Alumina–alumina bearings are among the most resistant to wear in total hip replacement. Examination of their surfaces is one way of comparing damage caused by wear of hip joints simulated in vitro to that seen in explanted bearings. The aim of this study was to determine whether second-generation ceramic bearings exhibited a better pattern of wear than those reported in the literature for first-generation bearings. We considered both macro- and microscopic findings.

We found that long-term alumina wear in association with a loose acetabular component could be categorised into three groups. Of 20 specimens, four had ‘low wear’, eight ‘crescent wear’ and eight ‘severe wear’, which was characterised by a change in the physical shape of the bearing and a loss of volume. This suggests that the wear in alumina–alumina bearings in association with a loose acetabular component may be variable in pattern, and may explain, in part, why the wear of a ceramic head in vivo may be greater than that seen after in vitro testing.

Osteolysis is due to particulate wear debris and is responsible for the long-term failure of total hip replacements. It has stimulated the development of alternative joint surfaces such as metal-on-metal or ceramic-on-ceramic implants.

Since 1988 the second-generation metal-on-metal implant Metasul has been used in over 60 000 hips. Analysis of 118 retrieved specimens of the head or cup showed rates of wear of approximately 25 μm for the whole articulation per year in the first year, decreasing to about 5 μm per year after the third. Metal surfaces have a ‘self-polishing’ capacity. Scratches are worn out by further joint movement. Volumetric wear was decreased some 60-fold compared with that of metal-on-polyethylene implants, suggesting that second-generation metal-on-metal prostheses may considerably reduce osteolysis.

Aims

This study aims to assess the relationship between history of pseudotumour formation secondary to metal-on-metal (MoM) implants and periprosthetic joint infection (PJI) rate, as well as establish ESR and CRP thresholds that are suggestive of infection in these patients. We hypothesized that patients with a pseudotumour were at increased risk of infection.

Aims

The Exeter V40 femoral stem is the most implanted stem in the National Joint Registry (NJR) for primary total hip arthroplasty (THA). In 2004, the 44/00/125 stem was released for use in ‘cement-in-cement’ revision cases. It has, however, been used ‘off-label’ as a primary stem when patient anatomy requires a smaller stem with a 44 mm offset. We aimed to investigate survival of this implant in comparison to others in the range when used in primary THAs recorded in the NJR.

Aims. To determine ten-year failure rates following 36 mm metal-on-metal (MoM) Pinnacle total hip arthroplasty (THA), and identify predictors of failure. Patients and Methods. We retrospectively assessed a single-centre cohort of 569 primary 36 mm MoM Pinnacle THAs (all Corail stems) followed up since 2012 according to Medicines and Healthcare Products Regulation Agency recommendations. All-cause failure rates (all-cause revision, and non-revised cross-sectional imaging failures) were calculated, with predictors for failure identified using multivariable Cox regression. Results. Failure occurred in 97 hips (17.0%). The ten-year cumulative failure rate was 27.1% (95% confidence interval (CI) 21.6 to 33.7). Primary implantation from 2006 onwards (hazard ratio (HR) 4.30; 95% CI 1.82 to 10.1; p = 0.001) and bilateral MoM hip arthroplasty (HR 1.59; 95% CI 1.03 to 2.46; p = 0.037) predicted failure. The effect of implantation year on failure varied over time. From four years onwards following surgery, hips implanted since 2006 had significantly higher failure rates (eight years 28.3%; 95% CI 23.1 to 34.5) compared with hips implanted before 2006 (eight years 6.3%; 95% CI 2.4 to 15.8) (HR 15.2; 95% CI 2.11 to 110.4; p = 0.007). Conclusion. We observed that 36 mm MoM Pinnacle THAs have an unacceptably high ten-year failure rate, especially if implanted from 2006 onwards or in bilateral MoM hip patients. Our findings regarding implantation year and failure support recent concerns about the device manufacturing process. We recommend all patients undergoing implantation since 2006 and those with bilateral MoM hips undergo regular investigation, regardless of symptoms. Cite this article: Bone Joint J 2017;99-B:592–600

Aims

Several different designs of hemiarthroplasty are used to treat intracapsular fractures of the proximal femur, with large variations in costs. No clinical benefit of modular over monoblock designs has been reported in the literature. Long-term data are lacking. The aim of this study was to report the ten-year implant survival of commonly used designs of hemiarthroplasty.

