The survival of humeral hemiarthroplasties in patients with relatively intact glenoid cartilage could theoretically be extended by minimizing the associated postoperative glenoid erosion. Ceramic has gained attention as an alternative to metal as a material for hemiarthroplasties because of its superior tribological properties. The aim of this study was to assess the in vitro wear performance of ceramic and metal humeral hemiarthroplasties on natural glenoids. Intact right cadaveric shoulders from donors aged between 50 and 65 years were assigned to a ceramic group (n = 8, four male cadavers) and a metal group (n = 9, four male cadavers). A dedicated shoulder wear simulator was used to simulate daily activity by replicating the relevant joint motion and loading profiles. During testing, the joint was kept lubricated with diluted calf serum at room temperature. Each test of wear was performed for 500,000 cycles at 1.2 Hz. At intervals of 125,000 cycles, micro-CT scans of each glenoid were taken to characterize and quantify glenoid wear by calculating the change in the thickness of its articular cartilage.Aims
Methods
Bone defects are frequently observed in anterior shoulder instability. Over the last decade, knowledge of the association of bone loss with increased failure rates of soft-tissue repair has shifted the surgical management of chronic shoulder instability. On the glenoid side, there is no controversy about the critical glenoid bone loss being 20%. However, poor outcomes have been described even with a subcritical glenoid bone defect as low as 13.5%. On the humeral side, the Hill-Sachs lesion should be evaluated concomitantly with the glenoid defect as the two sides of the same bipolar lesion which interact in the instability process, as described by the glenoid track concept. We advocate adding remplissage to every Bankart repair in patients with a Hill-Sachs lesion, regardless of the glenoid bone loss. When critical or subcritical glenoid bone loss occurs in active patients (> 15%) or bipolar off-track lesions, we should consider anterior glenoid bone reconstructions. The techniques have evolved significantly over the last two decades, moving from open procedures to arthroscopic, and from screw fixation to metal-free fixation. The new arthroscopic techniques of glenoid bone reconstruction procedures allow precise positioning of the graft, identification, and treatment of concomitant injuries with low morbidity and faster recovery. Given the problems associated with bone resorption and metal hardware protrusion, the new metal-free techniques for Latarjet or free bone block procedures seem a good solution to avoid these complications, although no long-term data are yet available. Cite this article:
Uncemented implants are now commonly used at reimplantation of a two-stage revision total hip arthoplasty (THA) following periprosthetic joint infection (PJI). However, there is a paucity of data on the performance of the most commonly used uncemented femoral implants – modular fluted tapered (MFT) femoral components – in this setting. This study evaluated implant survival, radiological results, and clinical outcomes in a large cohort of reimplantation THAs using MFT components. We identified 236 reimplantation THAs from a single tertiary care academic institution from September 2000 to September 2020. Two designs of MFT femoral components were used as part of an established two-stage exchange protocol for the treatment of PJI. Mean age at reimplantation was 65 years (SD 11), mean BMI was 32 kg/m2 (SD 7), and 46% (n = 109) were female. Mean follow-up was seven years (SD 4). A competing risk model accounting for death was used.Aims
Methods
Dual-mobility (DM) components are increasingly used to prevent and treat dislocation after total hip arthroplasty (THA). Intraprosthetic dissociation (IPD) is a rare complication of DM that is believed to have decreased with contemporary implants. This study aimed to report incidence, treatment, and outcomes of contemporary DM IPD. A total of 1,453 DM components were implanted at a single academic institution between January 2010 and December 2021: 695 in primary and 758 in revision THA. Of these, 49 presented with a dislocation of the large DM head and five presented with an IPD. At the time of closed reduction of the large DM dislocation, six additional IPDs occurred. The mean age was 64 years (SD 9.6), 54.5% were female (n = 6), and mean follow-up was 4.2 years (SD 1.8). Of the 11 IPDs, seven had a history of instability, five had abductor insufficiency, four had prior lumbar fusion, and two were conversions for failed fracture management.Aims
Methods
Aims. Biofilm infections are among the most challenging complications in orthopaedics, as bacteria within the biofilms are protected from the host immune system and many antibiotics. Halicin exhibits broad-spectrum activity against many planktonic bacteria, and previous studies have demonstrated that halicin is also effective against Staphylococcus aureus biofilms grown on polystyrene or polypropylene substrates. However, the effectiveness of many antibiotics can be substantially altered depending on which orthopaedically relevant substrates the biofilms grow. This study, therefore, evaluated the activity of halicin against less mature and more mature S. aureus biofilms grown on titanium alloy,
Oxidized zirconium (OxZi) and highly cross-linked polyethylene (HXLPE) were developed to minimize wear and risk of osteolysis in total hip arthroplasty (THA). However, retrieval studies have shown that scratched femoral heads may lead to runaway wear, and few reports of long-term results have been published. The purpose of this investigation is to report minimum ten-year wear rates and clinical outcomes of THA with OxZi femoral heads on HXLPE, and to compare them with a retrospective control group of cobalt chrome (CoCr) or ceramic heads on HXLPE. From 2003 to 2006, 108 THAs were performed on 96 patients using an OxZi head with a HXLPE liner with minimum ten-year follow-up. Harris Hip Scores (HHS) were collected preoperatively and at the most recent follow-up (mean 13.3 years). Linear and volumetric liner wear was measured on radiographs of 85 hips with a minimum ten-year follow-up (mean 14.5 years). This was compared to a retrospective control group of 45 THAs using ceramic or CoCr heads from October 1999 to February 2005, with a minimum of ten years’ follow-up.Aims
Methods
The benefit of a dual-mobility acetabular component (DMC) for primary total hip arthroplasties (THAs) is controversial. This study aimed to compare the dislocation and complication rates when using a DMC compared to single-mobility (SM) acetabular component in primary elective THA using data collected at a single centre, and compare the revision rates and survival outcomes in these two groups. Between 2010 and 2019, 2,075 primary THAs using either a cementless DM or SM acetabular component were included. Indications for DMC were patients aged older than 70 years or with high risk of dislocation. All other patients received a SM acetabular component. Exclusion criteria were cemented implants, patients treated for femoral neck fracture, and follow-up of less than one year. In total, 1,940 THAs were analyzed: 1,149 DMC (59.2%) and 791 SM (40.8%). The mean age was 73 years (SD 9.2) in the DMC group and 57 years (SD 12) in the SM group. Complications and revisions have been analyzed retrospectively.Aims
Methods
The primary outcome was investigating differences in wear, as measured by femoral head penetration, between cross-linked vitamin E-diffused polyethylene (vE-PE) and cross-linked polyethylene (XLPE) acetabular component liners and between 32 and 36 mm head sizes at the ten-year follow-up. Secondary outcomes included acetabular component migration and patient-reported outcome measures (PROMs) such as the EuroQol five-dimension questionnaire, 36-Item Short-Form Health Survey, Harris Hip Score, and University of California, Los Angeles Activity Scale (UCLA). A single-blinded, multi-arm, 2 × 2 factorial randomized controlled trial was undertaken. Patients were recruited between May 2009 and April 2011. Radiostereometric analyses (RSAs) were performed from baseline to ten years. Of the 220 eligible patients, 116 underwent randomization, and 82 remained at the ten-year follow-up. Eligible patients were randomized into one of four interventions: vE-PE acetabular liner with either 32 or 36 mm femoral head, and XLPE acetabular liner with either 32 or 36 mm femoral head. Parameters were otherwise identical except for acetabular liner material and femoral head size.Aims
Methods
Contemporary outcomes of primary total hip arthroplasties (THAs) with highly cross-linked polyethylene (HXLPE) liners in patients with inflammatory arthritis have not been well studied. This study examined the implant survivorship, complications, radiological results, and clinical outcomes of THA in patients with inflammatory arthritis. We identified 418 hips (350 patients) with a primary diagnosis of inflammatory arthritis who underwent primary THA with HXLPE liners from January 2000 to December 2017. Of these hips, 68% had rheumatoid arthritis (n = 286), 13% ankylosing spondylitis (n = 53), 7% juvenile rheumatoid arthritis (n = 29), 6% psoriatic arthritis (n = 24), 5% systemic lupus erythematosus (n = 23), and 1% scleroderma (n = 3). Mean age was 58 years (SD 14.8), 66.3% were female (n = 277), and mean BMI was 29 kg/m2 (SD 7). Uncemented femoral components were used in 77% of cases (n = 320). Uncemented acetabular components were used in all patients. Competing risk analysis was used accounting for death. Mean follow-up was 4.5 years (2 to 18).Aims
