Alumina–alumina bearings are among the most resistant to wear in total hip replacement. Examination of their surfaces is one way of comparing damage caused by wear of hip joints simulated in vitro to that seen in explanted bearings. The aim of this study was to determine whether second-generation ceramic bearings exhibited a better pattern of wear than those reported in the literature for first-generation bearings. We considered both macro- and microscopic findings.

We found that long-term alumina wear in association with a loose acetabular component could be categorised into three groups. Of 20 specimens, four had ‘low wear’, eight ‘crescent wear’ and eight ‘severe wear’, which was characterised by a change in the physical shape of the bearing and a loss of volume. This suggests that the wear in alumina–alumina bearings in association with a loose acetabular component may be variable in pattern, and may explain, in part, why the wear of a ceramic head in vivo may be greater than that seen after in vitro testing.

Aims

The purpose of this study was to assess mid-term survivorship following primary total knee arthroplasty (TKA) with Optetrak Logic components and identify the most common revision indications at a single institution.

Aims

The aim of this study was to longitudinally compare the clinical and radiological outcomes of anatomical total shoulder arthroplasty (aTSA) up to long-term follow-up, when using cemented keel, cemented peg, and hybrid cage peg glenoid components and the same humeral system.

The issues surrounding raised levels of metal ions in the blood following large head metal-on-metal total hip replacement (THR), such as cobalt and chromium, have been well documented. Despite the national popularity of uncemented metal-on-polyethylene (MoP) THR using a large-diameter femoral head, few papers have reported the levels of metal ions in the blood following this combination. Following an isolated failure of a 44 mm Trident–Accolade uncemented THR associated with severe wear between the femoral head and the trunnion in the presence of markedly elevated levels of cobalt ions in the blood, we investigated the relationship between modular femoral head diameter and the levels of cobalt and chromium ions in the blood following this THR. A total of 69 patients received an uncemented Trident–Accolade MoP THR in 2009. Of these, 43 patients (23 men and 20 women, mean age 67.0 years) were recruited and had levels of cobalt and chromium ions in the blood measured between May and June 2012. The patients were then divided into three groups according to the diameter of the femoral head used: 12 patients in the 28 mm group (controls), 18 patients in the 36 mm group and 13 patients in the 40 mm group. A total of four patients had identical bilateral prostheses in situ at phlebotomy: one each in the 28 mm and 36 mm groups and two in the 40 mm group. There was a significant increase in the mean levels of cobalt ions in the blood in those with a 36 mm diameter femoral head compared with those with a 28 mm diameter head (p = 0.013). The levels of cobalt ions in the blood were raised in those with a 40 mm diameter head but there was no statistically significant difference between this group and the control group (p = 0.152). The levels of chromium ions in the blood were normal in all patients. The clinical significance of this finding is unclear, but we have stopped using femoral heads with a diameter of ≤ 36 mm, and await further larger studies to clarify whether, for instance, this issue particularly affects this combination of components. Cite this article: Bone Joint J 2014;96-B:43–7

We examined 86 polyethylene inserts, retrieved from total and unicompartmental knee prostheses after an average of 39.5 months in situ, grading them from 0 to 3 for seven modes of polyethylene degradation. Severe wear, with delamination or deformation, was observed in 51% of the implants, and was associated with time in situ, lack of congruency, thin polyethylene, third-body wear debris, and heat-pressed polyethylene. Significant under-surface cold flow was identified in some areas of unsupported polyethylene, and was associated with delamination in the load-bearing areas of thin inserts above screw holes in the underlying metal tray. We recommend the use of thicker polyethylene inserts, particularly in young, active patients and in designs with screw holes in the tibial baseplate. Thin polyethylene inserts which are at risk for accelerated wear and premature failure should be monitored radiographically at annual intervals

Aims

This study aimed to determine outcomes of isolated tibial insert exchange (ITIE) during revision total knee arthroplasty (TKA).

Aims

The aim of this study was to establish the results of isolated exchange of the tibial polyethylene insert in revision total knee arthroplasty (RTKA) in patients with well-fixed femoral or tibial components. We report on a series of RTKAs where only the polyethylene was replaced, and the patients were followed for a mean of 13.2 years (10.0 to 19.1).

