Objectives. Few studies have assessed outcomes following non-metal-on-metal hip arthroplasty (non-MoMHA) revision surgery performed for adverse reactions to metal debris (ARMD). We assessed outcomes following non-MoMHA revision surgery performed for ARMD, and identified predictors of re-revision. Methods. We performed a retrospective observational study using data from the National Joint Registry for England and Wales. All non-MoMHAs undergoing revision surgery for ARMD between 2008 and 2014 were included (185 hips in 185 patients). Outcome measures following ARMD revision were intra-operative complications, mortality and re-revision surgery. Predictors of re-revision were identified using Cox regression. Results. Intra-operative complications occurred in 6.0% (n = 11) of the 185 cases. The cumulative four-year patient survival rate was 98.2% (95% CI 92.9 to 99.5). Re-revision surgery was performed in 13.5% (n = 25) of hips at a mean time of 1.2 years (0.1 to 3.1 years) following ARMD revision. Infection (32%; n = 8), dislocation/subluxation (24%; n = 6), and aseptic loosening (24%; n = 6) were the most common re-revision indications. The cumulative four-year implant survival rate was 83.8% (95% CI 76.7 to 88.9). Multivariable analysis identified three predictors of re-revision: multiple revision indications (hazard ratio (HR) = 2.78; 95% CI 1.03 to 7.49; p = 0.043); selective component revisions (HR = 5.76; 95% CI 1.28 to 25.9; p = 0.022); and ceramic-on-polyethylene revision bearings (HR = 3.08; 95% CI 1.01 to 9.36; p = 0.047). Conclusions. Non-MoMHAs revised for ARMD have a high short-term risk of re-revision, with important predictors of future re-revision including selective component revision, multiple revision indications, and ceramic-on-polyethylene revision bearings. Our findings may help counsel patients about the risks of ARMD revision, and guide reconstructive decisions. Future studies attempting to validate the predictors identified should also assess the effects of implant design (metallurgy and modularity), given that this was an important study limitation potentially influencing the reported prognostic factors. Cite this article: G. S. Matharu, A. Judge, D. W. Murray, H. G. Pandit. Outcomes following revision surgery performed for adverse reactions to metal debris in non-metal-on-metal hip arthroplasty patients: Analysis of 185 revisions from the National Joint Registry for England and Wales. Bone Joint Res 2017;6:405–413. DOI: 10.1302/2046-3758.67.BJR-2017-0017.R2

Objectives. Alarm over the reported high failure rates for metal-on-metal (MoM) hip implants as well as their potential for locally aggressive Adverse Reactions to Metal Debris (ARMDs) has prompted government agencies, internationally, to recommend the monitoring of patients with MoM hip implants. Some have advised that a blood ion level >7 µg/L indicates potential for ARMDs. We report a systematic review and meta-analysis of the performance of metal ion testing for ARMDs. Methods. We searched MEDLINE and EMBASE to identify articles from which it was possible to reconstruct a 2 × 2 table. Two readers independently reviewed all articles and extracted data using explicit criteria. We computed a summary receiver operating curve using a Bayesian random-effects hierarchical model. Results. Our literature search returned 575 unique articles; only six met inclusion criteria defined a priori. The discriminative capacity of ion tests was homogeneous across studies but that there was substantial cut-point heterogeneity. Our best estimate of the “true” area under curve (AUC) for metal ion testing is 0.615, with a 95% credible interval of 0.480 to 0.735, thus we can state that the probability that metal ion testing is actually clinically useful with an AUC ≥ 0.75 is 1.7%. Conclusion. Metal ion levels are not useful as a screening test for identifying high risk patients because ion testing will either lead to a large burden of false positive patients, or otherwise marginally modify the pre-test probability. With the availability of more accurate non-invasive tests, we did not find any evidence for using blood ion levels to diagnose symptomatic patients. Cite this article: M. Pahuta, J. M. Smolders, J. L. van Susante, J. Peck, P. R. Kim, P. E. Beaule. Blood metal ion levels are not a useful test for adverse reactions to metal debris: a systematic review and meta-analysis. Bone Joint Res 2016;5:379–386. DOI: 10.1302/2046-3758.59.BJR-2016-0027.R1