Methods
The aim of this study was to investigate the incidence and characteristics of instrumentation failure (IF) after total en bloc spondylectomy (TES), and to analyze risk factors for IF. The medical records from 136 patients (65 male, 71 female) with a mean age of 52.7 years (14 to 80) who underwent TES were retrospectively reviewed. The mean follow-up period was 101 months (36 to 232). Analyzed factors included incidence of IF, age, sex, BMI, history of chemotherapy or radiotherapy, tumour histology (primary or metastasis; benign or malignant), surgical approach (posterior or combined), tumour location (thoracic or lumbar; junctional or non-junctional), number of resected vertebrae (single or multilevel), anterior resection line (disc-to-disc or intravertebra), type of bone graft (autograft or frozen autograft), cage subsidence (CS), and local alignment (LA). A survival analysis of the instrumentation was performed, and relationships between IF and other factors were investigated using the Cox regression model.Aims
Methods
Head-taper corrosion is a cause of failure in total hip arthroplasty (THA). Recent reports have described an increasing number of V40 taper failures with adverse local tissue reaction (ALTR). However, the real incidence of V40 taper damage and its cause remain unknown. The aim of this study was to evaluate the long-term incidence of ALTR in a consecutive series of THAs using a V40 taper and identify potentially related factors. Between January 2006 and June 2007, a total of 121 patients underwent THA using either an uncemented (Accolade I, made of Ti12Mo6Zr2Fe; Stryker, USA) or a cemented (ABG II, made of cobalt-chrome-molybdenum (CoCrMo); Stryker) femoral component, both with a V40 taper (Stryker). Uncemented acetabular components (Trident; Stryker) with crosslinked polyethylene liners and CoCr femoral heads of 36 mm diameter were used in all patients. At a mean folllow-up of 10.8 years (SD 1.1), 94 patients (79%) were eligible for follow-up (six patients had already undergone a revision, 15 had died, and six were lost to follow-up). A total of 85 THAs in 80 patients (mean age 61 years (24 to 75); 47 (56%) were female) underwent clinical and radiological evaluation, including the measurement of whole blood levels of cobalt and chrome. Metal artifact reduction sequence MRI scans of the hip were performed in 71 patients.Aims
Methods
Aims. This study reports the ten-year wear rates, incidence of osteolysis, clinical outcomes, and complications of a multicentre randomized controlled trial comparing oxidized zirconium (OxZr) versus
Adverse spinal motion or balance (spine mobility) and adverse pelvic mobility, in combination, are often referred to as adverse spinopelvic mobility (SPM). A stiff lumbar spine, large posterior standing pelvic tilt, and severe sagittal spinal deformity have been identified as risk factors for increased hip instability. Adverse SPM can create functional malposition of the acetabular components and hence is an instability risk. Adverse pelvic mobility is often, but not always, associated with abnormal spinal motion parameters. Dislocation rates for dual-mobility articulations (DMAs) have been reported to be between 0% and 1.1%. The aim of this study was to determine the early survivorship from the Australian Orthopaedic Association National Joint Replacement Registry (AOANJRR) of patients with adverse SPM who received a DMA. A multicentre study was performed using data from 227 patients undergoing primary total hip arthroplasty (THA), enrolled consecutively. All the patients who had one or more adverse spine or pelvic mobility parameter had a DMA inserted at the time of their surgery. The mean age was 76 years (22 to 93) and 63% were female (n = 145). At a mean of 14 months (5 to 31) postoperatively, the AOANJRR was analyzed for follow-up information. Reasons for revision and types of revision were identified.Aims
Methods
Aims. A recent report from France suggested an association between the use of
We aimed to evaluate the long-term outcome of highly cross-linked polyethylene (HXLPE) cemented acetabular components and assess whether any radiolucent lines (RLLs) which arose were progressive. We retrospectively reviewed 170 patients who underwent 187 total hip arthroplasties at two hospitals with a minimum follow-up of ten years. All interventions were performed using the same combination of HXLPE cemented acetabular components with femoral stems made of titanium alloy. Kaplan-Meier survival analysis was performed for the primary endpoint of acetabular component revision surgery for any reason and secondary endpoint of the appearance of RLLs. RLLs that had appeared once were observed over time. We statistically assessed potential relationships between RLLs and a number of factors, including the technique of femoral head autografting and the Japanese Orthopaedic Association score.Aims
Methods
Orthopaedic and reconstructive surgeons are faced with large defects after the resection of malignant tumours of the sacrum. Spinopelvic reconstruction is advocated for resections above the level of the S1 neural foramina or involving the sacroiliac joint. Fixation may be augmented with either free vascularized fibular flaps (FVFs) or allograft fibular struts (AFSs) in a cathedral style. However, there are no studies comparing these reconstructive techniques. We reviewed 44 patients (23 female, 21 male) with a mean age of 40 years (SD 17), who underwent en bloc sacrectomy for a malignant tumour of the sacrum with a reconstruction using a total (n = 20), subtotal (n = 2), or hemicathedral (n = 25) technique. The reconstructions were supplemented with a FVF in 25 patients (57%) and an AFS in 19 patients (43%). The mean length of the strut graft was 13 cm (SD 4). The mean follow-up was seven years (SD 5).Aims
Methods
To establish our early clinical results of a new total knee arthroplasty (TKA) tibial component introduced in 2013 and compare it to other designs in use at our hospital during the same period. This is a retrospective study of 166 (154 patients) consecutive cemented, fixed bearing, posterior-stabilized (PS) TKAs (ATTUNE) at one hospital performed by five surgeons. These were compared with a reference cohort of 511 knees (470 patients) of other designs (seven manufacturers) performed at the same hospital by the same surgeons. There were no significant differences in age, sex, BMI, or follow-up times between the two cohorts. The primary outcome was revision performed or pending.Aims
Methods
To report the mid-term results of a modified self-growing rod (SGR) technique for the treatment of idiopathic and neuromuscular early-onset scoliosis (EOS). We carried out a retrospective analysis of 16 consecutive patients with EOS treated with an SGR construct at a single hospital between September 2008 and December 2014. General demographics and deformity variables (i.e. major Cobb angle, T1 to T12 length, T1 to S1 length, pelvic obliquity, shoulder obliquity, and C7 plumb line) were recorded preoperatively, and postoperatively at yearly follow-up. Complications and revision procedures were also recorded. Only patients with a minimum follow-up of five years after surgery were included.Aims
Methods
To evaluate the histopathological examination of peri-implant tissue samples as a technique in the diagnosis of postoperative spinal implant infection (PSII). This was a retrospective analysis. Patients who underwent revision spinal surgery at our institution were recruited for this study. PSII was diagnosed by clinical signs, histopathology, and microbiological examination of intraoperatively collected samples. Histopathology was defined as the gold standard. The sensitivity for histopathology was calculated. A total of 47 patients with PSII and at least one microbiological and histopathological sample were included in the study.Aims
Methods
We have previously demonstrated raised cobalt and chromium levels in patients with larger diameter femoral heads, following metal-on-polyethylene uncemented total hip arthroplasty. Further data have been collected, to see whether these associations have altered with time and to determine the long-term implications for these patients and our practice. Patients from our previous study who underwent Trident-Accolade primary total hip arthroplasties using a metal-on-polyethylene bearing in 2009 were reviewed. Patients were invited to have their cobalt and chromium levels retested, and were provided an Oxford Hip Score. Serum ion levels were then compared between groups (28 mm, 36 mm, and 40 mm heads) and over time.Aims
Methods
Aims. This combined clinical and in vitro study aimed to determine the incidence of liner malseating in modular dual mobility (MDM) constructs in primary total hip arthroplasties (THAs) from a large volume arthroplasty centre, and determine whether malseating increases the potential for fretting and corrosion at the modular metal interface in malseated MDM constructs using a simulated corrosion chamber. Methods. For the clinical arm of the study, observers independently reviewed postoperative radiographs of 551 primary THAs using MDM constructs from a single manufacturer over a three-year period, to identify the incidence of MDM liner-shell malseating. Multivariable logistic regression analysis was performed to identify risk factors including age, sex, body mass index (BMI), cup design, cup size, and the MDM case volume of the surgeon. For the in vitro arm, six pristine MDM implants with
