Aims. Head-taper corrosion is a cause of failure in total hip arthroplasty (THA). Recent reports have described an increasing number of V40 taper failures with adverse local tissue reaction (ALTR). However, the real incidence of V40 taper damage and its cause remain unknown. The aim of this study was to evaluate the long-term incidence of ALTR in a consecutive series of THAs using a V40 taper and identify potentially related factors. Methods. Between January 2006 and June 2007, a total of 121 patients underwent THA using either an uncemented (Accolade I, made of Ti. 12. Mo. 6. Zr. 2. Fe; Stryker, USA) or a cemented (ABG II, made of cobalt-chrome-molybdenum (CoCrMo); Stryker) femoral component, both with a V40 taper (Stryker). Uncemented acetabular components (Trident; Stryker) with crosslinked polyethylene liners and CoCr femoral heads of 36 mm diameter were used in all patients. At a mean folllow-up of 10.8 years (SD 1.1), 94 patients (79%) were eligible for follow-up (six patients had already undergone a revision, 15 had died, and six were lost to follow-up). A total of 85 THAs in 80 patients (mean age 61 years (24 to 75); 47 (56%) were female) underwent clinical and radiological evaluation, including the measurement of whole blood levels of cobalt and chrome. Metal artifact reduction sequence MRI scans of the hip were performed in 71 patients. Results. A total of 20 ALTRs were identified on MRI, with an incidence of 26%. Patients with ALTR had significantly higher median Co levels compared with those without ALTR (2.96 μg/l (interquartile range (IQR) 1.35 to 4.98) vs 1.44 μg/l (IQR 0.79 to 2.5); p = 0.019). Radiological evidence of osteolysis was also significantly associated with ALTR (p = 0.014). Median Cr levels were not significantly higher in those with ALTR compared with those without one (0.97 μg/l (IQR 0.72 to 1.9) v 0.67 μg/l (IQR 0.5 to 1.19; p = 0.080). BMI, sex, age, type of femoral component, head length, the inclination of the acetabular component, and heterotopic ossification formation showed no significant relationship with ALTR. Conclusion. Due to the high incidence of local ALTR in our cohort after more than ten years postoperatively, we recommend regular follow-up investigation even in asymptomatic patients with V40 taper and metal heads. As cobalt levels correlate with ALTR occurrence, routine metal ion screening and consecutive MRI investigation upon elevation could be discussed. Cite this article: Bone Joint J 2022;104-B(7):852–858

Aims. Modular dual mobility (DM) prostheses in which a cobalt-chromium liner is inserted into a titanium acetabular shell (vs a monoblock acetabular component) have the advantage of allowing supplementary screw fixation, but the potential for corrosion between the liner and acetabulum has raised concerns. While DM prostheses have shown improved stability in patients deemed ‘high-risk’ for dislocation undergoing total hip arthroplasty (THA), their performance in young, active patients has not been reported. This study’s purpose was to assess clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) in young, active patients receiving a modular DM acetabulum and recently introduced titanium, proximally coated, tapered femoral stem design. Patients and Methods. This was a prospective study of patients between 18 and 65 years of age, with a body mass index (BMI) < 35 kg/m. 2. and University of California at Los Angeles (UCLA) activity score > 6, who received a modular cobalt-chromium acetabular liner, highly crosslinked polyethylene mobile bearing, and cementless titanium femoral stem for their primary THA. Patients with a history of renal disease and metal hardware elsewhere in the body were excluded. A total of 43 patients (30 male, 13 female; mean age 52.6 years (. sd. 6.5)) were enrolled. All patients had a minimum of two years’ clinical follow-up. Patient-reported outcome measures, whole blood metal ion levels (ug/l), and periprosthetic femoral BMD were measured at baseline, as well as at one and two years postoperatively. Power analysis indicated 40 patients necessary to demonstrate a five-fold increase in cobalt levels from baseline (alpha = 0.05, beta = 0.80). A mixed model with repeated measures was used for statistical analysis. Results. Mean Harris Hip Scores improved from 54.1 (. sd. 20.5) to 91.2 (. sd. 10.8) at two years postoperatively (p < 0.001). All patients had radiologically well-fixed components, no patients experienced any instability, and no patients required any further intervention. Mean cobalt levels increased from 0.065 ug/l (. sd. 0.03) preoperatively to 0.30 ug/l (. sd. 0.51) at one year postoperatively (p = 0.01) but decreased at two years postoperatively to 0.16 ug/l (. sd. 0.23; p = 0.2). Four patients (9.3%) had a cobalt level outside the reference range (0.03 ug/l to 0.29 ug/l) at two years postoperatively, with values from 0.32 ug/l to 0.94 ug/l. The mean femoral BMD ratio was maintained in Gruen zones 2 to 7 at both one and two years postoperatively using this stem design. At two years postoperatively, mean BMD in the medial calcar was 101.5% of the baseline value. Conclusion. Use of a modular DM prosthesis and cementless, tapered femoral stem has shown encouraging results in young, active patients undergoing primary THA. Elevation in mean cobalt levels and the presence of four patients outside the reference range at two years postoperatively demonstrates the necessity of continued surveillance in this cohort. Cite this article: Bone Joint J 2019;101-B:365–371

