Aims

The aim of this study was to evaluate the suitability of the tapered cone stem in total hip arthroplasty (THA) in patients with excessive femoral anteversion and after femoral osteotomy.

Aims

This study reports the results of 38 total hip arthroplasties (THAs) in 33 patients aged less than 50 years, using the JRI Furlong hydroxyapatite ceramic (HAC)-coated femoral component.

Aims

To compare long-term survival of all-cemented and hybrid total hip arthroplasty (THA) using the Exeter Universal stem.

Aims. Our aim in this study was to describe a continuing review of 11 total hip arthroplasties using 22.225 mm Alumina ceramic femoral heads on a Charnley flanged femoral component, articulating against a silane crosslinked polyethylene. Patients and Methods. Nine patients (11 THAs) were reviewed at a mean of 27.5 years (26 to 28) post-operatively. Outcome was assessed using the d’Aubigne and Postel, and Charnley scores and penetration was recorded on radiographs. In addition, the oxidation of a 29-year-old shelf-aged acetabular component was analysed. Results. The mean clinical outcome scores remained excellent at final follow-up. The mean total penetration remained 0.41 mm (0.40 to 0.41). There was no radiographic evidence of acetabular or femoral loosening or osteolysis. There was negligible oxidation in the shelf-aged sample despite gamma irradiation and storage in air. Conclusion. These results highlight the long-term stability and durability of this type of crosslinked, antioxidant containing polyethylene when used in combination with a small diameter alumina ceramic femoral head. Cite this article: Bone Joint J 2017;99-B:1286–9

Aims

Ceramic-on-ceramic (CoC) bearings in total hip arthroplasty (THA) are commonly used, but concerns exist regarding ceramic fracture. This study aims to report the risk of revision for fracture of modern CoC bearings and identify factors that might influence this risk, using data from the National Joint Registry (NJR) for England, Wales, Northern Ireland and the Isle of Man.

Aims

To determine the effect of a change in design of a cementless ceramic acetabular component in fixation and clinical outcome after total hip arthroplasty

Aims

We conducted a prospective study of a delta ceramic total hip arthroplasty (THA) to determine the rate of ceramic fracture, to characterise post-operative noise, and to evaluate the mid-term results and survivorship.

Objectives

Studies reporting specifically on squeaking in total hip arthroplasty have focused on cementless, and not on hybrid, fixation. We hypothesised that the cement mantle of the femur might have a damping effect on the sound transmitted through the metal stem. The objective of this study was to test the effect of cement on sound propagation along different stem designs and under different fixation conditions.

Most published randomised controlled trials which compare the rates of wear of conventional and cross-linked (XL) polyethylene (PE) in total hip arthroplasty (THA) have described their use with a cementless acetabular component.

We conducted a prospective randomised study to assess the rates of penetration of two distinct types of PE in otherwise identical cemented all-PE acetabular components.

A total of 100 consecutive patients for THA were randomised to receive an acetabular component which had been either highly XL then remelted or moderately XL then annealed.

After a minimum of eight years follow-up, 38 hips in the XL group and 30 hips in the annealed group had complete data (mean follow-up of 9.1 years (7.6 to 10.7) and 8.7 years (7.2 to 10.2), respectively). In the XL group, the steady state rate of penetration from one year onwards was -0.0002 mm/year (sd 0.108): in the annealed group it was 0.1382 mm/year (sd 0.129) (Mann–Whitney U test, p < 0.001). No complication specific to either material was recorded.

These results show that the yearly linear rate of femoral head penetration can be significantly reduced by using a highly XLPE cemented acetabular component.

Cite this article: Bone Joint J 2015;97-B:1458–62.

This study reports the results of 38 total hip arthroplasties (THAs) in 33 patients aged <  50 years, using the JRI Furlong hydroxyapatite ceramic (HAC)-coated femoral component. This represents an update of previous reports of the same cohort at ten and 16 years, which were reported in 2004 and 2009, respectively. We describe the survival, radiological and functional outcomes at a mean follow-up of 21 years (17 to 25). Of the surviving 34 THAs, one underwent femoral revision for peri-prosthetic fracture after 21 years, and one patient (one hip) was lost to follow-up. Using aseptic loosening as the end-point, 12 hips (31.5%) needed acetabular revision but none needed femoral revision, demonstrating 100% survival (95% confidence interval 89 to 100).

In young patients with high demands, the Furlong HAC–coated femoral component gives excellent long-term results.

Cite this article: Bone Joint J 2015;97-B:749–54.

Large femoral heads have become popular in total hip replacement (THR) as a method of reducing the risk of dislocation. However, if large heads are used in ceramic-on-ceramic THR, the liner must be thinner, which may increase the risk of fracture. To compare the rates of ceramic fracture and dislocation between 28 mm and 32 mm ceramic heads, 120 hips in 109 patients (51 men and 58 women, mean age 49.2 years) were randomised to THR with either a 28 mm or a 32 mm ceramic articulation. A total of 57/60 hips assigned to the 28 mm group and 55/60 hips assigned to the 32 mm group were followed for at least five years. No ceramic component fractures occured in any patient in either group. There was one dislocation in the 32 mm group and none in the 28 mm group (p = 0.464). No hip had detectable wear, focal osteolysis or prosthetic loosening. In our small study the 32 mm ceramic articulation appeared to be safe in terms of ceramic liner fracture.