Aims. We propose a state-of-the-art temporary spacer, consisting of a
Biofilm formation is intrinsic to prosthetic joint infection (PJI). In the current study, we evaluated the effects of silver-containing hydroxyapatite (Ag-HA) coating and vancomycin (VCM) on methicillin-resistant Pure titanium discs (Ti discs), Ti discs coated with HA (HA discs), and 3% Ag-HA discs developed using a thermal spraying were inoculated with MRSA suspensions containing a mean in vitro 4.3 (SD 0.8) x 106 or 43.0 (SD 8.4) x 105 colony-forming units (CFUs). Immediately after MRSA inoculation, sterile phosphate-buffered saline or VCM (20 µg/ml) was added, and the discs were incubated for 24 hours at 37°C. Viable cell counting, 3D confocal laser scanning microscopy with Airyscan, and scanning electron microscopy were then performed. HA discs and Ag HA discs were implanted subcutaneously in vivo in the dorsum of rats, and MRSA suspensions containing a mean in vivo 7.2 (SD 0.4) x 106 or 72.0 (SD 4.2) x 105 CFUs were inoculated on the discs. VCM was injected subcutaneously daily every 12 hours followed by viable cell counting.Aims
Methods
The aim of this study was to conduct the largest low contact stress (LCS) retrieval study to elucidate the failure mechanisms of the Porocoat and Duofix femoral component. The latter design was voluntarily recalled by the manufacturer. Uncemented LCS explants were divided into three groups: Duofix, Porocoat, and mixed. Demographics, polyethylene wear, tissue ingrowth, and metallurgical analyses were performed.Aims
Materials and Methods
Objectives. Modern metal-on-metal (MoM) hip resurfacing arthroplasty (HRA), while achieving good results with well-orientated, well-designed components in ideal patients, is contraindicated in women, men with head size under 50 mm, or metal hypersensitivity. These patients currently have no access to the benefits of HRA. Highly crosslinked polyethylene (XLPE) has demonstrated clinical success in total hip arthroplasty (THA) and, when used in HRA, potentially reduces metal ion-related sequelae. We report the early performance of HRA using a direct-to-bone cementless mono-bloc XLPE component coupled with a
The aim of this study was to give estimates of the incidence of component incompatibility in hip and knee arthroplasty and to test the effect of an online, real-time compatibility check. Intraoperative barcode registration of arthroplasty implants was introduced in Denmark in 2013. We developed a compatibility database and, from May 2017, real-time compatibility checking was implemented and became part of the registration. We defined four classes of component incompatibility: A-I, A-II, B-I, and B-II, depending on an assessment of the level of risk to the patient (A/B), and on whether incompatibility was knowingly accepted (I/II).Aims
Materials and Methods
We previously reported the long-term results of the cementless Duraloc-Profile total hip arthroplasty (THA) system in a 12- to 15-year follow-up study. In this paper, we provide an update on the clinical and radiological results of a previously reported cohort of patients at 23 to 26 years´ follow-up. Of the 99 original patients (111 hips), 73 patients (82 hips) with a mean age of 56.8 years (21 to 70) were available for clinical and radiological study at a minimum follow-up of 23 years. There were 40 female patients (44 hips) and 33 male patients (38 hips).Aims
Patients and Methods
Objectives. Bone void fillers are increasingly being used for dead space management in arthroplasty revision surgery. The aim of this study was to investigate the influence of calcium sulphate bone void filler (CS-BVF) on the damage and wear of total knee arthroplasty using experimental wear simulation. Methods. A total of 18 fixed-bearing U2 total knee arthroplasty system implants (United Orthopedic Corp., Hsinchu, Taiwan) were used. Implants challenged with CS-BVF were compared with new implants (negative controls) and those intentionally scratched with a diamond stylus (positive controls) representative of severe surface damage (n = 6 for each experimental group). Three million cycles (MC) of experimental simulation were carried out to simulate a walking gait cycle. Wear of the ultra-high-molecular-weight polyethylene (UHMWPE) tibial inserts was measured gravimetrically, and damage to articulating surfaces was assessed using profilometry. Results. There was no significant difference (p > 0.05) between the wear rate of implants challenged with CS-BVF (3.3 mm. 3. /MC (95% confidence interval (CI) 1.8 to 4.8)) and the wear rate of those not challenged (2.8 mm. 3. /MC (95% CI 1.3 to 4.3)). However, scratching the
This study compares the PFC total knee arthroplasty (TKA) system in a prospective randomized control trial (RCT) of the mobile-bearing rotating-platform (RP) TKA against the fixed-bearing (FB) TKA. This is the largest RCT with the longest follow-up where cruciate-retaining PFC total knee arthroplasties are compared in a non-bilateral TKA study. A total of 167 patients (190 knees with 23 bilateral cases), were recruited prospectively and randomly assigned, with 91 knees receiving the RP and 99 knees receiving FB. The mean age was 65.5 years (48 to 82), the mean body mass index (BMI) was 29.7 kg/m2 (20 to 52) and 73 patients were female. The Knee Society Score (KSS), Knee Society Functional Score (KSFS), Oxford Knee Score (OKS), Western Ontario and McMaster Universities Arthritis Index (WOMAC), and 12-Item Short-Form Health Survey Physical and Mental Component Scores (SF-12 PCS, SF-12 MCS) were gathered and recorded preoperatively, at five-years’ follow-up, and at ten years’ follow-up. Additionally, Knee Injury and Osteoarthritis Outcome Scores (KOOS) were collected at five- and ten-year follow-ups. The prevalence of radiolucent lines (RL) on radiographs and implant survival were recorded at five- and ten-year follow-ups.Aims
Patients and Methods
The aim of this study was to report the initial results of the
Exeter V40 stem, which became available in 2000. A total of 540 total hip arthroplasties (THAs) were performed
in our unit using this stem between December 2000 and May 2002.
Our routine protocol is to review patients postoperatively and at
one, five, and ten years following surgery.Aims
Patients and Methods
Taper junctions between modular hip arthroplasty femoral heads and stems fail by wear or corrosion which can be caused by relative motion at their interface. Increasing the assembly force can reduce relative motion and corrosion but may also damage surrounding tissues. The purpose of this study was to determine the effects of increasing the impaction energy and the stiffness of the impactor tool on the stability of the taper junction and on the forces transmitted through the patient’s surrounding tissues. A commercially available impaction tool was modified to assemble components in the laboratory using impactor tips with varying stiffness at different applied energy levels. Springs were mounted below the modular components to represent the patient. The pull-off force of the head from the stem was measured to assess stability, and the displacement of the springs was measured to assess the force transmitted to the patient’s tissues.Objectives
Methods
The aim of this study was to determine whether the rates of revision
for metal-on-metal (MoM) total hip arthroplasties (THAs) with Pinnacle
components varied according to the year of the initial operation,
and compare these with the rates of revision for other designs of
MoM THA. Data from the National Joint Registry for England and Wales included
36 mm MoM THAs with Pinnacle acetabular components which were undertaken
between 2003 and 2012 with follow-up for at least five years (n
= 10 776) and a control group of other MoM THAs (n = 13 817). The
effect of the year of the primary operation on all-cause rates of revision
was assessed using Cox regression and interrupted time-series analysis.Aims
Patients and Methods
To present a surgically relevant update of trunnionosis. Systematic review performed April 2017.Aims
Materials and Methods
We present the ten-year data of a cohort of patients, aged between
18 and 65 years (mean age 52.7 years; 19 to 64), who underwent total
hip arthroplasty. Patients were randomised to be treated with a
cobalt-chrome (CoCr) femoral head with an ultra-high molecular weight
polyethylene (UHMWPE), highly cross-linked polyethylene (XLPE) or
ceramic-on-ceramic (CoC) bearing surface. A total of 102 hips (91 patients) were randomised into the three
groups. At ten years, 97 hips were available for radiological and
functional follow-up. Two hips (two patients) had been revised (one
with deep infection and one for periprosthetic fracture) and three
were lost to follow-up. Radiological analysis was performed using
a validated digital assessment programme to give linear, directional
and volumetric wear of the two polyethylene groups.Aims
Patients and Methods
The aim of this study was to report a retrospective, consecutive
series of patients with adolescent idiopathic scoliosis (AIS) who
were treated with posterior minimally invasive surgery (MIS) with
a mean follow-up of two years ( We prospectively collected the data of 70 consecutive patients
with AIS treated with MIS using three incisions and a muscle-splitting
approach by a single surgeon between June 2013 and February 2016
and these were retrospectively reviewed. There were eight male and
62 female patients with a mean age of 15 years (Aims
Patients and Methods
Advances in polyethylene (PE) in total hip arthroplasty
have led to interest and increased use of highly crosslinked PE