We sought to establish the incidence of joint failure secondary to adverse reaction to metal debris (ARMD) following metal-on-metal hip resurfacing in a large, three surgeon, multicentre study involving 4226 hips with a follow-up of 10 to 142 months. Three implants were studied: the Articular Surface Replacement; the Birmingham Hip Resurfacing; and the Conserve Plus. Retrieved implants underwent analysis using a co-ordinate measuring machine to determine volumetric wear. There were 58 failures associated with ARMD. The median chromium and cobalt concentrations in the failed group were significantly higher than in the control group (p < 0.001). Survival analysis showed a failure rate in the patients with Articular Surface Replacement of 9.8% at five years, compared with < 1% at five years for the Conserve Plus and 1.5% at ten years for the Birmingham Hip Resurfacing. Two ARMD patients had relatively low wear of the retrieved components. Increased wear from the metal-on-metal bearing surface was associated with an increased rate of failure secondary to ARMD. However, the extent of tissue destruction at revision surgery did not appear to be dose-related to the volumetric wear

Objectives. We investigated the reliability of the cobalt-chromium (CoCr) synovial joint fluid ratio (JFR) in identifying the presence of a severe aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL) response and/or suboptimal taper performance (SOTP) following metal-on-metal (MoM) hip arthroplasty. We then examined the possibility that the CoCr JFR may influence the serum partitioning of Co and Cr. Methods. For part A, we included all revision surgeries carried out at our unit with the relevant data, including volumetric wear analysis, joint fluid (JF) Co and Cr concentrations, and ALVAL grade (n = 315). Receiver operating characteristic curves were constructed to assess the reliability of the CoCr JFR in identifying severe ALVAL and/or SOTP. For part B, we included only patients with unilateral prostheses who had given matched serum and whole blood samples for Co and Cr analysis (n = 155). Multiple regression was used to examine the influence of JF concentrations on the serum partitioning of Co and Cr in the blood. Results. A CoCr JFR > 1 showed a specificity of 83% (77% to 88%) and sensitivity of 63% (55% to 70%) for the detection of severe ALVAL and/or SOTP. In patients with CoCr JFRs > 1, the median blood Cr to serum Cr ratio was 0.99, compared with 0.71 in patients with CoCr JFRs < 1 (p < 0.001). Regression analysis demonstrated that the blood Cr to serum Cr value was positively associated with the JF Co concentration (p = 0.011) and inversely related to the JF Cr concentration (p < 0.001). Conclusion. Elevations in CoCr JFRs are associated with adverse biological (severe ALVAL) or tribocorrosive processes (SOTP). Comparison of serum Cr with blood Cr concentrations may be a useful additional clinical tool to help to identify these conditions. Cite this article: D. J. Langton, S. Natu, C. F. Harrington, J. G. Bowsher, A. V. F. Nargol. Is the synovial fluid cobalt-to-chromium ratio related to the serum partitioning of metal debris following metal-on-metal hip arthroplasty? Bone Joint Res 2019;8:146–155. DOI: 10.1302/2046-3758.83.BJR-2018-0049.R1