Aims

The aims of this study were to determine if an increasing serum cobalt (Co) and/or chromium (Cr) concentration is correlated with a decreasing Harris Hip Score (HHS) and Hip disability and Osteoarthritis Outcome Score (HOOS) in patients who received the Articular Surface Replacement (ASR) hip resurfacing arthroplasty (HRA), and to evaluate the ten-year revision rate and show if sex, inclination angle, and Co level influenced the revision rate.

Aims . The primary aim of this independent prospective randomised trial was to compare serum metal ion levels for ceramic-on-metal (CoM) and metal-on-metal (MoM) bearing surfaces in total hip arthroplasty (THA). Our one-year results demonstrated elevation in metal ion levels above baseline with no significant difference between the CoM and MoM groups. This paper reviews the five-year data. Patients and Methods. The implants used in each patient differed only in respect to the type of femoral head (ceramic or metal). At five-year follow-up of the 83 enrolled patients, data from 67 (36 CoM, 31 MoM) was available for comparison. Results. The mean serum cobalt (Co) and chromium (Cr) ion levels remained above baseline in both groups (CoM: Co 1.16 μg/l (0.41 to 14.67), Cr 1.05 μg/l (0.16 to 12.58); MoM: Co 2.93 μg/l (0.35 to 30.29), Cr 1.85 μg/l (0.36 to 17.00)) but the increase was significantly less in the CoM cohort (Co difference p = 0.001, Cr difference p = 0.002). These medium-term results, coupled with lower revision rates from national joint registries, suggest that the performance of CoM THA may be superior to that of MoM. . Conclusion. While both bearing combinations have since been withdrawn these results provide useful information for planning clinical surveillance of CoM THAs and warrants continued monitoring. Cite this article: Bone Joint J 2017;99-B:1298–1303

Aims

This study aimed to use intraoperative free electromyography to examine how the placement of a retractor at different positions along the anterior acetabular wall may affect the femoral nerve during total hip arthroplasty (THA) when undertaken using the direct anterior approach (THA-DAA).

Metal-on-metal bearings are being increasingly used in young patients. The potential adverse effects of systemic metal ion elevation are the subject of ongoing investigation. The purpose of this study was to investigate whether cobalt and chromium ions cross the placenta of pregnant women with a metal-on-metal hip resurfacing and reach the developing fetus. Whole blood levels were estimated using high-resolution inductively-coupled plasma mass spectrometry. Our findings showed that cobalt and chromium are able to cross the placenta in the study patients with metal-on-metal hip resurfacings and in control subjects without any metal implants. In the study group the mean concentrations of cobalt and chromium in the maternal blood were 1.39 μg/l (0.55 to 2.55) and 1.28 μg/l (0.52 to 2.39), respectively. The mean umbilical cord blood concentrations of cobalt and chromium were comparatively lower, at 0.839 μg/l (0.42 to 1.75) and 0.378 μg/l (0.14 to 1.03), respectively, and this difference was significant with respect to chromium (p < 0.05). In the control group, the mean concentrations of cobalt and chromium in the maternal blood were 0.341 μg/l (0.18 to 0.54) and 0.199 μg/l (0.12 to 0.33), and in the umbilical cord blood they were 0.336 μg/l (0.17 to 0.5) and 0.194 μg/l (0.11 to 0.56), respectively. The differences between the maternal and umbilical cord blood levels in the controls were marginal, and not statistically significant (p > 0.05). The mean cord blood level of cobalt in the study patients was significantly greater than that in the control group (p < 0.01). Although the mean umbilical cord blood chromium level was nearly twice as high in the study patients (0.378 μg/l) as in the controls (0.1934 μg/l), this difference was not statistically significant. (p > 0.05). The transplacental transfer rate was in excess of 95% in the controls for both metals, but only 29% for chromium and 60% for cobalt in study patients, suggesting that the placenta exerts a modulatory effect on the rate of metal ion transfer

Aims

Dual mobility (DM) implants have been shown to reduce the dislocation rate after total hip arthroplasty (THA), but there remain concerns about the use of cobalt chrome liners inserted into titanium shells. The aim of this study was to assess the clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) at mid-term follow-up in young, active patients receiving a modular DM THA.