(HXLPE) in total knee arthroplasty (TKA). Biomechanical data suggest
improved wear characteristics for HXLPE inserts over conventional
PE in TKA. Short-term results from registry data and few clinical
trials are promising. Our aim is to present a review of the history
of HXLPEs, the use of HXLPE inserts in TKA, concerns regarding potential mechanical
complications, and a thorough review of the available biomechanical
and clinical data. Cite this article:
Femoral stems with exchangeable (modular) necks were introduced
to offer surgeons an increased choice when determining the version,
offset and length of the femoral neck during total hip arthroplasty
(THA). It was hoped that this would improve outcomes and reduce
complications, particularly dislocation. In 2010, the Australian Orthopaedic
Association National Joint Replacement Registry (AOANJRR) first
reported an increased rate of revision after primary THA using femoral
stems with an exchangeable neck. The aim of this study was to provide
a more comprehensive up-to-date analysis of primary THA using femoral
stems with exchangeable and fixed necks. The data included all primary THA procedures performed for osteoarthritis
(OA), reported to the AOANJRR between 01 September 1999 and 31 December
2014. There were 9289 femoral stems with an exchangeable neck and
253 165 femoral stems with a fixed neck. The characteristics of
the patients and prostheses including the bearing surface and stem/neck
metal combinations were examined using Cox proportional hazard ratios
(HRs) and Kaplan-Meier estimates of survivorship. Aims
Materials and Methods
Loss or absence of proximal femoral bone in revision total hip
arthroplasty (THA) remains a significant challenge. While the main
indication for the use of proximal femoral replacements (PFRs) is
in the treatment of malignant disease, they have a valuable role
in revision THA for loosening, fracture and infection in patients
with bone loss. Our aim was to determine the clinical outcomes,
implant survivorship, and complications of PFRs used in revision
THA for indications other than malignancy. A retrospective review of 44 patients who underwent revision
THA using a PFR between 2000 and 2013 was undertaken. Their mean
age was 79 years (53 to 97); 31 (70%) were women. The bone loss
was classified as Paprosky IIIB or IV in all patients. The mean
follow-up was six years (2 to 12), at which time 22 patients had
died and five were lost to follow-up.Aims
Patients and Methods
We report on the outcome of the Synergy cementless femoral stem
with a minimum follow-up of 15 years (15 to 17). A retrospective review was undertaken of a consecutive series
of 112 routine primary cementless total hip arthroplasties (THAs)
in 102 patients (112 hips). There were 60 female and 42 male patients
with a mean age of 61 years (18 to 82) at the time of surgery. A
total of 78 hips in the 69 patients remain Aims
Patients and Methods
Up to 40% of unicompartmental knee arthroplasty (UKA) revisions are performed for unexplained pain which may be caused by elevated proximal tibial bone strain. This study investigates the effect of tibial component metal backing and polyethylene thickness on bone strain in a cemented fixed-bearing medial UKA using a finite element model (FEM) validated experimentally by digital image correlation (DIC) and acoustic emission (AE). A total of ten composite tibias implanted with all-polyethylene (AP) and metal-backed (MB) tibial components were loaded to 2500 N. Cortical strain was measured using DIC and cancellous microdamage using AE. FEMs were created and validated and polyethylene thickness varied from 6 mm to 10 mm. The volume of cancellous bone exposed to < -3000 µε (pathological loading) and < -7000 µε (yield point) minimum principal (compressive) microstrain and > 3000 µε and > 7000 µε maximum principal (tensile) microstrain was computed.Objectives
Materials and Methods
Reconstruction of the acetabulum after failed total hip arthroplasty
(THA) can be a surgical challenge in the presence of severe bone
loss. We report the long-term survival of a porous tantalum revision
acetabular component, its radiological appearance and quality of
life outcomes. We reviewed the results of 46 patients who had undergone revision
of a failed acetabular component with a Paprosky II or III bone
defect and reconstruction with a hemispherical, tantalum acetabular
component, supplementary screws and a cemented polyethylene liner.Aims
Patients and Methods
Pathological assessment of periprosthetic tissues is important, not only for diagnosis, but also for understanding the pathobiology of implant failure. The host response to wear particle deposition in periprosthetic tissues is characterised by cell and tissue injury, and a reparative and inflammatory response in which there is an innate and adaptive immune response to the material components of implant wear. Physical and chemical characteristics of implant wear influence the nature of the response in periprosthetic tissues and account for the development of particular complications that lead to implant failure, such as osteolysis which leads to aseptic loosening, and soft-tissue necrosis/inflammation, which can result in pseudotumour formation. The innate response involves phagocytosis of implant-derived wear particles by macrophages; this is determined by pattern recognition receptors and results in expression of cytokines, chemokines and growth factors promoting inflammation and osteoclastogenesis; phagocytosed particles can also be cytotoxic and cause cell and tissue necrosis. The adaptive immune response to wear debris is characterised by the presence of lymphoid cells and most likely occurs as a result of a cell-mediated hypersensitivity reaction to cell and tissue components altered by interaction with the material components of particulate wear, particularly metal ions released from
Hips with metal-on-metal total hip arthroplasty (MoM THA) have a high rate of adverse local tissue reactions (ALTR), often associated with hypersensitivity reactions. Dynamic contrast-enhanced magnetic resonance imaging (DCE-MRI) measures tissue perfusion with the parameter Ktrans (volume transfer constant of contrast agent). Our purpose was 1) to evaluate the feasibility of DCE-MRI in patients with THA and 2) to compare DCE-MRI in patients with MoM bearings with metal-on-polyethylene (MoP) bearings, hypothesising that the perfusion index Ktrans in hips with MoM THA is higher than in hips with MoP THA. In this pilot study, 16 patients with primary THA were recruited (eight MoM, eight MoP). DCE-MRI of the hip was performed at 1.5 Tesla (T). For each patient, Ktrans was computed voxel-by-voxel in all tissue lateral to the bladder. The mean Ktrans for all voxels was then calculated. These values were compared with respect to implant type and gender, and further correlated with clinical parameters.Objectives
Methods
We present a case series of ten metal-on-polyethylene total hip
arthroplasties (MoP THAs) with delayed dislocation associated with
unrecognised adverse local tissue reaction due to corrosion at the
trunnion and pseudotumour formation. The diagnosis was not suspected in nine of the ten patients (six
female/four male; mean age 66 years), despite treatment in a specialist
unit (mean time from index surgery to revision was 58 months, 36
to 84). It was identified at revision surgery and subsequently confirmed
by histological examination of resected tissue. Pre-operative assessment
and culture results ruled out infection. A variety of treatment
strategies were used, including resection of the pseudotumour and
efforts to avoid recurrent dislocation. Aims
Methods
Aims. The purpose of this study was to compare the long-term results
of primary total hip arthroplasty (THA) in young patients using
either a conventional (CPE) or a highly cross-linked (HXLPE) polyethylene
liner in terms of functional outcome, incidence of osteolysis, radiological
wear and rate of revision. Methods. We included all patients between the ages of 45 and 65 years
who, between January 2000 and December 2001, had undergone a primary
THA for osteoarthritis at our hospital using a CPE or HXLPE acetabular
liner and a 28 mm
Tapered fluted titanium stems are increasingly
used for femoral revision arthroplasty. They are available in modular and
non-modular forms. Modularity has advantages when the bone loss
is severe, the proximal femur is mis shapen or the surgeon is unfamiliar
with the implant, but it introduces the risk of fracture of the
stem at the junction between it and the proximal body segment. For
that reason, and while awaiting intermediate-term results of more recently
introduced designs of this junction, non-modularity has attracted
attention, at least for straightforward revision cases. We review the risks and causes of fracture of tapered titanium
modular revision stems and present an argument in favour of the
more selective use of modular designs. Cite this article:
Oxidised zirconium (OxZi) has been developed
as an alternative bearing surface for femoral heads in total hip arthroplasty
(THA). This study has investigated polyethylene wear, functional
outcomes and complications, comparing OxZi and cobalt–chrome (CoCr)
as part of a three-arm, multicentre randomised controlled trial.
Patients undergoing THA from four institutions were prospectively
randomised into three groups. Group A received a CoCr femoral head
and highly cross-linked polyethylene (XLPE) liner; Group B received
an OxZi femoral head and XLPE liner; Group C received an OxZi femoral
head and ultra-high molecular weight polyethylene (UHMWPE) liner.