We undertook a retrospective cohort study to determine clinical outcomes following the revision of metal-on-metal (MoM) hip replacements for adverse reaction to metal debris (ARMD), and to identify predictors of time to revision and outcomes following revision. Between 1998 and 2012 a total of 64 MoM hips (mean age at revision of 57.8 years; 46 (72%) female; 46 (72%) hip resurfacings and 18 (28%) total hip replacements) were revised for ARMD at one specialist centre. At a mean follow-up of 4.5 years (1.0 to 14.6) from revision for ARMD there were 13 hips (20.3%) with post-operative complications and eight (12.5%) requiring re-revision. . The Kaplan–Meier five-year survival rate for ARMD revision was 87.9% (95% confidence interval 78.9 to 98.0; 19 hips at risk). Excluding re-revisions, the median absolute Oxford hip score (OHS) following ARMD revision using the percentage method (0% best outcome and 100% worst outcome) was 18.8% (interquartile range (IQR) 7.8% to 48.3%), which is equivalent to 39/48 (IQR 24.8/48 to 44.3/48) when using the modified OHS. Histopathological response did not affect time to revision for ARMD (p = 0.334) or the subsequent risk of re-revision (p = 0.879). Similarly, the presence or absence of a contralateral MoM hip bearing did not affect time to revision for ARMD (p = 0.066) or the subsequent risk of re-revision (p = 0.178). . Patients revised to MoM bearings had higher rates of re-revision (five of 16 MoM hips re-revised; p = 0.046), but those not requiring re-revision had good functional results (median absolute OHS 14.6% or 41.0/48). Short-term morbidity following revision for ARMD was comparable with previous reports. Caution should be exercised when choosing bearing surfaces for ARMD revisions. Cite this article: Bone Joint J 2014;96-B:1600–9

Aims. We investigated whether blood metal ion levels could effectively identify patients with bilateral Birmingham Hip Resurfacing (BHR) implants who have adverse reactions to metal debris (ARMD). Patients and Methods. Metal ion levels in whole blood were measured in 185 patients with bilateral BHRs. Patients were divided into those with ARMD who either had undergone a revision for ARMD or had ARMD on imaging (n = 30), and those without ARMD (n = 155). Receiver operating characteristic analysis was used to determine the optimal thresholds of blood metal ion levels for identifying patients with ARMD. Results. The maximum level of cobalt or chromium ions in the blood was the parameter which produced the highest area under the curve (91.0%). The optimal threshold for distinguishing between patients with and without ARMD was 5.5 µg/l (83.3% sensitivity, 88.4% specificity, 58.1% positive and 96.5% negative predictive values). Similar results were obtained in a subgroup of 111 patients who all underwent cross-sectional imaging. Between 3.2% and 4.3% of patients with ARMD were missed if United Kingdom (7 µg/l) and United States (10 µg/l) authority thresholds were used respectively, compared with 2.7% if our implant specific threshold was used, though these differences did not reach statistical significance (p ≥ 0.248). Conclusion. Patients with bilateral BHRs who have blood metal ion levels below our implant specific threshold were at low-risk of having ARMD. Cite this article: Bone Joint J 2016;98-B:1455–62

We conducted a retrospective study to assess the prevalence of adverse reactions to metal debris (ARMD) in patients operated on at our institution with metal-on-metal (MoM) total hip replacements with 36 mm heads using a Pinnacle acetabular shell. A total of 326 patients (150 males, 175 hips; 176 females, 203 hips) with a mean age of 62.7 years (28 to 85) and mean follow-up of 7.5 years (0.1 to 10.8) participating in our in-depth modern MoM follow-up programme were included in the study, which involved recording whole blood cobalt and chromium ion measurements, Oxford hip scores (OHS) and plain radiographs of the hip and targeted cross-sectional imaging. Elevated blood metal ion levels (> 5 parts per billion) were seen in 32 (16.1%) of the 199 patients who underwent unilateral replacement. At 23 months after the start of our modern MoM follow-up programme, 29 new cases of ARMD had been revealed. Hence, the nine-year survival of this cohort declined from 96% (95% CI 95 to 98) with the old surveillance routine to 86% (95% CI 82 to 90) following the new protocol. Although ARMD may not be as common in 36 mm MoM THRs as in those with larger heads, these results support the Medicines and Healthcare Products Regulatory Agency guidelines on regular reviews and further investigations, and emphasise the need for specific a follow-up programme for patients with MoM THRs. Cite this article: Bone Joint J 2014; 96-B:1610–17

Aims

To determine the outcomes following revision surgery of metal-on-metal hip arthroplasties (MoMHA) performed for adverse reactions to metal debris (ARMD), and to identify factors predictive of re-revision.