Aims

The risk of mechanical failure of modular revision hip stems is frequently mentioned in the literature, but little is currently known about the actual clinical failure rates of this type of prosthesis. The current retrospective long-term analysis examines the distal and modular failure patterns of the Prevision hip stem from 18 years of clinical use. A design improvement of the modular taper was introduced in 2008, and the data could also be used to compare the original and the current design of the modular connection.

Aims. There are many guidelines that help direct the management of patients with metal-on-metal (MOM) hip arthroplasties. We have undertaken a study to compare the management of patients with MOM hip arthroplasties in different countries. . Methods. Six international tertiary referral orthopaedic centres were invited to participate by organising a multi-disciplinary team (MDT) meeting, consisting of two or more revision hip arthroplasty surgeons and a musculoskeletal radiologist. A full clinical dataset including history, blood tests and imaging for ten patients was sent to each unit, for discussion and treatment planning. Differences in the interpretation of findings, management decisions and rationale for decisions were compared using quantitative and qualitative methods. Results. Overall agreement between the orthopaedic centres and the recommended treatment plans for the ten patients with MOM hip implants was moderate (kappa = 0.6). Full agreement was seen in a third of cases, however split decisions were also seen in a third of cases. Units differed in their interpretation of the significance of the investigation findings and put varying emphasis on serial changes, in the presence of symptoms. Discussion. In conclusion, the management of raised or rising blood metal ions, cystic pseudotumours and peri-acetabular osteolysis led to inconsistency in the agreement between centres. Coordinated international guidance and MDT panel discussions are recommended to improve consensus in decision making. Take home message: A lack of evidence and the subsequent variation in regulator guidance leads to differences in opinions, the clinical impact of which can be reduced through a multi-disciplinary team approach to managing patients with MOM hip implants. Cite this article: Bone Joint J 2016;98-B:179–86

Aims. The aim of this retrospective audit was to determine the route of referral or presentation of patients requiring revision following primary total hip arthroplasty (THA). Patients and Methods. A total of 4802 patients were implanted with an Orthopaedic Data Evaluation Panel (ODEP) 10A* cementless implant (Corail/Pinnacle) between 2005 and 2015; 80 patients with a mean age of 67.8 years (. sd. 10.8) underwent a subsequent revision. The primary outcome measure was route of referral for revision. Results. Of the 80 revisions, 31 (38.8%) took place within the first year and 69 (86.3%) took place within six years. Only two of the 80 patients were picked up at a routine review clinic, one for infection and the other for liner dissociation. A total of 36 revised patients (45.0%) were reviewed following self-referral. Of the remaining 44 revised patients (55.0%), 15 (18.8%) were General Practitioner referrals, 13 (16.3%) were other hospital referrals, six (7.5%) were inpatients, six (7.5%) were Emergency Department referrals, and two (2.5%) were readmitted from their homes. No revisions were carried out on asymptomatic patients. Conclusion. Our experience suggests that if there is a robust system in place for self-referral, patients with an ODEP 10A* hip implant can, if asymptomatic, be safely discharged at the time of their first postoperative review. Cite this article: Bone Joint J 2019;101-B:536–539

Aims. Despite advances in the treatment of paediatric hip disease, adolescent and young adult patients can develop early onset end-stage osteoarthritis. The aims of this study were to address the indications and medium-term outcomes for total hip arthroplasty (THA) with ceramic bearings for teenage patients. Methods. Surgery was performed by a single surgeon working in the paediatric orthopaedic unit of a tertiary referral hospital. Databases were interrogated from 2003 to 2017 for all teenage patients undergoing THA with a minimum 2.3 year follow-up. Data capture included patient demographics, the underlying hip pathology, number of previous surgeries, and THA prostheses used. Institutional ethical approval was granted to contact patients for prospective clinical outcomes and obtain up-to-date radiographs. In total, 60 primary hips were implanted in 51 patients (35 female, 16 male) with nine bilateral cases. The mean age was 16.7 years (12 to 19) and mean follow-up was 9.3 years (2.3 to 16.8). Results. The most common indication for teenage hip arthroplasty was avascular necrosis secondary to slipped upper femoral epiphysis (31%; n = 16). Overall, 64% of patients (n = 33) had undergone multiple previous operations. The survival at follow-up was 97%; two patients required revision for aseptic loosening (one femoral stem, one acetabular component). Both patients had fused hips noted at the time of arthroplasty. A further two patients had radiolucent lines but were asymptomatic. At latest follow-up the mean Oxford Hip Score was 44 (31 to 48) and a Visual Analogue Scale measurement of 1.5, indicating satisfactory function. Conclusion. Operating on this cohort can be complicated by multiple previous surgeries and distorted anatomy, which in some cases require custom-made prostheses. We have demonstrated a good outcome with low revision rate in this complex group of patients. Cite this article: Bone Joint J 2020;102-B(11):1491–1496

Aims

The aim of this study was to evaluate the performance of first-generation annealed highly cross-linked polyethylene (HXLPE) in cementless total hip arthroplasty (THA).