At five years, 368 patients had no statistically significant differences
in short-form-36 (p = 0.176 mental, p = 0.756 physical), Western
Ontario and McMaster Universities Osteoarthritis Index (p = 0.847),
pain scores
(p = 0.458) or complications. The mean rate of linear wear was 0.028
mm/year (standard deviation ( Cite this article:
Inherent disadvantages of reverse shoulder arthroplasty
designs based on the Grammont concept have raised a renewed interest
in less-medialised designs and techniques. The aim of this study
was to evaluate the outcome of reverse shoulder arthroplasty (RSA)
with the fully-constrained, less-medialised, Bayley–Walker prosthesis performed
for the treatment of rotator-cuff-deficient shoulders with glenohumeral
arthritis. A total of 97 arthroplasties in 92 patients (53 women
and 44 men, mean age 67 years (standard deviation ( The Bayley–Walker prosthesis provides reliable pain relief and
reasonable functional improvement for patients with symptomatic
cuff-deficient shoulders. Compared with other designs of RSA, it
offers a modest improvement in forward elevation, but restores external
rotation to some extent and prevents scapular notching. A longer
follow-up is required to assess the survival of the prosthesis and
the clinical performance over time. Cite this article:
A modular femoral head–neck junction has practical
advantages in total hip replacement. Taper fretting and corrosion
have so far been an infrequent cause of revision. The role of design
and manufacturing variables continues to be debated. Over the past
decade several changes in technology and clinical practice might
result in an increase in clinically significant taper fretting and
corrosion. Those factors include an increased usage of large diameter
(36 mm) heads, reduced femoral neck and taper dimensions, greater
variability in taper assembly with smaller incision surgery, and
higher taper stresses due to increased patient weight and/or physical
activity. Additional studies are needed to determine the role of
taper assembly compared with design, manufacturing and other implant
variables. Cite this article:
The October 2013 Hip &
Pelvis Roundup360 looks at: Young and impinging; Clothes, weather and femoral heads?; Go long, go cemented; Surgical repair of the abductors?; Aspirin for DVT prophylaxis?; Ceramic-on-polyethylene: a low-wear solution?; ALVAL and ASR™: the story continues….; Salvaging Legg-Calve-Perthes’ disease
The August 2013 Hip &
Pelvis Roundup360 looks at: are we getting it right first time?; tantalum augments in revision hip surgery; lower wear in dual mobility?; changing faces changes outcomes; synovial fluid aspiration in MOM hips; taper disease: the new epidemic of hip surgery; the super-obese and THR; and whether well fixed stems can remain in infected hips
Between 1999 and 2001, 90 patients underwent
total hip replacement using the same uncemented acetabular and femoral
components with a 28 mm metallic femoral head but with prospective
randomisation of the acetabular liner to either Durasul highly cross-linked
polyethylene or nitrogen-sterilised Sulene polyethylene. We assessed
83 patients at a minimum follow-up of ten years. Linear penetration
of the femoral head was estimated at six weeks, six and 12 months
and annually thereafter, using the Dorr method, given the non-spherical
shape of the acetabular component. There was no loosening of any component; only one hip in the
Sulene group showed proximal femoral osteolysis. The mean penetration
of the femoral head at six weeks was 0.08 mm (0.02 to 0.15) for
the Durasul group and 0.16 mm (0.05 to 0.28) for the Sulene group
(p = 0.001). The mean yearly linear penetration was 64.8% lower
for the Durasul group at 0.05 mm/year ( Cite this article:
In this study we present our experience with
four generations of uncemented total knee arthroplasty (TKA) from Smith
&
Nephew: Tricon M, Tricon LS, Tricon II and Profix, focusing
on the failure rates correlating with each design change. Beginning
in 1984, 380 Tricon M, 435 Tricon LS, 305 Tricon 2 and 588 Profix
were implanted by the senior author. The rate of revision for loosening
was 1.1% for the Tricon M, 1.1% for the Tricon LS, 0.5% for the
Tricon 2 with a HA coated tibial component, and 1.3% for the Profix
TKA. No loosening of the femoral component was seen with the Tricon
M, Tricon LS or Tricon 2, with no loosening seen of the tibial component
with the Profix TKA. Regarding revision for wear, the incidence
was 13.1% for the Tricon M, 6.6% for the Tricon LS, 2.3% for the
Tricon 2, and 0% for the Profix. These results demonstrate that
improvements in the design of uncemented components, including increased
polyethylene thickness, improved polyethylene quality, and the introduction
of hydroxyapatite coating, has improved the outcomes of uncemented
TKA over time.
The purpose of this paper is to discuss the risk
factors, prevention strategies, classification, and treatment of
intra-operative femur fractures sustained during primary and revision
total hip arthroplasty.
Despite many claims of good wear properties following
total knee replacement (TKR) with an oxidised zirconium (OxZr) femoral
component, there are conflicting clinical results. We hypothesised
that there would be no difference in either the mid-term clinical
and radiological outcomes or the characteristics of the polyethylene
wear particles (weight, size and shape) in patients using an OxZr
or
Stems improve the mechanical stability of tibial
components in total knee replacement (TKR), but come at a cost of stress
shielding along their length. Their advantages include resistance
to shear, reduced tibial lift-off and increased stability by reducing
micromotion. Longer stems may have disadvantages including stress
shielding along the length of the stem with associated reduction
in bone density and a theoretical risk of subsidence and loosening, peri-prosthetic
fracture and end-of-stem pain. These features make long stems unattractive
in the primary TKR setting, but often desirable in revision surgery
with bone loss and instability. In the revision scenario, stems
are beneficial in order to convey structural stability to the construct
and protect the reconstruction of bony defects. Cemented and uncemented
long stemmed implants have different roles depending on the nature
of the bone loss involved. This review discusses the biomechanics of the design of tibial
components and stems to inform the selection of the component and
the technique of implantation.
A consecutive series of patients with a hydroxyapatite-coated
uncemented total knee replacement (TKR) performed by a single surgeon
between 1992 and 1995 was analysed. All patients were invited for
clinical review and radiological assessment. Revision for aseptic
loosening was the primary outcome. Assessment was based on the Knee
Society clinical score (KSS) and an independent radiological analysis.
Of 471 TKRs performed in 356 patients, 432 TKRs in 325 patients
were followed for a mean of 16.4 years (15 to 18). The 39 TKRs in
31 patients lost to follow-up had a mean KSS of 176 (148 to 198)
at a mean of ten years. There were revisions in 26 TKRs (5.5%),
of which 11 (2.3%) were for aseptic loosening. Other further surgery
was carried out on 49 TKRs (10.4%) including patellar resurfacing
in 20, arthrolysis in 19, manipulation under anaesthetic in nine
and extensor mechanism reconstruction in one. Survivorship at up to 18 years without aseptic loosening was
96% (95% confidence interval 91.9 to 98.1), at which point the mean
KSS was 176 (134 to 200). Of 110 knees that underwent radiological
evaluation, osteolysis was observed in five (4.5%), one of which
was revised. These data indicate that uncemented hydroxyapatite-coated TKR
can achieve favourable long-term survivorship, at least as good
as that of cemented designs.
We present a series of 35 patients (19 men and
16 women) with a mean age of 64 years (36.7 to 75.9), who underwent
total hip replacement using the ESKA dual-modular short stem with
metal on-polyethylene bearing surfaces. This implant has a modular
neck section in addition to the modular head. Of these patients,
three presented with increasing post-operative pain due to pseudotumour
formation that resulted from corrosion at the modular neck-stem
junction. These patients underwent further surgery and aseptic lymphocytic
vaculitis associated lesions were demonstrated on histological analysis. Retrieval analysis of two modular necks showed corrosion at the
neck-stem taper. Blood cobalt and chromium levels were measured
at a mean of nine months (3 to 28) following surgery. These were
compared with the levels in seven control patients (three men and
four women) with a mean age of 53.4 years (32.1 to 64.1), who had
an identical prosthesis and articulation but with a prosthesis that
had no modularity at neck-stem junction. The mean blood levels of
cobalt in the study group were raised at 50.75 nmol/l (5 to 145)
compared with 5.6 nmol/l (2 to 13) in control patients. Corrosion at neck-stem tapers has been identified as an important
source of metal ion release and pseudotumour formation requiring
revision surgery. Finite element modelling of the dual modular stem
demonstrated high stresses at the modular stem-neck junction. Dual
modular
Persistent groin pain after seemingly successful
total hip replacement (THR) appears to have become more common.
Recent studies have indicated a high incidence after metal-on-polyethylene
and metal-on-metal conventional THR and it has been documented in
up to 18% of patients after metal-on-metal resurfacing. There are many
causes, including acetabular loosening, stress fracture, and iliopsoas
tendonitis and impingement. The evaluation of this problem requires
a careful history and examination, plain radiographs and an algorithmic approach
to special diagnostic imaging and tests. Non-operative treatment
is not usually successful. Specific operative treatment depending
on the cause of the pain usually involves revision of the acetabular
component, iliopsoas tenotomy or other procedures, and is usually
successful. Here, an appropriate algorithm is described.
The most frequent cause of failure after total
hip replacement in all reported arthroplasty registries is peri-prosthetic
osteolysis. Osteolysis is an active biological process initiated
in response to wear debris. The eventual response to this process
is the activation of macrophages and loss of bone. Activation of macrophages initiates a complex biological cascade
resulting in the final common pathway of an increase in osteolytic
activity. The biological initiators, mechanisms for and regulation
of this process are beginning to be understood. This article explores current
concepts in the causes of, and underlying biological mechanism resulting
in peri-prosthetic osteolysis, reviewing the current basic science
and clinical literature surrounding the topic.