We report a 12- to 15-year implant survival assessment of a prospective single-surgeon series of Birmingham Hip Resurfacings (BHRs). The earliest 1000 consecutive BHRs including 288 women (335 hips) and 598 men (665 hips) of all ages and diagnoses with no exclusions were prospectively followed-up with postal questionnaires, of whom the first 402 BHRs (350 patients) also had clinical and radiological review.

Mean follow-up was 13.7 years (12.3 to 15.3). In total, 59 patients (68 hips) died 0.7 to 12.6 years following surgery from unrelated causes. There were 38 revisions, 0.1 to 13.9 years (median 8.7) following operation, including 17 femoral failures (1.7%) and seven each of infections, soft-tissue reactions and other causes. With revision for any reason as the end-point Kaplan–Meier survival analysis showed 97.4% (95% confidence interval (CI) 96.9 to 97.9) and 95.8% (95% CI 95.1 to 96.5) survival at ten and 15 years, respectively. Radiological assessment showed 11 (3.5%) femoral and 13 (4.1%) acetabular radiolucencies which were not deemed failures and one radiological femoral failure (0.3%).

Our study shows that the performance of the BHR continues to be good at 12- to 15-year follow-up. Men have better implant survival (98.0%; 95% CI 97.4 to 98.6) at 15 years than women (91.5%; 95% CI 89.8 to 93.2), and women < 60 years (90.5%; 95% CI 88.3 to 92.7) fare worse than others. Hip dysplasia and osteonecrosis are risk factors for failure. Patients under 50 years with osteoarthritis fare best (99.4%; 95% CI 98.8 to 100 survival at 15 years), with no failures in men in this group.

Cite this article: Bone Joint J 2014;96-B:1298–1306.

Aims. The Birmingham Hip Resurfacing (BHR) was introduced in 1997 to address the needs of young active patients using a historically proven large-diameter metal-on-metal (MoM) bearing. A single designer surgeon’s consecutive series of 130 patients (144 hips) was previously reported at five and ten years, reporting three and ten failures, respectively. The aim of this study was to extend the follow-up of this original cohort at 25 years. Methods. The study extends the reporting on the first consecutive 144 resurfacing procedures in 130 patients for all indications. All operations were undertaken between August 1997 and May 1998. The mean age at operation was 52.1 years (SD 9.93; 17 to 76), and included 37 female patients (28.5%). Failure was defined as revision of either component for any reason. Kaplan-Meier survival analysis was performed. Routine follow-up with serum metal ion levels, radiographs, and Oxford Hip Scores (OHSs) was undertaken. Results. Overall implant survival was 83.50% (95% confidence interval (CI) 0.79 to 0.90) at 25 years, and the number at risk was 79. Survival in male patients at 25 years was 89.5% (95% CI 0.83 to 0.96) compared to 66.9% for female patients (95% CI 0.51 to 0.83). Ten additional failures occurred in the period of ten to 25 years. These involved an adverse reaction to metal debris in four patients, a periprosthetic femoral neck fracture affecting five patients, and aseptic loosening in one patient. The median chromium levels were 49.50 nmol/l (interquartile range (IQR) 34 to 70), and the median cobalt serum levels were 42 nmol/l (IQR 24.50 to 71.25). The median OHS at last follow-up was 35 (IQR 10 to 48). During the 25-year study period, 29 patients died. Patient survival at 25 years was 75.10% (95% CI 0.67 to 0.83). Conclusion. This study demonstrates that MoM hip resurfacing using the BHR provides a durable alternative to total hip arthroplasty (THA), particularly in younger male patients with osteoarthritis wishing to maintain a high level of function. These results compare favourably to the best results for THAs. Cite this article: Bone Joint J 2024;106-B(6):540–547