We compared and quantified the modes of failure and patterns of wear of 11 Mittelmeier and 11 Ceraver-Ostal retrieved alumina-alumina hip prostheses with reference to the corresponding clinical and radiological histories. Macroscopic wear was assessed using a three-dimensional co-ordinate measuring machine. Talysurf contacting profilometry was used to measure surface roughness on a microscopic scale and SEM to determine mechanisms of wear at the submicron level. The components were classified into one of three categories of wear: low (no visible/measurable wear), stripe (elliptical wear stripe on the heads and larger worn areas on the cups) and severe (macroscopic wear, large volumes of material lost). Overall, the volumetric wear of the alumina-alumina prostheses was substantially less than the widely used metal and ceramic-on-polyethylene combinations. By identifying and eliminating the factors which accelerate wear, it is expected that the lifetime of these devices can be further increased

Osteoarthritis of the medial compartment of the knee often shows a specific pattern of anterior wear. Review of our revisions from a series of medial metal-backed Brigham unicondylar knee replacements performed between 1983 and 1989 showed that this wear pattern was common on the tibial polyethylene surface. We reviewed these cases retrospectively to compare the pattern of preoperative erosion with the wear of the prosthesis. In all 14 knees with severe anterior wear in a unicompartmental replacement, the prearthroplasty radiographs showed similar patterns, suggesting that the implanted tibial component may continue to be subjected to the same localised stresses that precipitated the failure of the original articular cartilage. Many tibial components implanted during the 1980s had an unacceptably thin anterior rim of polyethylene and it seems that greater thickness is essential at the anterior and peripheral margins of the tibial plateau

Aims

We present our experience of using a metal-backed prosthesis and autologous bone graft to treat gross glenoid bone deficiency.

A number of studies have reported satisfactory results from the isolated revision of an acetabular component. However, many of these studies reported only the short- to intermediate-term results of heterogeneous bearing surfaces in a mixed age group.

We present our experience of using a ceramic-on-ceramic (CoC) bearing for isolated revision of an uncemented acetabular component in 166 patients (187 hips) who were under the age of 50 years at the time of revision. There were 78 men and 88 women with a mean age of 47.4 years (28 to 49). The most common reason for revision was polyethylene wear and acetabular osteolysis in 123 hips (66%), followed by aseptic loosening in 49 hips (26%).

We report the clinical and radiological outcome, complication rate, and survivorship of this group. The mean duration of follow-up was 15.6 years (11 to 19).

The mean pre-operative Harris hip score was 33 points (1 to 58), and improved to a mean of 88 points (51 to 100) at follow-up. The mean pre-operative total Western Ontario and McMaster Universities Osteoarthritis Index score was 63.2 (43 to 91) and improved to 19.8 points (9 to 61) post-operatively. Overall, 153 of 166 patients (92%) were satisfied with their outcome. Kaplan–Meier survivorship analysis, with revision or radiological evidence of implant failure (13 patients, 8%) as end-points, was 92% at 15 years (95% confidence interval 0.89 to 0.97).

Isolated revision of a cementless acetabular component using a CoC bearing gives good results in patients under 50 years of age.

Cite this article: Bone Joint J 2015;97-B:1197–1203.

Aims

We wished to investigate the influence of metal debris exposure on the subsequent immune response and resulting soft-tissue injury following metal-on-metal (MoM) hip arthroplasty. Some reports have suggested that debris generated from the head-neck taper junction is more destructive than equivalent doses from metal bearing surfaces.

Objectives

Third-body wear is believed to be one trigger for adverse results with metal-on-metal (MOM) bearings. Impingement and subluxation may release metal particles from MOM replacements. We therefore challenged MOM bearings with relevant debris types of cobalt–chrome alloy (CoCr), titanium alloy (Ti6Al4V) and polymethylmethacrylate bone cement (PMMA).

Components from 73 failed knee replacements (TKRs) consisting of rotating-platform, mobile-bearing and fixed-bearing implants were examined to assess the patterns of wear. The patterns were divided into low-grade (burnishing, abrasion and cold flow) and high-grade (scratching, pitting/metal embedding and delamination) to assess the severity of the wear of polyethylene.

The rotating-platform group had a higher incidence of low-grade wear on the upper surface compared with the fixed-bearing group. By contrast, high-grade wear comprising scratching, pitting and third-body embedding was seen on the lower surface. Linear regression analysis showed a significant correlation of the wear scores between the upper and lower surfaces of the tibial insert (R² = 0.29, p = 0.04) for the rotating-platform group, but no significant correlation was found for the fixed-bearing counterpart.