Complications involving the patellofemoral joint,
caused by malrotation of the femoral component during total knee replacement,
are an important cause of persistent pain and failure leading to
revision surgery. The aim of this study was to determine and quantify
the influence of femoral component malrotation on patellofemoral
wear, and to determine whether or not there is a difference in the
rate of wear of the patellar component when articulated against
oxidised zirconium (OxZr) and
Correct positioning and alignment of components during primary total knee replacement (TKR) is widely accepted to be an important predictor of patient satisfaction and implant durability. This retrospective study reports the effect of the post-operative mechanical axis of the lower limb in the coronal plane on implant survival following primary TKR. A total of 501 TKRs in 396 patients were divided into an aligned group with a neutral mechanical axis (± 3°) and a malaligned group where the mechanical axis deviated from neutral by >
3°. At 15 years’ follow-up, 33 of 458 (7.2%) TKRs were revised for aseptic loosening. Kaplan-Meier survival analysis showed a weak tendency towards improved survival with restoration of a neutral mechanical axis, but this did not reach statistical significance (p = 0.47). We found that the relationship between survival of a primary TKR and mechanical axis alignment is weaker than that described in a number of previous reports.
This study reports the mid-term results of a large-bearing hybrid metal-on-metal total hip replacement in 199 hips (185 patients) with a mean follow-up of 62 months (32 to 83). Two patients died of unrelated causes and 13 were lost to follow-up. In all, 17 hips (8.5%) have undergone revision, and a further 14 are awaiting surgery. All revisions were symptomatic. Of the revision cases, 14 hips showed evidence of adverse reactions to metal debris. The patients revised or awaiting revision had significantly higher whole blood cobalt ion levels (p = 0.001), but no significant difference in acetabular component size or position compared with the unrevised patients. Wear analysis (n = 5) showed increased wear at the trunnion-head interface, normal levels of wear at the articulating surfaces and evidence of corrosion on the surface of the stem. The cumulative survival rate, with revision for any reason, was 92.4% (95% confidence interval 87.4 to 95.4) at five years. Including those awaiting surgery, the revision rate would be 15.1% with a cumulative survival at five years of 89.6% (95% confidence interval 83.9 to 93.4). This hybrid metal-on-metal total hip replacement series has shown an unacceptably high rate of failure, with evidence of high wear at the trunnion-head interface and passive corrosion of the stem surface. This raises concerns about the use of large heads on conventional 12/14 tapers.
Our aim in this pilot study was to evaluate the fixation of, the bone remodelling around, and the clinical outcome after surgery of a new, uncemented, fully hydroxyapatite-coated, collared and tapered femoral component, designed specifically for elderly patients with a fracture of the femoral neck. We enrolled 50 patients, of at least 70 years of age, with an acute displaced fracture of the femoral neck in this prospective single-series study. They received a total hip replacement using the new component and were followed up regularly for two years. Fixation was evaluated by radiostereometric analysis and bone remodelling by dual-energy x-ray absorptiometry. Hip function and the health-related quality of life were assessed using the Harris hip score and the EuroQol-5D. Up to six weeks post-operatively there was a mean subsidence of 0.2 mm (−2.1 to +0.5) and a retroversion of a mean of 1.2° (−8.2° to +1.5°). No component migrated after three months. The patients had a continuous loss of peri-prosthetic bone which amounted to a mean of 16% (−49% to +10%) at two years. The mean Harris hip score was 82 (51 to 100) after two years. The two-year results from this pilot study indicate that this new, uncemented femoral component can be used for elderly patients with osteoporotic fractures of the femoral neck.
Lately, concerns have arisen following the use of large metal-on-metal bearings in hip replacements owing to reports of catastrophic soft-tissue reactions resulting in implant failure and associated complications. This review examines the literature and contemporary presentations on current clinical dilemmas in metal-on-metal hip replacement.
Our aim was to determine the success rate of repeated debridement and two-stage cementless revision arthroplasty according to the type of infected total hip replacement (THR). We enrolled 294 patients (294 hips) with an infected THR in the study. There were 222 men and 72 women with a mean age of 55.1 years (24.0 to 78.0). The rate of control of infection after the initial treatment and after repeated debridement and two-stage revisions was determined. The clinical (Harris hip score) and radiological results were evaluated. The mean follow-up was 10.4 years (5.0 to 14.0). The eventual rate of control of infection was 100.0% for early superficial post-operative infection, 98.4% for early deep post-operative infection, 98.5% for late chronic infection and 91.0% for acute haematogenous infection. Overall, 288 patients (98%) maintained a functioning THR at the latest follow-up. All the allografts appeared to be united and there were no failures. These techniques effectively controlled infection and maintained a functional THR with firm fixation in most patients. Repeated debridement and two-stage or repeated two-stage revisions further improved the rate of control of infection after the initial treatment and increased the likelihood of maintaining a functional THR.
We report the survival, radiological and functional outcomes of a single surgeon series of his first 144 consecutive Birmingham hip resurfacing procedures (130 patients) at a minimum of ten years. There were ten revisions during this time. Although no patients were lost to follow-up some did not complete the scoring assessment or undergo radiological assessment at ten years. The ten-year survival for male patients was 98.0% (95% confidence interval 95.2 to 100). The ten-year survival for the total cohort with aseptic revision as the endpoint was 95.5% (95% confidence interval 91.8 to 99.0) and including revisions for sepsis was 93.5% (95% confidence interval 89.2 to 97.6). The median modified Oxford hip score at ten years was 4.2% (interquartile range 0 to 19) and the median University of California, Los Angeles score was 7.0 (interquartile range 5.0 to 8.0). This study confirms the midterm reports that metal-on-metal hip resurfacing using the Birmingham Hip provides a durable alternative to total hip replacement, particularly in younger male patients wishing to maintain a high level of function, with low risk of revision for at least ten years.
We review the history and literature of hip resurfacing arthroplasty. Resurfacing and the science behind it continues to evolve. Recent results, particularly from the national arthroplasty registers, have spread disquiet among both surgeons and patients. A hip resurfacing arthroplasty is not a total hip replacement, but should perhaps be seen as a means of delaying it. The time when hip resurfacing is offered to a patient may be different from that for a total hip replacement. The same logic can apply to the timing of revision surgery. Consequently, the comparison of resurfacing with total hip replacement may be a false one. Nevertheless, the need for innovative solutions for young arthroplasty patients is clear. Total hip replacement can be usefully delayed in many of these patients by the use of hip resurfacing arthroplasty.
We undertook a randomised prospective follow-up study of changes in peri-prosthetic bone mineral density (BMD) after hip resurfacing and compared them with the results after total hip replacement. A total of 59 patients were allocated to receive a hip resurfacing (n = 29) or an uncemented distally fixed total hip replacement (n = 30). The BMD was prospectively determined in four separate regions of interest of the femoral neck and in the calcar region corresponding to Gruen zone 7 for the hip resurfacing group and compared only to the calcar region in the total hip replacement group. Standardised measurements were performed pre-operatively and after three, six and 12 months. The groups were well matched in terms of gender distribution and mean age. The mean BMD in the calcar region increased after one year to 105.2% of baseline levels in the resurfaced group compared with a significant decrease to 82.1% in the total hip replacement group (p <
0.001) by 12 months. For the resurfaced group, there was a decrease in bone density in all four regions of the femoral neck at three months which did not reach statistical significance and was followed by recovery to baseline levels after 12 months. Hip resurfacing did indeed preserve BMD in the inferior femoral neck. In contrast, a decrease in the mean BMD in Gruen zone 7 followed uncemented distally fixed total hip replacement. Long term follow-up studies are necessary to see whether this benefit in preservation of BMD will be clinically relevant at future revision surgery.
Metal-on-metal total hip replacement has been targeted at younger patients with anticipated long-term survival, but the effect of the production of metal ions is a concern because of their possible toxicity to cells. We have reviewed the results of the use of the Ultima hybrid metal-on-metal total hip replacement, with a cemented polished tapered femoral component with a 28 mm diameter and a
We implanted titanium and carbon fibre-reinforced plastic (CFRP) femoral prostheses of the same dimensions into five prosthetic femora. An abductor jig was attached and a 1 kN load applied. This was repeated with five control femora. Digital image correlation was used to give a detailed two-dimensional strain map of the medial cortex of the proximal femur. Both implants caused stress shielding around the calcar. Distally, the titanium implant showed stress shielding, whereas the CFRP prosthesis did not produce a strain pattern which was statistically different from the controls. There was a reduction in strain beyond the tip of both the implants. This investigation indicates that use of the CFRP stem should avoid stress shielding in total hip replacement.