Aims. We wished to investigate the influence of metal debris exposure on the subsequent immune response and resulting soft-tissue injury following metal-on-metal (MoM) hip arthroplasty. Some reports have suggested that debris generated from the head-neck taper junction is more destructive than equivalent doses from metal bearing surfaces. . Patients and Methods. We investigated the influence of the source and volume of metal debris on chromium (Cr) and cobalt (Co) concentrations in corresponding blood and hip synovial fluid samples and the observed agglomerated particle sizes in excised tissues using multiple regression analysis of prospectively collected data. A total of 199 explanted MoM hips (177 patients; 132 hips female) were analysed to determine rates of volumetric wear at the bearing surfaces and taper junctions. . Results. The statistical modelling suggested that a greater source contribution of metal debris from the taper junction was associated with smaller aggregated particle sizes in the local tissues and a relative reduction of Cr ion concentrations in the corresponding synovial fluid and blood samples. Metal debris generated from taper junctions appears to be of a different morphology, composition and therefore, potentially, immunogenicity to that generated from bearing surfaces. Conclusion. The differences in debris arising from the taper and the articulating surfaces may provide some understanding of the increased incidence of soft-tissue reactions reported in patients implanted with MoM total hip arthroplasties compared with patients with hip resurfacings. Cite this article: Bone Joint J 2016;98-B:925–33

Early failure associated with adverse reactions to metal debris is an emerging problem after hip resurfacing but the exact mechanism is unclear. We analysed our entire series of 660 metal-on-metal resurfacings (Articular Surface Replacement (ASR) and Birmingham Hip Resurfacing (BHR)) and large-bearing ASR total hip replacements, to establish associations with metal debris-related failures. Clinical and radiological outcomes, metal ion levels, explant studies and lymphocyte transformation tests were performed. A total of 17 patients (3.4%) were identified (all ASR bearings) with adverse reactions to metal debris, for which revision was required. This group had significantly smaller components, significantly higher acetabular component anteversion, and significantly higher whole concentrations of blood and joint chromium and cobalt ions than asymptomatic patients did (all p < 0.001). Post-revision lymphocyte transformation tests on this group showed no reactivity to chromium or cobalt ions. Explants from these revisions had greater surface wear than retrievals for uncomplicated fractures. The absence of adverse reactions to metal debris in patients with well-positioned implants usually implies high component wear. Surgeons must consider implant design, expected component size and acetabular component positioning in order to reduce early failures when performing large-bearing metal-on-metal hip resurfacing and replacement

We investigated the changes seen on serial metal artefact reduction magnetic resonance imaging scans (MARS-MRI) of metal-on-metal total hip arthroplasties (MoM THAs). In total 155 THAs, in 35 male and 100 female patients (mean age 70.4 years, 42 to 91), underwent at least two MRI scans at a mean interval of 14.6 months (2.6 to 57.1), at a mean of 48.2 months (3.5 to 93.3) after primary hip surgery. Scans were graded using a modification of the Oxford classification. Progression of disease was defined as an increase in grade or a minimum 10% increase in fluid lesion volume at second scan. A total of 16 hips (30%) initially classified as ‘normal’ developed an abnormality on the second scan. Of those with ‘isolated trochanteric fluid’ 9 (47%) underwent disease progression, as did 7 (58%) of ‘effusions’. A total of 54 (77%) of hips initially classified as showing adverse reactions to metal debris (ARMD) progressed, with higher rates of progression in higher grades. Disease progression was associated with high blood cobalt levels or an irregular pseudocapsule lining at the initial scan. There was no association with changes in functional scores. Adverse reactions to metal debris in MoM THAs may not be as benign as previous reports have suggested. Close radiological follow-up is recommended, particularly in high-risk groups. Cite this article: Bone Joint J 2015;97-B:1328–37

Few independent studies have reported the outcome of resurfacing arthroplasty of the hip. The aim of this study was to report the five-year clinical outcome and seven-year survival of an independent series. A total of 610 Birmingham Hip Resurfacing arthroplasties were performed in 532 patients with a mean age of 51.8 years (16.5 to 81.6). They were followed for between two and eight years; 107 patients (120 hips) had been followed up for more than five years. Two patients were lost to follow-up. At a minimum of five years’ follow-up, 79 of 85 hips (93%) had an excellent or good outcome according to the Harris hip score. The mean Oxford hip score was 16.1 points (. sd. 7.7) and the mean University of California Los Angeles activity score was 6.6 points (. sd. 1.9). There were no patients with definite radiological evidence of loosening or of narrowing of the femoral neck exceeding 10% of its width. There were 23 revisions (3.8%), giving an overall survival of 95% (95% confidence interval 85.3 to 99.2) at seven years. Fractured neck of femur in 12 hips was the most common indication for revision, followed by aseptic loosening in four. In three hips (three patients) (0.5%), failure was possibly related to metal debris. Considering that these patients are young and active these results are good, and support the use of resurfacing. Further study is needed to address the early failures, particularly those related to fracture and metal debris