Cite this article: Bone Joint J 2014;96-B:1459–63.

Large-head metal-on-metal (MoM) total hip replacements (THR) have given rise to concern. Comparative studies of small-head MoM THRs over a longer follow-up period are lacking. Our objective was to compare the incidence of complications such as infection, dislocation, revision, adverse local tissue reactions, mortality and radiological and clinical outcomes in small-head (28 mm) MoM and ceramic-on-polyethylene (CoP) THRs up to 12 years post-operatively.

A prospective cohort study included 3341 THRs in 2714 patients. The mean age was 69.1 years (range 24 to 98) and 1848 (55.3%) were performed in women, with a mean follow-up of 115 months (18 to 201). There were 883 MoM and 2458 CoP bearings. Crude incidence rates (cases/1000 person-years) were: infection 1.3 vs 0.8; dislocation 3.3 vs 3.1 and all-cause revision 4.3 vs 2.2, respectively. There was a significantly higher revision rate after ten years (adjusted hazard ratio 9.4; 95% CI 2.6 to 33.6) in the MoM group, and ten of 26 patients presented with an adverse local tissue reaction at revision. No differences in mortality, osteolysis or clinical outcome were seen.

In conclusion, we found similar results for small-head MoM and CoP bearings up to ten years post-operatively, but after ten years MoM THRs had a higher risk of all-cause revision. Furthermore, the presence of an adverse response to metal debris seen in the small-head MOM group at revision is a cause for concern.

Cite this article: Bone Joint J 2014; 96-B:868–75.

We report on 397 consecutive revision total hip replacements in 371 patients with a mean clinical and radiological follow-up of 12.9 years (10 to 17.7). The mean age at surgery was 69 years (37 to 93). A total of 28 patients (8%) underwent further revision, including 16 (4%) femoral components. In all 223 patients (56%, 233 hips) died without further revision and 20 patients (5%, 20 hips) were lost to follow-up. Of the remaining patients, 209 (221 hips) were available for clinical assessment and 194 (205 hips) for radiological review at mean follow-up of 12.9 years (10 to 17.7).

The mean Harris Hip Score improved from 58.7 (11 to 92) points to 80.7 (21 to 100) (p <  0.001) and the mean Merle d’Aubigné and Postel hip scores at final follow-up were 4.9 (2 to 6), 4.5 (2 to 6) and 4.3 (2 to 6), respectively for pain, mobility and function. Radiographs showed no lucencies around 186 (90.7%) femoral stems with stable bony ingrowth seen in 199 stems (97%). The survival of the S-ROM femoral stem at 15 years with revision for any reason as the endpoint was 90.5% (95% confidence interval (CI) 85.7 to 93.8) and with revision for aseptic loosening as the endpoint 99.3% (95% CI 97.2 to 99.8).

We have shown excellent long-term survivorship and good clinical outcome of a cementless hydroxyapatite proximally-coated modular femoral stem in revision hip surgery.

Cite this article: Bone Joint J 2014;96-B:730–6.

We report the clinical and radiological outcomes of a series of contemporary cementless ceramic-on-ceramic total hip replacements (THRs) at ten years in patients aged ≤ 55 years of age. Pre- and post-operative activity levels are described. A total of 120 consecutive ceramic cementless THRs were performed at a single centre in 110 patients from 1997 to 1999. The mean age of the patients at operation was 45 years (20 to 55). At ten years, four patients had died and six were lost to follow-up, comprising ten hips. The mean post-operative Harris hip score was 94.7 (55 to 100). Radiological analysis was undertaken in 90 available THRs of the surviving 106 hips at final review: all had evidence of stable bony ingrowth, with no cases of osteolysis. Wear was undetectable. There were four revisions. The survival for both components with revision for any cause as an endpoint was 96.5% (95% confidence interval 94.5 to 98.7). The mean modified University of California, Los Angeles activity level rose from a mean of 6.4 (4 to 10) pre-operatively to 9.0 (6 to 10) at the ten-year post-operative period.

Alumina ceramic-on-ceramic bearings in cementless primary THR in this series have resulted in good clinical and radiological outcomes with undetectable rates of wear and excellent function in the demanding younger patient group at ten years.

Cite this article: Bone Joint J 2013;95-B:1603–9.

