The occurrence of a radiolucent line at the interface of bone and cement in total joint prostheses is a frequently observed, although little understood, phenomenon. Because of an operative technique utilised in instances of bone loss, we have, within a single implant mass used in each of a series of 18 total knee replacements, been able to observe two separate interfaces, one between bone and cement and the other between bone and cobalt chrome. The average period of observation was 32 months. All of the knees except one demonstrated a lucency at the bone-cement interface; only one of the knees had a similar lucency at the bone-CoCr interface. One of the knees was studied histologically. In the light of the universal observation of macrophages at bone-cement interfaces and the recent finding that osteoclasts are derived from macrophages, these observations are significant in relation to the aetiology of bone-cement lucencies

Aims

The aim of this study was to conduct the largest low contact stress (LCS) retrieval study to elucidate the failure mechanisms of the Porocoat and Duofix femoral component. The latter design was voluntarily recalled by the manufacturer.

Bone cement containing gentamicin may release antibiotic when fractured during revision operations. Tissue samples taken during surgery may be contaminated by gentamicin and give inaccurate microbiological assessment. We studied five patients in whom cement containing gentamicin had been used in the primary procedure. During revision hip replacement, samples of joint fluid, tissues and cement were taken both before and after disruption of the cement. With the exception of one sample of joint fluid, low concentrations of gentamicin were recorded in the samples taken before the cement was disrupted, but after disruption the specimens contained gentamicin at concentrations high enough to inhibit or prevent growth of sensitive organisms. The cement contained very high levels up to ten years after insertion. Our findings suggest that no reliance can be placed on the microbiological assessment of specimens taken once cement splitting has started and that specimens should therefore be taken as early as possible

Aims

The use of vitamin E-infused highly crosslinked polyethylene (HXLPE) in total knee prostheses is controversial. In this paper we have compared the clinical and radiological results between conventional polyethylene and vitamin E-infused HXLPE inserts in total knee arthroplasty (TKA).

We report the clinical and tribological performance of 67 ceramic acetabular prostheses implanted between 1976 and 1979 without bone cement. They articulated with ceramic femoral heads mounted on mental femoral stems. After a mean elapsed period of 144 months, 59 sockets were radiographically stable but two showed early signs and six showed late signs of loosening. Four of the loose sockets have been revised. Histological analysis of the retrieved tissue showed a fibrous membrane around all the implants, with fibrocartilage in some. There was no bone ingrowth, and the fibrous membrane was up to 6 mm thick and infiltrated with lymphocytes, plasma cells, and macrophages. Intra- and extracellular birefringent wear particles were seen. Tribological analysis showed total wear rates in two retrieved alumina-on-alumina joints of 2.6 microns per year in a stable implant and 68 microns in a loose implant. Survival analysis showed a revision rate of 12.4% at 136 months

Objectives

The aim of this study was to analyze drain fluid, blood, and urine simultaneously to follow the long-term release of vancomycin from a biphasic ceramic carrier in major hip surgery. Our hypothesis was that there would be high local vancomycin concentrations during the first week with safe low systemic trough levels and a complete antibiotic release during the first month.

Aims

The aim of this study was to report the results of custom-made endoprostheses with extracortical plates plus or minus a short, intramedullary stem aimed at preserving the physis after resection of bone sarcomas in children.

Objectives

Bone void fillers are increasingly being used for dead space management in arthroplasty revision surgery. The aim of this study was to investigate the influence of calcium sulphate bone void filler (CS-BVF) on the damage and wear of total knee arthroplasty using experimental wear simulation.

Aims

The aim of this study was to investigate mortality and risk of intraoperative medical complications depending on delay to hip fracture surgery by using data from the Norwegian Hip Fracture Register (NHFR) and the Norwegian Patient Registry (NPR).

Aims

We retrospectively report our experience of managing 30 patients with a primary malignant tumour of the distal tibia; 25 were treated by limb salvage surgery and five by amputation. We compared the clinical outcomes of following the use of different methods of reconstruction.