Bone mineral density (BMD) around the femoral component has been reported to decrease after total knee replacement (TKR) because of stress shielding. Our aim was to determine whether a cemented mobile-bearing component reduced the post-operative loss of BMD. In our study 28 knees receiving a cemented fixed-bearing TKR were matched with 28 receiving a cemented mobile-bearing TKR. They underwent dual-energy x-ray absorptiometry, pre-operatively and at three weeks and at three, six, 12, 18 and 24 months post-operatively. The patients were not taking medication to improve the BMD. The pre-operative differences in the BMD of the femoral neck, wrist, lumbar spine and knee in the two groups were not significant. The BMD of the femur decreased postoperatively in the fixed-bearing group, but not the mobile-bearing group. The difference in the post-operative change in the BMD in the two groups was statistically significant (p <
0.05) at 18 and 24 months. Our findings show that a cemented mobile-bearing TKR has a favourable effect on the BMD of the distal femur after TKR in the short term. Further study is required to determine the long-term effects.
Components from 73 failed knee replacements (TKRs) consisting of rotating-platform, mobile-bearing and fixed-bearing implants were examined to assess the patterns of wear. The patterns were divided into low-grade (burnishing, abrasion and cold flow) and high-grade (scratching, pitting/metal embedding and delamination) to assess the severity of the wear of polyethylene. The rotating-platform group had a higher incidence of low-grade wear on the upper surface compared with the fixed-bearing group. By contrast, high-grade wear comprising scratching, pitting and third-body embedding was seen on the lower surface. Linear regression analysis showed a significant correlation of the wear scores between the upper and lower surfaces of the tibial insert (R2 = 0.29, p = 0.04) for the rotating-platform group, but no significant correlation was found for the fixed-bearing counterpart. This suggests that high-grade wear patterns on the upper surface are reduced with the rotating-platform design. However, the incidence of burnishing, pitting/third-body embedding and scratching wear patterns on the lower surface was higher compared with that in the fixed-bearing knee.
The survivorship of contemporary resurfacing arthroplasty of the hip using metal-on-metal bearings is better than that of first generation designs, but short-term failures still occur. The most common reasons for failure are fracture of the femoral neck, loosening of the component, osteonecrosis of the femoral head, reaction to metal debris and malpositioning of the component. In 2008 the Australian National Joint Registry reported an inverse relationship between the size of the head component and the risk of revision in resurfacing hip arthroplasty. Hips with a femoral component size of ≤ 44 mm have a fivefold increased risk of revision than those with femoral components of ≥ 55 mm irrespective of gender. We have reviewed the literature to explore this observation and to identify possible reasons including the design of the implant, loading of the femoral neck, the orientation of the component, the production of wear debris and the effects of metal ions, penetration of cement and vascularity of the femoral head. Our conclusion is that although multifactorial, the most important contributors to failure in resurfacing arthroplasty of the hip are likely to be the design and geometry of the component and the orientation of the acetabular component.
The Norwegian Arthroplasty Register has shown that several designs of uncemented femoral stems give good or excellent survivorship. The overall findings for uncemented total hip replacement however, have been disappointing because of poor results with the use of metal-backed acetabular components. In this study, we exclusively investigated the medium-to long-term performance of primary uncemented metal-backed acetabular components. A total of 9113 primary uncemented acetabular components were implanted in 7937 patients between 1987 and 2007. These were included in a prospective, population-based observational study. All the implants were modular and metal-backed with ultra-high-molecular-weight polyethylene liners. The femoral heads were made of stainless steel,
Second-generation metal-on-metal bearings were introduced as a response to the considerable incidence of wear-induced failures associated with conventional replacements, especially in young patients. We present the results at ten years of a consecutive series of patients treated using a metal-on-metal hip resurfacing. A distinct feature of the bearings used in our series was that they had been subjected to double-heat treatments during the post-casting phase of their manufacture. In the past these bearings had not been subjected to thermal treatments, making this a unique metal-on-metal bearing which had not been used before in clinical practice. We report the outcome of 184 consecutive hips (160 patients) treated using a hybrid-fixed metal-on-metal hip resurfacing during 1996. Patients were invited for a clinicoradiological follow-up at a minimum of ten years. The Oxford hip score and anteroposterior and lateral radiographs were obtained. The mean age at operation was 54 years (21 to 75). A series of 107 consecutive hips (99 patients) who received the same prosthesis, but subjected to a single thermal treatment after being cast, between March 1994 and December 1995, were used as a control group for comparison. In the 1994 to 1995 group seven patients (seven hips) died from unrelated causes and there were four revisions (4%) for osteolysis and aseptic loosening. In the 1996 group nine patients died at a mean of 6.9 years after operation because of unrelated causes. There were 30 revisions (16%) at a mean of 7.3 years (1.2 to 10.9), one for infection at 1.2 years and 29 for osteolysis and aseptic loosening. Furthermore, in the latter group there were radiological signs of failure in 27 (24%) of the 111 surviving hips. The magnitude of the problem of osteolysis and aseptic loosening in the 1996 cohort did not become obvious until five years after the operation. Our results indicate that double-heat treatments of metal-on-metal bearings can lead to an increased incidence of wear-induced osteolysis.
We undertook a retrospective review of 33 patients who underwent total femoral endoprosthetic replacement as limb salvage following excision of a malignant bone tumour. In 22 patients this was performed as a primary procedure following total femoral resection for malignant disease. Revision to a total femoral replacement was required in 11 patients following failed segmental endoprosthetic or allograft reconstruction. There were 33 patients with primary malignant tumours, and three had metastatic lesions. The mean age of the patients was 31 years (5 to 68). The mean follow-up was 4.2 years (9 months to 16.4 years). At five years the survival of the implants was 100%, with removal as the endpoint and 56% where the endpoint was another surgical intervention. At five years the patient survival was 32%. Complications included dislocation of the hip in six patients (18%), local recurrence in three (9%), peri-prosthetic fracture in two and infection in one. One patient subsequently developed pulmonary metastases. There were no cases of aseptic loosening or amputation. Four patients required a change of bushings. The mean Musculoskeletal Tumour Society functional outcome score was 67%, the mean Harris Hip Score was 70, and the mean Oxford Knee Score was 34. Total femoral endoprosthetic replacement can provide good functional outcome without compromising patient survival, and in selected cases provides an effective alternative to amputation.
This study reports on ceramic-on-metal (CoM) bearings in total hip replacement. Whole blood metal ion levels were measured. The median increase in chromium and cobalt at 12 months was 0.08 μg/1 and 0.22 μg/1, respectively, in CoM bearings. Comparable values for metal-on-metal (MoM) were 0.48 μg/1 and 0.32 μg/1. The chromium levels were significantly lower in CoM than in MoM bearings (p = 0.02). The cobalt levels were lower, but the difference was not significant. Examination of two explanted ceramic heads revealed areas of thin metal transfer. CoM bearings (one explanted head and acetabular component, one explanted head and new acetabular component, and three new heads and acetabular components) were tested in a hip joint simulator. The explanted head and acetabular component had higher bedding-in. However, after one million cycles all the wear rates were the same and an order of magnitude less than that reported for MoM bearings. There were four outliers in each clinical group, primarily related to component malposition.
The rate and mode of early failure in 463 Birmingham hip resurfacings in a two-centre, multisurgeon series were examined. Of the 463 patients two have died and three were lost to follow-up. The mean radiological and clinical follow-up was for 43 months (6 to 90). We have revised 13 resurfacings (2.8%) including seven for pain, three for fracture, two for dislocation and another for sepsis. Of these, nine had macroscopic and histological evidence of metallosis. The survival at five years was 95.8% (95% confidence interval (CI) 94.1 to 96.8) for revision for all causes and 96.9% (95% CI 95.5 to 98.3) for metallosis. The rate of metallosis related revision was 3.1% at five years. Risk factors for metallosis were female gender, a small femoral component, a high abduction angle and obesity. We do not advocate the use of the Birmingham Hip resurfacing procedure in patients with these risk factors.
Inflammatory pseudotumours occasionally occur after metal-on-metal hip resurfacing and often lead to revision. Our aim was to determine the severity of this complication by assessing the outcome of revision in these circumstances and by comparing this with the outcome of other metal-on-metal hip resurfacing revisions as well as that of matched primary total hip replacements. We identified 53 hips which had undergone metal-on-metal hip resurfacing and required revision at a mean of 1.59 years (0.01 to 6.69) after operation. Of these, 16 were revised for pseudotumours, 21 for fracture and 16 for other reasons. These were matched by age, gender and diagnosis with 103 patients undergoing primary total hip replacement with the Exeter implant. At a mean follow-up of three years (0.8 to 7.2) the outcome of metal-on-metal hip resurfacing revision for pseudotumour was poor with a mean Oxford hip score of 20.9 ( The outcome of revision for pseudotumour is poor and consideration should be given to early revision to limit the extent of the soft-tissue destruction. The outcome of resurfacing revision for other causes is good.