Metal-on-metal bearings for total hip replacement (THR) are becoming increasingly popular. Improved wear characteristics mean that these articulations are being inserted into younger patients in the form of THR and resurfacing procedures. This has led to concerns regarding potential carcinogenicity because of the increased exposure to metal ions that the procedure brings. We have studied the serum cobalt and chromium concentrations in patients who had primary, well-fixed Ring metal-on-metal THRs for more than 30 years. The levels of cobalt and chromium were elevated by five and three times, respectively compared with those in our reference groups. Metal-on-metal articulations appear to be the source of metal ions throughout the life of the prosthesis. In three patients who had undergone revision of a previous metal-on-metal THR to a metal-on-polyethylene replacement the levels of metal ions were within the normal range. The elevations of cobalt and chromium ions seen in our study were comparable with those in patients with modern metal-on-metal THRs

As adverse events related to metal on metal hip arthroplasty have been better understood, there has been increased interest in toxicity related to the high circulating levels of cobalt ions. However, distinguishing true toxicity from benign elevations in cobalt levels can be challenging. The purpose of this review is to examine the use of cobalt alloys in total hip arthroplasty, to review the methods of measuring circulating cobalt levels, to define a level of cobalt which is considered pathological and to review the pathophysiology, risk factors and treatment of cobalt toxicity. To the best of our knowledge, there are 18 published cases where cobalt metal ion toxicity has been attributed to the use of cobalt-chromium alloys in hip arthroplasty. Of these cases, the great majority reported systemic toxic reactions at serum cobalt levels more than 100 μg/L. This review highlights some of the clinical features of cobalt toxicity, with the goal that early awareness may decrease the risk factors for the development of cobalt toxicity and/or reduce its severity. Take home message: Severe adverse events can arise from the release of cobalt from metal-on-metal arthroplasties, and as such, orthopaedic surgeons should not only be aware of the presenting problems, but also have the knowledge to treat appropriately. Cite this article: Bone Joint J 2016;98-B:14–20

Aims

The direct anterior approach (DAA) for total hip arthroplasty (THA) has potential advantages over other approaches and is most commonly performed with the patient in the supine position. We describe a technique for DAA THA with the patient in the lateral decubitus position and report the early clinical and radiological outcomes, the characteristics of the learning curve, and perioperative complications.

We reviewed the outcome of curved intertrochanteric varus osteotomy in the treatment of osteonecrosis of the femoral head in 20 hips. A mean varus angulation of 31° was obtained by the osteotomy. The ratio of intact area on the weight-bearing portion increased from 19% to 61%. The mean elevation and lateral displacement of the greater trochanter were 1.2 cm and 0.5 cm, respectively. These changes in the position of the greater trochanter were very small when compared with those after conventional varus wedge osteotomy. Nonunion or delayed union was not observed. Quantitative analyses showed aggressive bone remodelling in the medial intertrochanteric region. Eighteen hips survived without collapse after a mean follow-up of 48 months. We conclude that curved varus osteotomy can be used to preserve the hip joint in patients with osteonecrosis of the femoral head

Aims

To establish whether there was a consensus among the members of the Hip Society (HS) on the role of direct anterior approach (DAA) contemporary primary total hip arthroplasty (THA).

Aims

Modular dual-mobility constructs reduce the risk of dislocation after revision total hip arthroplasty (THA). However, questions about metal ions from the cobalt-chromium (CoCr) liner persist, and are particularly germane to patients being revised for adverse local tissue reactions (ALTR) to metal. We determined the early- to mid-term serum Co and Cr levels after modular dual-mobility components were used in revision and complex primary THAs, and specifically included patients revised for ALTR.

Aims

We previously reported the long-term results of the cementless Duraloc-Profile total hip arthroplasty (THA) system in a 12- to 15-year follow-up study. In this paper, we provide an update on the clinical and radiological results of a previously reported cohort of patients at 23 to 26 years´ follow-up.

Aims

To report our experience with trunnion corrosion following metal-on-polyethylene total hip arthroplasty, in particular to report the spectrum of presentation and determine the mean time to presentation.

