p < 0.001). Survival analysis showed a failure rate in the patients with Articular Surface Replacement of 9.8% at five years, compared with < 1% at five years for the Conserve Plus and 1.5% at ten years for the Birmingham Hip Resurfacing. Two ARMD patients had relatively low wear of the retrieved components. Increased wear from the metal-on-metal bearing surface was associated with an increased rate of failure secondary to ARMD. However, the extent of tissue destruction at revision surgery did not appear to be dose-related to the volumetric wear.

We retrospectively reviewed, ten years after surgery, 100 consecutive total hip replacements in which the Duraloc 300 cup had been used. Post-operative radiographs were analysed for placement of the cup and interface gaps and follow-up radiographs for lucent lines, osteolysis, wear and migration.

All the components were found to be stable with no evidence of loosening. The mean rate of wear was 0.12 mm/year. Three hips developed acetabular osteolysis at the level of the apex hole. Two have successfully undergone bone grafting without removal of the implants and one patient is awaiting surgery. The Duraloc 300 cup has a survival of 100% at ten years with no aseptic loosening and a low incidence of pelvic osteolysis.

Bisphosphonates reduce peri-prosthetic bone loss in the short term after total hip replacement but the mid- and longer term effects are not known. The aims of this randomised trial were to examine the effect of a single dose of 90 mg of pamidronate on the clinical and radiological outcome and peri-prosthetic bone mineral density in 50 patients (56 hips) over a five-year period, following total hip replacement.

At five years, 37 patients (42 hips) returned for assessment. The Harris hip scores were similar in the pamidronate and placebo groups throughout the study. Also at five years, four patients, two from each group had osteolytic lesions on plain radiography. These were located around the acetabular component in three patients and in the femoral calcar in one. The femoral and acetabular peri-prosthetic bone mineral density in the pamidronate group and the control group was similar at five years.

Pamidronate given as a single post-operative dose does not appear to influence the clinical outcome or prevent the development of osteolytic lesions at five years after total hip replacement.

There have been no large comparative studies of the blood levels of metal ions after implantation of commercially available hip resurfacing devices which have taken into account the effects of femoral size and inclination and anteversion of the acetabular component. We present the results in 90 patients with unilateral articular surface replacement (ASR) hip resurfacings (mean time to blood sampling 26 months) and 70 patients with unilateral Birmingham Hip Resurfacing (BHR) implants (mean time 47 months).

The whole blood and serum chromium (Cr) and cobalt (Co) concentrations were inversely related to the size of the femoral component in both groups (p < 0.05). Cr and Co were more strongly influenced by the position of the acetabular component in the case of the ASR, with an increase in metal ions observed at inclinations > 45° and anteversion angles of < 10° and > 20°. These levels were only increased in the BHR group when the acetabular component was implanted with an inclination > 55°.

A significant relationship was identified between the anteversion of the BHR acetabular component and the levels of Cr and Co (p < 0.05 for Co), with an increase observed at anteversion angles < 10° and > 20°. The median whole blood and serum Cr concentrations of the male ASR patients were significantly lower than those of the BHR men (p < 0.001). This indicates that reduced diametral clearance may equate to a reduction in metal ion concentrations in larger joints with satisfactory orientation of the acetabular component.