Aims. Fretting and corrosion at the modular head/neck junction, known as trunnionosis, in total hip arthroplasty (THA) is a cause of adverse reaction to metal debris (ARMD). We describe the outcome of revision of metal-on-polyethylene (MoP) THA for ARMD due to trunnionosis with emphasis on the risk of major complications. Patients and Methods. A total of 36 patients with a MoP THA who underwent revision for ARMD due to trunnionosis were identified. Three were excluded as their revision had been to another metal head. The remaining 33 were revised to a ceramic head with a titanium sleeve. We describe the presentation, revision findings, and risk of complications in these patients. Results. The patients presented with pain, swelling, stiffness, or instability and an inflammatory mass was confirmed radiologically. Macroscopic material deposition on the trunnion was seen in all patients, associated with ARMD. Following revision, six (18.2%) dislocated, requiring further revision in four. Three (9.1%) developed a deep infection and six (18.2%) had significant persistent pain without an obvious cause. One developed a femoral artery thrombosis after excision of an iliofemoral pseudotumor, requiring a thrombectomy. Conclusion. The risk of serious complications following revision MoP THA for ARMD associated with trunnionosis is high. In the presence of extensive tissue damage, a constrained liner or dual mobility construct is recommended in these patients. Cite this article: Bone Joint J 2018;100-B:720–4

Objectives. This study aimed to characterise and qualitatively grade the severity of the corrosion particles released into the hip joint following taper corrosion. Methods. The 26 cases examined were CoC/ABG Modular (n = 13) and ASR/SROM (n = 13). Blood serum metal ion levels were collected before and after revision surgery. The haematoxylin and eosin tissue sections were graded on the presence of fibrin exudates, necrosis, inflammatory cells and corrosion products. The corrosion products were identified based on visible observation and graded on abundance. Two independent observers blinded to the clinical patient findings scored all cases. Elemental analysis was performed on corrosion products within tissue sections. X-Ray diffraction was used to identify crystalline structures present in taper debris. Results. The CoC/ABG Modular patients had a mean age of 64.6 years (49.4 to 76.5) and ASR/SROM patients had a mean age of 58.2 years (33.3 to 85.6). The mean time in situ for CoC/ABG was 4.9 years (2 to 6.4) and ASR/SROM was 6.1 years (2.5 to 8.1). The blood serum metal ion concentrations reduced following revision surgery with the exception of Cr levels within CoC/ABG. The grading of tissue sections showed that the macrophage response and metal debris were significantly higher for the ASR/SROM patients (p < 0.001). The brown/red particles were significantly higher for ASR/SROM (p < 0.001). The taper debris contained traces of titanium oxide, chromium oxide and aluminium nitride. Conclusion. This study characterised and qualitatively graded the severity of the corrosion particles released into the hip joint from tapers that had corrosion damage. Cite this article: S. Munir, R. A. Oliver, B. Zicat, W. L. Walter, W. K. Walter, W. R. Walsh. The histological and elemental characterisation of corrosion particles from taper junctions. Bone Joint Res 2016;5:370–378. DOI: 10.1302/2046-3758.59.2000507

We report 17 patients (20 hips) in whom metal-on-metal resurfacing had been performed and who presented with various symptoms and a soft-tissue mass which we termed a pseudotumour. Each patient underwent plain radiography and in some, CT, MRI and ultrasonography were also performed. In addition, histological examination of available samples was undertaken. All the patients were women and their presentation was variable. The most common symptom was discomfort in the region of the hip. Other symptoms included spontaneous dislocation, nerve palsy, a noticeable mass or a rash. The common histological features were extensive necrosis and lymphocytic infiltration. To date, 13 of the 20 hips have required revision to a conventional hip replacement. Two are awaiting revision. We estimate that approximately 1% of patients who have a metal-on-metal resurfacing develop a pseudotumour within five years. The cause is unknown and is probably multifactorial. There may be a toxic reaction to an excess of particulate metal wear debris or a hypersensitivity reaction to a normal amount of metal debris. We are concerned that with time the incidence of these pseudotumours may increase. Further investigation is required to define their cause