Aims

The aim of this study was to examine whether socioeconomic status (SES) is associated with a higher risk of infections following total hip arthroplasty (THA) at 30 and 90 days.

Aims

To find out if there is an inverse association between estimated glomerular filtration rate (eGFR) and whole blood cobalt (Co) and chromium (Cr) levels in patients with metal-on-metal (MoM) hip arthroplasties and renal insufficiency, suggesting that renal insufficiency could cause accumulation of Co and Cr in blood.

Aims

The aim of our study was to investigate the effect of asymmetric crosslinked polyethylene liner use on the risk of revision of cementless and hybrid total hip arthroplasties (THAs).

Aims

Aseptic loosening is a leading cause of uncemented arthroplasty failure, often accompanied by fibrotic tissue at the bone-implant interface. A biological target, neutrophil extracellular traps (NETs), was investigated as a crucial connection between the innate immune system’s response to injury, fibrotic tissue development, and proper bone healing. Prevalence of NETs in peri-implant fibrotic tissue from aseptic loosening patients was assessed. A murine model of osseointegration failure was used to test the hypothesis that inhibition (through Pad4^-/- mice that display defects in peptidyl arginine deiminase 4 (PAD4), an essential protein required for NETs) or resolution (via DNase 1 treatment, an enzyme that degrades the cytotoxic DNA matrix) of NETs can prevent osseointegration failure and formation of peri-implant fibrotic tissue.

Aims

Uncemented metal acetabular components show good osseointegration, but material stiffness causes stress shielding and retroacetabular bone loss. Cemented monoblock polyethylene components load more physiologically; however, the cement bone interface can suffer fibrous encapsulation and loosening. It was hypothesized that an uncemented titanium-sintered monoblock polyethylene component may offer the optimum combination of osseointegration and anatomical loading.

Aims

We have previously demonstrated raised cobalt and chromium levels in patients with larger diameter femoral heads, following metal-on-polyethylene uncemented total hip arthroplasty. Further data have been collected, to see whether these associations have altered with time and to determine the long-term implications for these patients and our practice.

We have analysed from the Finnish Arthroplasty Register the long-term survivorship of the 12 most commonly-used cemented implants between 1980 and 2005 in patients aged 55 years or older with osteoarthritis. Only two designs of femoral component, the Exeter Universal and the Müller Straight femoral component had a survivorship of over 95% at ten years with revision for aseptic loosening as the endpoint. At 15 years of the femoral and acetabular component combinations, only the Exeter Universal/Exeter All-poly implant had a survival rate of over 90% with revision for aseptic loosening as the endpoint. In the subgroup of patients aged between 55 and 64 years, survivorship overall was less than 90% at ten years. The variation in the long-term rates of survival of different cemented hip implants was considerable in patients aged 55 years or older. In those aged between 55 and 64 years, none of the cemented prostheses studied yielded excellent long-term survival rates (≥ 90% at 15 years)

Aims

This combined clinical and in vitro study aimed to determine the incidence of liner malseating in modular dual mobility (MDM) constructs in primary total hip arthroplasties (THAs) from a large volume arthroplasty centre, and determine whether malseating increases the potential for fretting and corrosion at the modular metal interface in malseated MDM constructs using a simulated corrosion chamber.

The National Institute for Clinical Excellence (NICE) published the guidelines on the selection of prostheses for primary hip replacement in 2000. They supported the use of cemented hip prostheses to the exclusion of uncemented and hybrid implants. The information from the Trent (and Wales) Regional Arthroplasty Study has been examined to identify retrospectively the types of hip prostheses used between 1990 and 2005, and to assess the impact that the guidelines have had on orthopaedic practice. The results show that the publication of the NICE guidelines has had little impact on clinical practice, with the use of uncemented prostheses increasing from 6.7% (137) in 2001 to 19.2% (632) in 2005. The use of hybrid prostheses has more than doubled from 8.8% (181) to 22% (722) of all hips implanted in the same period. The recommendations made by NICE are not being followed, which calls into question their value