This suggests that high-grade wear patterns on the upper surface are reduced with the rotating-platform design. However, the incidence of burnishing, pitting/third-body embedding and scratching wear patterns on the lower surface was higher compared with that in the fixed-bearing knee.

We measured the contact areas and contact stresses at the post-cam mechanism of a posterior-stabilised total knee arthroplasty when a posterior force of 500 N was applied to the Kirschner Performance, Scorpio Superflex, NexGen LPS Flex Fixed, and NexGen LPS Flex Mobile knee systems. Measurements were made at 90°, 120°, and 150° of flexion both in neutral rotation and 10° of internal rotation of the tibial component. Peak contact stresses at 90°, 120°, and 150° were 24.0, 33.9, and 28.8 MPa, respectively, for the Kirschner; 26.0, 32.4, and 22.1 MPa, respectively, for the Scorpio; and 34.1, 31.5, and 32.5 MPa, respectively, for the NexGen LPS Flex Fixed. With an internally rotated tibia, the contact stress increased significantly with all the fixed-bearing arthroplasties but not with the NexGen LPS Flex Mobile arthroplasty. The post-cam design should be modified in order to provide a larger contact area whilst avoiding any impingement and edge loading.

We investigated the characteristics of patients who achieved Japanese-style deep flexion (seiza-sitting) after total knee replacement (TKR) and measured three-dimensional positioning and the contact positions of the femoral and tibial components. Seiza-sitting was achieved after surgery by 23 patients (29 knees) of a series of 463 TKRs in 341 patients. Pre-operatively most of these patients were capable of seiza-sitting, had a lower body mass index and a favourable attitude towards the Japanese lifestyle (27 of 29 knees). According to two-/three-dimensional image registration analysis in the seiza-sitting position, flexion, varus and internal rotation angles of the tibial component relative to the femoral component had means of 148° (sd 8.0), 1.9° (sd 3.2) and 13.4° (sd 5.9), respectively. Femoral surface contact positions tended to be close to the posterior edge of the tibial polyethylene insert, particularly in the lateral compartment, but only 8.3% (two of 24) of knees showed femoral subluxation over the posterior edge. The mean contact positions of the femoral cam on the tibial post were located 7.8 mm (sd 1.5) proximal to the lowest point of the polyethylene surface and 5.5 mm (sd 0.9) medial to the centre of the post, indicating that the post-cam contact position translated medially during seiza-sitting, but not proximally. Collectively, the seiza-sitting position seems safe against component dislocation, but the risks of posterior edge loading and breakage of the tibial polyethylene post remain.

Cite this article: Bone Joint J 2013;95-B:782–7.

We report on the long-term results of 163 bicruciate-retaining Hermes 2C total knee replacements in 130 patients at a mean follow-up of 22.4 years (20.3 to 23.5). Even when the anterior cruciate ligament had a partially degenerative appearance it was preserved as long as the knee had a normal anterior drawer and Lachman’s test pre-operatively. The description and surgical technique of this minimally constrained prosthesis were published in 1983 and the ten-year clinical results in 1999.

A total of 12% of the knees (20 of 163) in this study were revised because of wear of the polyethylene tibial insert. Excellent stability was achieved and the incidence of aseptic component loosening was 4.3% (seven of 163). The survival rate using revision for any reason as the endpoint was 82% (95% confidence interval 76.2 to 88.0).

Although this series included a relatively small number of replacements, it demonstrated that the anterior cruciate ligament, even when partially degenerated at the time of TKR, remained functional and provided adequate stability at a long-term follow-up.

Cite this article: Bone Joint J 2013;95-B:917–22.

The practice of removing a well-fixed cementless femoral component is associated with high morbidity. Ceramic bearing couples are low wearing and their use minimises the risk of subsequent further revision due to the production of wear debris. A total of 165 revision hip replacements were performed, in which a polyethylene-lined acetabular component was revised to a new acetabular component with a ceramic liner, while retaining the well-fixed femoral component. A titanium sleeve was placed over the used femoral trunnion, to which a ceramic head was added. There were 100 alumina and 65 Delta bearing couples inserted.