There is widespread concern regarding the incidence of adverse soft-tissue reactions after metal-on-metal (MoM) hip replacement. Recent National Joint Registry data have shown clear differences in the rates of failure of different designs of hip resurfacing. Our aim was to update the failure rates related to metal debris for the Articular Surface Replacement (ASR). A total of 505 of these were implanted. Kaplan-Meier analysis showed a failure rate of 25% at six years for the ASR resurfacing and of 48.8% for the ASR total hip replacement (THR). Of 257 patients with a minimum follow-up of two years, 67 (26.1%) had a serum cobalt concentration which was greater than 7 μg/l. Co-ordinate measuring machine analysis of revised components showed that all patients suffering adverse tissue reactions in the resurfacing group had abnormal wear of the bearing surfaces. Six THR patients had relatively low rates of articular wear, but were found to have considerable damage at the trunion-taper interface. Our results suggest that wear at the modular junction is an important factor in the development of adverse tissue reactions after implantation of a large-diameter MoM THR

Trabecular metal (TM) augments are a relatively new option for reconstructing segmental bone loss during acetabular revision. We studied 34 failed hip replacements in 34 patients that were revised between October 2003 and March 2010 using a TM acetabular shell and one or two augments. The mean age of the patients at the time of surgery was 69.3 years (46 to 86) and the mean follow-up was 64.5 months (27 to 107). In all, 18 patients had a minor column defect, 14 had a major column defect, and two were associated with pelvic discontinuity. The hip centre of rotation was restored in 27 patients (79.4%). The Oxford hip score increased from a mean of 15.4 points (6 to 25) before revision to a mean of 37.7 (29 to 47) at the final follow-up. There were three aseptic loosenings of the construct, two of them in the patients with pelvic discontinuity. One septic loosening also occurred in a patient who had previously had an infected hip replacement. The augments remained stable in two of the failed hips. Whenever there was a loose acetabular component in contact with a stable augment, progressive metal debris shedding was evident on the serial radiographs. Complications included another deep infection treated without revision surgery. Good clinical and radiological results can be expected for bone-deficient acetabula treated by a TM cup and augment, but for pelvic discontinuities this might not be a reliable option. Cite this article: Bone Joint J 2013;95-B:166–72

There are no recent studies comparing cable with wire for the fixation of osteotomies or fractures in total hip replacement (THR). Our objective was to evaluate the five-year clinical and radiological outcomes and complication rates of the two techniques. We undertook a review including all primary and revision THRs performed in one hospital between 1996 and 2005 using cable or wire fixation. Clinical and radiological evaluation was performed five years post-operatively. Cables were used in 51 THRs and wires in 126, and of these, 36 THRs with cable (71%) and 101 with wire (80%) were evaluated at follow-up. The five-year radiographs available for 33 cable and 91 wire THRs revealed rates of breakage of fixation of 12 of 33 (36%) and 42 of 91 (46%), respectively. With cable there was a significantly higher risk of metal debris (68% vs 9%; adjusted relative risk (RR) 6.6; 95% confidence interval (CI) 3.0 to 14.1), nonunion (36% vs 21%; adjusted RR 2.0; 95% CI 1.0 to 3.9) and osteolysis around the material, acetabulum or femur (61% vs 19%; adjusted RR 3.9; 95% CI 2.3 to 6.5). Cable breakage increased the risk of osteolysis to 83%. There was a trend towards foreign-body reaction and increased infection with cables. Clinical results did not differ between the groups. In conclusion, we found a higher incidence of complications and a trend towards increased infection and foreign-body reaction with the use of cables