Aims

The aim of this study was to give estimates of the incidence of component incompatibility in hip and knee arthroplasty and to test the effect of an online, real-time compatibility check.

We describe the development and early clinical application of a ported, proximally-cemented titanium stem for cemented total hip arthroplasty. PMMA bone cement is delivered to the proximal femur under pressure after the stem has been positioned within the femoral canal. A mid-stem cement occluder contains the cement to the proximal stem only. A tapered body is incorporated in the design of the stem to reduce the structural stiffness and hence the degree of stress shielding within the reconstructed joint. We performed preclinical studies to measure the reduction in porosity and the pressurisation achieved. The porosity, as measured by the void percentage within the cured cement mantle, was reduced by more than 50% and there was an almost threefold increase in the mean pressure. Mechanical testing of the stem, using a three-point bend test, showed that the addition of cement injection ports on the anterior and posterior sides of the body of the proximal stem did not reduce its strength. Finite-element analysis indicated that, compared with a fully-cemented conventional stem, there was no change in the stresses within the cement mantle. In a series of 40 proximally-cemented stems followed for up to six years (mean 51 months) the mean Harris hip score was 91, and 85% of patients had good or excellent results. There was excellent pain relief, an increased level of activity and good patient satisfaction. One mechanical failure of the stem required revision at three years after implantation. The early results indicate that the clinical performance was equal to that achieved with other modern cemented stems. Radiological evaluation showed excellent results with no evidence of stress shielding. Further follow-up will determine if long-term stress shielding is reduced and if revision is made easier by the absence of a distal cement mantle

Aims

Loosening of the tibial component after total knee arthroplasty (TKA) is a common indication for revision. Increasing the strength of the initial tibial implant/cement interface is desirable. There is little information about the surgical techniques that lead to the highest strength. We investigated the effects of eight variables on the strength of the initial tibial baseplate/cement interface.

Aims

Fungal prosthetic joint infections (PJIs) are rare and account for about 1% of total PJIs. Our aim was to present clinical and microbiological results in treating these patients with a two-stage approach and antifungal spacers.

During the last decades, several research groups have used bisphosphonates for local application to counteract secondary bone resorption after bone grafting, to improve implant fixation or to control bone resorption caused by bone morphogenetic proteins (BMPs). We focused on zoledronate (a bisphosphonate) due to its greater antiresorptive potential over other bisphosphonates. Recently, it has become obvious that the carrier is of importance to modulate the concentration and elution profile of the zoledronic acid locally. Incorporating one fifth of the recommended systemic dose of zoledronate with different apatite matrices and types of bone defects has been shown to enhance bone regeneration significantly in vivo. We expect the local delivery of zoledronate to overcome the limitations and side effects associated with systemic usage; however, we need to know more about the bioavailability and the biological effects. The local use of BMP-2 and zoledronate as a combination has a proven additional effect on bone regeneration. This review focuses primarily on the local use of zoledronate alone, or in combination with bone anabolic factors, in various preclinical models mimicking different orthopaedic conditions.

Cite this article: I. Qayoom, D. B. Raina, A. Širka, Š. Tarasevičius, M. Tägil, A. Kumar, L. Lidgren. Anabolic and antiresorptive actions of locally delivered bisphosphonates for bone repair: A review. Bone Joint Res 2018;7:548–560. DOI: 10.1302/2046-3758.710.BJR-2018-0015.R2.

Aims

The aim of this paper was to investigate the prognostic factors for local recurrence in patients with pathological fracture through giant cell tumours of bone (GCTB).

Objectives

Prosthetic joint infection (PJI) diagnosis is a major challenge in orthopaedics, and no reliable parameters have been established for accurate, preoperative predictions in the differential diagnosis of aseptic loosening or PJI. This study surveyed factors in synovial fluid (SF) for improving PJI diagnosis.

Aims

The hip’s capsular ligaments passively restrain extreme range of movement (ROM) by wrapping around the native femoral head/neck. We determined the effect of hip resurfacing arthroplasty (HRA), dual-mobility total hip arthroplasty (DM-THA), conventional THA, and surgical approach on ligament function.