The mean Harris hip score improved significantly from 71.3 (9.0 to 100.0) pre-operatively to 91.0 (41.0 to 100.0) at a mean follow up of 4.8 years (2.1 to 12.5) (p < 0.001). No patients reported squeaking of the hip.

There were two fractures of the ceramic head, both in alumina bearings. No liners were seen to fracture. No fractures were observed in components made of Delta ceramic. At 8.3 years post-operatively the survival with any cause of failure as the endpoint was 96.6% (95% confidence interval (CI) 85.7 to 99.3) for the acetabular component and 94.0% (95% CI 82.1 to 98.4) for the femoral component.

The technique of revising the acetabular component in the presence of a well-fixed femoral component with a ceramic head placed on a titanium sleeve over the used trunnion is a useful adjunct in revision hip practice. The use of Delta ceramic is recommended.

Cite this article: Bone Joint J 2013;95-B:333–8.

Revision after failed femoral components may be technically demanding due to loss of peri-prosthetic bone. This retrospective study evaluated the long-term results of femoral revision using the cementless Wagner Self-Locking stem. Between 1992 and 1998, 68 consecutive hips in 66 patients underwent femoral revision using this implant. A total of 25 patients died from unrelated causes without further revision; the remaining 41 hips in 41 patients (12 men and 29 women) with a mean age of 61 years (29 to 80) were reviewed at a mean follow-up of 13.9 years (10.4 to 15.8). A transfemoral approach was used in 32 hips. A total of five stems required further revision because of infection in two, progressive subsidence in two and recurrent dislocation in one. Four hips had dislocated and eight stems had subsided ≥ 10 mm. The mean Harris hip score improved from 33 points pre-operatively to 75 points at final follow-up (p < 0.001). In all, 33 stems (91.7%) showed radiological signs of stable bone fixation. The cumulative survival rates at 15.8 years with femoral revision for any reason and for stem failure as the endpoints were 92.0% (95% confidence interval (CI) 86.0% to 98.4%) and 96.6% (95% CI 92.2% to 100%), respectively. The survivorship with revision and ≥ 10 mm migration of the stem as the endpoint was 83.6% (95% CI 76.6% to 91.4%).

This study shows quite good survival and moderate clinical outcome when using a monoblock tapered titanium stem for supporting the regeneration of bone in complex revision hip surgery.

Mechanical failure because of wear or fracture of the polyethylene tibial post in posteriorly-stabilised total knee replacements has been extensively described. In this study of 12 patients with a clinically and radiologically successful NexGen LPS posteriorly-stabilised prosthesis impingement of the anterior tibial post was evaluated in vivo in three dimensions during gait using radiologically-based image-matching techniques.

Impingement was observed in all images of the patients during the stance phase, although the NexGen LPS was designed to accommodate 14° of hyperextension of the component before impingement occurred. Impingement arises as a result of posterior translation of the femur during the stance phase. Further attention must therefore be given to the configuration of the anterior portion of the femoral component and the polyethylene post when designing posteriorly-stabilised total knee replacements.

A modular layered acetabular component (metal-polyethylene-ceramic) was developed in Japan for use in alumina ceramic-on-ceramic total hip replacement. Between May 1999 and July 2000, we performed 35 alumina ceramic-on-ceramic total hip replacements in 30 consecutive patients, using this layered component and evaluated the clinical and radiological results over a mean follow-up of 5.8 years (5 to 6.5). A total of six hips underwent revision, one for infection, two for dislocation with loosening of the acetabular component, two for alumina liner fractures and one for component dissociation with pelvic osteolysis. There were no fractures of the ceramic heads, and no loosening of the femoral or acetabular component in the unrevised hips was seen at final follow-up. Osteolysis was not observed in any of the unrevised hips. The survivorship analysis at six years after surgery was 83%. The layered acetabular component in our experience, has poor durability because of unexpected mechanical failures including alumina liner fracture and component dissociation.

There have been few reports in the literature of total elbow arthroplasty extending beyond 10 to 15 years. We reviewed 40 patients (41 elbows) with a mean age of 56 years (19 to 83) who had undergone a Coonrad/Coonrad-Morrey elbow arthroplasty by one surgeon for various diagnoses between 1974 and 1994. Surgical selection excluded patients with previous elbow infection or who refused to accept a sedentary level of elbow activity postoperatively. Objective data were collected from charts, radiographs, clinical photographs and supplemented by the referring orthopaedic surgeons’ records and radiographs if health or distance prevented a patient from returning for final review. Subjective outcome was defined by patient satisfaction.