Wear of polyethylene is associated with aseptic loosening of orthopaedic implants and has been observed in hip and knee prostheses and anatomical implants for the shoulder. The reversed shoulder prostheses have not been assessed as yet. We investigated the volumetric polyethylene wear of the reversed and anatomical Aequalis shoulder prostheses using a mathematical musculoskeletal model. Movement and joint stability were achieved by EMG-controlled activation of the muscles. A non-constant wear factor was considered. Simulated activities of daily living were estimated from After one year of use, the volumetric wear was 8.4 mm3 for the anatomical prosthesis, but 44.6 mm3 for the reversed version. For the anatomical prosthesis the predictions for contact pressure and wear were consistent with biomechanical and clinical data. The abrasive wear of the polyethylene in reversed prostheses should not be underestimated, and further analysis, both experimental and clinical, is required.
We describe the survivorship of the Medial Rotation total knee replacement (TKR) at ten years in 228 cemented primary replacements implanted between October 1994 and October 2006, with their clinical and radiological outcome. This implant has a highly congruent medial compartment, with the femoral component represented by a portion of a sphere which articulates with a matched concave surface on the medial side of the tibial insert. There were 78 men (17 bilateral TKRs) and 111 women (22 bilateral TKRs) with a mean age of 67.9 years (28 to 90). All the patients were assessed clinically and radiologically using the American Knee Society scoring systems. The mean follow-up was for six years (1 to 13) with only two patients lost to follow-up and 34 dying during the period of study, one of whom had required revision for infection. There were 11 revisions performed in total, three for aseptic loosening, six for infection, one for a periprosthetic fracture and one for a painful but well-fixed replacement performed at another centre. With revision for any cause as the endpoint, the survival at ten years was 94.5% (95% CI 85.1 to 100), and with aseptic loosening as the endpoint 98.4% (95% CI 93 to 100). The mean American Knee Society score improved from 47.6 (0 to 88) to 72.2 (26 to 100) and for function from 45.1 (0 to 100) to 93.1 (45 to 100). Radiological review failed to detect migration in any of the surviving knees. The clinical and radiological results of the Medial Rotation TKR are satisfactory at ten years. The increased congruence of the medial compartment has not led to an increased rate of loosening and continued use can be supported.
We describe a technique to salvage a painful hemiarthroplasty due to erosion of the acetabular cartilage in the absence of loosening of the femoral component. A press-fit metallic acetabular component which matched the femoral component was used as a metal-on-metal articulation. The procedure offered a shorter operation time with less blood loss and no risk of femoral fracture as might have occurred during conventional revision to a total hip replacement. The patient made an unremarkable recovery with a good outcome at follow-up of 15 months.
We reviewed 111 hemispherical Duraloc series-500 acetabular components with a minimum follow-up of 12 years. The mean clinical and radiological follow-up was 13.4 years (12 to 15). A Profile hydroxyapatite-coated anatomical femoral component was used in each case. Six patients had a late dislocation, for whom the polyethylene liner was exchanged. Each acetabular component was well fixed and all femoral components showed signs of bone ingrowth. The mean rate of femoral head penetration was 0.10 mm/year (0.021 to 0.481). The probability of not developing femoral cortical hypertrophy and proximal osteopenia by 12 years was 80.2% (95% confidence interval, 72.7 to 87.6) and 77.5% (95% confidence interval, 69.7 to 85.2), respectively. Despite these good clinical results, further follow-up is needed to determine whether these prostheses will loosen with time.
We retrospectively reviewed 35 cemented unicompartmental knee replacements performed for medial unicompartmental osteoarthritis of the knee in 31 patients ≤50 years old (mean 46, 31 to 49). Patients were assessed clinically and radiologically using the Knee Society scores at a mean follow-up of 9.7 years (5 to 16) and survival at 12 years was calculated. The mean Knee Society Function Score improved from 54 points (25 to 64) pre-operatively to 89 (80 to 100) post-operatively (p <
0.0001). Six knees required revision, four for polyethylene wear treated with an isolated exchange of the tibial insert, one for aseptic loosening and one for progression of osteoarthritis. The 12-year survival according to Kaplan-Meier was 80.6% with revision for any reason as the endpoint. Despite encouraging clinical results, polyethylene wear remains a major concern affecting the survival of unicompartmental knee replacement in patients younger than 50.
We describe the findings at six years in an ongoing prospective clinicoradiological and metal ion study in a cohort of 26 consecutive male patients with unilateral Birmingham Hip Resurfacing arthroplasties with one of two femoral head sizes (50 mm and 54 mm). Their mean age was 52.9 years (29 to 67). We have previously shown an early increase in the 24-hour urinary excretion of metal ions, reaching a peak at six months (cobalt) and one year (chromium) after operation. Subsequently there is a decreasing trend in excretion of both cobalt and chromium. The levels of cobalt and chromium in whole blood also show a significant increase at one year, followed by a decreasing trend until the sixth year.
We describe the results of a randomised, prospective study of 200 ankle replacements carried out between March 2000 and July 2003 at a single centre to compare the Buechel-Pappas (BP) and the Scandinavian Total Ankle Replacement (STAR) implant with a minimum follow-up of 36 months. The two prostheses were similar in design consisting of three components with a meniscal polyethylene bearing which was highly congruent on its planar tibial surface and on its curved talar surface. However, the designs were markedly different with respect to the geometry of the articular surface of the talus and its overall shape. A total of 16 ankles (18%) was revised, of which 12 were from the BP group and four of the STAR group. The six-year survivorship of the BP design was 79% (95% confidence interval (CI) 63.4 to 88.5 and of the STAR 95% (95% CI 87.2 to 98.1). The difference did not reach statistical significance (p = 0.09). However, varus or valgus deformity before surgery did have a significant effect) (p = 0.02) on survivorship in both groups, with the likelihood of revision being directly proportional to the size of the angular deformity. Our findings support previous studies which suggested that total ankle replacement should be undertaken with extreme caution in the presence of marked varus or valgus deformity.
We report 17 patients (20 hips) in whom metal-on-metal resurfacing had been performed and who presented with various symptoms and a soft-tissue mass which we termed a pseudotumour. Each patient underwent plain radiography and in some, CT, MRI and ultrasonography were also performed. In addition, histological examination of available samples was undertaken. All the patients were women and their presentation was variable. The most common symptom was discomfort in the region of the hip. Other symptoms included spontaneous dislocation, nerve palsy, a noticeable mass or a rash. The common histological features were extensive necrosis and lymphocytic infiltration. To date, 13 of the 20 hips have required revision to a conventional hip replacement. Two are awaiting revision. We estimate that approximately 1% of patients who have a metal-on-metal resurfacing develop a pseudotumour within five years. The cause is unknown and is probably multifactorial. There may be a toxic reaction to an excess of particulate metal wear debris or a hypersensitivity reaction to a normal amount of metal debris. We are concerned that with time the incidence of these pseudotumours may increase. Further investigation is required to define their cause.
It has been suggested that the wear of ultra-high molecular weight polyethylene (UHMWPE) in total hip replacement is substantially reduced when the femoral head is ceramic rather than metal. However, studies of alumina and zirconia ceramic femoral heads on the penetration of an UHMWPE liner The purpose of this study was to examine the surface characteristics of 30 alumina and 24 zirconia ceramic femoral heads and to identify any phase transformation in the zirconia heads. We also studied the penetration rate of alumina and zirconia heads into contemporary UHMWPE liners. The alumina heads had been implanted for a mean of 11.3 years (8.1 to 16.2) and zirconia heads for a mean of 9.8 years (7.5 to 15). The mean surface roughness values of the explanted alumina heads (Ra 40.12 nm and Rpm 578.34 nm) were similar to those for the explanted zirconia heads (Ra 36.21 nm and Rpm 607.34 nm). The mean value of the monoclinic phase of two control zirconia heads was 1% (0.8% to 1.5%) and 1.2% (0.9% to 1.3%), respectively. The mean value of the monoclinic phase of 24 explanted zirconia heads was 7.3% (1% to 26%). In the alumina group, the mean linear penetration rate of the UMWPE liner was 0.10 mm/yr (0.09 to 0.12) in hips with low Ra and Rpm values (13.22 nm and 85.91 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.13 mm/yr (0.07 to 0.23) in hips with high Ra and Rpm values (198.72 nm and 1329 nm, respectively). This difference was significant (p = 0.041). In the zirconia head group, the mean linear penetration rate of the UHMWPE liner was 0.09 mm/yr (0.07 to 0.14) in hips with low Ra and Rpm values (12.78 nm and 92.99 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.12 mm/yr (0.08 to 0.22) in hips with high Ra and Rpm values (199.21 nm and 1381 nm, respectively). This difference was significant (p = 0.039). The explanted zirconia heads which had a minimal phase transformation had similar surface roughness and a similar penetration rate of UHMWPE liner as the explanted alumina head.