The early failure and revision of bimodular primary total hip arthroplasty prostheses requires the identification of the risk factors for material loss and wear at the taper junctions through taper wear analysis. Deviations in taper geometries between revised and pristine modular neck tapers were determined using high resolution tactile measurements. A new algorithm was developed and validated to allow the quantitative analysis of material loss, complementing the standard visual inspection currently used.

The algorithm was applied to a sample of 27 retrievals (in situ from 2.9 to 38.1 months) of the withdrawn Rejuvenate modular prosthesis. The mean wear volumes on the flat distal neck piece taper was 3.35 mm³ (0.55 to 7.57), mainly occurring in a characteristic pattern in areas with high mechanical loading. Wear volume tended to increase with time to revision (r² = 0.423, p = 0.001). Implant and patient specific data (offset, stem size, patient’s mass, age and body mass index) did not correlate with the amount of material loss observed (p >  0.078). Bilaterally revised implants showed higher amounts of combined total material loss and similar wear patterns on both sides. The consistent wear pattern found in this study has not been reported previously, suggesting that the device design and materials are associated with the failure of this prosthesis.

Cite this article: Bone Joint J 2015;97-B:1350–7.

Adverse reaction to wear and corrosion debris is a cause for concern in total hip arthroplasty (THA). Modular junctions are a potential source of such wear products and are associated with secondary pseudotumour formation.

We present a consecutive series of 17 patients treated at our unit for this complication following metal-on-highly cross-linked polyethylene (MoP) THA. We emphasise the risk of misdiagnosis as infection, and present the aggregate laboratory results and pathological findings in this series.

The clinical presentation was pain, swelling or instability. Solid, cystic and mixed soft-tissue lesions were noted on imaging and confirmed intra-operatively. Corrosion at the head–neck junction was noted in all cases. No bacteria were isolated on multiple pre- and intra-operative samples yet the mean erythrocyte sedimentation rate was 49 (9 to 100) and C-reactive protein 32 (0.6 to 106) and stromal polymorphonuclear cell counts were noted in nine cases.

Adverse soft–tissue reactions can occur in MoP THA owing to corrosion products released from the head–neck junction. The diagnosis should be carefully considered when investigating pain after THA. This may avoid the misdiagnosis of periprosthetic infection with an unidentified organism and mitigate the unnecessary management of these cases with complete single- or two-stage exchange.

Cite this article: Bone Joint J 2015;97-B:1024–1030.

The custom triflange is a patient-specific implant for the treatment of severe bone loss in revision total hip arthroplasty (THA). Through a process of three-dimensional modelling and prototyping, a hydroxyapatite-coated component is created for acetabular reconstruction. There are seven level IV studies describing the clinical results of triflange components. The most common complications include dislocation and infection, although the rates of implant removal are low. Clinical results are promising given the challenging problem. We describe the design, manufacture and implantation process and review the clinical results, contrasting them to other methods of acetabular reconstruction in revision THA.

Cite this article: Bone Joint J 2016;98-B(1 Suppl A):68–72.

Aims

The primary aim of this study was to analyse the position of the acetabular and femoral components in total hip arthroplasty undertaken using an anterior surgical approach.

Sciatic nerve palsy following total hip arthroplasty (THA) is a relatively rare yet potentially devastating complication. The purpose of this case series was to report the results of patients with a sciatic nerve palsy who presented between 2000 and 2010, following primary and revision THA and were treated with neurolysis. A retrospective review was made of 12 patients (eight women and four men), with sciatic nerve palsy following THA. The mean age of the patients was 62.7 years (50 to 72; standard deviation 6.9). They underwent interfascicular neurolysis for sciatic nerve palsy, after failing a trial of non-operative treatment for a minimum of six months. Following surgery, a statistically and clinically significant improvement in motor function was seen in all patients. The mean peroneal nerve score function improved from 0.42 (0 to 3) to 3 (1 to 5) (p < 0.001). The mean tibial nerve motor function score improved from 1.75 (1 to 4) to 3.92 (3 to 5) (p = 0.02).The mean improvement in sensory function was a clinically negligible 1 out of 5 in all patients. In total, 11 patients reported improvement in their pain following surgery.

We conclude that neurolysis of the sciatic nerve has a favourable prognosis in patients with a sciatic nerve palsy following THA. Our findings suggest that surgery should not be delayed for > 12 months following injury.

Cite this article: Bone Joint J 2015;97-B:1345–9