Of the 41 elbows, 21 were functional between 10 and 14 years after operation, ten between 15 and 19 years and ten between 20 and 31 years. There were 14 complications and 13 revisions, but no cases of acute infection, or permanent removal of any implant.

We reviewed 123 second-generation uncemented total hip replacements performed on 115 patients by a single surgeon between 1993 and 1994. The acetabular component used in all cases was a fully porous-coated threaded hemispheric titanium shell (T-Tap ST) with a calcium ion stearate-free, isostatically compression-moulded polyethylene liner. The titanium femoral component used was a Taperloc with a reduced distal stem. No patient was lost to follow-up. Complete clinical and radiological follow-up was obtained for all 123 hips at a mean of 14 years (12 to 16). One femoral component was revised after a fracture, and three acetabular components for aseptic loosening. No additional femoral or acetabular components were judged loose by radiological criteria. Mild proximal femoral osteolysis was identified in two hips and minor acetabular osteolysis was present in four. The mean rate of penetration of the femoral head was 0.036 mm/year (0.000 to 0.227).

These findings suggest that refinements in component design may be associated with excellent long-term fixation in cementless primary total hip replacement.

Isolated patellofemoral osteoarthritis can be a disabling disease. When conservative treatment fails, surgical options can be unpredictable and may be considered too aggressive for middle-aged and active people. We analysed the clinical and radiological results of a new coronal osteotomy involving thinning of the patella in a selected group of patients with isolated patellofemoral osteoarthritis. Since 1991, 31 patients (35 knees) have been treated, of whom 34 were available for follow-up at a mean of 9.1 years. The Knee Society Score, the Patellar score and the Short-form-36 questionnaire were used for clinical evaluation. We also examined the radiological features to confirm bone consolidation and assess the progression of osteoarthritis. A significant improvement in the functional scores and radiological parameters was noted. All patients except one were satisfied with the operation. Radiological progression of the patellofemoral osteoarthritis was slowed but radiological femorotibial osteoarthritis progressed in 23 (65%) cases, with a total knee replacement becoming necessary in four cases without technical problems in resurfacing the patella. We compared the results with other forms of surgical treatment reported in the literature.

This treatment offers good clinical and radiological results, presenting an alternative method of managing patellofemoral osteoarthritis.

We describe a cohort of patients with a high rate of mid-term failure following Kinemax Plus total knee replacement inserted between 1998 and 2001. This implant has been recorded as having a survival rate of 96% at ten years. However, in our series the survival rate was 75% at nine years. This was also significantly lower than that of subsequent consecutive series of PFC Sigma knee replacements performed by the same surgeon. No differences were found in the clinical and radiological parameters between the two groups. At revision the most striking finding was polyethylene wear. An independent analysis of the polyethylene components was therefore undertaken. Scanning electron microscopy revealed type 2 fusion defects in the ultra-high molecular weight polyethylene (UHMWPE), which indicated incomplete boundary fusion. Other abnormalities consistent with weak UHMWPE particle interface strength were present in both the explanted inserts and in unused inserts from the same period.

We consider that these type 2 fusion defects are the cause of the early failure of the Kinemax implants. This may represent a manufacturing defect resulting in a form of programmed polyethylene failure.

We analysed at a mean follow-up of 7.25 years the clinical and radiological outcome of 117 patients (125 knees) who had undergone a primary, cemented, modular Freeman-Samuelson total knee replacement. While the tibial and femoral components were cemented, the patellar component was uncemented. A surface-cementing technique was used to secure the tibial components. A total of 82 knees was available for radiological assessment. Radiolucent lines were seen in 41 knees (50%) and osteolytic lesions were seen in 13 knees (16%). Asymptomatic, rotational loosening of the patellar implant was seen in four patients and osteolysis was more common in patients with a patellar resurfacing. Functional outcome scores were available for 41 patients (41 knees, 35%) and the mean Western Ontario McMasters Universities score was 77.5 (sd 19.5) and the cumulative survival was 93.4% at ten years with revision for aseptic loosening as an endpoint. Increased polyethylene wear from modular components, a rotationally-loose patella, and the surface-cementing technique may have contributed to the high rate of osteolysis seen in our study.