Symptomatic hip osteonecrosis is a disabling condition with a poorly understood aetiology and pathogenesis. Numerous treatment options for hip osteonecrosis are described, which include non-operative management and joint preserving procedures, as well as total hip replacement (THR). Non-operative or joint preserving treatment may improve outcomes when an early diagnosis is made before the lesion has become too large or there is radiographic evidence of femoral head collapse. The presence of a crescent sign, femoral head flattening, and acetabular involvement indicate a more advanced-stage disease in which joint preserving options are less effective than THR. Since many patients present after disease progression, primary THR is often the only reliable treatment option available. Prior to the 1990s, outcomes of THR for osteonecrosis were poor. However, according to recent reports and systemic reviews, it is encouraging that with the introduction of newer ceramic and/or highly cross-linked polyethylene bearings as well as highly-porous fixation interfaces, THR appears to be a reliable option in the management of end-stage arthritis following hip osteonecrosis in this historically difficult to treat patient population.

Cite this article: Bone Joint J 2013;95-B, Supple A:46–50.

We prospectively assessed the efficacy of a ceramic-on-metal (CoM) hip bearing with uncemented acetabular and femoral components in which cobalt­–chrome acetabular liners and alumina ceramic heads were used. The cohort comprised 94 total hip replacements (THRs) in 83 patients (38 women and 45 men) with a mean age of 58 years (42 to 70). Minimum follow-up was two years. All patients had pre- and post-operative assessment using the Western Ontario and McMaster Universities osteoarthritis index (WOMAC), Oxford hip score and Short-Form 12 scores. All showed a statistically significant improvement from three months post-operatively onwards (all p < 0.001). After two years whole blood metal ion levels were measured and chromosomal analysis was performed. The levels of all metal ions were elevated except vanadium. Levels of chromium, cobalt, molybdenum and titanium were significantly higher in patients who underwent bilateral THR compared with those undergoing unilateral THR (p < 0.001). Chromosomal analysis demonstrated both structural and aneuploidy mutations. There were significantly more breaks and losses than in the normal population (p < 0.001). There was no significant difference in chromosomal aberration between those undergoing unilateral and bilateral procedures (all analyses p ≥ 0.62). The use of a CoM THR is effective clinically in the short-term, with no concerns, but the significance of high metal ion levels and chromosomal aberrations in the long-term remains unclear. Cite this article: Bone Joint J 2013;95-B:1040–44

The practice of removing a well-fixed cementless femoral component is associated with high morbidity. Ceramic bearing couples are low wearing and their use minimises the risk of subsequent further revision due to the production of wear debris. A total of 165 revision hip replacements were performed, in which a polyethylene-lined acetabular component was revised to a new acetabular component with a ceramic liner, while retaining the well-fixed femoral component. A titanium sleeve was placed over the used femoral trunnion, to which a ceramic head was added. There were 100 alumina and 65 Delta bearing couples inserted.

The mean Harris hip score improved significantly from 71.3 (9.0 to 100.0) pre-operatively to 91.0 (41.0 to 100.0) at a mean follow up of 4.8 years (2.1 to 12.5) (p < 0.001). No patients reported squeaking of the hip.

There were two fractures of the ceramic head, both in alumina bearings. No liners were seen to fracture. No fractures were observed in components made of Delta ceramic. At 8.3 years post-operatively the survival with any cause of failure as the endpoint was 96.6% (95% confidence interval (CI) 85.7 to 99.3) for the acetabular component and 94.0% (95% CI 82.1 to 98.4) for the femoral component.

The technique of revising the acetabular component in the presence of a well-fixed femoral component with a ceramic head placed on a titanium sleeve over the used trunnion is a useful adjunct in revision hip practice. The use of Delta ceramic is recommended.

Cite this article: Bone Joint J 2013;95-B:333–8.

In this paper, we will consider the current role of metal-on-metal bearings by looking at three subtypes of MoM hip arthroplasty separately: Hip resurfacing, large head (> 36 mm) MoM THA and MoM THA with traditional femoral head sizes.

A moderator and panel of five experts led an interactive session in discussing five challenging and interesting patient case presentations involving surgery of the hip. The hip pathologies reviewed included failed open reduction internal fixation of subcapital femoral neck fracture, bilateral hip disease, evaluation of pain after metal-on-metal hip arthroplasty, avascular necrosis, aseptic loosening secondary to osteolysis and polyethylene wear, and management of ceramic femoral head fracture.

We analysed 54 alumina ceramic-on-ceramic bearings from total hip replacements retrieved at one centre after a mean duration of 3.5 years (0.2 to 10.6) in situ. These implants were obtained from 54 patients (16 men and 38 women) with a mean age of 67 years (33 to 88) who underwent revision for a variety of reasons. Posterior edge loading was found in the majority of these retrievals (32 out of 54). Anterosuperior edge loading occurred less often but produced a higher rate of wear. Stripe wear on the femoral heads had a median volumetric wear rate of 0.2 mm³/year (0 to 7.2). The wear volume on the femoral heads corresponded to the width of edge wear on the matching liner. Anteversion of the acetabular component was found to be a more important determinant than inclination for wear in ceramic bearings. Posterior edge loading may be considered to be a normal occurrence in ceramic-on-ceramic bearings, with minimal clinical consequences. Edge loading should be defined as either anterosuperior or posterior, as each edge loading mechanism may result in different clinical implications.